Outokumpu 4841 High Temperature Austenitic Stainless Steel price 1868 per MT

Physical Properties
Density
7.80 g/cc

Mechanical Properties
Tensile Strength, Ultimate
595 MPa
Tensile Strength, Yield
275 MPa @Strain 0.200 %
Tensile Strength, Yield
315 MPa @Strain 1.00 %
Elongation at Break
55 %
Rupture Strength
10.0 MPa @Temperature 900 °C, Time 3.60e+7 sec
Rupture Strength
14.0 MPa @Temperature 850 °C, Time 3.60e+7 sec
Rupture Strength
20.0 MPa @Temperature 800 °C, Time 3.60e+7 sec
Rupture Strength
28.0 MPa @Temperature 750 °C, Time 3.60e+7 sec
Rupture Strength
40.0 MPa @Temperature 700 °C, Time 3.60e+7 sec
Rupture Strength
65.0 MPa @Temperature 650 °C, Time 3.60e+7 sec
Rupture Strength
130 MPa @Temperature 600 °C, Time 3.60e+7 sec
Modulus of Elasticity
196 GPa
Modulus of Elasticity
120 GPa @Temperature 1000 °C
Modulus of Elasticity
158 GPa @Temperature 500 °C

Thermal Properties
CTE, linear
18.8 µm/m-°C @Temperature 500 °C
CTE, linear
20.0 µm/m-°C @Temperature 1000 °C
Specific Heat Capacity
0.470 J/g-°C
Specific Heat Capacity
0.530 J/g-°C @Temperature 500 °C
Thermal Conductivity
11.9 W/m-K
Thermal Conductivity
27.8 W/m-K @Temperature 1000 °C
Maximum Service Temperature, Air
1125 °C

Component Elements Properties
Carbon, C
0.020 %
Chromium, Cr
25 %
Iron, Fe
54.98 %
Nickel, Ni
20 %

Electrical Properties
Electrical Resistivity
0.0000960 ohm-cm

Processing Properties
Annealing Temperature
1040 - 1070 °C
Annealing Temperature
1050 - 1150 °C

Alternative products

Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel accurate 99%

$ 2111/MT

Density: 8.00 g/cc
Hardness, Brinell: 165
Tensile Strength, Ultimate: 570 MPa
Tensile Strength, Ultimate: 380 MPa @Temperature 300 °C
Tensile Strength, Ultimate: 390 MPa @Temperature 200 °C

Carpenter 20-Mo6® Stainless Steel, Tensile Properties at 93°C accurate 99%

$ 1974/MT

Density: 8.133 g/cc
Tensile Strength, Ultimate: 600 MPa
Tensile Strength, Ultimate: 448 MPa @Temperature 593 °C
Tensile Strength, Ultimate: 462 MPa @Temperature 538 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 482 °C

Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled accurate 99%

$ 1669/MT

Density: 8.45 g/cc
Density: 8.61 g/cc
Tensile Strength, Ultimate: 842 MPa
Tensile Strength, Yield: 662 MPa @Strain 0.200 %
Elongation at Break: 2.0 %

Kennametal Stellite Stellite® 31 PM cast accurate 99%

$ 1671/MT

Density: 8.45 g/cc
Density: 8.61 g/cc
Tensile Strength, Ultimate: 745 MPa
Tensile Strength, Ultimate: 436 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 521 MPa @Temperature 649 °C

Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire accurate 99%

$ 1540/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 696 MPa
Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 503 MPa @Temperature 538 °C
Tensile Strength, Yield: 365 MPa @Strain 0.200 %

Outokumpu 4307 Cr-Ni Austenitic Stainless Steel accurate 99%

$ 2175/MT

Density: 7.90 g/cc
Hardness, Brinell: 165
Hardness, Brinell: 175
Tensile Strength, Ultimate: >= 500 MPa
Tensile Strength, Ultimate: 580 MPa

Outokumpu 4311 Cr-Ni Austenitic Stainless Steel accurate 99%

$ 1487/MT

Density: 7.90 g/cc
Tensile Strength, Ultimate: >= 550 MPa
Tensile Strength, Ultimate: 640 MPa
Tensile Strength, Ultimate: 410 MPa @Temperature 300 °C
Tensile Strength, Ultimate: 430 MPa @Temperature 200 °C

Outokumpu 4401 Cr-Ni-Mo Austenitic Stainless Steel accurate 99%

$ 2204/MT

Density: 8.00 g/cc
Hardness, Brinell: 160
Tensile Strength, Ultimate: 570 MPa
Tensile Strength, Ultimate: 360 MPa @Temperature 500 °C
Tensile Strength, Ultimate: 380 MPa @Temperature 300 °C

Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel accurate 99%

$ 1599/MT

Density: 8.00 g/cc
Hardness, Brinell: 150
Tensile Strength, Ultimate: 570 MPa
Tensile Strength, Ultimate: 370 MPa @Temperature 300 °C
Tensile Strength, Ultimate: 380 MPa @Temperature 200 °C

Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled accurate 99%

$ 1987/MT

Density: 8.45 g/cc
Density: 8.61 g/cc
Tensile Strength, Ultimate: 1035 MPa
Tensile Strength, Yield: 725 MPa @Strain 0.200 %
Elongation at Break: 1.5 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker price. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Outokumpu 4841 High Temperature Austenitic Stainless Steel

Seller from Montréal – 2021-06-17:

Seller from Montréal work with company: PolyOne Corporation, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1868 per MT