Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY price 1723 per MT

Physical Properties
Density
1.36 g/cc
Water Absorption
1.05 % @Temperature 23.0 °C, Time 86400 sec
Viscosity
30 cP @Shear Rate 10000 1/s, Temperature 240 °C
Viscosity
30 cP @Shear Rate 10000 1/s, Temperature 250 °C
Viscosity
30 cP @Shear Rate 10000 1/s, Temperature 260 °C
Viscosity
150 cP @Shear Rate 1000 1/s, Temperature 260 °C
Viscosity
190 cP @Shear Rate 1000 1/s, Temperature 250 °C
Viscosity
200 cP @Shear Rate 1000 1/s, Temperature 240 °C
Viscosity
300 cP @Shear Rate 100 1/s, Temperature 260 °C
Viscosity
400 cP @Shear Rate 100 1/s, Temperature 250 °C
Viscosity
500 cP @Shear Rate 100 1/s, Temperature 240 °C
Linear Mold Shrinkage
0.0043 cm/cm
Linear Mold Shrinkage, Flow
0.0030 cm/cm
Linear Mold Shrinkage, Transverse
0.0070 cm/cm

Mechanical Properties
Tensile Strength at Break
170 MPa
Tensile Strength at Break
190 MPa
Tensile Stress
60.0 MPa @Strain 0.500 %
Tensile Stress
100 MPa @Strain 1.00 %
Tensile Stress
160 MPa @Strain 2.00 %
Tensile Stress
180 MPa @Strain 3.00 %
Elongation at Break
3.2 %
Elongation at Break
3.5 %
Tensile Modulus
9.60 GPa
Flexural Strength
255 MPa
Flexural Modulus
8.40 GPa
Izod Impact, Notched (ISO)
14.0 kJ/m²
Izod Impact, Notched (ISO)
125 kJ/m²
Charpy Impact Unnotched
9.20 J/cm²
Charpy Impact, Notched
1.50 J/cm²

Thermal Properties
CTE, linear, Parallel to Flow
32.0 µm/m-°C @Temperature 23.0 - 85.0 °C
Melting Point
222 °C
Deflection Temperature at 1.8 MPa (264 psi)
205 °C
Flammability, UL94
HB @Thickness 0.400 - 3.20 mm
Oxygen Index
23 %
Glow Wire Test
650 °C @Thickness 1.60 - 3.20 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+13 ohm
Dielectric Constant
3.8
Dissipation Factor
0.020
Comparative Tracking Index
475 V
Comparative Tracking Index
600 V

Processing Properties
Feed Temperature
230 - 235 °C
Mold Temperature
70.0 - 100 °C
Drying Temperature
80.0 °C
Moisture Content
<= 0.20 %

Descriptive Properties
Compression Zone
235-245°C
Mixing Zone
245-250°C

Alternative products

BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) accurate 60%

$ 1456/MT

Density: 1.136 g/cc
Density: 1.39 g/cc
Water Absorption: 1.1 %
Water Absorption: 6.4 %
Moisture Absorption at Equilibrium: 1.8 %

SABIC Innovative Plastics Valox® 4031 PBT (Europe-Africa-Middle East) accurate 53%

$ 1609/MT

Specific Gravity: 1.54 g/cc
Density: 1.54 g/cc
Filler Content: 20 %
Moisture Absorption: 0.0600 %
Water Absorption at Saturation: 0.26 %

Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY accurate 67%

$ 1895/MT

Density: 1.34 g/cc
Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0054 cm/cm
Linear Mold Shrinkage, Flow: 0.0035 cm/cm
Linear Mold Shrinkage, Transverse: 0.0065 cm/cm

Solvay TECHNYL® A 218 V30 PA66, 30% glass fiber, DRY accurate 63%

$ 1644/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 280 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 290 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 300 °C

Solvay TECHNYL® A 216 V33 PA66, 33% glass fiber, DRY accurate 60%

$ 1524/MT

Density: 1.38 g/cc
Water Absorption: 0.78 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0062 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Solvay TECHNYL® A 216 V30 PA66, 33% glass fiber, DRY accurate 60%

$ 1537/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0062 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Solvay TECHNYL® A 218 V25 Black 21 N PA66, 25% glass fiber, DRY accurate 60%

$ 1508/MT

Density: 1.32 g/cc
Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
Viscosity: 30 cP @Shear Rate 1000 1/s, Temperature 280 °C
Viscosity: 30 cP @Shear Rate 1000 1/s, Temperature 290 °C
Viscosity: 30 cP @Shear Rate 1000 1/s, Temperature 300 °C

Solvay TECHNYL® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY accurate 67%

$ 1554/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 280 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 290 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 300 °C

Solvay TECHNYL® A 218G1 V30 Black 34N PA66, 30% glass fiber, DRY accurate 56%

$ 1556/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
Tensile Strength at Break: 195 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, passenger catamarans for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY

Seller from Bangkok – 2021-07-18:

Seller from Bangkok work with company: Solvay, Techmer ES, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2181 per MT

Seller from Riyadh – 2021-08-18:

Seller from Riyadh work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1880 per MT

Seller from Bangkok – 2021-02-26:

Seller from Bangkok work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1723 per MT