$ 1510/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 36
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1632/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 56.1 MPa
- Tensile Modulus: 2.65 GPa
- Flexural Strength: 99.9 MPa
$ 1834/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.7 MPa
- Tensile Modulus: 3.30 GPa
- Flexural Strength: 83.6 MPa
$ 1467/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 42.1 MPa
- Tensile Modulus: 2.69 GPa
$ 1473/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 43.9 MPa
- Tensile Modulus: 2.61 GPa
- Flexural Strength: 80.7 MPa
$ 2319/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 63.5 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 49.0 MPa
$ 1547/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -42.0 °C
$ 1862/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 41.6 MPa
- Tensile Modulus: 2.95 GPa
- Flexural Strength: 79.3 MPa
$ 1496/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 55.9 cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 50.3 MPa
$ 1484/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: >= 80 @Temperature 23.0 °C
- Tensile Strength, Yield: 39.3 MPa
- Elongation at Break: 160 %
- Tensile Modulus: 2.34 GPa
$ 2454/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 46.9 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 95.1 MPa
$ 2024/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 85
- Tensile Strength, Yield: 56.9 MPa
- Tensile Modulus: 2.87 GPa
- Flexural Strength: 93.5 MPa
$ 2356/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 47.2 MPa
- Tensile Modulus: 2.97 GPa
- Flexural Strength: 87.4 MPa
$ 1525/MT
- Specific Gravity: 1.40 g/cc
- Deformation: 20 % @Temperature 55.0 °C, Time 3600 sec
- Hardness, Shore A: 76
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 350 %
$ 1916/MT
- Specific Gravity: 1.54 g/cc
- Spiral Flow: 66.0 cm
- Hardness, Shore D: 85
- Tensile Strength, Yield: 86.2 MPa
- Elongation at Break: 3.0 %
$ 1574/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 2.79 GPa
$ 1604/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1944/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1746/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2356/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Rockwell R: 111
- Hardness, Shore D: 78
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.69 GPa
$ 1634/MT
- Specific Gravity: 1.37 g/cc
- Deformation: 25 % @Temperature 121 °C, Time 3600 sec
- Hardness, Shore D: 41
- Hardness, Shore D: 47
- Tensile Strength, Yield: 17.2 MPa
$ 2111/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 77
- Tensile Strength, Yield: 49.4 MPa
- Elongation at Break: 55 %
- Izod Impact, Notched: 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C
$ 1943/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 57
- Hardness, Shore D: 68
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 300 %
$ 2284/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 250 %
- Tensile Modulus: 0.00896 GPa
$ 1451/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 85
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 91.9 MPa
$ 1514/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1607/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 91.4 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.4 MPa
$ 1655/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 44.6 MPa
- Tensile Modulus: 2.56 GPa
- Flexural Strength: 74.6 MPa
$ 1994/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 330 %
- Tensile Modulus: 0.00827 GPa
$ 1653/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Shore A: 84
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2273/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 42.3 MPa
- Tensile Modulus: 3.06 GPa
- Flexural Strength: 82.7 MPa
$ 1685/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 46.5 MPa
- Tensile Modulus: 2.56 GPa
- Flexural Strength: 78.6 MPa
$ 2306/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 17.4 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 105 °C
$ 2334/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 41.9 MPa
- Tensile Modulus: 2.71 GPa
- Flexural Strength: 72.1 MPa
$ 1471/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 450 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1747/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.1 MPa
- Tensile Modulus: 2.59 GPa
- Flexural Strength: 78.2 MPa
$ 1924/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 92
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1553/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 92
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1755/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -23.0 °C
$ 1798/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1682/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -19.0 °C
