PTS Tristar® PC-10FR 12 MFI Flame Retardant Polycarbonate With Release price 2187 per MT

Physical Properties
Density
1.23 g/cc
Melt Flow
12 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell R
120
Tensile Strength, Yield
62.1 MPa @Thickness 3.17 mm
Elongation at Break
75 % @Thickness 3.17 mm
Flexural Yield Strength
89.6 MPa @Thickness 3.17 mm
Flexural Modulus
2.21 GPa @Thickness 3.17 mm
Izod Impact, Notched
5.87 J/cm @Thickness 3.17 mm

Thermal Properties
CTE, linear, Parallel to Flow
70.2 µm/m-°C @Temperature -40.0 - 95.0 °C
CTE, linear, Transverse to Flow
68.4 µm/m-°C @Temperature -40.0 - 95.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
127 °C
Deflection Temperature at 1.8 MPa (264 psi)
137 °C
UL RTI, Electrical
125 °C
UL RTI, Mechanical with Impact
115 °C
UL RTI, Mechanical without Impact
125 °C
Flammability, UL94
V-1 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 3.00 mm
Oxygen Index
36.9 %
Glow Wire Test
775 °C
Glow Wire Test
960 °C

Electrical Properties
Arc Resistance
60 - 120 sec
Comparative Tracking Index
250 - 400 V
Hot Wire Ignition, HWI
15 - 30 sec @Thickness 1.50 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness 3.00 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Processing Properties
Rear Barrel Temperature
254 - 274 °C
Middle Barrel Temperature
266 - 277 °C
Front Barrel Temperature
277 - 293 °C
Nozzle Temperature
271 - 293 °C
Melt Temperature
282 - 304 °C
Mold Temperature
71.1 - 93.3 °C
Drying Temperature
121 °C
Dry Time
3 - 4 hour
Injection Pressure
75.8 - 124 MPa
Back Pressure
0.345 - 1.38 MPa
Clamp Pressure
27.6 - 68.9 MPa
Shot Size
40 - 60 %
Screw Speed
40 - 70 rpm

Descriptive Properties
Injection Speed- Edge Gate
Slow to Medium
Injection Speed- Tab Gate
Medium to Fast
Injection Speed- Tunnel Gate
Fast

Alternative products

PTS Tristar® PC-10R-(IM) 10 MFI Impact Modified Polycarbonate With Release accurate 92%

$ 1871/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 55.2 MPa @Thickness 3.17 mm

PTS Tristar® PC-10FR-(V) 12 MFI Flame Retardant, UV Stabilized Polycarbonate With Release accurate 99%

$ 1735/MT

Density: 1.23 g/cc
Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm
Elongation at Break: 75 % @Thickness 3.17 mm

PTS Tristar® PC-10R-(V15) 15 MFI UV Stabilized Polycarbonate With Release accurate 92%

$ 2193/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 58.6 MPa @Thickness 3.17 mm

PTS Tristar® PC-10FR-(V8) 8 MFI Flame Retardant, UV Stabilized Polycarbonate With Release accurate 99%

$ 2376/MT

Density: 1.23 g/cc
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm
Elongation at Break: 75 % @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(22) 22 MFI Clear Polycarbonate with Release accurate 92%

$ 1484/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

PTS Tristar® PC-10FR-(18) 18 MFI Flame Retardant Polycarbonate With Release accurate 92%

$ 1665/MT

Density: 1.23 g/cc
Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm
Elongation at Break: 75 % @Thickness 3.17 mm

PTS Tristar® PC-10R-(V) 10 MFI UV Stabilized Polycarbonate With Release accurate 92%

$ 1532/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(V22) 22 MFI UV Stabilized Clear Polycarbonate with Release accurate 92%

$ 1614/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

PTS Tristar® PC-10FR-(8) 8 MFI Flame Retardant Polycarbonate With Release accurate 99%

$ 1513/MT

Density: 1.23 g/cc
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm
Elongation at Break: 75 % @Thickness 3.17 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for PTS Tristar® PC-10FR 12 MFI Flame Retardant Polycarbonate With Release

Seller from Dongguan – 2021-05-27:

Seller from Dongguan work with company: PolyOne Corporation, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2214 per MT

Seller from Sydney – 2021-05-19:

Seller from Sydney work with company: RTP Company, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2187 per MT