Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced price 1716 per MT

Physical Properties
Volatiles
<= 2.0 % @Temperature 135 °C
Thickness
178 microns

Mechanical Properties
Tensile Strength, Yield
545 MPa @Temperature 93.3 °C
Tensile Strength, Yield
565 MPa @Temperature 71.1 °C
Tensile Strength, Yield
593 MPa @Temperature 71.1 °C
Tensile Strength, Yield
621 MPa @Temperature 21.1 °C
Tensile Strength, Yield
648 MPa @Temperature 21.1 °C
Tensile Modulus
57.9 GPa @Temperature 71.1 °C
Tensile Modulus
60.0 GPa @Temperature 71.1 °C
Tensile Modulus
60.0 GPa @Temperature 93.3 °C
Tensile Modulus
60.0 GPa @Temperature 21.1 °C
Tensile Modulus
60.7 GPa @Temperature 21.1 °C
Flexural Strength
490 MPa @Temperature 71.1 °C
Flexural Strength
545 MPa @Temperature 93.3 °C
Flexural Strength
579 MPa @Temperature 71.1 °C
Flexural Strength
689 MPa @Temperature 21.1 °C
Flexural Strength
745 MPa @Temperature 21.1 °C
Flexural Modulus
46.9 GPa @Temperature 71.1 °C
Flexural Modulus
46.9 GPa @Temperature 71.1 °C
Flexural Modulus
47.6 GPa @Temperature 93.3 °C
Flexural Modulus
47.6 GPa @Temperature 21.1 °C
Flexural Modulus
49.6 GPa @Temperature 21.1 °C
Compressive Strength
310 MPa @Temperature 71.1 °C
Compressive Strength
310 MPa @Temperature 93.3 °C
Compressive Strength
352 MPa @Temperature 71.1 °C
Compressive Strength
400 MPa @Temperature 21.1 °C
Compressive Strength
427 MPa @Temperature 21.1 °C
Compressive Modulus
57.9 GPa @Temperature 21.1 °C
Compressive Modulus
59.3 GPa @Temperature 71.1 °C
Compressive Modulus
59.3 GPa @Temperature 93.3 °C
Compressive Modulus
62.1 GPa @Temperature 21.1 °C
Compressive Modulus
67.6 GPa @Temperature 71.1 °C
Shear Strength
30.3 MPa @Temperature 71.1 °C
Shear Strength
32.4 MPa @Temperature 93.3 °C
Shear Strength
37.9 MPa @Temperature 71.1 °C
Shear Strength
44.8 MPa @Temperature 21.1 °C
Shear Strength
51.0 MPa @Temperature 21.1 °C

Thermal Properties
Glass Transition Temp, Tg
115 °C

Processing Properties
Gel Time
6.00 min
Shelf Life
12.0 Month @Temperature -17.8 °C

Descriptive Properties
Fabric Area Weight (g/m²)
192.9
Prepreg Resin Content (%)
42
Resin Flow (%)
10

Alternative products

Parker Chomerics CHO-BOND 1038 Conductive Silicone RTV Adhesive accurate 99%

$ 1445/MT

Specific Gravity: 3.20 - 3.90 g/cc
Volatile Organic Compounds (VOC) Content: 117 g/l
Thickness: >= 178 microns
Hardness, Shore A: >= 55
Shear Strength: 1.03 MPa

Arlon 31580R025 0.025" (0.635 mm) Uncured Unsupported Silicone Rubber on HDPE Carrier (discontinued **)& accurate 99%

$ 1625/MT

Thickness: 76.2 microns
Thickness: 178 microns
Thickness: 584 - 686 microns
Thickness: 584 - 686 microns
Hardness, Shore A: 40 - 50

Parker Chomerics CHO-BOND 1035 Electrically Conductive Sealant accurate 99%

$ 1571/MT

Specific Gravity: 1.80 - 2.00 g/cc
Volatile Organic Compounds (VOC) Content: 151 g/l
Thickness: 178 microns
Shear Strength: >= 0.689 MPa
Maximum Service Temperature, Air: 200 °C

Tra-Con Tra-Bond 789-4 Thermally Conductive Adhesive accurate 99%

$ 2016/MT

Viscosity: 75000 cP
Adhesive Bond Strength: 24.1 MPa
Adhesive Bond Strength: 27.6 MPa
CTE, linear: 35.0 µm/m-°C
CTE, linear: 100 µm/m-°C

Arlon 55103R030 0.030" (0.762 mm) Cured Silicone Rubber with Fiberglass Substrate accurate 99%

$ 2169/MT

Density: 1.35 g/cc
Thickness: 63.5 microns
Thickness: 178 microns
Thickness: 178 microns
Thickness: 406 microns

Parker Chomerics Tecknit® 0002 Highly Conductive Adhesive-Sealant Silver Silicone accurate 99%

$ 2227/MT

Specific Gravity: 3.10 g/cc
Volatile Organic Compounds (VOC) Content: 9.0 g/l
Thickness: 178 microns
Shear Strength: >= 1.03 MPa
Volume Resistivity: <= 0.010 ohm-cm

Tra-Con Tra-Bond 342-1 Room Temperature Cure Epoxy Adhesive accurate 99%

$ 1857/MT

Viscosity: 5000 cP @Temperature 25.0 °C
Hardness, Shore D: 86
Adhesive Bond Strength: 26.2 MPa
Glass Transition Temp, Tg: 71.0 °C
Cure Time: 60.0 min @Temperature 120 °C

Arlon 31580R015 0.015" (0.381 mm) Uncured Unsupported Silicone Rubber on an HDPE Carrier (discontinued * accurate 99%

$ 1480/MT

Thickness: 76.2 microns
Thickness: 178 microns
Thickness: 343 - 419 microns
Thickness: 343 - 419 microns
Hardness, Shore A: 40 - 50

Master Bond EP21TDCS Two Component Silver Conductive Epoxy Adhesive accurate 99%

$ 1463/MT

Adhesive Bond Strength: >= 5.86 MPa
Adhesive Bond Strength: >= 5.86 MPa
Peel Strength: >= 1.75 kN/m
Thermal Conductivity: 1.59 W/m-K
Maximum Service Temperature, Air: 135 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, container ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced

Seller from London – 2021-02-28:

Seller from London work with company: Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1716 per MT

Seller from Hanoi – 2021-07-13:

Seller from Hanoi work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2139 per MT

Seller from Singapore – 2021-07-29:

Seller from Singapore work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2372 per MT