$ 2487/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1739/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 105 °C
$ 2447/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore D: 42
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 250 %
- Tensile Modulus: 0.0124 GPa
$ 1531/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00896 GPa
$ 1528/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00896 GPa
$ 1520/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 43.7 MPa
- Tensile Modulus: 2.89 GPa
- Flexural Strength: 82.3 MPa
$ 2420/MT
- Specific Gravity: 1.62 g/cc
- Spiral Flow: 63.5 cm
- Hardness, Shore D: 88
- Tensile Strength, Yield: 103 MPa
- Elongation at Break: 2.0 %
$ 1447/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 2.88 GPa
$ 1747/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1602/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 53.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 88.5 MPa
$ 1578/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 290 %
- Brittleness Temperature: -26.0 °C
$ 2273/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.833 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.5 MPa
- Tensile Modulus: 2.53 GPa
$ 2163/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 53.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 88.5 MPa
$ 1464/MT
- Specific Gravity: 1.32 g/cc
- Density: <= 0.833 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 44.4 MPa
- Tensile Modulus: 2.36 GPa
$ 2054/MT
- Specific Gravity: 1.43 g/cc
- Spiral Flow: 58.4 cm
- Tensile Strength, Yield: 46.2 MPa
- Elongation at Break: 29 %
- Tensile Modulus: 2.74 GPa
$ 1444/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -25.0 °C
$ 2316/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1447/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 52.2 MPa
- Tensile Modulus: 2.78 GPa
- Flexural Strength: 92.6 MPa
$ 2514/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 71.1 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 46.2 MPa
$ 1613/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 48.3 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 89.6 MPa
$ 1987/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00896 GPa
$ 1552/MT
- Specific Gravity: 1.48 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.92 GPa
- Flexural Strength: 84.3 MPa
$ 1886/MT
- Specific Gravity: 1.35 g/cc
- Density: 0.801 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 43.1 MPa
- Tensile Modulus: 2.32 GPa
$ 2327/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 84
- Hardness, Shore A: 90
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 390 %
$ 1666/MT
- Specific Gravity: 1.62 g/cc
- Hardness, Shore D: 48
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1933/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 61
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2148/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1848/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 43.1 MPa
- Tensile Modulus: 2.84 GPa
- Flexural Strength: 78.0 MPa
$ 1517/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 41.6 MPa
- Tensile Modulus: 2.95 GPa
- Flexural Strength: 79.3 MPa
$ 2150/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 61.0 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.3 MPa
$ 1505/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 70.3 MPa
$ 1635/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 119.38 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.4 MPa
$ 2235/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1449/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 40.7 MPa
- Tensile Modulus: 3.01 GPa
- Flexural Yield Strength: 66.4 MPa
$ 2283/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 47.9 MPa
- Tensile Modulus: 3.09 GPa
- Flexural Strength: 90.3 MPa
$ 2268/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -28.1 °C
$ 1750/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1501/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 50.5 MPa
- Tensile Modulus: 2.83 GPa
- Flexural Strength: 104 MPa
$ 2206/MT
- Specific Gravity: 0.707 g/cc
- Hardness, Shore D: 75
- Tensile Modulus: 1.26 GPa
- Flexural Strength: 33.0 MPa
- Flexural Modulus: 1.81 GPa
$ 1447/MT
- Specific Gravity: 1.35 g/cc
- Tensile Strength, Yield: 48.3 MPa
- Tensile Modulus: 3.24 GPa
- Flexural Strength: 86.9 MPa
- Flexural Modulus: 2.76 GPa
$ 1663/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.4 MPa
$ 1975/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 90.0 °C
$ 2281/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1696/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 105 °C
$ 1524/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 80
- Tensile Strength, Yield: 44.8 MPa
