LG Chemical Lupoy 1261-03 Polycarbonate Resin price 1486 per MT

Physical Properties
Specific Gravity
1.20 g/cc
Water Absorption
0.32 % @Temperature 23.0 °C
Water Absorption
0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.00050 - 0.00070 cm/cm
Melt Flow
2.5 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell M
74
Hardness, Rockwell R
118
Tensile Strength, Ultimate
72.0 MPa
Tensile Strength, Yield
60.0 MPa
Elongation at Break
150 %
Elongation at Yield
6.0 %
Tensile Modulus
2.41 GPa
Flexural Yield Strength
96.0 MPa
Flexural Modulus
2.41 GPa
Izod Impact, Notched
9.608 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
Izod Impact, Unnotched
NB @Temperature 23.0 °C
Dart Drop, Total Energy
94.0 J @Thickness 3.20 mm
Abrasion
45 @Load 1.00 kg

Thermal Properties
CTE, linear
68.0 µm/m-°C @Temperature -40.0 - 82.0 °C
Hot Ball Pressure Test
>= 125 °C
Deflection Temperature at 0.46 MPa (66 psi)
146 °C @Thickness 4.00 mm
Deflection Temperature at 1.8 MPa (264 psi)
132 °C @Thickness 4.00 mm
Deflection Temperature at 1.8 MPa (264 psi)
143 °C @Thickness 4.00 mm
Vicat Softening Point
151 °C @Load 5.10 kg
Softening Point
150 - 200 °C
Flash Point
>= 450 °C
Oxygen Index
26 %
Glow Wire Test
850 °C @Thickness 2.00 mm, Time 5.00 sec

Optical Properties
Refractive Index
1.586
Haze
0.70 - 1.5 %
Transmission, Visible
89 %

Electrical Properties
Volume Resistivity
2.00e+17 ohm-cm
Dielectric Constant
3.0 @Frequency 60.0 Hz
Dielectric Strength
17.0 kV/mm
Dissipation Factor
0.0010 @Frequency 60.0 Hz
Comparative Tracking Index
250 V @Thickness 2.00 mm

Descriptive Properties
Autoignition Temperature
>450°C
Average Extent of Burning
ASTM D635

Alternative products

LG Chemical Lupoy 1201-08 Polycarbonate Resin accurate 99%

$ 1501/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1201-10 Polycarbonate Resin accurate 99%

$ 1865/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1302-07 Polycarbonate Resin accurate 99%

$ 1885/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1300-03 Polycarbonate Resin accurate 99%

$ 1612/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1302UV-08 Polycarbonate Resin accurate 99%

$ 2061/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1301V-7 Polycarbonate Resin accurate 99%

$ 1468/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1201-05 Polycarbonate Resin accurate 99%

$ 1481/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1302-05 Polycarbonate Resin accurate 99%

$ 2174/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1200-08 Polycarbonate Resin accurate 99%

$ 2186/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, small cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for LG Chemical Lupoy 1261-03 Polycarbonate Resin

Seller from Boston – 2021-03-06:

Seller from Boston work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2090 per MT

Seller from Moscow – 2021-03-04:

Seller from Moscow work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1486 per MT