LNP Thermocomp® EF-1006 BK8-114 Polyetherimide, Glass Fiber Reinforcement (discontinued **) price 1474 per MT

Physical Properties
Specific Gravity
1.52 g/cc
Water Absorption
0.10 %
Linear Mold Shrinkage
0.0020 cm/cm
Linear Mold Shrinkage, Transverse
0.0050 cm/cm

Mechanical Properties
Tensile Strength at Break
188 MPa
Tensile Strength, Yield
188 MPa
Elongation at Break
2.4 %
Elongation at Yield
2.4 %
Tensile Modulus
11.4 GPa
Flexural Strength
269 MPa
Flexural Modulus
11.4 GPa
Izod Impact, Notched (ISO)
10.5 kJ/m²
Izod Impact, Unnotched (ISO)
48.7 kJ/m²
Falling Dart Impact
12.4 J
Impact Test
2.64 J
Coefficient of Friction, Dynamic
0.55
Coefficient of Friction, Static
0.50
K (wear) Factor
262 x 10 mm³/N-M

Thermal Properties
Deflection Temperature at 1.8 MPa (264 psi)
204 °C

Processing Properties
Melt Temperature
360 - 366 °C
Mold Temperature
121 - 149 °C
Drying Temperature
121 - 149 °C
Dry Time
4 hour
Moisture Content
0.020 %
Back Pressure
0.345 - 0.689 MPa

Descriptive Properties
Color
Black

Alternative products

Celanese FORTRON 1131L4 ITT PPS, 30% Glass Reinforced (Unverified Data**) accurate 72%

$ 2078/MT

Specific Gravity: 1.40 g/cc
Specific Gravity: 1.41 g/cc
Density: 1.40 g/cc
Density: 1.56 g/cc
Water Absorption: 0.020 %

LNP Thermocomp® JF-1006 Polyethersulfone, Glass Fiber Reinforcement (discontinued **) accurate 72%

$ 2269/MT

Specific Gravity: 1.58 g/cc
Water Absorption: 0.30 %
Linear Mold Shrinkage: 0.0030 cm/cm
Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
Tensile Strength at Break: 143 MPa

LNP Lubricomp® UFL-4036 HS Polyphthalamide, Glass Fiber Reinforced, PTFE Lubricant (discontinued **) accurate 72%

$ 1759/MT

Specific Gravity: 1.55 g/cc
Density: 1.55 g/cc
Water Absorption: 0.30 %
Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Celanese FORTRON 1342L4 PPS, 40% Specialty (Unverified Data**) accurate 79%

$ 1491/MT

Specific Gravity: 1.70 g/cc
Density: 1.69 g/cc
Water Absorption: 0.020 %
Water Absorption: 0.020 %
Thickness: 3180 microns

LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement (discontinued **) accurate 72%

$ 1500/MT

Specific Gravity: 1.31 g/cc
Water Absorption: 0.30 %
Linear Mold Shrinkage: 0.0020 cm/cm
Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
Tensile Strength at Break: 161 MPa

LNP Lubricomp® EFL-4036 UFE Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **) accurate 72%

$ 1564/MT

Specific Gravity: 1.62 g/cc
Density: 1.62 g/cc
Water Absorption: 0.10 %
Linear Mold Shrinkage: 0.0020 cm/cm
Linear Mold Shrinkage, Transverse: 0.0050 cm/cm

Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA) (Unverified Data**) accurate 72%

$ 1937/MT

Density: 1.45 g/cc
Filler Content: 35 %
Water Absorption: 0.29 % @Temperature 23.0 °C, Time 86400 sec
Water Absorption: 0.30 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 cm/cm

LNP Lubricomp® QFL-4036 BK8-115 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant (disconti accurate 72%

$ 1824/MT

Specific Gravity: 1.46 g/cc
Density: 1.46 g/cc
Water Absorption: 0.10 %
Linear Mold Shrinkage: 0.0020 cm/cm
Linear Mold Shrinkage, Transverse: 0.0070 - 0.0080 cm/cm

LNP Thermocomp® UF-1006 A HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **) accurate 72%

$ 2067/MT

Specific Gravity: 1.45 g/cc
Water Absorption: 0.20 %
Linear Mold Shrinkage: 0.0020 cm/cm
Linear Mold Shrinkage, Transverse: 0.010 cm/cm
Tensile Strength at Break: 183 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for LNP Thermocomp® EF-1006 BK8-114 Polyetherimide, Glass Fiber Reinforcement (discontinued **)

Seller from Alexandria – 2021-05-05:

Seller from Alexandria work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1628 per MT

Seller from Istanbul – 2021-05-13:

Seller from Istanbul work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2005 per MT

Seller from Hong Kong – 2021-06-10:

Seller from Hong Kong work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2147 per MT

Seller from Dhaka – 2021-04-21:

Seller from Dhaka work with company: 3M, Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics)

Price: $1474 per MT

Seller from London – 2021-07-27:

Seller from London work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1604 per MT