$ 1657/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2407/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -46.0 °C
$ 1848/MT
- Specific Gravity: 0.549 - 0.648 g/cc
- Hardness, Shore D: 47
- Tensile Strength, Yield: 14.9 MPa
- Tensile Modulus: 1.14 GPa
- Flexural Strength: 29.1 MPa
$ 1573/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.6 MPa
- Tensile Modulus: 2.81 GPa
$ 1572/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 109.22 cm
- Hardness, Shore D: 84
- Tensile Strength, Yield: 62.7 MPa
$ 1588/MT
- Specific Gravity: 1.31 g/cc
- Deformation: 12 % @Temperature 121 °C, Time 3600 sec
- Hardness, Shore D: 58
- Tensile Strength, Yield: 25.2 MPa
- Elongation at Break: 300 %
$ 1458/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -37.0 °C
$ 1889/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 76
- Tensile Strength, Yield: 30.4 MPa
- Tensile Modulus: 2.01 GPa
- Flexural Yield Strength: 54.1 MPa
$ 2050/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1935/MT
- Specific Gravity: 0.549 - 0.648 g/cc
- Hardness, Shore D: 47
- Tensile Strength, Yield: 14.9 MPa
- Tensile Modulus: 1.14 GPa
- Flexural Strength: 29.1 MPa
$ 2358/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -25.0 °C
$ 2433/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore D: 59
- Tensile Strength: 19.3 MPa @Strain 100 %
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: 220 %
$ 1497/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 44.1 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 84.8 MPa
$ 1510/MT
- Specific Gravity: 1.31 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 79
- Tensile Strength, Yield: 44.1 MPa
$ 2031/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 43.7 MPa
- Tensile Modulus: 2.46 GPa
- Flexural Strength: 75.8 MPa
$ 1890/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 85
- Tensile Strength, Yield: 56.9 MPa
- Tensile Modulus: 2.87 GPa
- Flexural Strength: 93.5 MPa
$ 1671/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore D: 56
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 290 %
- Brittleness Temperature: -20.0 °C
$ 2578/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 61.0 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 44.8 MPa
$ 1633/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore D: 35
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 105 °C
$ 2256/MT
- Specific Gravity: 0.549 - 0.748 g/cc
- Hardness, Shore D: 47
- Tensile Strength, Yield: 14.9 MPa
- Tensile Modulus: 1.14 GPa
- Flexural Strength: 29.1 MPa
$ 1901/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore D: 33
- Hardness, Shore D: 45
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 250 %
$ 2012/MT
- Specific Gravity: 1.43 g/cc
- Density: 0.863 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 44.5 MPa
- Flexural Strength: 78.6 MPa
$ 1604/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 81
- Tensile Strength: 45.5 MPa
- Elongation at Break: 32 %
$ 1801/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 66.0 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 55.6 MPa
$ 1837/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 53.8 MPa
- Tensile Modulus: 2.83 GPa
- Izod Impact, Notched: 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C
$ 1457/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1444/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1468/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 69
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1530/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore D: 43
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.0152 GPa
$ 2210/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 79
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -42.0 °C
$ 1589/MT
- Specific Gravity: 1.30 g/cc
- Density: 0.785 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 45.3 MPa
- Flexural Strength: 82.7 MPa
$ 1725/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 40.9 MPa
- Tensile Modulus: 2.61 GPa
- Flexural Strength: 73.0 MPa
$ 1569/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2206/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1501/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore D: 77
- Tensile Strength at Break: 28.3 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 105 °C
$ 1852/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 45.5 MPa
- Tensile Modulus: 2.58 GPa
- Flexural Strength: 78.9 MPa
$ 2149/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 85
- Tensile Strength, Yield: 56.9 MPa
- Tensile Modulus: 2.87 GPa
- Flexural Strength: 93.5 MPa
$ 2489/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 46.0 MPa
- Tensile Modulus: 2.72 GPa
- Flexural Strength: 80.6 MPa
$ 1455/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 51.0 MPa
