Solvay TECHNYL® A 218 PA66, 33% glass fiber, DRY price 1704 per MT

Physical Properties
Density
1.14 g/cc
Water Absorption
1.3 % @Temperature 23.0 °C, Time 86400 sec
Viscosity
20 cP @Shear Rate 1000 1/s, Temperature 290 °C
Viscosity
20.5 cP @Shear Rate 1000 1/s, Temperature 280 °C
Viscosity
60 cP @Shear Rate 100 1/s, Temperature 300 °C
Viscosity
70 cP @Shear Rate 100 1/s, Temperature 290 °C
Viscosity
100 cP @Shear Rate 100 1/s, Temperature 280 °C
Viscosity
101 cP @Shear Rate 10.0 1/s, Temperature 300 °C
Viscosity
105 cP @Shear Rate 10.0 1/s, Temperature 290 °C
Viscosity
120 cP @Shear Rate 10.0 1/s, Temperature 280 °C
Linear Mold Shrinkage
0.010 cm/cm
Linear Mold Shrinkage, Flow
0.019 cm/cm
Linear Mold Shrinkage, Transverse
0.019 cm/cm

Mechanical Properties
Tensile Strength at Break
55.0 MPa
Tensile Stress
30.0 MPa @Strain 1.00 %
Tensile Stress
58.0 MPa @Strain 2.00 %
Tensile Stress
78.0 MPa @Strain 3.00 %
Tensile Stress
85.0 MPa @Strain 4.00 %
Tensile Strength, Yield
90.0 MPa
Elongation at Break
30 %
Elongation at Break
50 %
Elongation at Yield
4.0 %
Tensile Modulus
3.00 GPa
Flexural Strength
120 MPa
Flexural Strength
125 MPa
Flexural Modulus
3.00 GPa
Flexural Modulus
3.30 GPa
Izod Impact, Notched
0.800 J/cm
Izod Impact, Unnotched
NB
Izod Impact, Notched (ISO)
4.00 kJ/m²
Charpy Impact Unnotched
NB
Charpy Impact, Notched
0.450 J/cm²

Thermal Properties
CTE, linear, Parallel to Flow
70.0 µm/m-°C @Temperature 23.0 - 85.0 °C
Melting Point
263 °C
Deflection Temperature at 0.46 MPa (66 psi)
200 °C
Deflection Temperature at 0.46 MPa (66 psi)
220 °C
Flammability, UL94
V-2 @Thickness 1.60 mm
Flammability, UL94
V-2 @Thickness 3.20 mm
Oxygen Index
26 %
Glow Wire Test
650 °C @Thickness 1.60 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+15 ohm
Dielectric Constant
2.9
Dielectric Strength
25.0 kV/mm
Dissipation Factor
0.030
Comparative Tracking Index
350 V
Comparative Tracking Index
600 V

Processing Properties
Feed Temperature
265 - 275 °C
Mold Temperature
60.0 - 80.0 °C
Drying Temperature
80.0 °C
Moisture Content
<= 0.20 %

Descriptive Properties
Compression Zone
270-280°C
Mixing Zone
280-290°C

Alternative products

Solvay TECHNYL® A 221 PA66, DRY accurate 65%

$ 1444/MT

Density: 1.14 g/cc
Water Absorption: 1.1 % @Temperature 23.0 °C, Time 86400 sec
Viscosity: 17 cP @Shear Rate 1000 1/s, Temperature 300 °C
Viscosity: 19 cP @Shear Rate 1000 1/s, Temperature 290 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 280 °C

Solvay TECHNYL® A 216 NATURAL FA PA66, DRY accurate 56%

$ 1612/MT

Density: 1.14 g/cc
Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.010 cm/cm
Linear Mold Shrinkage, Flow: 0.019 cm/cm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm

Solvay TECHNYL® A 217 PA66, DRY accurate 59%

$ 2407/MT

Density: 1.14 g/cc
Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
Water Absorption: 1.5 % @Temperature 100 °C, Time 1800 sec
Linear Mold Shrinkage: 0.010 cm/cm
Linear Mold Shrinkage, Flow: 0.019 cm/cm

BASF Ultramid® 8202C HS PA6 (Dry) accurate 50%

$ 1552/MT

Density: 1.13 g/cc
Water Absorption: 1.6 %
Water Absorption: 9.3 %
Moisture Absorption at Equilibrium: 2.6 %
Relative Viscosity: 2.6 cP

BASF Ultramid® 8202C PA6 (Dry) accurate 50%

$ 1565/MT

Density: 1.13 g/cc
Water Absorption: 1.6 %
Water Absorption: 9.3 %
Moisture Absorption at Equilibrium: 2.6 %
Relative Viscosity: 2.6 cP

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 50%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

Solvay TECHNYL® A 216 PA66, DRY accurate 56%

$ 1745/MT

Density: 1.14 g/cc
Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.010 cm/cm
Linear Mold Shrinkage, Flow: 0.019 cm/cm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm

Celanese CELANEX 2002 PBT, Unfilled accurate 56%

$ 1521/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.0900 % @Temperature 22.8 °C
Moisture Absorption: 0.190 %
Linear Mold Shrinkage, Flow: 0.0180 - 0.0200 cm/cm

Celanese Celanex® 2002-2 PBT (Unverified Data**) accurate 53%

$ 1547/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.090 %
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Solvay TECHNYL® A 218 PA66, 33% glass fiber, DRY

Seller from Hechi – 2021-06-28:

Seller from Hechi work with company: 3M, Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1704 per MT

Seller from Dhaka – 2021-06-10:

Seller from Dhaka work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1820 per MT

Seller from Alexandria – 2021-08-14:

Seller from Alexandria work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2252 per MT