SABIC Innovative Plastics Ultem 1010X PEI (Europe-Africa-Middle East) price 1621 per MT

Physical Properties
Density
1.27 g/cc
Moisture Absorption at Equilibrium
0.70 %
Water Absorption at Saturation
1.25 % @Temperature 23.0 °C
Melt Flow
13 g/10 min @Load 5.00 kg, Temperature 340 °C
Melt Flow
25 g/10 min @Load 5.00 kg, Temperature 360 °C

Mechanical Properties
Hardness, H358/30
140 MPa
Tensile Strength at Break
85.0 MPa
Tensile Strength, Yield
105 MPa
Elongation at Break
60 %
Elongation at Yield
6.0 %
Tensile Modulus
3.20 GPa
Flexural Yield Strength
160 MPa
Flexural Modulus
3.30 GPa
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature 23.0 °C
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature -30.0 °C
Izod Impact, Unnotched (ISO)
NB @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Temperature -30.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature 23.0 °C
Taber Abrasion, mg/1000 Cycles
10 @Load 1.00 kg

Thermal Properties
CTE, linear, Parallel to Flow
50.0 µm/m-°C @Temperature 23.0 - 150 °C
CTE, linear, Transverse to Flow
50.0 µm/m-°C @Temperature 23.0 - 150 °C
Thermal Conductivity
0.210 W/m-K
Deflection Temperature at 0.46 MPa (66 psi)
200 °C
Deflection Temperature at 1.8 MPa (264 psi)
190 °C
Vicat Softening Point
211 °C
Vicat Softening Point
212 °C
Vicat Softening Point
215 °C
Glass Transition Temp, Tg
217 °C
UL RTI, Electrical
170 °C
Oxygen Index
47 %

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
2.9 @Frequency 1.00e+6 Hz
Dielectric Constant
2.9 @Frequency 50.0 - 60.0 Hz
Dielectric Strength
16.0 kV/mm @Thickness 3.20 mm
Dielectric Strength
25.0 kV/mm @Thickness 1.60 mm
Dielectric Strength
33.0 kV/mm @Thickness 0.800 mm
Dissipation Factor
0.00050 @Frequency 50.0 - 60.0 Hz
Dissipation Factor
0.0025 @Frequency 2.45e+9 Hz
Dissipation Factor
0.0060 @Frequency 1.00e+6 Hz
Comparative Tracking Index
>= 100 V
Comparative Tracking Index
150 V

Descriptive Properties
Ball Pressure Test, 125Â°C +/- 2Â°C
PASSES

Alternative products

SABIC Innovative Plastics ULTEM 1000EF PEI (Asia Pacific) accurate 88%

$ 2439/MT

Specific Gravity: 1.27 g/cc
Density: 1.27 g/cc
Water Absorption: 0.25 % @Time 86400 sec
Moisture Absorption: 0.700 %
Moisture Absorption at Equilibrium: 1.25 %

SABIC Innovative Plastics ULTEM 1000FC PEI (Europe-Africa-Middle East) accurate 88%

$ 2295/MT

Density: 1.27 g/cc
Moisture Absorption: 0.700 %
Water Absorption at Saturation: 1.25 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 360 °C

SABIC Innovative Plastics ULTEM MD141 PEI (Europe-Africa-Middle East) accurate 88%

$ 1981/MT

Density: 1.27 g/cc
Moisture Absorption: 0.700 %
Water Absorption at Saturation: 1.25 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 360 °C

SABIC Innovative Plastics ULTEM 1000R PEI (Europe-Africa-Middle East) accurate 88%

$ 1936/MT

Density: 1.27 g/cc
Moisture Absorption: 0.700 %
Water Absorption at Saturation: 1.25 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 360 °C

SABIC Innovative Plastics ULTEM HU1010 PEI (Europe-Africa-Middle East) accurate 88%

$ 1570/MT

Density: 1.27 g/cc
Moisture Absorption: 0.700 %
Water Absorption at Saturation: 1.25 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 340 °C

SABIC Innovative Plastics Ultem 1010RF PEI accurate 99%

$ 1565/MT

Specific Gravity: 1.27 g/cc
Density: 1.27 g/cc
Water Absorption: 0.25 % @Time 86400 sec
Moisture Absorption at Equilibrium: 0.70 %
Moisture Absorption at Equilibrium: 1.25 % @Temperature 23.0 °C

SABIC Innovative Plastics ULTEM 1000EF PEI accurate 88%

$ 1535/MT

Specific Gravity: 1.27 g/cc
Density: 1.27 g/cc
Water Absorption: 0.25 % @Time 86400 sec
Moisture Absorption: 0.700 %
Moisture Absorption at Equilibrium: 1.25 %

SABIC Innovative Plastics ULTEM 1010 PEI (Europe-Africa-Middle East) accurate 88%

$ 1513/MT

Density: 1.27 g/cc
Moisture Absorption: 0.700 %
Water Absorption at Saturation: 1.25 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 340 °C

SABIC Innovative Plastics ULTEM 1000E PEI (Europe-Africa-Middle East) accurate 88%

$ 1859/MT

Specific Gravity: 1.27 g/cc
Density: 1.27 g/cc
Water Absorption: 0.25 % @Time 86400 sec
Moisture Absorption: 0.700 %
Moisture Absorption at Equilibrium: 1.25 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil/chemical tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for SABIC Innovative Plastics Ultem 1010X PEI (Europe-Africa-Middle East)

Seller from Shenzhen – 2021-03-13:

Seller from Shenzhen work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2113 per MT

Seller from Tianjin – 2021-05-12:

Seller from Tianjin work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2057 per MT

Seller from Tehran – 2021-04-27:

Seller from Tehran work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1621 per MT

Seller from Chengdu – 2021-05-22:

Seller from Chengdu work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1640 per MT