UBE UBESTA® 3030JI44 Plasticized Industrial Grade Nylon 12 price 2340 per MT

Physical Properties
Density
1.00 g/cc
Melt Flow
11 g/10 min @Load 2.16 kg, Temperature 235 °C

Mechanical Properties
Hardness, Shore D
50
Tensile Strength at Break
>= 30.0 MPa
Tensile Strength, Yield
16.0 MPa
Elongation at Break
>= 300 %
Flexural Strength
10.0 MPa
Flexural Modulus
0.200 GPa
Izod Impact, Notched
0.880 J/cm

Thermal Properties
Melting Point
169 °C
Deflection Temperature at 0.46 MPa (66 psi)
101 °C

Processing Properties
Processing Temperature
230 °C
Feed Temperature
40.0 °C
Zone 1
190 °C
Zone 1
230 °C
Zone 2
210 °C
Zone 2
225 °C
Zone 3
220 °C
Zone 3
230 °C
Zone 4
215 °C
Die Temperature
230 °C
Mold Temperature
40.0 - 60.0 °C
Injection Velocity
100 mm/sec
Die Opening
0.0400 cm
Roll Temperature
50.0 °C
Drying Temperature
80.0 °C
Drying Temperature
100 °C
Drying Temperature
110 °C
Dry Time
2 - 4 hour
Dry Time
4 - 6 hour
Dry Time
6 - 8 hour
Injection Pressure
40.0 - 50.0 MPa
Hold Pressure
25.0 - 50.0 MPa
Back Pressure
5.00 MPa
Screw Speed
15 - 76 rpm

Descriptive Properties
C/R
3-3.5:1
Calibrating Vacuum
100 mbar
Calibration
9.95 mm
Compression Ratio
2.5-3.5:1
Compression Ratio
min 3:1
Die Diameter
16 mm
Die Width
300 mm
Extractables
22%
Extruder
Barmag, Screw Diameter = 30 mm
Extruder Characteristics
65 mm screw diameter
Film Thickness
60 microns
Flight Depth in the Feeding Zone
10-15% of Screw Diameter
Flight Depth in the Metering Zone
5-7% of Screw Diameter
Haul Off Speed
5 m/min
Haul Speed
10-55 m/min
L/D Ratio
25:1
L/D Ratio
min 20:1
Length of Compression Zone
25-45% of total screw length
Length of Compression Zone
30% of screw length
Length of Feeding Zone
20-40% of total screw length
Length of Feeding Zone
30-40% of screw length
Length of Metering Zone
30-45% of screw length
Length of Metering Zone
35-45% of total screw length
Mandrel Diameter
12 mm
Peripheral screw speed
10 m/min
Water Temperature
10-18°C

Alternative products

UBE UBESTA® 3030JI6L Plasticized Automotive Grade Nylon 12 accurate 89%

$ 1796/MT

Density: 1.00 g/cc
Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 66
Tensile Strength at Break: >= 56.0 MPa
Tensile Strength, Yield: 28.0 MPa

UBE UBESTA® 3030JI5L Plasticized Automotive Grade Nylon 12 accurate 92%

$ 1700/MT

Density: 1.02 g/cc
Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 64
Tensile Strength at Break: >= 41.0 MPa
Tensile Strength, Yield: 26.0 MPa

UBE UBESTA® 3030JLX2 Plasticized Automotive Grade Nylon 12 accurate 92%

$ 1777/MT

Density: 1.02 g/cc
Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 68
Tensile Strength at Break: >= 56.0 MPa
Tensile Strength, Yield: 32.0 MPa

UBE UBESTA® 3030JLX1 Plasticized Automotive Grade Nylon 12 accurate 92%

$ 1526/MT

Density: 1.03 g/cc
Melt Flow: 7.7 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 67
Tensile Strength at Break: >= 56.0 MPa
Tensile Strength, Yield: 26.0 MPa

UBE UBESTA® 3030JFX1 Plasticized Industrial Grade Nylon 12 accurate 92%

$ 1976/MT

Density: 1.03 g/cc
Melt Flow: 7.4 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 65
Tensile Strength at Break: >= 58.0 MPa
Tensile Strength, Yield: 25.0 MPa

UBE UBESTA® 3030JNU Short Cycle Time Electronic Grade Nylon 12 accurate 89%

$ 1512/MT

Density: 1.00 g/cc
Melt Flow: 8.2 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Rockwell R: 71
Tensile Strength at Break: >= 56.0 MPa
Tensile Strength, Yield: 23.0 MPa

UBE UBESTA® 3030JI9L Plasticized Automotive Grade Nylon 12 accurate 92%

$ 2219/MT

Density: 1.03 g/cc
Melt Flow: 4.3 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 69
Tensile Strength at Break: >= 46.0 MPa
Tensile Strength, Yield: 28.0 MPa

UBE UBESTA® 3035JX47 Plasticized Industrial Grade Nylon 12 accurate 89%

$ 1677/MT

Density: 1.07 g/cc
Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 63
Tensile Strength at Break: >= 17.0 MPa
Tensile Strength, Yield: 18.0 MPa

UBE UBESTA® 3035JU5 Plasticized Industrial Grade Nylon 12 accurate 97%

$ 2208/MT

Density: 1.03 g/cc
Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 54
Tensile Strength at Break: >= 30.0 MPa
Tensile Strength, Yield: 13.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships forsale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for UBE UBESTA® 3030JI44 Plasticized Industrial Grade Nylon 12

Seller from Hāora – 2021-06-15:

Seller from Hāora work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2340 per MT

Seller from Nanjing – 2021-04-20:

Seller from Nanjing work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2568 per MT