Styron CALIBREâ„¢ 201-6 Polycarbonate Resin price 1452 per MT

Physical Properties
Density
1.20 g/cc
Water Absorption
0.32 % @Temperature 23.0 °C
Water Absorption
0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.0050 - 0.0070 cm/cm
Melt Flow
6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell M
73
Hardness, Rockwell R
118
Tensile Strength at Break
72.0 MPa
Tensile Strength at Break
72.4 MPa
Tensile Strength, Yield
60.0 MPa
Elongation at Break
150 %
Elongation at Yield
6.0 %
Tensile Modulus
2.30 GPa
Tensile Modulus
2.41 GPa
Flexural Strength
96.5 MPa
Flexural Strength
97.0 MPa
Flexural Modulus
2.40 GPa
Flexural Modulus
2.41 GPa
Izod Impact, Notched
9.10 J/cm @Temperature 23.0 °C
Izod Impact, Notched (ISO)
93.0 kJ/m² @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Temperature 23.0 °C
Tensile Impact Strength
588 kJ/m²
Dart Drop, Total Energy
90.4 J
Abrasion
45

Thermal Properties
CTE, linear, Parallel to Flow
68.0 µm/m-°C @Temperature -40.0 - 82.0 °C
Hot Ball Pressure Test
125 °C
Deflection Temperature at 0.46 MPa (66 psi)
145 °C
Deflection Temperature at 0.46 MPa (66 psi)
146 °C
Deflection Temperature at 1.8 MPa (264 psi)
126 °C
Deflection Temperature at 1.8 MPa (264 psi)
129 °C
Deflection Temperature at 1.8 MPa (264 psi)
142 °C
Deflection Temperature at 1.8 MPa (264 psi)
143 °C
Vicat Softening Point
151 °C @Load 5.10 kg
Flammability, UL94
HB @Thickness 1.59 mm
Flammability, UL94
HB @Thickness 3.20 mm

Optical Properties
Refractive Index
1.586
Haze
1.0 %
Transmission, Visible
89 %

Electrical Properties
Volume Resistivity
2.00e+17 ohm-cm
Dielectric Constant
3.0 @Frequency 60.0 Hz
Dielectric Constant
3.0 @Frequency 1.00e+6 Hz
Dielectric Strength
17.0 kV/mm
Dissipation Factor
0.0010 @Frequency 50.0 Hz
Dissipation Factor
0.0020 @Frequency 1.00e+6 Hz
Comparative Tracking Index
250 V @Thickness 2.00 mm

Descriptive Properties
Average Extent of Burring
3 cm

Alternative products

Styron CALIBREâ„¢ 200-3 Polycarbonate Resin accurate 70%

$ 1805/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 301-6 Polycarbonate Resin accurate 97%

$ 2512/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 300-6 Polycarbonate Resin accurate 97%

$ 1854/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 300-10 Polycarbonate Resin accurate 70%

$ 1526/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 200-6 Polycarbonate Resin accurate 97%

$ 1502/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 302-6 Polycarbonate Resin accurate 99%

$ 1666/MT

Density: 1.20 g/cc
Water Absorption: 0.25 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 302V-6 Polycarbonate Resin accurate 68%

$ 2203/MT

Density: 1.20 g/cc
Water Absorption: 0.25 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 302-10 Polycarbonate Resin accurate 70%

$ 1494/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 201-22 Polycarbonate Resin accurate 68%

$ 1490/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, old cruise ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Styron CALIBREâ„¢ 201-6 Polycarbonate Resin

Seller from Washington – 2021-07-22:

Seller from Washington work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1452 per MT

Seller from Xi’an – 2021-06-06:

Seller from Xi’an work with company: 3M, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2588 per MT

Seller from Luanda – 2021-05-07:

Seller from Luanda work with company: Celanese Corporation, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1691 per MT