Kaiser 7068 T6, T6511 Rod & Bar price 2312 per MT

Physical Properties
Density
2.85 g/cc

Mechanical Properties
Hardness, Brinell
190 @Load 500 kg, Thickness 10.0 mm
Tensile Strength, Ultimate
710 MPa @Diameter 12.7 mm
Tensile Strength, Yield
683 MPa @Diameter 12.7 mm
Elongation at Break
9.0 % @Diameter 12.7 mm
Fracture Toughness
16.482 MPa-m½
Fracture Toughness
27.471 MPa-m½
Shear Strength
365 MPa

Thermal Properties
CTE, linear
23.4 µm/m-°C @Temperature 20.0 - 100 °C
Specific Heat Capacity
1.05 J/g-°C @Temperature 100 °C
Thermal Conductivity
190 W/m-K @Temperature 20.0 °C
Melting Point
476 - 635 °C
Solidus
476 °C
Liquidus
635 °C

Component Elements Properties
Aluminum, Al
85.48 - 88.85 %
Chromium, Cr
<= 0.050 %
Copper, Cu
1.6 - 2.4 %
Iron, Fe
<= 0.15 %
Magnesium, Mg
2.2 - 3.0 %
Manganese, Mn
<= 0.10 %
Other, each
<= 0.050 %
Other, total
<= 0.15 %
Silicon, Si
<= 0.12 %
Titanium, Ti
<= 0.10 %
Zinc, Zn
7.3 - 8.3 %
Zirconium, Zr
0.050 - 0.15 %

Electrical Properties
Electrical Resistivity
0.00000494 ohm-cm @Temperature 20.0 °C

Descriptive Properties
Anodize Response3
B
Arc Weldability4
D
Brazeability4
D
Cold Workability3
D
Gas Weldability4
D
General Corrosion Resistance1
C
Machinability3
C
Spot Weldability4
B
Stress Corrosion Resistance2
C
Volumetric CTE mÂ³/mÂ³-K
0.000068

Alternative products

Alcoa 7055-T77511 Aluminum Extrusions accurate 82%

$ 1847/MT

Density: 2.86 g/cc
Tensile Strength, Ultimate: 634 MPa @Thickness 25.4 mm
Tensile Strength, Ultimate: 641 MPa @Thickness 25.4 mm
Tensile Strength, Yield: 614 MPa @Thickness 25.4 mm
Tensile Strength, Yield: 614 MPa @Thickness 25.4 mm

Kazanorgsintez Bisphenol A, Diphenylpropane accurate 99%

$ 2323/MT

Crystallization Temperature: >= 154 °C
Crystallization Temperature: >= 155 °C
Crystallization Temperature: >= 156.4 °C
Crystallization Temperature: >= 156.6 °C
Crystallization Temperature: >= 156.7 °C

Kaiser 6040 T8 Rod & Bar accurate 82%

$ 1769/MT

Hardness, Rockwell B: 62
Tensile Strength, Ultimate: 324 MPa @Diameter 12.7 mm
Tensile Strength, Yield: 303 MPa @Diameter 12.7 mm
Elongation at Break: 14 % @Diameter 12.7 mm
Shear Strength: 207 MPa

Indium Corp. Germanium Corporation® GeCl4 Germanium Tetrachloride accurate 99%

$ 1866/MT

Specific Gravity: 1.875 g/cc @Temperature 20.0 °C
Molecular Weight: 214.45 g/mol
Vapor Pressure: 0.101 bar @Temperature 20.0 °C
Boiling Point: 83.0 °C
Aluminum, Al: <= 1.0e-7 %

Aleris 55HX® Aluminum (5005-H14) accurate 82%

$ 2348/MT

Density: 2.70 g/cc
Tensile Strength, Ultimate: 145 - 185 MPa @Thickness 0.200 - 1.50 mm
Tensile Strength, Ultimate: 145 - 185 MPa @Thickness 1.50 - 3.00 mm
Tensile Strength, Ultimate: 145 - 185 MPa @Thickness 3.00 - 5.00 mm
Tensile Strength, Yield: >= 120 MPa @Strain 0.200 %, Thickness 0.200 - 1.50 mm

Kaiser 7068 T76, T76511 Rod & Bar accurate 82%

$ 1535/MT

Density: 2.85 g/cc
Hardness, Brinell: 170 @Load 500 kg, Thickness 10.0 mm
Tensile Strength, Ultimate: 614 MPa @Diameter 12.7 mm
Tensile Strength, Yield: 572 MPa @Diameter 12.7 mm
Elongation at Break: 9.0 % @Diameter 12.7 mm

Kaiser 6040 T6, T651 Rod & Bar accurate 82%

$ 1478/MT

Tensile Strength, Ultimate: 324 MPa @Diameter 12.7 mm
Tensile Strength, Yield: 296 MPa @Diameter 12.7 mm
Elongation at Break: 15 % @Diameter 12.7 mm
Aluminum, Al: 93.75 - 98.15 %
Bismuth, Bi: 0.15 - 0.70 %

Alcoa 7055-T7751 Aluminum Plate accurate 82%

$ 1813/MT

Density: 2.86 g/cc
Tensile Strength, Ultimate: 627 MPa @Thickness 25.4 mm
Tensile Strength, Ultimate: 669 MPa @Thickness 25.4 mm
Tensile Strength, Yield: 614 MPa @Thickness 25.4 mm
Tensile Strength, Yield: 655 MPa @Thickness 25.4 mm

Alcoa 2090-T83 Aluminum accurate 82%

$ 1655/MT

Density: 2.59 g/cc
Tensile Strength, Ultimate: >= 441 MPa @Thickness 3.17 mm
Tensile Strength, Ultimate: >= 503 MPa @Thickness 3.17 mm
Tensile Strength, Ultimate: >= 531 MPa @Thickness 3.17 mm
Tensile Strength, Yield: >= 386 MPa @Thickness 3.17 mm

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 99%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Kaiser 7068 T6, T6511 Rod & Bar

Seller from Madrid – 2021-05-14:

Seller from Madrid work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2312 per MT