- Tensile Modulus: 2.92 GPa
$ 1938/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 72
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1550/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.45 GPa
- Flexural Strength: 77.9 MPa
$ 1488/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore D: 47
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1453/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 46.7 MPa
- Tensile Modulus: 2.60 GPa
- Flexural Strength: 89.7 MPa
$ 2274/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 42.7 MPa
$ 1462/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 50.3 MPa
- Tensile Modulus: 2.83 GPa
- Flexural Strength: 103 MPa
$ 2164/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 87
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -45.0 °C
$ 2164/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 42.2 MPa
- Tensile Modulus: 3.36 GPa
- Flexural Strength: 77.2 MPa
$ 2410/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1569/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1790/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 73.7 cm
- Hardness, Shore D: 83
- Tensile Strength, Yield: 54.5 MPa
$ 2253/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 53.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 88.5 MPa
$ 1758/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 105 °C
$ 1612/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 105 °C
$ 2127/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 43.2 MPa
- Tensile Modulus: 2.85 GPa
- Flexural Strength: 84.8 MPa
$ 1777/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 68.6 cm
- Hardness, Shore D: 74
- Tensile Strength, Yield: 49.6 MPa
$ 1728/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 74
- Tensile Strength, Yield: 14.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1648/MT
- Specific Gravity: 1.63 g/cc
- Hardness, Shore A: 92
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 180 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1456/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 42.7 MPa
$ 1625/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.3 MPa
- Tensile Modulus: 2.90 GPa
- Flexural Strength: 84.8 MPa
$ 1614/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 45.9 MPa
- Tensile Modulus: 2.68 GPa
- Flexural Strength: 84.1 MPa
$ 1649/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 77
- Tensile Strength, Yield: 49.8 MPa
- Izod Impact, Notched: 1.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C
- Mold Temperature: 202 - 207 °C
$ 2047/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 31.2 MPa
- Tensile Modulus: 1.93 GPa
- Flexural Yield Strength: 55.9 MPa
$ 1610/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 43.2 MPa
- Tensile Modulus: 2.85 GPa
- Flexural Strength: 84.8 MPa
$ 1806/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 63
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1538/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 77
- Tensile Strength at Break: 14.5 MPa
- Tensile Strength: 12.8 MPa @Strain 100 %
- Elongation at Break: 300 %
$ 1739/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 42.1 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 75.8 MPa
$ 1708/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 250 %
- Tensile Modulus: 0.00896 GPa
$ 1735/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 100
- Hardness, Shore D: 80
- Tensile Strength, Yield: 41.4 MPa
$ 1464/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 100
- Hardness, Shore D: 83
- Tensile Strength, Yield: 41.4 MPa
$ 1964/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 84
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1474/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 53.2 MPa
- Tensile Modulus: 2.88 GPa
- Flexural Strength: 98.6 MPa
$ 1500/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 56
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1682/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 56
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1662/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2155/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 40
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -45.0 °C
$ 1556/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 75
- Tensile Strength, Yield: 37.9 MPa
$ 1931/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 40 %
$ 1484/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -45.0 °C
$ 2442/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 2.79 GPa
$ 2506/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.833 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 44.4 MPa
- Tensile Modulus: 2.36 GPa
$ 2179/MT
- Specific Gravity: 1.33 g/cc
- Density: 0.833 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 47.6 MPa
