Kazanorgsintez PE2NT75-15 High Density Polyethylene for Blow Molding price 1573 per MT

Physical Properties
Density
0.950 - 0.956 g/cc @Temperature 23.0 °C
Density
0.952 - 0.958 g/cc @Temperature 20.0 °C
Environmental Stress Crack Resistance
>= 30 hour
Melt Flow
1.8 - 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength, Yield
>= 26.0 MPa
Elongation at Break
>= 750 %
Tear Strength Test
>= 30

Alternative products

BASF Ultramid® 8254 HS BK-102 PA6 (Conditioned) accurate 99%

$ 1760/MT

Density: 1.07 g/cc
Water Absorption: 1.2 %
Water Absorption: 7.1 %
Moisture Absorption at Equilibrium: 2.0 %
Linear Mold Shrinkage: 0.013 cm/cm

LG Chemical SEETEC PB270 HDPE accurate 66%

$ 1587/MT

Specific Gravity: 0.953 - 0.956 g/cc
Environmental Stress Crack Resistance: >= 30 hour
Melt Flow: 0.30 - 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 26.5 MPa
Elongation at Break: >= 800 % @Thickness 50.0 mm

Petromont 5000 High Density Polyethylene Resin accurate 66%

$ 1833/MT

Density: 0.955 g/cc
ESCR 100% Igepal®: 30 hour
Melt Flow: 0.30 g/10 min
Melt Flow: 28 g/10 min
Hardness, Shore D: 65

DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin accurate 66%

$ 2294/MT

Density: 0.941 g/cc
Vinyl Acetate Content: 18 %
Melt Index of Compound: 2.5 g/10 min
Hardness, Shore A: 90
Hardness, Shore D: 39

DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin accurate 66%

$ 1520/MT

Density: 0.933 g/cc
Vinyl Acetate Content: 12 %
Melt Index of Compound: 2.5 g/10 min
Hardness, Shore A: 95
Hardness, Shore D: 44

Equate EMDA-6147 HDPE Blow Molding Resin accurate 66%

$ 2047/MT

Density: 0.952 g/cc
ESCR 100% Igepal®: 1000 hour @Temperature 50.0 °C
Melt Flow: 0.070 g/10 min @Load 2.16 kg
High Load Melt Index: 9.0 g/10 min @Load 21.6 kg
Tensile Strength, Ultimate: 35.0 MPa

Equate EPDA-5040 HDPE Non-Pressure Gravity Pipe Resin accurate 66%

$ 1564/MT

Density: 0.952 g/cc
ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
High Load Melt Index: 10 g/10 min @Load 21.0 kg
Tensile Strength, Ultimate: 35.0 MPa
Tensile Strength, Yield: 26.0 MPa

Kazanorgsintez PE2NT76-17 High Density Polyethylene for Blow Molding accurate 99%

$ 1560/MT

Density: 0.955 - 0.961 g/cc @Temperature 23.0 °C
Density: 0.957 - 0.963 g/cc @Temperature 20.0 °C
Volatiles: <= 0.0000090 %
Environmental Stress Crack Resistance: >= 30 hour
Melt Flow: 2.3 - 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C

ExxonMobil PP7033N Impact Copolymer accurate 66%

$ 1746/MT

Density: 0.900 g/cc
Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength, Yield: 25.8 MPa
Tensile Strength, Yield: 25.9 MPa
Elongation at Yield: 4.0 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Kazanorgsintez PE2NT75-15 High Density Polyethylene for Blow Molding

Seller from Luanda – 2021-04-20:

Seller from Luanda work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1573 per MT