Taiwan PU Corporation TPUI-L75 Low Temperature Resistance, Injection Molding Polyester Base TPU price 2253 per MT

Mechanical Properties
Hardness, Shore A
75
Tensile Strength at Break
29.42 MPa
Elongation at Break
800 %
100% Modulus
0.00390 GPa
300% Modulus
0.00740 GPa
Resilience
50
Taber Abrasion, mg/1000 Cycles
20

Processing Properties
Feed Temperature
170 °C
Middle Barrel Temperature
175 °C
Front Barrel Temperature
180 °C
Adapter Temperature
185 °C
Die Temperature
185 °C

Alternative products

Taiwan PU Corporation TPU-EH80 High Hydrolysis Resistance, Extrusion Molding Polyether Base TPU accurate 59%

$ 1926/MT

Hardness, Shore A: 80
Tensile Strength at Break: 22.56 MPa
Elongation at Break: 1000 %
100% Modulus: 0.00540 GPa
300% Modulus: 0.00780 GPa

Precision Polymer Engineering N70M Nitrile Rubber accurate 39%

$ 1602/MT

Hardness, Shore A: 75
Hardness, Shore A: 70 - 85
Tensile Strength, Yield: 13.0 MPa
Tensile Strength, Yield: 12.35 - 13.65 MPa
Elongation at Break: 280 %

Taiwan PU Corporation TPU-CH85 High Hydrolysis Resistance, Calender Molding Polyether Base TPU accurate 39%

$ 1467/MT

Hardness, Shore A: 40
Tensile Strength at Break: 21.57 MPa
Elongation at Break: 950 %
100% Modulus: 0.00590 GPa
300% Modulus: 0.00590 GPa

Braskem GF4960 HDPE Blow Molding Polyethylene Homopolymer accurate 39%

$ 1485/MT

Density: 0.961 g/cc
ESCR 100% Igepal®: 25 hour @Thickness 2.00 mm, Temperature 50.0 °C
Melt Flow: 0.34 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow: 28 g/10 min @Load 21.6 kg, Temperature 190 °C
Tensile Strength at Break: 35.0 MPa

Taiwan PU Corporation TPU-C85 General Grade, Calender Molding Polyester Base TPU accurate 59%

$ 1628/MT

Hardness, Shore A: 40
Tensile Strength at Break: 23.54 MPa
Elongation at Break: 900 %
100% Modulus: 0.00490 GPa
300% Modulus: 0.00490 GPa

Braskem GF4950HS HDPE Blow Molding Polyethylene Copolymer accurate 39%

$ 2062/MT

Density: 0.951 g/cc
ESCR 100% Igepal®: 480 hour @Thickness 2.00 mm, Temperature 50.0 °C
ESCR 10% Igepal®: 150 hour @Thickness 2.00 mm, Temperature 50.0 °C
Melt Flow: 0.21 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow: 20 g/10 min @Load 21.6 kg, Temperature 190 °C

Kraiburg TPE THERMOLAST® K TF0STL Thermoplastic Elastomer, very low rubber hardness accurate 39%

$ 1997/MT

Density: 0.870 g/cc
Tensile Strength: 1.50 MPa
Elongation at Break: 800 %
Tear Strength: 3.00 kN/m
Rear Barrel Temperature: 140 °C

ExxonMobil ESCOR™ AT 325 Molding, extrusion and compounding resin (discontinued **) accurate 39%

$ 1935/MT

Density: 0.951 g/cc
Methyl Acrylate Content: 20 %
Acrylic Acid Content: 6.0 %
Melt Flow: 20 g/10 min
Hardness, Shore A: 75

Taiwan PU Corporation TPUI-E80 General Grade, Injection Molding Polyester Base TPU accurate 59%

$ 2361/MT

Hardness, Shore A: 80
Tensile Strength at Break: 31.38 MPa
Elongation at Break: 800 %
100% Modulus: 0.00540 GPa
300% Modulus: 0.00780 GPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship on sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Taiwan PU Corporation TPUI-L75 Low Temperature Resistance, Injection Molding Polyester Base TPU

Seller from Los Angeles – 2021-05-21:

Seller from Los Angeles work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2253 per MT