SGL Carbon Group PANOX® SA C063 SSC High performance oxidized textile fiber, Crimped staple fiber, For felts and non-wovens price 1712 per MT

Physical Properties
Density
1.39 - 1.43 g/cc
Filament Diameter
15 µm
Fiber Count
2.22 dtex

Mechanical Properties
Tensile Strength at Break
190 MPa
Elongation at Break
15 - 27 %
Tenacity
>= 0.140 N/tex

Descriptive Properties
Mean Fiber Length, mm
63
Typical Finish Content, %
1

Alternative products

SGL Carbon Group PANOX® FA C063 EEA High performance Crimped staple oxidized textile fiber, For carbon/carbon and spinning accurate 99%

$ 1546/MT

Density: 1.39 - 1.43 g/cc
Filament Diameter: 13 µm
Fiber Count: 1.67 dtex
Tensile Strength at Break: 190 MPa
Elongation at Break: 15 - 27 %

SGL Carbon Group PANOX® FA T320 EEA High performance oxidized textile fiber, Continuous Tow with 320k filaments accurate 99%

$ 1590/MT

Density: 1.39 - 1.43 g/cc
Filament Diameter: 13 µm
Fiber Count: 1.67 dtex
Tensile Strength at Break: 190 MPa
Elongation at Break: 15 - 27 %

RTP Company RTP 3483-1 Liquid Crystal Polymer (LCP), Carbon Fiber accurate 99%

$ 1783/MT

Specific Gravity: 1.46 g/cc
Filler Content: 20 %
Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.17 mm
Tensile Strength at Break: 190 MPa
Elongation at Break: 2.0 - 3.0 %

SGL Carbon Group PANOX® FA C063 SSC High performance Crimped staple oxidized textile fiber, For felts and non-wovens accurate 99%

$ 2258/MT

Density: 1.39 - 1.43 g/cc
Filament Diameter: 13 µm
Fiber Count: 1.67 dtex
Tensile Strength at Break: 190 MPa
Elongation at Break: 15 - 27 %

SGL Carbon Group PANOX® SA C063 EEA High performance oxidized textile fiber, Crimped staple fiber, For carbon/carbon and spinning accurate 99%

$ 1547/MT

Density: 1.39 - 1.43 g/cc
Filament Diameter: 15 µm
Fiber Count: 2.22 dtex
Tensile Strength at Break: 190 MPa
Elongation at Break: 15 - 27 %

Loxim 433 01HB Nylon 6,6 accurate 99%

$ 1519/MT

Specific Gravity: 1.37 g/cc
Linear Mold Shrinkage: 0.0030 cm/cm
Tensile Strength at Break: 190 MPa
Elongation at Break: 3.0 - 4.0 %
Flexural Modulus: 9.00 GPa

RTP Company RTP 283 A Nylon 6 (PA); Carbon Fiber accurate 99%

$ 1916/MT

Specific Gravity: 1.22 g/cc
Additive Loading: 20 %
Linear Mold Shrinkage: 0.00020 - 0.0010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 190 MPa
Elongation at Break: 2.0 - 3.0 %

RTP Company RTP 209 A Nylon 6 (PA), Glass Fiber accurate 99%

$ 2181/MT

Specific Gravity: 1.56 g/cc
Filler Content: 50 %
Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
Tensile Strength at Break: 190 MPa
Elongation at Break: 2.0 - 3.0 %

SGL Carbon Group PANOX® SA T320 EEA High performance oxidized textile fiber, Continuous Tow with 320k filaments accurate 99%

$ 1568/MT

Density: 1.39 - 1.43 g/cc
Filament Diameter: 15 µm
Fiber Count: 2.22 dtex
Tensile Strength at Break: 190 MPa
Elongation at Break: 15 - 27 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale japan. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for SGL Carbon Group PANOX® SA C063 SSC High performance oxidized textile fiber, Crimped staple fiber, For felts and non-wovens

Seller from Saint Petersburg – 2021-07-26:

Seller from Saint Petersburg work with company: 3M, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1712 per MT