LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)  (Unverified Data**)

Seller in Toronto price: $2333 per MT

LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)  (Unverified Data**) in Polymer, Thermoplastic, Polyphenylene Ether/PPO, Polyphenylene Ether, 20% Glass Filled

  • Physical Properties
  • Density
  • 1.23 g/cc
  • Water Absorption
  • 0.050 %
  • Linear Mold Shrinkage
  • 0.0040 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0040 cm/cm
  • Mechanical Properties
  • Hardness, Rockwell M
  • 93
  • Tensile Strength, Ultimate
  • 98.0 MPa
  • Tensile Strength, Ultimate
  • 50.0 MPa @Temperature 120 °C
  • Tensile Strength, Ultimate
  • 70.0 MPa @Temperature 90.0 °C
  • Tensile Strength, Ultimate
  • 85.0 MPa @Temperature 60.0 °C
  • Flexural Modulus
  • 6.00 GPa
  • Flexural Modulus
  • 4.00 GPa @Temperature 120 °C
  • Flexural Modulus
  • 5.00 GPa @Temperature 90.0 °C
  • Flexural Modulus
  • 5.70 GPa @Temperature 60.0 °C
  • Izod Impact, Notched
  • 0.550 J/cm @Temperature -40.0 °C
  • Izod Impact, Notched
  • 0.550 J/cm @Temperature -20.0 °C
  • Izod Impact, Notched
  • 0.700 J/cm @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature -20.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature -40.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • CTE, linear
  • 40.0 µm/m-°C @Temperature 20.0 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 132 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 125 °C
  • Vicat Softening Point
  • 132 °C
  • Flammability, UL94
  • V-1 @Thickness 1.50 mm
  • Flammability, UL94
  • V-0 @Thickness 6.00 mm
  • Oxygen Index
  • 31 %
  • Glow Wire Test
  • 960 °C @Thickness 2.00 mm
  • Electrical Properties
  • Dielectric Strength
  • 22.0 kV/mm @Thickness 2.00 mm
  • Comparative Tracking Index
  • 250 V
  • Processing Properties
  • Melt Temperature
  • 260 - 280 °C
  • Mold Temperature
  • 80.0 - 100 °C
  • Drying Temperature
  • 100 - 110 °C
  • Dry Time
  • >= 3 hour
  • Descriptive Properties
  • Heat Resistance - Ball Test (125°C)
  • Y
  • Heat Resistance - Ball Test (165°C)
  • N
  • Injection Speed
  • medium
  • Needle Burner Test
  • Y
  • Needle Burner Test
  • Y

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ship sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)  (Unverified Data**)

Seller from Toronto – 2021-06-18:

Seller from Toronto work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2333 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)  (Unverified Data**)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Arborist and tree surgeon in Singapore open-nearme.com