Huntsman KRYSTALFLEX® PE 900 Polyurethane Optical Aliphatic Film price 2588 per MT

Mechanical Properties
Tensile Strength at Break
35.2 MPa
Elongation at Break
760 %
100% Modulus
0.00345 GPa
300% Modulus
0.0214 GPa
Tear Strength
50.8 kN/m

Processing Properties
Melt Temperature
90.0 - 140 °C

Alternative products

Dow Engage® ENR 7380.00 Ethylene-Butene Copolymer accurate 99%

$ 1643/MT

Density: 0.870 g/cc
Viscosity: 3.60e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
Viscosity: 1.10e+7 cP @Shear Rate 10.0 1/s, Temperature 190 °C
Viscosity: 1.80e+7 cP @Shear Rate 1.58 1/s, Temperature 190 °C
Viscosity: 2.83e+7 cP @Shear Rate 0.100 1/s, Temperature 190 °C

Multibase Multi-Flex® TPE A 6221 LA BLK accurate 99%

$ 1520/MT

Density: 1.17 g/cc
Linear Mold Shrinkage: 0.014 cm/cm
Linear Mold Shrinkage, Transverse: 0.011 cm/cm
Hardness, Shore A: 43
Tensile Strength, Ultimate: >= 5.17 MPa

Lubrizol ESTANE® GP80AE Ester Based Thermoplastic Polyurethane (European Grade) accurate 99%

$ 2159/MT

Specific Gravity: 1.22 g/cc
Hardness, Shore A: 80
Hardness, Shore D: 30
Tensile Strength, Ultimate: 35.0 MPa
Elongation at Break: 760 %

Mearthane Durethaneâ„¢ F DF-255A Closed Cell Foam Polyurethane accurate 99%

$ 2128/MT

Density: 0.880 g/cc
Hardness, Shore A: 55
Tensile Strength, Ultimate: 72.4 MPa
Elongation at Break: 760 %
100% Modulus: 0.00110 GPa

ExxonMobil Escorene® LD-402 LDPE Electrical Jacketing Resin (discontinued **) accurate 99%

$ 1501/MT

Density: 0.917 g/cc
Environmental Stress Crack Resistance: <= 5.0 hour
Melt Flow: 12 g/10 min
Hardness, Shore D: 48
Tensile Strength, Ultimate: 9.00 MPa

Arkema Group OREVAC® 18334 Grafted Maleic Anhydride Polyethylene accurate 99%

$ 2111/MT

Density: 0.920 g/cc @Temperature 23.0 °C
Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore D: 45
Tensile Strength at Break: 30.0 MPa
Tensile Strength, Yield: 4.50 MPa

UBE UMERIT 2500F Metallocene LLDPE accurate 99%

$ 1927/MT

Density: 0.923 g/cc
Environmental Stress Crack Resistance: 1000 hour
Melt Flow: 4.0 g/10 min
Hardness, Shore D: 56
Tensile Strength, Yield: 36.0 MPa

Dow Engage® ENR 7467.00 Ethylene-Butene Copolymer accurate 99%

$ 1651/MT

Density: 0.862 g/cc
Viscosity: 2.06e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
Viscosity: 4.20e+6 cP @Shear Rate 10.0 1/s, Temperature 190 °C
Viscosity: 5.59e+6 cP @Shear Rate 1.58 1/s, Temperature 190 °C
Viscosity: 6.58e+6 cP @Shear Rate 0.100 1/s, Temperature 190 °C

Kraiburg TPE THERMOLAST® K TP7CCN Natural Cable Extrusion TPE accurate 99%

$ 1587/MT

Density: 1.15 g/cc
Hardness, Shore A: 70
Tensile Strength at Break: 10.5 MPa
Elongation at Break: 760 %
Tear Strength: 18.0 kN/m

Polymax® Maxelast® A9860 TPE, ABS/PC Overmold accurate 99%

$ 1563/MT

Specific Gravity: 1.15 g/cc
Hardness, Shore A: 60 @Time 10.0 sec
Tensile Stress: 2.03 MPa @Strain 100 %
Tensile Stress: 3.24 MPa @Strain 300 %
Tensile Strength, Yield: 8.00 MPa
Elongation at Break: 760 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Huntsman KRYSTALFLEX® PE 900 Polyurethane Optical Aliphatic Film

Seller from Bangkok – 2021-04-25:

Seller from Bangkok work with company: Solvay, Techmer ES, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2588 per MT