Physical Properties
Specific Gravity
1.70 - 1.80 g/cc
Apparent Bulk Density
0.750 - 0.950 g/cc
Water Absorption
<= 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage
0.0070 - 0.010 cm/cm

Mechanical Properties
Tensile Strength, Yield
30.0 - 50.0 MPa
Tensile Strength, Yield
45.0 - 55.0 MPa
Modulus of Elasticity
5.00 - 7.00 GPa
Modulus of Elasticity
9.00 - 10.0 GPa
Flexural Strength
60.0 - 90.0 MPa
Flexural Strength
90.0 - 110 MPa
Flexural Modulus
6.00 - 8.00 GPa
Flexural Modulus
9.00 - 11.0 GPa
Compressive Strength
150 - 200 MPa
Charpy Impact Unnotched
0.600 - 0.800 J/cm² @Temperature 23.0 °C
Charpy Impact Unnotched
0.900 - 1.10 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.150 - 0.250 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.200 - 0.300 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
20.0 - 30.0 µm/m-°C @Temperature 50.0 - 100 °C
Thermal Conductivity
0.600 - 0.700 W/m-K
Maximum Service Temperature, Air
140 °C
Maximum Service Temperature, Air
190 °C
Deflection Temperature at 1.8 MPa (264 psi)
>= 200 °C
Deflection Temperature at 8.0 MPa
80.0 - 110 °C
Flammability, UL94
V-0 @Thickness 0.750 mm
Shrinkage
0.20 - 0.40 % @Temperature 110 °C, Time 605000 sec

Electrical Properties
Volume Resistivity
1.00e+13 - 1.00e+14 ohm-cm
Surface Resistance
1.00e+12 - 1.00e+13 ohm
Dielectric Constant
4.0 - 5.0 @Frequency 1.00e+6 Hz
Dielectric Constant
5.0 - 7.0 @Frequency 100 Hz
Dielectric Strength
30.0 - 40.0 kV/mm
Dissipation Factor
0.030 - 0.050 @Frequency 1.00e+6 Hz
Dissipation Factor
0.10 - 0.20 @Frequency 100 Hz
Comparative Tracking Index
600 V

Processing Properties
Shelf Life
6.00 Month @Temperature 15.0 - 25.0 °C

Descriptive Properties
Arc Resistance
4 Stufe
Glow wire ignitability test
825/1
Glow-wire flammability test
960/1
Water Absorption
<50 mg

Alternative products

Raschig Group 2567 AMC accurate 66%

$ 2281/MT

Specific Gravity: 2.00 - 2.20 g/cc
Apparent Bulk Density: 0.700 - 0.850 g/cc
Water Absorption: <= 0.30 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0015 - 0.0045 cm/cm
Tensile Strength, Yield: 35.0 - 60.0 MPa

Raschig Group 2572 AMC accurate 66%

$ 1563/MT

Specific Gravity: 1.90 - 2.10 g/cc
Apparent Bulk Density: 0.700 - 0.850 g/cc
Water Absorption: <= 0.30 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0020 - 0.0045 cm/cm
Tensile Strength, Yield: 60.0 - 70.0 MPa

Raschig Group 2568 AMC accurate 66%

$ 1472/MT

Specific Gravity: 2.00 - 2.20 g/cc
Apparent Bulk Density: 0.800 - 0.950 g/cc
Water Absorption: <= 0.30 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0025 - 0.0045 cm/cm
Tensile Strength, Yield: 35.0 - 60.0 MPa

Raschig Group SURAPLAST UPA 63 UP accurate 49%

$ 2015/MT

Specific Gravity: 1.90 - 2.10 g/cc
Apparent Bulk Density: 0.650 - 0.850 g/cc
Water Absorption: <= 0.50 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
Tensile Strength, Yield: 50.0 - 70.0 MPa

Raschig Group AMPLA® 7500 melamine-modified polyester accurate 66%

$ 2173/MT

Specific Gravity: 1.60 - 1.70 g/cc
Apparent Bulk Density: 0.700 - 0.900 g/cc
Water Absorption: <= 1.4 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
Linear Mold Shrinkage: 0.0090 - 0.012 cm/cm

Raschig Group RALUPOL® 4806 UP accurate 49%

$ 1550/MT

Specific Gravity: 1.90 - 2.10 g/cc
Apparent Bulk Density: 0.750 - 0.950 g/cc
Water Absorption: <= 0.50 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm

Raschig Group RALUPOL® 8605 UP Polyester accurate 49%

$ 1489/MT

Specific Gravity: 1.90 - 2.10 g/cc
Apparent Bulk Density: 0.700 - 0.950 g/cc
Water Absorption: <= 0.300 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00300 - 0.00400 cm/cm
Tensile Strength: 70.0 - 100 MPa

Raschig Group MELOPAS® 156 MF Melamine accurate 66%

$ 1627/MT

Specific Gravity: 1.80 - 1.90 g/cc
Apparent Bulk Density: 0.600 - 0.800 g/cc
Water Absorption: <= 1.00 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00500 - 0.00900 cm/cm
Tensile Strength: 40.0 - 50.0 MPa

Raschig Group RALUPOL® 4566 UP Polyester accurate 66%

$ 2392/MT

Specific Gravity: 2.00 - 2.20 g/cc
Apparent Bulk Density: 0.900 - 1.10 g/cc
Water Absorption: <= 0.600 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00600 cm/cm
Flexural Strength: 60.0 - 80.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Raschig Group AMPLA® 2000 melamine-modified polyester

Seller from Jakarta – 2021-03-25:

Seller from Jakarta work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $2111 per MT

Seller from Karachi – 2021-07-08:

Seller from Karachi work with company: 3M, Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $1962 per MT

Seller from Philadelphia – 2021-06-30:

Seller from Philadelphia work with company: Solvay, RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $1649 per MT