LG Chemical Lupoy 1303EP-22 Polycarbonate Resin price 1516 per MT

Physical Properties
Specific Gravity
1.20 g/cc
Water Absorption
0.32 % @Temperature 23.0 °C
Water Absorption
0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.00050 - 0.00070 cm/cm
Melt Flow
22 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell M
72
Hardness, Rockwell R
118
Tensile Strength, Ultimate
66.0 MPa
Tensile Strength, Yield
60.0 MPa
Elongation at Break
120 %
Elongation at Yield
6.0 %
Tensile Modulus
2.34 GPa
Flexural Yield Strength
96.0 MPa
Flexural Modulus
2.41 GPa
Izod Impact, Notched
7.47 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
Izod Impact, Unnotched
NB @Temperature 23.0 °C
Dart Drop, Total Energy
72.0 J @Thickness 3.20 mm
Abrasion
45 @Load 1.00 kg

Thermal Properties
CTE, linear
68.0 µm/m-°C @Temperature -40.0 - 82.0 °C
Hot Ball Pressure Test
>= 125 °C
Deflection Temperature at 0.46 MPa (66 psi)
142 °C @Thickness 4.00 mm
Deflection Temperature at 1.8 MPa (264 psi)
126 °C @Thickness 4.00 mm
Deflection Temperature at 1.8 MPa (264 psi)
139 °C @Thickness 4.00 mm
Vicat Softening Point
147 °C @Load 5.10 kg
Softening Point
150 - 200 °C
UL RTI, Electrical
120 °C @Thickness >=1.50 mm
UL RTI, Electrical
120 °C @Thickness >=3.00 mm
UL RTI, Mechanical with Impact
105 °C @Thickness >=1.50 mm
UL RTI, Mechanical with Impact
110 °C @Thickness >=3.00 mm
UL RTI, Mechanical without Impact
120 °C @Thickness >=1.50 mm
UL RTI, Mechanical without Impact
120 °C @Thickness >=3.00 mm
Flammability, UL94
V-2 @Thickness 1.50 mm
Flammability, UL94
V-2 @Thickness 3.00 mm
Flash Point
>= 450 °C
Oxygen Index
26 %
Glow Wire Test
850 °C @Thickness 2.00 mm, Time 5.00 sec

Optical Properties
Refractive Index
1.586
Haze
0.70 - 1.5 %
Transmission, Visible
89 %

Electrical Properties
Volume Resistivity
2.00e+17 ohm-cm
Dielectric Constant
3.0 @Frequency 60.0 Hz
Dielectric Strength
17.0 kV/mm
Dissipation Factor
0.0010 @Frequency 60.0 Hz
Arc Resistance
120 - 180 sec
Comparative Tracking Index
250 V @Thickness 2.00 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness >=1.50 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness >=3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR
25.4 - 50.0 mm/min

Descriptive Properties
Autoignition Temperature
>450°C
Average Extent of Burning
ASTM D635

Alternative products

LG Chemical Lupoy 1302HP-22 Polycarbonate Resin accurate 95%

$ 2244/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1201HP-22 Polycarbonate Resin accurate 95%

$ 2002/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1301EP-22 Polycarbonate Resin accurate 99%

$ 2028/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1201-22 Polycarbonate Resin accurate 99%

$ 1938/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1201HP-21 Polycarbonate Resin accurate 95%

$ 2009/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 21 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1200-22 Polycarbonate Resin accurate 95%

$ 2399/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1303-15 Polycarbonate Resin accurate 91%

$ 1612/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1301EP22 Polycarbonate Resin accurate 99%

$ 1604/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy 1200-15 Polycarbonate Resin accurate 91%

$ 1704/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship for sale in india. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for LG Chemical Lupoy 1303EP-22 Polycarbonate Resin

Seller from Chengdu – 2021-03-11:

Seller from Chengdu work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1516 per MT

Seller from Luanda – 2021-03-01:

Seller from Luanda work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2462 per MT

Seller from Rangoon – 2021-03-25:

Seller from Rangoon work with company: 3M, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2520 per MT