LG Chemical Lupoy NF1009F 08R Polycarbonate Resin price 1683 per MT

Physical Properties
Specific Gravity
1.20 g/cc
Water Absorption
0.32 % @Temperature 23.0 °C
Water Absorption
0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.00050 - 0.00070 cm/cm
Melt Flow
8.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell M
73
Tensile Strength, Ultimate
72.0 MPa
Tensile Strength, Yield
60.0 MPa
Elongation at Break
150 %
Elongation at Yield
6.0 %
Tensile Modulus
2.41 GPa
Flexural Yield Strength
96.0 MPa
Flexural Modulus
2.41 GPa
Izod Impact, Notched
9.074 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
Izod Impact, Unnotched
NB @Temperature 23.0 °C
Dart Drop, Total Energy
89.0 J @Thickness 3.20 mm
Abrasion
45 @Load 1.00 kg

Thermal Properties
CTE, linear
68.0 µm/m-°C @Temperature -40.0 - 82.0 °C
Hot Ball Pressure Test
>= 125 °C
Deflection Temperature at 0.46 MPa (66 psi)
138 °C @Thickness 4.00 mm
Deflection Temperature at 1.8 MPa (264 psi)
126 °C @Thickness 4.00 mm
Vicat Softening Point
147 °C @Load 5.10 kg
Softening Point
150 - 200 °C
UL RTI, Electrical
130 °C @Thickness >=0.750 mm
UL RTI, Electrical
130 °C @Thickness >=1.50 mm
UL RTI, Electrical
130 °C @Thickness >=2.00 mm
UL RTI, Electrical
130 °C @Thickness >=3.00 mm
UL RTI, Mechanical with Impact
110 °C @Thickness >=0.750 mm
UL RTI, Mechanical with Impact
110 °C @Thickness >=1.50 mm
UL RTI, Mechanical with Impact
110 °C @Thickness >=2.00 mm
UL RTI, Mechanical with Impact
110 °C @Thickness >=3.00 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=0.750 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=1.50 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=2.00 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=3.00 mm
Flammability, UL94
V-2 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 2.00 mm
Flammability, UL94
V-0 @Thickness 3.00 mm
Flash Point
>= 450 °C
Oxygen Index
35 %
Glow Wire Test
850 °C @Thickness 2.00 mm, Time 5.00 sec

Optical Properties
Refractive Index
1.586
Haze
0.70 - 1.5 %
Transmission, Visible
89 %

Electrical Properties
Volume Resistivity
2.00e+17 ohm-cm
Dielectric Constant
3.0 @Frequency 60.0 Hz
Dielectric Strength
17.0 kV/mm
Dissipation Factor
0.0010 @Frequency 60.0 Hz
Arc Resistance
0.00 - 60 sec
Comparative Tracking Index
250 V @Thickness 2.00 mm
Hot Wire Ignition, HWI
15 - 30 sec @Thickness >=1.50 mm
Hot Wire Ignition, HWI
15 - 30 sec @Thickness >=2.00 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness >=3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 2.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Descriptive Properties
Autoignition Temperature
>450°C

Alternative products

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 2242/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1909/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1775/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1480/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1525/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1448/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1482/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1009F 15 Polycarbonate Resin accurate 90%

$ 1836/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

LG Chemical Lupoy NF1007F 10R Polycarbonate Resin accurate 95%

$ 1531/MT

Specific Gravity: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, used lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for LG Chemical Lupoy NF1009F 08R Polycarbonate Resin

Seller from Guadalajara – 2021-06-14:

Seller from Guadalajara work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2511 per MT

Seller from Chennai – 2021-08-18:

Seller from Chennai work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1883 per MT

Seller from Moscow – 2021-03-29:

Seller from Moscow work with company: 3M, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1683 per MT

Seller from Santiago – 2021-04-06:

Seller from Santiago work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1690 per MT