LG Chemical HT700 ABS, High Stiffness price 1702 per MT

Physical Properties
Specific Gravity
1.05 g/cc
Maximum Moisture Content
0.010
Linear Mold Shrinkage, Flow
0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
Melt Flow
20 g/10 min @Load 10.0 kg, Temperature 220 °C

Mechanical Properties
Hardness, Rockwell R
113
Tensile Strength, Yield
53.0 MPa @Thickness 3.20 mm
Elongation at Break
>= 10 % @Thickness 3.20 mm
Tensile Modulus
2.38 GPa @Thickness 3.20 mm
Flexural Yield Strength
86.3 MPa @Thickness 3.20 mm
Flexural Modulus
2.79 GPa @Thickness 3.20 mm
Izod Impact, Notched
1.96 J/cm @Thickness 6.40 mm, Temperature 23.0 °C
Izod Impact, Notched
2.16 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
Izod Impact, Unnotched
0.588 J/cm @Thickness 3.20 mm, Temperature -30.0 °C
Izod Impact, Unnotched
0.785 J/cm @Thickness 6.40 mm, Temperature -30.0 °C

Thermal Properties
Deflection Temperature at 1.8 MPa (264 psi)
87.0 °C @Thickness 6.40 mm
Deflection Temperature at 1.8 MPa (264 psi)
90.0 °C @Thickness 6.40 mm
Vicat Softening Point
95.0 °C @Load 5.00 kg
UL RTI, Electrical
60.0 °C @Thickness >=1.50 mm
UL RTI, Electrical
60.0 °C @Thickness >=3.00 mm
UL RTI, Mechanical with Impact
60.0 °C @Thickness >=1.50 mm
UL RTI, Mechanical with Impact
60.0 °C @Thickness >=3.00 mm
UL RTI, Mechanical without Impact
60.0 °C @Thickness >=1.50 mm
UL RTI, Mechanical without Impact
60.0 °C @Thickness >=3.00 mm
Flammability, UL94
HB @Thickness >=1.50 mm
Flammability, UL94
HB @Thickness >=3.00 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Dielectric Strength
35.0 kV/mm
Arc Resistance
120 - 180 sec
Comparative Tracking Index
>= 600 V
Hot Wire Ignition, HWI
7.0 - 15 sec @Thickness >=1.50 mm
Hot Wire Ignition, HWI
15 - 30 sec @Thickness >=3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR
25.4 - 50.0 mm/min

Processing Properties
Rear Barrel Temperature
180 - 200 °C
Middle Barrel Temperature
190 - 210 °C
Front Barrel Temperature
200 - 220 °C
Nozzle Temperature
200 - 230 °C
Melt Temperature
210 - 240 °C
Mold Temperature
40.0 - 70.0 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Back Pressure
29.4 - 58.8 MPa
Screw Speed
30 - 60 rpm

Alternative products

ChevronTexaco 46 Heat Transfer Oil accurate 72%

$ 2438/MT

Specific Gravity: 0.3215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

ChevronTexaco Texatherm® accurate 81%

$ 1472/MT

Specific Gravity: 0.6215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

LG Chemical HG173 ABS, High Surface Gloss accurate 72%

$ 1544/MT

Specific Gravity: 1.05 g/cc
Maximum Moisture Content: 0.010
Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Rockwell R: 110

ACC QM 2128 QSI Quantum Silicones 28 Durometer Condensation Cure Moldmaking Material accurate 72%

$ 1508/MT

Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.13 g/cc

ACC QM 2125 QSI Quantum Silicones 25 Durometer Condensation Cure Moldmaking Material accurate 72%

$ 1692/MT

Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.13 g/cc
Specific Gravity: 1.13 g/cc

LG Chemical PT270 ABS accurate 72%

$ 1703/MT

Specific Gravity: 1.04 g/cc
Maximum Moisture Content: 0.010
Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
Melt Flow: 28 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Rockwell R: 100

LG Chemical HI100 ABS, High Impact accurate 72%

$ 1748/MT

Specific Gravity: 1.02 g/cc
Maximum Moisture Content: 0.010
Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Rockwell R: 92

ChevronTexaco 22 Heat Transfer Oil accurate 72%

$ 2024/MT

Specific Gravity: 0.6083 g/cc
Specific Gravity: 0.655 g/cc
Specific Gravity: 0.6916 g/cc
Specific Gravity: 0.729 g/cc
Specific Gravity: 0.7658 g/cc

LG Chemical HI100K ABS, High Impact accurate 72%

$ 1613/MT

Specific Gravity: 1.04 g/cc
Maximum Moisture Content: 0.010
Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Rockwell R: 97

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for LG Chemical HT700 ABS, High Stiffness

Seller from Shanghai – 2021-07-15:

Seller from Shanghai work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2526 per MT

Seller from Melbourne – 2021-06-08:

Seller from Melbourne work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2414 per MT

Seller from Tianjin – 2021-08-09:

Seller from Tianjin work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1702 per MT

Seller from Jakarta – 2021-06-28:

Seller from Jakarta work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1718 per MT