SCG Chemicals EL-Leneâ„¢ LD1902F Low Density Polyethylene Film price 1580 per MT

Physical Properties
Specific Gravity
0.919 g/cc
Thickness
38.0 microns
Melt Flow
2.0 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Film Tensile Strength at Yield, TD
12.0 MPa
Film Elongation at Break, MD
260 %
Film Elongation at Break, TD
720 %
Secant Modulus, MD
0.250 GPa
Secant Modulus, TD
0.270 GPa
Elmendorf Tear Strength, MD
14.6 g/micron
Elmendorf Tear Strength, TD
3.94 g/micron
Dart Drop
3.90 g/micron
Dart Drop Test
150 g
Film Tensile Strength at Break, MD
23.0 MPa
Film Tensile Strength at Break, TD
19.0 MPa

Thermal Properties
Melting Point
110 °C
Vicat Softening Point
92.0 °C
Brittleness Temperature
<= -71.0 °C

Optical Properties
Haze
9.0 %
Gloss
50 %

Alternative products

ExxonMobil LD 124.MS General Purpose Clarity Film Resin accurate 39%

$ 1449/MT

Density: 0.923 g/cc
Thickness: 38.1 microns
Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
Antiblock Level: 2000 ppm
Slip Level: 400 ppm

NOVA Chemicals Novapol® LF-0224-A LDPE (discontinued **) accurate 49%

$ 1969/MT

Density: 0.924 g/cc
Thickness: 38.1 microns
Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, MD: 11.2 MPa
Film Tensile Strength at Yield, TD: 12.0 MPa

ExxonMobil LD 129.24 Cast Overwrap Film Resin accurate 49%

$ 1720/MT

Density: 0.929 g/cc
Thickness: 38.1 microns
Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
Antiblock Level: 1000 ppm
Film Tensile Strength at Yield, MD: 14.5 MPa

SCG Chemicals EL-Leneâ„¢ LD1902FA Low Density Polyethylene Film accurate 79%

$ 1564/MT

Specific Gravity: 0.919 g/cc
Thickness: 38.0 microns
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, TD: 12.0 MPa
Film Elongation at Break, MD: 260 %

ExxonMobil LD 146.NH Packaging Film Resin (discontinued **) accurate 39%

$ 1899/MT

Density: 0.920 g/cc
Thickness: 38.1 microns
Melt Flow: 3.75 g/10 min
Antiblock Level: 1200 ppm
Slip Level: 900 ppm

ExxonMobil LD 136.NI Packaging Film Resin (discontinued **) accurate 39%

$ 1528/MT

Density: 0.921 g/cc
Thickness: 38.1 microns
Melt Flow: 2.0 g/10 min
Antiblock Level: 450 ppm
Slip Level: 500 ppm

ExxonMobil LD 136.MV Packaging Film Resin (discontinued **) accurate 39%

$ 1905/MT

Density: 0.921 g/cc
Thickness: 38.1 microns
Melt Flow: 2.0 g/10 min
Film Tensile Strength at Yield, MD: 10.7 MPa
Film Tensile Strength at Yield, TD: 10.7 MPa

SCG Chemicals EL-Leneâ„¢ LD1905FA Low Density Polyethylene Film accurate 39%

$ 2008/MT

Specific Gravity: 0.919 g/cc
Thickness: 38.0 microns
Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, TD: 10.0 MPa
Film Elongation at Break, MD: 400 %

SCG Chemicals EL-Leneâ„¢ LD2305F Low Density Polyethylene Film accurate 49%

$ 1720/MT

Specific Gravity: 0.923 g/cc
Thickness: 38.0 microns
Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, TD: 9.00 MPa
Film Elongation at Break, MD: 300 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for SCG Chemicals EL-Leneâ„¢ LD1902F Low Density Polyethylene Film

Seller from Santiago – 2021-08-09:

Seller from Santiago work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1580 per MT