- Tensile Modulus: 2.47 GPa
$ 1489/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1473/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00758 GPa
$ 1768/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 47.0 MPa
- Tensile Modulus: 3.07 GPa
- Flexural Strength: 84.0 MPa
$ 1696/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 81
- Tensile Strength, Yield: 44.8 MPa
$ 2124/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 46
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 240 %
- Brittleness Temperature: -28.0 °C
$ 1978/MT
- Specific Gravity: 1.48 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 54.8 MPa
- Tensile Modulus: 4.72 GPa
- Flexural Strength: 95.1 MPa
$ 2195/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 45.1 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 82.0 MPa
$ 1478/MT
- Specific Gravity: 1.50 g/cc
- Hardness, Shore D: 53
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 250 %
- Brittleness Temperature: -20.0 °C
$ 2050/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 47.6 MPa
- Elongation at Break: 13 %
- Tensile Modulus: 2.53 GPa
$ 1624/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 48.3 MPa
- Tensile Modulus: 2.57 GPa
- Flexural Strength: 78.0 MPa
$ 1709/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 49.2 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 85.5 MPa
$ 1488/MT
- Specific Gravity: 1.33 g/cc
- Density: 0.801 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 43.8 MPa
- Tensile Modulus: 2.35 GPa
$ 2093/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 41
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1837/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 105 °C
$ 1469/MT
- Forms: Powder
- Generic Material: PVC, Rigid
- Generic Name: Polyvinyl Chloride, Rigid (PVC, Rigid)
- Processing Method: Extrusion
- Regional Availability: Africa & Middle East
$ 1992/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 53.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 88.5 MPa
$ 1605/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.6 MPa
- Tensile Modulus: 2.62 GPa
- Flexural Strength: 79.3 MPa
$ 1548/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 280 %
- Brittleness Temperature: -28.0 °C
$ 1702/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 51.2 MPa
- Tensile Modulus: 2.77 GPa
- Flexural Strength: 86.2 MPa
$ 1792/MT
- Forms: Powder
- Generic Material: PVC, Rigid
- Generic Name: Polyvinyl Chloride, Rigid (PVC, Rigid)
- Processing Method: Extrusion
- Regional Availability: Africa & Middle East
$ 1492/MT
- Specific Gravity: 1.30 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 100
- Hardness, Shore D: 79
- Tensile Strength, Yield: 46.5 MPa
$ 2313/MT
- Specific Gravity: 1.53 g/cc
- Spiral Flow: 81.3 cm
- Hardness, Shore D: 87
- Tensile Strength, Yield: 96.5 MPa
- Elongation at Break: 2.0 %
$ 1946/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 360 %
- Tensile Modulus: 0.00869 GPa
$ 1643/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.4 MPa
$ 2001/MT
- Specific Gravity: 1.33 g/cc
- Density: 0.801 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 45.9 MPa
- Tensile Modulus: 2.54 GPa
$ 1744/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 111.76 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.4 MPa
$ 2023/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.833 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.5 MPa
- Tensile Modulus: 2.53 GPa
$ 1628/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -49.0 °C
$ 2553/MT
- Specific Gravity: 1.34 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 107
- Hardness, Shore D: 82
- Tensile Strength, Yield: 51.0 MPa
$ 2080/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 38.2 MPa
- Tensile Modulus: 3.72 GPa
- Flexural Strength: 79.5 MPa
$ 1688/MT
- Specific Gravity: 1.34 g/cc
- Melt Flow: 16 g/10 min @Load 21.6 kg, Temperature 190 °C
- Spiral Flow: 73.7 cm
- Tensile Strength, Yield: 39.3 MPa
- Elongation at Break: 160 %
$ 1492/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 44.1 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 84.8 MPa
$ 1531/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -45.0 °C
$ 1476/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore D: 45
- Tensile Strength, Yield: 21.4 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 105 °C
$ 1452/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 81
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -43.9 °C
$ 1567/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 42.7 MPa
$ 1485/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 68.6 cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 52.4 MPa
$ 1971/MT
- Specific Gravity: 1.48 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 40.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 71.7 MPa
