Phillips 66 COPYLENE® CR020N Polypropylene Random Copolymer price 1840 per MT

Physical Properties
Density
0.902 g/cc
Melt Flow
2.0 g/10 min @Load 2.16 kg, Temperature 230 °C

Mechanical Properties
Tensile Strength, Yield
26.5 MPa
Elongation at Yield
13.5 %
Flexural Modulus
0.965 GPa
Izod Impact, Notched
4.27 J/cm

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
90.0 °C

Descriptive Properties
Process
Blow Molding
Process
Extrusion
Region
Mexico
Region
US & Canada

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 85%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

LyondellBasell Alathon® M4855 High Density Polyethylene, Injection Molding Grade accurate 70%

$ 1773/MT

Bulk Density: 0.593 - 0.625 g/cc
Density: 0.948 g/cc
Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Spiral Flow: 20.3 cm
Tensile Strength at Break: 24.1 MPa

SABIC Innovative Plastics SABIC PPCOMPOUND 7450 PP accurate 99%

$ 1551/MT

Specific Gravity: 0.970 g/cc
Density: 0.970 g/cc
Linear Mold Shrinkage, Flow: 0.0069 cm/cm
Linear Mold Shrinkage, Flow: 0.0074 cm/cm
Linear Mold Shrinkage, Transverse: 0.010 cm/cm

Celanese RITEFLEX 672 TPC, Unfilled accurate 70%

$ 1945/MT

Specific Gravity: 1.25 g/cc
Density: 0.000721 g/cc
Density: 1.26 g/cc
Water Absorption: 0.200 % @Temperature 22.8 °C
Linear Mold Shrinkage, Flow: 0.0170 - 0.0220 cm/cm

Thermal Ceramics Cerafelt accurate 85%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Total PPC 4624WZ Polypropylene, Impact Copolymer accurate 70%

$ 2106/MT

Density: 0.905 g/cc
Melt Flow: 13 g/10 min
Tensile Strength, Yield: 26.0 MPa
Elongation at Yield: 7.0 %
Flexural Modulus: 1.15 GPa

Styrolution Terblend® N NM-11 ABS/PA6 (Dry) accurate 70%

$ 1458/MT

Density: 1.07 g/cc
Moisture Absorption at Equilibrium: 1.3 %
Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 240 °C
Tensile Strength at Break: 36.0 MPa
Tensile Strength, Yield: 43.0 MPa

ExxonMobil PP7033N Impact Copolymer accurate 99%

$ 1746/MT

Density: 0.900 g/cc
Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength, Yield: 25.8 MPa
Tensile Strength, Yield: 25.9 MPa
Elongation at Yield: 4.0 %

LyondellBasell Pro-fax 7624 Polypropylene Impact Copolymer, Heat- and Extraction-Resistant accurate 70%

$ 1913/MT

Density: 0.900 g/cc
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength, Yield: 27.0 MPa
Elongation at Yield: 9.0 %
Flexural Modulus: 1.20 GPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Phillips 66 COPYLENE® CR020N Polypropylene Random Copolymer

Seller from Melbourne – 2021-07-21:

Seller from Melbourne work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1840 per MT

Seller from Bangkok – 2021-05-09:

Seller from Bangkok work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2293 per MT