Overview of materials for Nylon 612, Unreinforced price 1521 per MT

Physical Properties
Density
1.01 - 1.35 g/cc
Apparent Bulk Density
0.265 - 0.450 g/cc
Water Absorption
0.200 - 2.00 %
Water Absorption
14.75 - 14.75 % @Temperature 100 - 100 °C
Moisture Absorption at Equilibrium
0.500 - 3.00 %
Water Absorption at Saturation
2.20 - 7.00 %
Particle Size
7.00 - 23.0 µm
pH
4.00
Specific Surface Area
1.50 - 20.0 m²/g
Linear Mold Shrinkage
0.00100 - 0.0250 cm/cm
Linear Mold Shrinkage, Transverse
0.0100 - 0.0150 cm/cm

Mechanical Properties
Hardness, Rockwell R
114 - 115
Hardness, Shore D
75.0 - 82.0
Tensile Strength, Ultimate
44.0 - 130 MPa
Tensile Strength, Yield
29.0 - 79.3 MPa
Elongation at Break
2.10 - 370 %
Elongation at Yield
2.10 - 30.0 %
Modulus of Elasticity
0.750 - 9.98 GPa
Modulus of Elasticity
0.0860 - 2.228 GPa @Temperature -40.0 - 150 °C
Flexural Yield Strength
30.0 - 145 MPa
Flexural Modulus
0.800 - 9.26 GPa
Izod Impact, Notched
0.320 - 1.07 J/cm
Izod Impact, Notched
0.500 - 0.500 J/cm @Temperature -40.0 - -40.0 °C
Izod Impact, Unnotched
2.14 - 5340 J/cm
Charpy Impact Unnotched
3.00 J/cm² - NB
Charpy Impact Unnotched
2.00 J/cm² - NB @Temperature -40.0 - -30.0 °C
Charpy Impact, Notched
0.500 - 12.0 J/cm²
Charpy Impact, Notched
0.350 - 1.90 J/cm² @Temperature -40.0 - -30.0 °C

Thermal Properties
CTE, linear
50.0 - 170 µm/m-°C
CTE, linear
180 - 180 µm/m-°C @Temperature 50.0 - 160 °C
Specific Heat Capacity
1.67 - 1.88 J/g-°C
Thermal Conductivity
0.280 - 1.10 W/m-K
Melting Point
142 - 224 °C
Maximum Service Temperature, Air
100 - 160 °C
Deflection Temperature at 0.46 MPa (66 psi)
83.0 - 210 °C
Deflection Temperature at 1.8 MPa (264 psi)
47.0 - 190 °C
Vicat Softening Point
110 - 210 °C
Minimum Service Temperature, Air
-100 - -40.0 °C
Flammability, UL94
HB - V-0

Electrical Properties
Electrical Resistivity
3.00e+12 - 1.00e+15 ohm-cm
Surface Resistance
1.00e+10 - 1.00e+15 ohm
Dielectric Constant
2.90 - 12.0
Dielectric Strength
15.0 - 38.0 kV/mm
Dissipation Factor
0.0200 - 0.150
Comparative Tracking Index
600 V

Processing Properties
Processing Temperature
190 - 279 °C
Melt Temperature
221 - 290 °C
Mold Temperature
50.0 - 93.3 °C
Drying Temperature
73.9 - 85.0 °C
Moisture Content
0.0200 - 2.00 %
Dew Point
-17.8 °C
Injection Pressure
68.9 - 124 MPa

Alternative products

Celanese RITEFLEX 655A TPC, Unfilled accurate 99%

$ 1571/MT

Specific Gravity: 1.19 g/cc
Density: 0.000689 g/cc
Density: 1.19 g/cc
Density of Compound: 1.19 g/cc
Water Absorption: 0.400 % @Temperature 22.8 °C

Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry) accurate 99%

$ 1761/MT

Density: 1.68 g/cc
Filler Content: 50 %
Water Absorption: 0.30 % @Time 86400 sec
Water Absorption at Saturation: 1.0 %
Water Absorption at Saturation: 1.3 %

Menzolit Menzolit® SMC 0421 Unsaturated Polyester UP accurate 66%

$ 1870/MT

Density: 1.50 g/cc
Water Absorption: <= 0.50 %
Linear Mold Shrinkage: -0.000500 cm/cm
Tensile Strength, Ultimate: 75.0 MPa @Temperature 22.0 °C
Tensile Strength, Yield: 75.0 MPa @Temperature 22.0 °C

Celanese RITEFLEX 663 TPC, Unfilled accurate 99%

$ 2042/MT

Specific Gravity: 1.24 g/cc
Density: 1.24 g/cc
Water Absorption: 0.300 % @Temperature 22.8 °C
Linear Mold Shrinkage, Flow: 0.0170 - 0.0200 cm/cm
Linear Mold Shrinkage, Flow: 0.0190 cm/cm

Celanese RITEFLEX 655HS TPC, Unfilled accurate 99%

$ 1574/MT

Specific Gravity: 1.20 g/cc
Density: 0.000689 g/cc
Density: 1.19 g/cc
Water Absorption: 0.400 % @Temperature 22.8 °C
Linear Mold Shrinkage, Flow: 0.0100 cm/cm

Celanese RITEFLEX 677 TPC, Unfilled accurate 99%

$ 2272/MT

Specific Gravity: 1.29 g/cc
Density: 1.27 g/cc
Water Absorption: 0.100 % @Temperature 22.8 °C
Viscosity: 461200 cP
Linear Mold Shrinkage, Flow: 0.0200 cm/cm

Celanese RITEFLEX 640A TPC, Unfilled accurate 99%

$ 2533/MT

Specific Gravity: 1.15 g/cc
Density: 0.000657 g/cc
Density: 1.13 g/cc
Water Absorption: 0.500 % @Temperature 22.8 °C
Viscosity: 351100 cP

DSM Arnite® T06 202 XL (T-X01151) PBT (European Grade) accurate 66%

$ 1494/MT

Density: 1.30 g/cc
Water Absorption: 0.45 %
Moisture Absorption at Equilibrium: 0.18 %
Melt Flow: 39 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 58.0 MPa

Menzolit Menzolit® SMC 0900 Unsaturated Polyester UP accurate 66%

$ 2074/MT

Density: 1.70 g/cc
Water Absorption: <= 0.30 %
Linear Mold Shrinkage: 0.00080 cm/cm
Tensile Strength, Ultimate: 76.0 MPa @Temperature 22.0 °C
Tensile Strength, Yield: 76.0 MPa @Temperature 22.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Overview of materials for Nylon 612, Unreinforced

Seller from Istanbul – 2021-03-22:

Seller from Istanbul work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1685 per MT

Seller from Dhaka – 2021-03-02:

Seller from Dhaka work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2070 per MT

Seller from Kinshasa – 2021-03-09:

Seller from Kinshasa work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1521 per MT

Seller from Dallas – 2021-05-30:

Seller from Dallas work with company: Solvay, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2220 per MT