$ 2228/MT
- Specific Gravity: 1.49 g/cc
- Hardness, Shore D: 84
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.92 GPa
- Flexural Strength: 79.4 MPa
$ 1695/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 42.3 MPa
- Tensile Modulus: 3.27 GPa
- Flexural Strength: 80.6 MPa
$ 1967/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 46
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 270 %
- Brittleness Temperature: -25.0 °C
$ 1568/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 44.1 MPa
- Tensile Modulus: 3.21 GPa
- Flexural Strength: 83.2 MPa
$ 2407/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -24.0 °C
$ 2335/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1594/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -30.0 °C
$ 1761/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 58
- Hardness, Shore D: 70
- Tensile Strength at Break: 25.5 MPa
- Elongation at Break: 290 %
$ 1681/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1826/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 38
- Hardness, Shore D: 50
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 280 %
$ 1483/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.4 MPa
$ 1457/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 92
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1508/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 45.0 MPa
- Tensile Modulus: 2.65 GPa
- Flexural Strength: 82.0 MPa
$ 1671/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 66.0 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 49.6 MPa
$ 1826/MT
- Appearance: Clear/Transparent
- Forms: Pellets
- Generic Material: PVC, Rigid
- Generic Name: Polyvinyl Chloride, Rigid (PVC, Rigid)
- Processing Method: Blow Molding
$ 1687/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 63.5 cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 49.6 MPa
$ 1566/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 58.4 cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 54.5 MPa
$ 1938/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 310 %
- Brittleness Temperature: -20.0 °C
$ 1574/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore D: 40
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2012/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 54
- Tensile Strength at Break: 20.7 MPa
- Tensile Strength: 13.8 MPa @Strain 100 %
- Elongation at Break: 180 %
$ 1935/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 54
- Tensile Strength at Break: 20.7 MPa
- Tensile Strength: 13.8 MPa @Strain 100 %
- Elongation at Break: 180 %
$ 2101/MT
- Specific Gravity: 1.37 g/cc
- Density: 0.815 g/cc
- Hardness, Rockwell R: 109
- Hardness, Shore D: 79
- Hardness, Shore D: 82
$ 2025/MT
- Specific Gravity: 1.25 g/cc
- Density: 0.801 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 52.5 MPa
- Tensile Modulus: 2.76 GPa
$ 2048/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -46.0 °C
$ 1898/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 77
- Tensile Strength, Yield: 55.4 MPa
- Tensile Modulus: 3.06 GPa
- Flexural Strength: 98.6 MPa
$ 1461/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 61.0 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 42.7 MPa
$ 1916/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 80
- Hardness, Shore A: 88
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 300 %
$ 1515/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1721/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 41.9 MPa
- Tensile Modulus: 2.62 GPa
- Flexural Strength: 70.4 MPa
$ 1612/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1665/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 430 %
- Maximum Service Temperature, Air: 105 °C
$ 1631/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore A: 84
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Tensile Modulus: 0.00827 GPa
$ 1495/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore D: 68
- Tensile Strength, Yield: 30.7 MPa
- Elongation at Break: 180 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1683/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.4 MPa
$ 1832/MT
- Forms: Powder
- Generic Material: PVC, Rigid
- Generic Name: Polyvinyl Chloride, Rigid (PVC, Rigid)
- Processing Method: Extrusion
- Regional Availability: Africa & Middle East
$ 1493/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.45 GPa
- Flexural Strength: 77.9 MPa
$ 1924/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 330 %
- Tensile Modulus: 0.0117 GPa
$ 1634/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 73
- Hardness, Shore A: 78
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 300 %
$ 1677/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore D: 41
- Hardness, Shore D: 53
