Phillips 66 COPYLENE® CH200L Polypropylene, Homopolymer, CR, Antistat, Injection Molding price 1679 per MT

Physical Properties
Density
0.902 g/cc
Melt Flow
20 g/10 min @Load 2.16 kg, Temperature 230 °C

Mechanical Properties
Tensile Strength, Yield
33.1 MPa
Elongation at Yield
10 %
Flexural Modulus
1.34 GPa
Izod Impact, Notched
0.374 J/cm @Temperature 23.0 °C

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
90.0 °C

Descriptive Properties
Process
Injection Molding
Region
Mexico
Region
US & Canada

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 99%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

BASF Ultraform N 2320 U03 UNC Q600 POM accurate 82%

$ 1745/MT

Density: 1.40 g/cc
Water Absorption: 0.80 %
Moisture Absorption at Equilibrium: 0.20 %
Linear Mold Shrinkage: 0.020 cm/cm
Linear Mold Shrinkage, Flow: 0.021 cm/cm

Thermal Ceramics Cerafelt accurate 99%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Diamond Polymers NPP50-1111 TF20 20% Talc Filled White High Density Polyethylene accurate 66%

$ 1601/MT

Density: 1.11 g/cc
Melt Flow: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow: 29.8 g/10 min @Load 21.6 kg, Temperature 190 °C
Tensile Strength, Yield: 32.6 MPa
Elongation at Break: >= 110 %

Thermal Ceramics Kaowool Blanket accurate 82%

$ 1501/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.192 g/cc

LyondellBasell Pro-fax 6331W Polypropylene Homopolymer, Antistat accurate 66%

$ 1990/MT

Density: 0.900 g/cc
Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
Hardness, Rockwell R: 89
Tensile Strength, Yield: 34.0 MPa
Elongation at Yield: 10 %

Phillips 66 COPYLENE® CH120 Polypropylene, Homopolymer, Injection Molding, Barefoot accurate 82%

$ 1703/MT

Density: 0.902 g/cc
Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength, Yield: 33.1 MPa
Elongation at Yield: 9.6 %
Flexural Modulus: 1.34 GPa

Styron MAGNUMâ„¢ 1250 BG Acrylonitrile Butadiene Styrene (ABS) Resin accurate 66%

$ 1675/MT

Density: 1.05 g/cc
Melt Flow: 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C
Melt Flow: 1.7 g/10 min @Load 10.0 kg, Temperature 220 °C
Tensile Strength at Break: 60.0 MPa
Tensile Strength, Yield: 33.6 MPa

LyondellBasell Pro-faxâ„¢ PH350 Polypropylene Homopolymer accurate 66%

$ 2566/MT

Density: 0.902 g/cc
Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
Hardness, Rockwell R: 85
Tensile Strength, Yield: 33.8 MPa
Elongation at Yield: 12 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship for sale price. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: a.kutuzov@plastic-price.com

Work with plastics from August, 2015

1 prices for Phillips 66 COPYLENE® CH200L Polypropylene, Homopolymer, CR, Antistat, Injection Molding

Seller from Houston – 2021-02-26:

Seller from Houston work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1679 per MT