Lehmann & Voss LUVOCOM® 80/TF/18/SI/2/BK Polyacetal-copolymer, with PTFE, lubricant modified price 2201 per MT

Physical Properties
Specific Gravity
1.49 g/cc
Water Absorption
<= 0.10 %
Linear Mold Shrinkage
0.018 - 0.025 cm/cm

Mechanical Properties
Tensile Stress
40.0 MPa
Elongation at Yield
15 %
Elongation at Yield
18 %
Modulus of Elasticity
2.00 GPa
Flexural Strength
60.0 MPa
Flexural Modulus
1.80 GPa
Charpy Impact Unnotched
6.00 J/cm²
Charpy Impact Unnotched
5.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
1.20 J/cm²
Charpy Impact, Notched
1.10 J/cm² @Temperature -30.0 °C
Coefficient of Friction, Dynamic
0.11
Coefficient of Friction, Static
0.060

Thermal Properties
CTE, linear
90.0 µm/m-°C
Thermal Conductivity
0.200 W/m-K
Maximum Service Temperature, Air
100 °C
Maximum Service Temperature, Air
120 °C
Deflection Temperature at 1.8 MPa (264 psi)
95.0 °C
Vicat Softening Point
160 °C

Electrical Properties
Insulation Resistance
>= 1.00e+12 ohm

Processing Properties
Processing Temperature
200 °C
Nozzle Temperature
175 - 200 °C
Zone 1
175 - 190 °C
Zone 2
185 - 205 °C
Zone 3
180 - 200 °C
Mold Temperature
80.0 - 120 °C
Drying Temperature
75.0 °C @Time 7200 - 28800 sec
Drying Temperature
120 °C @Time 7200 - 14400 sec

Descriptive Properties
Color
black

Alternative products

Lehmann & Voss LUVOCOM® 80-8318-1 Polyacetal-copolymer, with PTFE, easy flowing accurate 55%

$ 2090/MT

Specific Gravity: 1.46 g/cc
Water Absorption: 0.15 %
Linear Mold Shrinkage: 0.018 - 0.026 cm/cm
Melt Flow: >= 58.4 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Stress: 50.0 MPa

Lehmann & Voss LUVOCOM® 80-8162 Polyacetal-copolymer, lubricant modified accurate 55%

$ 1553/MT

Specific Gravity: 1.39 g/cc
Water Absorption: <= 0.10 %
Linear Mold Shrinkage: 0.018 - 0.030 cm/cm
Tensile Stress: 48.0 MPa
Elongation at Yield: 20 %

Lehmann & Voss LUVOCOM® 80/TF/22/NT Polyacetal-copolymer, with PTFE accurate 71%

$ 2416/MT

Specific Gravity: 1.49 g/cc
Water Absorption: 0.15 %
Linear Mold Shrinkage: 0.016 - 0.022 cm/cm
Tensile Stress: 45.0 MPa
Elongation at Yield: 10 %

Lehmann & Voss LUVOCOM® 80/TF/18/NT Polyacetal-copolymer, with PTFE accurate 71%

$ 1501/MT

Specific Gravity: 1.48 g/cc
Water Absorption: 0.15 %
Linear Mold Shrinkage: 0.016 - 0.022 cm/cm
Tensile Stress: 46.0 MPa
Elongation at Yield: 10 %

Lehmann & Voss LUVOCOM® 80-0837-1 Polyacetal-copolymer, with PTFE, lubricant modified accurate 51%

$ 1807/MT

Specific Gravity: 1.43 g/cc
Water Absorption: <= 0.10 %
Linear Mold Shrinkage: 0.018 - 0.030 cm/cm
Melt Flow: 24.31 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Stress: 44.0 MPa

Lehmann & Voss LUVOCOM® 80/TF/18/SI/2 Polyacetal-copolymer, with PTFE, lubricant modified accurate 91%

$ 1535/MT

Specific Gravity: 1.49 g/cc
Water Absorption: <= 0.10 %
Linear Mold Shrinkage: 0.018 - 0.025 cm/cm
Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Stress: 45.0 MPa

Lehmann & Voss LUVOCOM® 80-8268 Polyacetal-copolymer, with PTFE, lubricant modified accurate 55%

$ 2315/MT

Specific Gravity: 1.44 g/cc
Water Absorption: <= 0.10 %
Linear Mold Shrinkage: 0.018 - 0.025 cm/cm
Tensile Stress: 45.0 MPa
Elongation at Yield: 15 %

Lehmann & Voss LUVOCOM® 80-7919 Polyacetal-copolymer, with PTFE, easy flowing accurate 55%

$ 1694/MT

Specific Gravity: 1.49 g/cc
Water Absorption: 0.15 %
Linear Mold Shrinkage: 0.018 - 0.026 cm/cm
Melt Flow: 49.17 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Stress: 45.0 MPa

Lehmann & Voss LUVOCOM® 80-7655/RD Polyacetal-copolymer, with aramid reinforcement and PTFE, toughness-modified, high viscosity accurate 55%

$ 2599/MT

Specific Gravity: 1.46 g/cc
Water Absorption: <= 0.10 %
Linear Mold Shrinkage: 0.015 - 0.021 cm/cm
Tensile Stress: 40.0 MPa
Elongation at Yield: 8.0 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, freighters for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Lehmann & Voss LUVOCOM® 80/TF/18/SI/2/BK Polyacetal-copolymer, with PTFE, lubricant modified

Seller from Dhaka – 2021-05-15:

Seller from Dhaka work with company: RTP Company, PolyOne Corporation, Parker Chomerics, SABIC Innovative Plastics (GE Plastics)

Price: $2567 per MT

Seller from Ho Chi Minh City – 2021-05-25:

Seller from Ho Chi Minh City work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2527 per MT

Seller from Khartoum – 2021-04-02:

Seller from Khartoum work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2201 per MT