Victrex® PEEK 90HMF40 Polyetheretherketone (PEEK), 40% Carbon Fiber Reinforced price 2249 per MT

Physical Properties
Specific Gravity
1.45 g/cc @Temperature 23.0 °C
Water Absorption at Saturation
0.30 % @Temperature 23.0 °C
Water Absorption at Saturation
0.40 % @Temperature 100 °C
Viscosity
300000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow
0.00 cm/cm
Linear Mold Shrinkage, Transverse
0.0040 cm/cm
Spiral Flow
10.0 cm @Thickness 1.00 mm

Mechanical Properties
Hardness, Shore D
88.5
Tensile Strength at Break
85.0 MPa @Temperature 275 °C
Tensile Strength at Break
145 MPa @Temperature 180 °C
Tensile Strength at Break
220 MPa @Temperature 120 °C
Tensile Strength at Break
330 MPa @Temperature 23.0 °C
Elongation at Yield
1.2 % @Temperature 23.0 °C
Tensile Modulus
43.0 GPa @Temperature 23.0 °C
Flexural Strength
120 MPa @Temperature 275 °C
Flexural Strength
220 MPa @Temperature 180 °C
Flexural Strength
350 MPa @Temperature 120 °C
Flexural Strength
475 MPa @Temperature 23.0 °C
Flexural Modulus
37.0 GPa @Temperature 23.0 °C
Compressive Strength
120 MPa @Temperature 200 °C
Compressive Strength
250 MPa @Temperature 120 °C
Compressive Strength
310 MPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
10.5 kJ/m² @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
60.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
6.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.800 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear
35.0 µm/m-°C @Temperature <=143 °C
CTE, linear
80.0 µm/m-°C @Temperature >=143 °C
CTE, linear, Parallel to Flow
1.00 µm/m-°C @Temperature >=143 °C
CTE, linear, Parallel to Flow
3.00 µm/m-°C @Temperature <=143 °C
Thermal Conductivity
2.00 W/m-K
Thermal Conductivity
4.30 W/m-K
Melting Point
343 °C
Deflection Temperature at 1.8 MPa (264 psi)
349 °C
Glass Transition Temp, Tg
143 °C

Electrical Properties
Volume Resistivity
1e+05

Processing Properties
Processing Temperature
<= 100 °C
Nozzle Temperature
385 °C
Mold Temperature
190 - 200 °C
Drying Temperature
>= 150 °C @Time 10800 sec
Drying Temperature
>= 160 °C @Time 7200 sec

Alternative products

Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced accurate 70%

$ 1967/MT

Density: 1.44 g/cc
Water Absorption at Saturation: 0.25 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 850000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0010 cm/cm

Victrex® PEEK 450FC30 General Purpose accurate 70%

$ 1612/MT

Density: 1.45 g/cc
Water Absorption at Saturation: 0.35 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.35 % @Temperature 100 °C
Viscosity: 550000 cP @Temperature 400 °C
Linear Mold Shrinkage: 0.0030 cm/cm

Victrex® PEEK 450CA30 30% Carbon Fiber Reinforced accurate 85%

$ 1699/MT

Density: 1.40 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 675000 cP @Temperature 400 °C
Linear Mold Shrinkage: 0.0010 cm/cm

Victrex® PEEK 90HMF20 Polyetheretherketone (PEEK), 20% Carbon Fiber Reinforced accurate 70%

$ 1811/MT

Specific Gravity: 1.37 g/cc @Temperature 23.0 °C
Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.50 % @Temperature 100 °C
Viscosity: 175000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.00 cm/cm

Victrex® WG101™ Polyaryletherketone accurate 85%

$ 1740/MT

Density: 1.44 g/cc
Water Absorption: 0.30 %
Water Absorption: 0.60 % @Time 360000 sec
Viscosity: 325000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.00 cm/cm

Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone accurate 85%

$ 2368/MT

Density: 1.40 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 800000 cP @Temperature 420 °C
Linear Mold Shrinkage, Flow: 0.0010 cm/cm

Victrex® PEEK 150CA30 30% Carbon Fiber Reinforced accurate 70%

$ 1973/MT

Density: 1.40 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 300000 cP @Temperature 400 °C
Linear Mold Shrinkage: 0.0010 cm/cm

Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced accurate 99%

$ 2258/MT

Density: 1.40 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 250000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0010 cm/cm

Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced accurate 70%

$ 2017/MT

Density: 1.41 g/cc
Water Absorption at Saturation: 0.50 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.60 % @Temperature 100 °C
Viscosity: 525000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0010 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, container ship sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Victrex® PEEK 90HMF40 Polyetheretherketone (PEEK), 40% Carbon Fiber Reinforced

Seller from Istanbul – 2021-06-19:

Seller from Istanbul work with company: RTP Company, Teknor Apex Company, BASF, ALIMEX GmbH

Price: $2498 per MT

Seller from Hong Kong – 2021-05-12:

Seller from Hong Kong work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2249 per MT