LG Chemical KEYFLEX BT 1140D Ester Type TPE price 1693 per MT

Physical Properties
Specific Gravity
1.12 g/cc
Water Absorption
0.70 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight
458.458 g/mol
Maximum Moisture Content
0.010
Maximum Moisture Content
0.010
Linear Mold Shrinkage, Flow
0.0060 - 0.010 cm/cm @Thickness 3.20 mm
Melt Flow
12 g/10 min @Load 2.16 kg, Temperature 200 °C

Mechanical Properties
Hardness, Shore A
90
Hardness, Shore D
36
Tensile Strength at Break
25.5 MPa @Thickness 2.00 mm
Elongation at Break
750 % @Thickness 2.00 mm
Flexural Modulus
0.0588 GPa @Thickness 6.40 mm
Izod Impact, Notched
NB @Thickness 6.40 mm, Temperature 23.0 °C
Izod Impact, Notched
NB @Thickness 6.40 mm, Temperature -40.0 °C
Tear Strength
118 kN/m

Thermal Properties
Melting Point
170 °C
Boiling Point
140 - 230 °C
UL RTI, Electrical
50.0 °C @Thickness >=1.50 mm
UL RTI, Electrical
50.0 °C @Thickness >=3.00 mm
UL RTI, Mechanical with Impact
50.0 °C @Thickness >=1.50 mm
UL RTI, Mechanical with Impact
50.0 °C @Thickness >=3.00 mm
UL RTI, Mechanical without Impact
50.0 °C @Thickness >=1.50 mm
UL RTI, Mechanical without Impact
50.0 °C @Thickness >=3.00 mm
Flammability, UL94
HB @Thickness >=1.50 mm
Flammability, UL94
HB @Thickness >=3.00 mm
Flash Point
300 - 340 °C

Electrical Properties
Volume Resistivity
>= 1.00e+13 ohm-cm
Dielectric Strength
26.0 kV/mm @Thickness 1.00 mm
Arc Resistance
120 - 180 sec
Comparative Tracking Index
600 V
Hot Wire Ignition, HWI
30 - 60 sec @Thickness >=1.50 mm
Hot Wire Ignition, HWI
60 - 120 sec @Thickness >=3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR
10.0 - 25.4 mm/min

Processing Properties
Rear Barrel Temperature
180 - 200 °C
Middle Barrel Temperature
190 - 210 °C
Front Barrel Temperature
200 - 220 °C
Nozzle Temperature
200 - 220 °C
Zone 1
180 - 220 °C
Zone 2
180 - 200 °C
Zone 3
200 - 220 °C
Zone 4
200 - 220 °C
Adapter Temperature
200 - 220 °C
Die Temperature
190 - 230 °C
Melt Temperature
180 - 220 °C
Melt Temperature
180 - 220 °C
Mold Temperature
10.0 - 35.0 °C
Drying Temperature
80.0 - 90.0 °C
Drying Temperature
80.0 - 90.0 °C
Dry Time
3.00 - 4.00 hour
Dry Time
3.00 - 4.00 hour

Alternative products

LG Chemical KEYFLEX BT 1055D Ester Type TPE accurate 70%

$ 2305/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 1047D Ester Type TPE accurate 63%

$ 1469/MT

Specific Gravity: 1.17 g/cc
Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 1045D Ester Type TPE accurate 63%

$ 1822/MT

Specific Gravity: 1.14 g/cc
Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 3140D Ester Type TPE accurate 63%

$ 1617/MT

Specific Gravity: 1.16 g/cc
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010
Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C

LG Chemical KEYFLEX BT 1040D Ester Type TPE accurate 70%

$ 1649/MT

Specific Gravity: 1.13 g/cc
Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 1063D Ester Type TPE accurate 63%

$ 2035/MT

Specific Gravity: 1.23 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 1172D Ester Type TPE accurate 63%

$ 1671/MT

Specific Gravity: 1.25 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 1163D Ester Type TPE accurate 63%

$ 1652/MT

Specific Gravity: 1.21 g/cc
Water Absorption: 0.50 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

LG Chemical KEYFLEX BT 1155D Ester Type TPE accurate 63%

$ 2189/MT

Specific Gravity: 1.18 g/cc
Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
Molecular Weight: 458.458 g/mol
Maximum Moisture Content: 0.010
Maximum Moisture Content: 0.010

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, general cargo ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for LG Chemical KEYFLEX BT 1140D Ester Type TPE

Seller from Lagos – 2021-03-27:

Seller from Lagos work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2002 per MT

Seller from Manila – 2021-06-24:

Seller from Manila work with company: 3M, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1693 per MT

Seller from Dhaka – 2021-05-04:

Seller from Dhaka work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2119 per MT