Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone price 1588 per MT

Physical Properties
Density
1.51 g/cc
Water Absorption at Saturation
0.30 % @Temperature 23.0 °C
Water Absorption at Saturation
0.45 % @Temperature 100 °C
Viscosity
700000 cP @Temperature 420 °C
Linear Mold Shrinkage, Flow
0.0030 cm/cm
Linear Mold Shrinkage, Transverse
0.0080 cm/cm
Spiral Flow
9.00 cm @Thickness 1.00 mm
Spiral Flow
45.0 cm @Thickness 3.00 mm

Mechanical Properties
Tensile Strength at Break
30.0 MPa @Temperature 275 °C
Tensile Strength at Break
50.0 MPa @Temperature 175 °C
Tensile Strength at Break
95.0 MPa @Temperature 125 °C
Tensile Strength at Break
170 MPa @Temperature 23.0 °C
Elongation at Break
2.9 %
Tensile Modulus
11.5 GPa
Flexural Strength
45.0 MPa @Temperature 275 °C
Flexural Strength
75.0 MPa @Temperature 175 °C
Flexural Strength
170 MPa @Temperature 125 °C
Flexural Strength
260 MPa @Temperature 23.0 °C
Flexural Modulus
10.0 GPa
Compressive Strength
35.0 MPa @Temperature 200 °C
Compressive Strength
120 MPa @Temperature 120 °C
Compressive Strength
190 MPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
12.0 kJ/m²
Izod Impact, Unnotched (ISO)
65.0 kJ/m²
Charpy Impact Unnotched
7.00 J/cm²
Charpy Impact, Notched
1.20 J/cm²

Thermal Properties
CTE, linear
45.0 µm/m-°C @Temperature <=143 °C
CTE, linear
120 µm/m-°C @Temperature >=143 °C
CTE, linear, Parallel to Flow
18.0 µm/m-°C @Temperature <=143 °C
CTE, linear, Parallel to Flow
22.0 µm/m-°C @Temperature >=143 °C
Thermal Conductivity
0.300 W/m-K
Thermal Conductivity
0.350 W/m-K
Melting Point
343 °C
Deflection Temperature at 1.8 MPa (264 psi)
320 °C
Glass Transition Temp, Tg
>= 143 °C
Glass Transition Temp, Tg
150 °C

Electrical Properties
Volume Resistivity
1.00e+16 ohm-cm
Dielectric Constant
3.5 @Frequency 1000 Hz
Dielectric Strength
20.0 kV/mm @Thickness 2.00 mm
Dielectric Loss Index
0.0040 @Frequency 1.00e+6 Hz
Comparative Tracking Index
150 V

Processing Properties
Processing Temperature
<= 100 °C
Nozzle Temperature
405 °C
Mold Temperature
180 - 200 °C
Dry Time
3.00 hour @Temperature 150 °C
Dry Time
5.00 hour @Temperature 120 °C

Alternative products

Victrex® PEEK 90GL30 BLACK EU 30% Glass Fiber Filled, PolyEtherEtherKetone accurate 63%

$ 1470/MT

Density: 1.52 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 200000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

Victrex® PEEK 450GL20 Polyetheretherketone, 20% Glass Fibre Reinforced accurate 63%

$ 1559/MT

Density: 1.43 g/cc
Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 475000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

BASF Styrodur® 3035 CN Extruded Rigid Polystyrene Foam (Europe) accurate 99%

$ 1548/MT

Density: 0.0300 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 100 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

Victrex® PEEK 450GL30 30% Glass Fiber Reinforced accurate 67%

$ 1749/MT

Density: 1.51 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 550000 cP @Temperature 400 °C
Linear Mold Shrinkage: 0.0030 cm/cm

BASF Styrodur® 2800 C Extruded Rigid Polystyrene Foam (Europe) accurate 99%

$ 2010/MT

Density: 0.0300 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 5.0 %
Water Vapor Transmission: 80.0 - 200 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA) (Unverified Data**) accurate 63%

$ 1789/MT

Density: 1.44 g/cc
Filler Content: 33 %
Water Absorption: 0.21 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00 cm/cm
Linear Mold Shrinkage, Flow: 0.0040 cm/cm

BASF Styrodur® 4000 CS Extruded Rigid Polystyrene Foam (Europe) accurate 99%

$ 2342/MT

Density: 0.0350 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 80.0 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

BASF Styrodur® 3035 CS Extruded Rigid Polystyrene Foam (Europe) accurate 99%

$ 2271/MT

Density: 0.0330 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 50.0 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black accurate 63%

$ 1983/MT

Density: 1.51 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 550000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone

Seller from Luanda – 2021-05-15:

Seller from Luanda work with company: Celanese Corporation, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2404 per MT

Seller from Taipei – 2021-04-18:

Seller from Taipei work with company: RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1588 per MT