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 300 %
$ 1723/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 58.4 cm
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.3 MPa
$ 1811/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.6 MPa
- Tensile Modulus: 2.59 GPa
- Flexural Strength: 84.5 MPa
$ 1525/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 51.8 MPa
- Tensile Modulus: 2.73 GPa
- Flexural Strength: 86.2 MPa
$ 1735/MT
- Specific Gravity: 1.36 g/cc
- Deformation: 12 % @Temperature 121 °C, Time 3600 sec
- Hardness, Shore D: 58
- Tensile Strength, Yield: 25.2 MPa
- Elongation at Break: 300 %
$ 1586/MT
- Specific Gravity: 1.50 g/cc
- Hardness, Shore D: 53
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 250 %
- Brittleness Temperature: -20.0 °C
$ 1743/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore D: 45
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1463/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength, Yield: 48.6 MPa
- Tensile Modulus: 2.82 GPa
- Flexural Strength: 95.1 MPa
- Flexural Modulus: 3.23 GPa
$ 1876/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1950/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1922/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 13.4 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1987/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 55.9 cm
- Hardness, Shore D: 78
- Tensile Strength, Yield: 37.9 MPa
$ 1705/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 83
- Hardness, Shore A: 90
- Tensile Strength at Break: 14.5 MPa
- Tensile Strength: 8.96 MPa @Strain 100 %
$ 1527/MT
- Specific Gravity: 1.45 g/cc
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 82
- Tensile Strength, Yield: 55.2 MPa
- Elongation at Break: 4.0 %
$ 1556/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00862 GPa
$ 2487/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.7 MPa
- Tensile Modulus: 3.30 GPa
- Flexural Strength: 83.6 MPa
$ 1603/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 44.8 MPa
$ 1533/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore D: 74
- Tensile Strength, Yield: 23.8 MPa
- Tensile Modulus: 1.82 GPa
- Flexural Yield Strength: 50.7 MPa
$ 1509/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 2.99 GPa
- Flexural Strength: 98.6 MPa
$ 2299/MT
- Specific Gravity: 1.38 g/cc
- Deformation: 20 % @Temperature 55.0 °C, Time 3600 sec
- Hardness, Shore A: 76
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 380 %
$ 1656/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore D: 85
- Tensile Strength, Yield: 52.7 MPa
- Tensile Modulus: 2.68 GPa
- Flexural Strength: 92.5 MPa
$ 1503/MT
- Specific Gravity: 1.62 g/cc
- Hardness, Shore D: 76
- Tensile Strength, Yield: 32.9 MPa
- Tensile Modulus: 4.25 GPa
- Flexural Strength: 69.6 MPa
$ 1505/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 77
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1462/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 21.6 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1536/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 119.38 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.4 MPa
$ 1790/MT
- Maximum Service Temperature, Air: 60.0 °C
- Processing Temperature: 170 - 185 °C
- Addition Percentage Recommended: 2%
- Additive: Lead Stabilizer
- Features: Foamable
$ 1606/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.801 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 80
- Tensile Strength, Yield: 44.8 MPa
$ 1445/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 63.5 cm
- Hardness, Shore D: 81
- Tensile Strength, Yield: 49.6 MPa
$ 2385/MT
- Specific Gravity: 1.37 g/cc
- Deformation: 25 % @Temperature 121 °C, Time 3600 sec
- Hardness, Shore D: 47
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 250 %
$ 1456/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 44.5 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 80.0 MPa
$ 1710/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 48
- Tensile Strength, Yield: 22.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1614/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 40.6 MPa
- Tensile Modulus: 2.90 GPa
- Flexural Strength: 69.6 MPa
$ 2145/MT
- Specific Gravity: 1.33 g/cc
- Density: 0.801 g/cc
- Hardness, Shore D: 83
- Tensile Strength, Yield: 52.4 MPa
- Flexural Strength: 75.8 MPa
$ 1743/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 38.5 MPa
- Tensile Modulus: 3.10 GPa
- Flexural Strength: 73.1 MPa
$ 2119/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.833 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 44.4 MPa
- Tensile Modulus: 2.36 GPa
$ 1476/MT
- Specific Gravity: 1.46 g/cc
- Deformation: 16 % @Temperature 55.0 °C, Time 3600 sec
- Hardness, Shore A: 78
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 350 %
