PTS Tristar® PC-10R-(22) 22 MFI Polycarbonate With Release price 1951 per MT

Physical Properties
Density
1.20 g/cc
Water Absorption
0.15 %
Melt Flow
22 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell R
120
Tensile Strength, Yield
60.3 MPa @Thickness 3.17 mm
Elongation at Break
100 % @Thickness 3.17 mm
Flexural Yield Strength
89.6 MPa @Thickness 3.17 mm
Flexural Modulus
2.21 GPa @Thickness 3.17 mm
Izod Impact, Notched
6.94 J/cm @Thickness 3.17 mm

Thermal Properties
CTE, linear, Parallel to Flow
70.2 µm/m-°C @Temperature -40.0 - 95.0 °C
CTE, linear, Transverse to Flow
68.4 µm/m-°C @Temperature -40.0 - 95.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
132 °C
Deflection Temperature at 1.8 MPa (264 psi)
137 °C
UL RTI, Electrical
125 °C
UL RTI, Mechanical with Impact
115 °C
UL RTI, Mechanical without Impact
125 °C
Flammability, UL94
V-2 @Thickness 1.50 mm
Glow Wire Test
775 °C
Glow Wire Test
960 °C

Electrical Properties
Arc Resistance
60 - 120 sec
Comparative Tracking Index
250 - 400 V
Hot Wire Ignition, HWI
15 - 30 sec @Thickness 1.50 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness 3.00 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Processing Properties
Rear Barrel Temperature
243 - 260 °C
Middle Barrel Temperature
249 - 260 °C
Front Barrel Temperature
260 - 271 °C
Nozzle Temperature
254 - 271 °C
Melt Temperature
260 - 282 °C
Mold Temperature
71.1 - 93.3 °C
Drying Temperature
121 °C
Dry Time
3 - 4 hour
Injection Pressure
51.7 - 124 MPa
Back Pressure
0.345 - 1.38 MPa
Clamp Pressure
27.6 - 68.9 MPa
Shot Size
40 - 60 %
Screw Speed
40 - 70 rpm

Descriptive Properties
Injection Speed- Edge Gate
Slow to Medium
Injection Speed- Tab Gate
Medium to Fast
Injection Speed- Tunnel Gate
Fast

Alternative products

PTS Tristar® PC-10R-(V22) 22 MFI UV Stabilized Polycarbonate With Release accurate 99%

$ 1515/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-(V6) 6 MFI UV Stabilized Polycarbonate With Release accurate 92%

$ 1829/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(6) 6 MFI Clear Polycarbonate with Release accurate 92%

$ 1780/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-(8) 8 MFI Polycarbonate With Release accurate 99%

$ 1602/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-(14) 14 MFI Polycarbonate With Release accurate 92%

$ 1465/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 14 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 58.6 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(V6) 6 MFI UV Stabilized Clear Polycarbonate with Release accurate 92%

$ 2163/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-(V8) 8 MFI UV Stabilized Polycarbonate With Release accurate 99%

$ 1791/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-(V) 10 MFI UV Stabilized Polycarbonate With Release accurate 92%

$ 1532/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(V22) 22 MFI UV Stabilized Clear Polycarbonate with Release accurate 92%

$ 1614/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng carrier vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for PTS Tristar® PC-10R-(22) 22 MFI Polycarbonate With Release

Seller from Hanoi – 2021-03-09:

Seller from Hanoi work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2244 per MT

Seller from Toronto – 2021-05-19:

Seller from Toronto work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2054 per MT

Seller from Sūrat – 2021-03-02:

Seller from Sūrat work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1951 per MT