M. Holland Company MAGMA® LM112-K LLDPE (discontinued **) price 1937 per MT

Physical Properties
Density
0.913 g/cc
Thickness
31.8 microns
Melt Flow
1.0 g/10 min

Mechanical Properties
Film Elongation at Break, MD
520 %
Film Elongation at Break, TD
710 %
Elmendorf Tear Strength MD
390 g
Elmendorf Tear Strength TD
750 g
Dart Drop Test
380 g
Film Tensile Strength at Break, MD
36.9 MPa
Film Tensile Strength at Break, TD
19.3 MPa

Thermal Properties
Melting Point
104 °C

Processing Properties
Feed Temperature
<= 149 °C
Zone 1
149 °C
Melt Temperature
182 - 232 °C
Die Opening
0.0810 - 0.254 cm
Blow-up Ratio (BUR)
1.5 - 3.0

Descriptive Properties
Form
Pellets

Alternative products

LyondellBasell Petrothene® NA373244 Low Density Polyethylene, Cast/Blown Film Grade accurate 99%

$ 1457/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 6000 ppm

LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade accurate 99%

$ 1612/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 0.000 ppm

ExxonMobil Escorene® LD-317 EVA Film Resin, FMI (discontinued **) accurate 99%

$ 1468/MT

Density: 0.928 g/cc
Thickness: 31.8 microns
Melt Flow: 0.30 g/10 min
Film Tensile Strength at Yield, MD: 8.20 MPa
Film Tensile Strength at Yield, TD: 6.80 MPa

ExxonMobil Escorene® LD-307 EVA Film Resin, Clarity, High Impact (discontinued **) accurate 66%

$ 1613/MT

Density: 0.926 g/cc
Thickness: 31.8 microns
Melt Flow: 2.0 g/10 min
Film Tensile Strength at Yield, MD: 7.60 MPa
Film Tensile Strength at Yield, TD: 6.90 MPa

ExxonMobil Optema® TC-110 Blown Ethylene Methyl Acrylate accurate 66%

$ 1606/MT

Density: 0.942 g/cc
Methyl Acrylate Content: 21.5 %
Thickness: 31.8 microns
Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Elongation at Break, MD: 370 %

ExxonMobil Escorene® LD-334 EVA Film Resin, Clarity, High Impact (discontinued **) accurate 66%

$ 1728/MT

Density: 0.925 g/cc
Thickness: 31.8 microns
Melt Flow: 1.3 g/10 min
Film Tensile Strength at Yield, MD: 8.60 MPa
Film Tensile Strength at Yield, TD: 8.60 MPa

ExxonMobil Escorene® LD-303 EVA Film Resin, Clarity, High Impact (discontinued **) accurate 99%

$ 1725/MT

Density: 0.925 g/cc
Thickness: 31.8 microns
Melt Flow: 1.3 g/10 min
Film Tensile Strength at Yield, MD: 8.90 MPa
Film Tensile Strength at Yield, TD: 8.30 MPa

ExxonMobil Escorene® LD-302 EVA Film Resin, High Clarity, High Impact (discontinued **) accurate 99%

$ 1561/MT

Density: 0.925 g/cc
Thickness: 31.8 microns
Melt Flow: 1.3 g/10 min
Film Tensile Strength at Yield, MD: 8.30 MPa
Film Tensile Strength at Yield, TD: 8.90 MPa

Celanese Ateva® 1061 Ethylene Vinyl Acetate Copolymer Film (discontinued **) accurate 99%

$ 1686/MT

Density: 0.925 g/cc
Vinyl Acetate Content: 6.0 %
Thickness: 31.0 microns
Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, MD: 10.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tanker ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for M. Holland Company MAGMA® LM112-K LLDPE (discontinued **)

Seller from Lima – 2021-07-27:

Seller from Lima work with company: SABIC Innovative Plastics (GE Plastics), BASF, Braskem, ALIMEX GmbH

Price: $1937 per MT