Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film price 1558 per MT

Physical Properties
Density
1.40 g/cc @Temperature 23.0 °C
Water Absorption
0.50 % @Temperature 23.0 °C
Linear Mold Shrinkage
0.010 cm/cm @Temperature 150 °C, Time 900 sec
Linear Mold Shrinkage, Transverse
0.0030 cm/cm @Temperature 150 °C, Time 900 sec

Mechanical Properties
Film Tensile Strength at Yield, MD
150 MPa
Film Tensile Strength at Yield, TD
200 MPa
Film Elongation at Break, MD
>= 200 %
Film Elongation at Break, TD
140 %
Modulus of Elasticity
3.60 GPa @Temperature 23.0 °C
Modulus of Elasticity
4.30 GPa @Temperature 23.0 °C
Coefficient of Friction, Static
0.40

Optical Properties
Haze
25 %

Electrical Properties
Dielectric Constant
2.9 @Frequency 2.40e+8 Hz, Temperature 23.0 °C
Dielectric Constant
2.9 @Frequency 9.30e+9 Hz, Temperature 23.0 °C
Dielectric Constant
3.2 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Constant
3.3 @Frequency 50.0 Hz, Temperature 23.0 °C
Dielectric Constant
3.3 @Frequency 1000 Hz, Temperature 23.0 °C
Dielectric Constant
3.6 @Frequency 50.0 Hz, Temperature 150 °C
Dielectric Strength
450 kV/mm @Temperature 23.0 °C
Dielectric Strength
135 kV/mm @Frequency 50.0 Hz, Temperature 150 °C
Dielectric Strength
150 kV/mm @Frequency 50.0 Hz, Temperature 23.0 °C

Descriptive Properties
Conductivity of Aqueous Extract (ÂµS/cm)
2
F5-value (MPa)
105
F5-value (MPa)
105
Frigen Extract (%)
0.05
Trichloroethylene- Extract (%)
0.2

Alternative products

DuPont Elvaloy® 3108 AC Ethylene and 7% Butyl Acrylate Copolymer (discontinued **) accurate 49%

$ 2171/MT

Density: 0.924 g/cc
Thickness: 40.0 microns
Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, MD: 8.00 MPa
Film Tensile Strength at Yield, TD: 7.00 MPa

ExxonMobil LDPE LD 368HD Low Density Polyethylene Resin accurate 49%

$ 1506/MT

Density: 0.924 g/cc
Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Antiblock Level: 1800 ppm
Slip Level: 650 ppm
Film Elongation at Break, MD: 200 %

ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity (discontinued **) accurate 49%

$ 2191/MT

Density: 0.925 g/cc
Thickness: 31.8 microns
Melt Flow: 2.0 g/10 min
Film Tensile Strength at Yield, MD: 9.70 MPa
Film Tensile Strength at Yield, TD: 11.0 MPa

Iran Petrochemical (PCC) 2101TN47 Low Density Polyethylene accurate 49%

$ 1633/MT

Density: 0.921 g/cc
Melt Flow: 0.85 g/10 min
Film Tensile Strength at Yield, MD: 12.0 MPa
Film Tensile Strength at Yield, TD: 11.0 MPa
Film Elongation at Break, MD: >= 200 %

DuPont Teijin Films Melinex® 725 Polyester Film accurate 49%

$ 1805/MT

Film Tensile Strength at Yield, MD: 89.6 MPa
Film Tensile Strength at Yield, TD: 89.6 MPa
Film Elongation at Break, MD: 200 %
Film Elongation at Break, TD: 120 %
Coefficient of Friction, Dynamic: 0.40

ExxonMobil LD 146.NH Packaging Film Resin (discontinued **) accurate 49%

$ 1899/MT

Density: 0.920 g/cc
Thickness: 38.1 microns
Melt Flow: 3.75 g/10 min
Antiblock Level: 1200 ppm
Slip Level: 900 ppm

LyondellBasell Petrothene® NA960070 Low Density Polyethylene accurate 49%

$ 1827/MT

Density: 0.919 g/cc
Thickness: 31.8 microns
Melt Flow: 0.90 g/10 min
Tensile Strength at Break: 14.5 MPa
Film Elongation at Break, MD: 200 %

DuPont Teijin Films Melinex® 561 Polyester Film accurate 49%

$ 1482/MT

Film Tensile Strength at Yield, MD: 96.5 MPa
Film Tensile Strength at Yield, TD: 96.5 MPa
Film Elongation at Break, MD: 200 %
Film Elongation at Break, TD: 120 %
Coefficient of Friction, Dynamic: 0.50

Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous accurate 99%

$ 2085/MT

Specific Gravity: 1.26 g/cc @Temperature 23.0 °C
Moisture Absorption at Equilibrium: 0.21 % @Temperature 23.0 °C, Time 86400 sec
Film Elongation at Break, MD: >= 200 %
Film Elongation at Break, MD: >= 200 % @Thickness 0.0250 mm
Film Elongation at Break, MD: >= 200 % @Thickness 0.0250 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Seller from Madrid – 2021-07-18:

Seller from Madrid work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1834 per MT

Seller from Luanda – 2021-06-11:

Seller from Luanda work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2402 per MT

Seller from Baghdad – 2021-08-18:

Seller from Baghdad work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1558 per MT

Seller from Cairo – 2021-05-16:

Seller from Cairo work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co.

Price: $1835 per MT