NOVA Chemicals Sclair® 8406 BK, 8406 GBK MDPE Rotational Molding Resin (discontinued **) price 2216 per MT

Physical Properties
Density
0.943 g/cc
Environmental Stress Crack Resistance
300 hour
Melt Flow
3.7 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Hardness, Shore D
57
Tensile Strength, Yield
18.8 MPa
Elongation at Break
>= 1000 %
Flexural Modulus
0.620 GPa

Thermal Properties
Vicat Softening Point
112 °C

Processing Properties
Melt Temperature
170 - 215 °C

Alternative products

SABIC Innovative Plastics LNP THERMOCOMP DX07350 PC (Asia Pacific) accurate 66%

$ 1758/MT

Specific Gravity: 1.29 g/cc
Density: 1.29 g/cc
Moisture Absorption: 0.0500 %
Water Absorption at Saturation: 0.090 %
Linear Mold Shrinkage, Flow: 0.0035 - 0.0045 cm/cm @Thickness 3.20 mm

NOVA Chemicals Sclair® 8406 UV8D, 8406G UV8D MDPE Rotational Molding Resin (discontinued **) accurate 99%

$ 1855/MT

Density: 0.936 g/cc
Environmental Stress Crack Resistance: 300 hour
Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore D: 57
Tensile Strength, Yield: 18.8 MPa

ExxonMobil Paxon™ BC50-100 Sheet Extrusion and Blow Molding Resin (discontinued **) accurate 32%

$ 1472/MT

Density: 0.949 g/cc
ESCR 100% Igepal®: >= 800 hour
Melt Flow: 10 g/10 min
Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 26.2 MPa

Dow DOWLEX™ 2245D Linear Low Density Polyethylene, Heavy Duty Film Grade accurate 32%

$ 1829/MT

Density: 0.920 g/cc
Thickness: 25.0 microns
Melt Flow: 1.0 g/10 min @Load 2.16 kg
Tensile Strength, Ultimate: 26.2 MPa
Film Tensile Strength at Yield, MD: 10.7 MPa

SIDPEC EGYPTENE® HD 6070 UA HDPE Injection Molding accurate 32%

$ 1566/MT

Density: 0.960 g/cc
ESCR, Bottle: 55 hour @Temperature 23.0 °C
Melt Flow: 7.5 g/10 min @Load 2.16 kg
Tensile Strength, Yield: 31.0 MPa
Elongation at Break: >= 1000 %

Multibase Multi-Flex® TPE G 7455 BLK accurate 32%

$ 1666/MT

Density: 1.10 g/cc
Melt Flow: 2.0 g/10 min
Hardness, Shore A: 78
Tensile Strength, Ultimate: 8.30 MPa
Elongation at Break: 1000 %

SCG Chemicals EL-Leneâ„¢ H5840B High Density Polyethylene Blow Molding accurate 32%

$ 1798/MT

Specific Gravity: 0.958 g/cc
Environmental Stress Crack Resistance: 300 hour @Temperature 50.0 °C
Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore D: 66
Tensile Strength at Break: 27.0 MPa

Braskem LH 437 LMDPE Cast Film Extrusion Polyethylene (discontinued **) accurate 66%

$ 1485/MT

Density: 0.937 g/cc
Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore A: 98
Hardness, Shore D: 57
Tensile Strength at Break: 30.0 MPa

Styrolution Terluran® HH-112 ABS accurate 66%

$ 1876/MT

Density: 1.05 g/cc
Linear Mold Shrinkage: 0.0055 cm/cm
Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
Tensile Strength, Yield: 58.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for NOVA Chemicals Sclair® 8406 BK, 8406 GBK MDPE Rotational Molding Resin (discontinued **)

Seller from Rio de Janeiro – 2021-05-16:

Seller from Rio de Janeiro work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2216 per MT