LG Chemical HIPS 406AF PS, Flame Retardant

Seller in Saint Petersburg price: $2142 per MT

LG Chemical HIPS 406AF PS, Flame Retardant in Polymer, Thermoplastic, Flame Retardant, Polystyrene (PS), Polystyrene

  • Physical Properties
  • Specific Gravity
  • 1.10 g/cc
  • Maximum Moisture Content
  • 0.010
  • Linear Mold Shrinkage, Flow
  • 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
  • Melt Flow
  • 11 g/10 min @Load 5.00 kg, Temperature 200 °C
  • Mechanical Properties
  • Hardness, Rockwell R
  • 103
  • Tensile Strength, Yield
  • 32.4 MPa @Thickness 3.20 mm
  • Elongation at Break
  • 50 % @Thickness 3.20 mm
  • Elongation at Yield
  • >= 5.0 % @Thickness 3.20 mm
  • Flexural Yield Strength
  • 52.0 MPa @Thickness 3.20 mm
  • Flexural Modulus
  • 2.45 GPa @Thickness 3.20 mm
  • Izod Impact, Notched
  • 0.392 J/cm @Thickness 3.20 mm, Temperature -30.0 °C
  • Izod Impact, Notched
  • 0.392 J/cm @Thickness 6.40 mm, Temperature -30.0 °C
  • Izod Impact, Notched
  • 0.490 J/cm @Thickness 6.40 mm, Temperature 23.0 °C
  • Izod Impact, Notched
  • 0.785 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
  • Thermal Properties
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 85.0 °C @Thickness 6.40 mm
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 79.0 °C @Thickness 6.40 mm
  • Vicat Softening Point
  • 85.0 °C @Load 5.00 kg
  • UL RTI, Electrical
  • 50.0 °C @Thickness >=1.50 mm
  • UL RTI, Electrical
  • 50.0 °C @Thickness >=2.50 mm
  • UL RTI, Electrical
  • 50.0 °C @Thickness >=3.00 mm
  • UL RTI, Mechanical with Impact
  • 50.0 °C @Thickness >=1.50 mm
  • UL RTI, Mechanical with Impact
  • 50.0 °C @Thickness >=2.50 mm
  • UL RTI, Mechanical with Impact
  • 50.0 °C @Thickness >=3.00 mm
  • UL RTI, Mechanical without Impact
  • 50.0 °C @Thickness >=1.50 mm
  • UL RTI, Mechanical without Impact
  • 50.0 °C @Thickness >=2.50 mm
  • UL RTI, Mechanical without Impact
  • 50.0 °C @Thickness >=3.00 mm
  • Flammability, UL94
  • V-2 @Thickness >=1.50 mm
  • Flammability, UL94
  • V-2 @Thickness >=2.50 mm
  • Flammability, UL94
  • V-2 @Thickness >=3.00 mm
  • Processing Properties
  • Rear Barrel Temperature
  • 180 - 200 °C
  • Middle Barrel Temperature
  • 190 - 200 °C
  • Front Barrel Temperature
  • 200 - 210 °C
  • Nozzle Temperature
  • 200 - 230 °C
  • Melt Temperature
  • 200 - 230 °C
  • Mold Temperature
  • 40.0 - 60.0 °C
  • Drying Temperature
  • 60.0 - 70.0 °C
  • Dry Time
  • 3.00 - 4.00 hour
  • Back Pressure
  • 29.4 - 58.8 MPa
  • Screw Speed
  • 30 - 60 rpm

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for LG Chemical HIPS 406AF PS, Flame Retardant

Seller from Saint Petersburg – 2021-03-05:

Seller from Saint Petersburg work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2142 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell LG Chemical HIPS 406AF PS, Flame Retardant?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Training school in Singapore open-nearme.com