$ 1548/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 66
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -37.0 °C
$ 2210/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 87
- Tensile Strength at Break: 20.3 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1949/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 119.38 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.4 MPa
$ 2344/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1780/MT
- Specific Gravity: 1.32 g/cc
- Tensile Strength, Yield: 41.5 MPa
- Tensile Modulus: 2.39 GPa
- Flexural Strength: 73.1 MPa
- Flexural Modulus: 2.53 GPa
$ 1593/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 44.1 MPa
$ 2342/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.833 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 48.5 MPa
- Tensile Modulus: 2.53 GPa
$ 1610/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 45.9 MPa
- Tensile Modulus: 2.90 GPa
- Flexural Strength: 89.6 MPa
$ 1741/MT
- Forms: Pellets
- Generic Material: PVC, Rigid
- Generic Name: Polyvinyl Chloride, Rigid (PVC, Rigid)
- Processing Method: Extrusion
- Regional Availability: Africa & Middle East
$ 1484/MT
- Specific Gravity: 1.36 g/cc
- Deformation: 21 % @Temperature 121 °C, Time 3600 sec
- Hardness, Shore D: 52
- Tensile Strength, Yield: 22.4 MPa
- Elongation at Break: 290 %
$ 2260/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1518/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00896 GPa
$ 1808/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 47.6 MPa
- Elongation at Break: 13 %
- Tensile Modulus: 2.53 GPa
$ 2441/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 55.1 MPa
- Tensile Modulus: 2.92 GPa
- Flexural Strength: 94.5 MPa
$ 1966/MT
- Specific Gravity: 1.49 g/cc
- Hardness, Shore D: 80 @Temperature 23.0 °C
- Tensile Strength, Yield: 39.4 MPa
- Tensile Modulus: 3.33 GPa
- Flexural Yield Strength: 71.0 MPa
$ 1503/MT
- Specific Gravity: 1.40 g/cc
- Spiral Flow: 88.9 cm
- Hardness, Shore D: 82
- Tensile Strength, Yield: 62.1 MPa
- Elongation at Break: 5.0 %
$ 1857/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore D: 40
- Tensile Strength at Break: 22.4 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -37.8 °C
$ 1693/MT
- Appearance: Clear/Transparent
- Forms: Pellets
- Generic Material: PVC, Rigid
- Generic Name: Polyvinyl Chloride, Rigid (PVC, Rigid)
- Processing Method: Blow Molding
$ 1962/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 105 °C
$ 1804/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 53.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 88.5 MPa
$ 2124/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 62
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 105 °C
$ 1725/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore D: 80
- Tensile Strength, Yield: 42.1 MPa
- Tensile Modulus: 2.24 GPa
- Flexural Strength: 66.9 MPa
$ 2122/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 85
- Tensile Strength, Yield: 56.9 MPa
- Tensile Modulus: 2.87 GPa
- Flexural Strength: 93.5 MPa
$ 1514/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2477/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 53.4 MPa
- Tensile Modulus: 2.79 GPa
- Flexural Strength: 88.5 MPa
$ 2071/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2167/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1959/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 105 °C
$ 1593/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.99 GPa
- Flexural Strength: 81.2 MPa
$ 1635/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 74
- Hardness, Shore A: 82
- Tensile Strength, Yield: 14.2 MPa
- Elongation at Break: 340 %
$ 1947/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 92
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1520/MT
- Specific Gravity: 1.39 g/cc
- Density: 0.785 g/cc
- Hardness, Rockwell R: 106
- Hardness, Shore D: 78
- Hardness, Shore D: 82
$ 2206/MT
- Specific Gravity: 1.32 g/cc
- Density: 0.817 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 43.5 MPa
- Tensile Modulus: 2.32 GPa
$ 2000/MT
- Specific Gravity: 1.30 g/cc
- Density: 0.785 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 44.8 MPa
- Flexural Strength: 82.7 MPa
$ 1701/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore D: 77
- Tensile Strength, Yield: 37.6 MPa
- Tensile Modulus: 2.15 GPa
- Flexural Strength: 64.6 MPa
$ 1583/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 82
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 70.3 MPa
$ 1538/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Spiral Flow: 111.76 cm
- Hardness, Shore D: 79
- Tensile Strength, Yield: 41.4 MPa
Delivery PVC PolyOne Corporation
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
oil vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.