$ 1527/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Yield: 304.9 %
- Elongation at Yield: 350 %
$ 1513/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 2.78 GPa
- Flexural Strength: 77.9 MPa
$ 2075/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore D: 52 - 58
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 254.3 %
- Elongation at Yield: 290 %
$ 1657/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore D: 74
- Hardness, Shore D: 79
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.32 GPa
$ 1567/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 248 %
- Elongation at Yield: 310 %
$ 1782/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00586 GPa
- Melt Temperature: 171 °C
$ 2545/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00621 GPa
$ 1569/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 13.69 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00631 GPa
- Melt Temperature: 171 °C
$ 1547/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 330 %
- 100% Modulus: 0.00586 GPa
$ 1919/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.61 GPa
- Flexural Strength: 62.7 MPa
$ 1675/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.61 GPa
- Flexural Strength: 62.7 MPa
$ 2328/MT
- Specific Gravity: 1.54 - 1.58 g/cc
- Hardness, Shore D: 48 - 54
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 225.3 %
- Elongation at Yield: 250 %
$ 1499/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 78
- Tensile Strength, Yield: 41.5 MPa
- Tensile Modulus: 2.91 GPa
$ 1543/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 18.5 MPa
- Elongation at Yield: 285.8 %
- Elongation at Yield: 330 %
$ 2145/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 51.7 MPa
- Tensile Modulus: 2.90 GPa
$ 1486/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 325 %
- Brittleness Temperature: -35.0 °C
- Melt Temperature: 171 °C
$ 1936/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.008791 GPa
- Melt Temperature: 185 °C
$ 1613/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.0124 GPa
$ 1810/MT
- Specific Gravity: 1.61 - 1.65 g/cc
- Hardness, Shore D: 50 - 56
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 128 %
- Elongation at Yield: 160 %
$ 1648/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 245.5 %
- Elongation at Yield: 266.2 %
$ 1576/MT
- Specific Gravity: 1.26 - 1.30 g/cc
- Hardness, Shore A: 66 - 72
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00552 GPa
- Melt Temperature: 171 °C
$ 1517/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Yield: 325 %
- 100% Modulus: 0.00552 GPa
$ 1640/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 273 %
- Elongation at Yield: 325 %
$ 1466/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore A: 79 - 85
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 17.42 MPa
- Elongation at Yield: 302.6 %
$ 2210/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 9.51 MPa
- Elongation at Yield: 255 %
- 100% Modulus: 0.00503 GPa
- Melt Temperature: 179 °C
$ 1615/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 50.3 MPa
- Tensile Modulus: 2.83 GPa
$ 1578/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 81
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.97 GPa
$ 2338/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 81
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.97 GPa
$ 1632/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Yield: 350 %
- Melt Temperature: 177 °C
$ 1732/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 290 %
- 100% Modulus: 0.0134 GPa
$ 1901/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.0117 GPa
$ 1594/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Yield: 250 %
- Melt Temperature: 149 °C
$ 2136/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.48 GPa
$ 1484/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00648 GPa
- Melt Temperature: 171 °C
$ 1535/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 246 %
- Elongation at Yield: 300 %
$ 1698/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Rockwell R: 106
- Hardness, Shore D: 80
- Tensile Strength, Yield: 49.62 MPa
- Tensile Modulus: 2.73 GPa
$ 2142/MT
- Specific Gravity: 1.41 - 1.45 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Yield: 281 %
- Elongation at Yield: 320 %
$ 1560/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.62 GPa
$ 1683/MT
- Specific Gravity: 1.29 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.41 GPa
- Flexural Strength: 69.6 MPa
- Flexural Modulus: 2.24 GPa
$ 2177/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.62 GPa
$ 1754/MT
- Specific Gravity: 1.26 - 1.30 g/cc
- Hardness, Shore A: 75 - 81
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.008101 GPa
$ 1537/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 62.1 MPa
- Tensile Modulus: 2.90 GPa
$ 1624/MT
- Specific Gravity: 1.26 - 1.30 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Yield: 330 %
- 100% Modulus: 0.0179 GPa
$ 1529/MT
- Specific Gravity: 1.50 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 82
- Tensile Strength, Yield: 51.7 MPa
- Elongation at Yield: 4.0 %
$ 1624/MT
- Specific Gravity: 1.41 - 1.45 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00517 GPa
$ 2039/MT
- Specific Gravity: 1.26 - 1.30 g/cc
- Hardness, Shore D: 53 - 59
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Yield: 275 %
- Melt Temperature: 188 °C
$ 2044/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 231 %
- Elongation at Yield: 300 %
$ 2073/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 80
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.21 GPa
$ 1572/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 281.1 %
- Elongation at Yield: 350 %
$ 1827/MT
- Specific Gravity: 1.19 - 1.23 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00552 GPa
- Melt Temperature: 174 °C
$ 1550/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore D: 40 - 46
- Hardness, Shore D: 52 - 58
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 248.2 %
$ 1556/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 84 - 90
- Hardness, Shore D: 33 - 39
- Tensile Strength, Yield: 18.3 MPa
- Elongation at Yield: 263.7 %
$ 1898/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.01051 GPa
$ 1669/MT
- Specific Gravity: 1.41 - 1.45 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 264.3 %
- Elongation at Yield: 320 %
$ 1707/MT
- Specific Gravity: 1.48 - 1.52 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 240 %
- Elongation at Yield: 300 %
$ 1940/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 80
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.83 GPa
$ 1892/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore D: 52 - 58
- Hardness, Shore D: 63 - 69
- Tensile Strength, Yield: 23.2 MPa
- Elongation at Yield: 255 %
$ 1557/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 233.4 %
- Elongation at Yield: 300 %
$ 1656/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00517 GPa
$ 2326/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 265 %
- Elongation at Yield: 330 %
$ 1683/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.0128 GPa
$ 1499/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.74 GPa
$ 1520/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Yield: 276.6 %
- Elongation at Yield: 325 %
$ 1662/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 300 %
- Brittleness Temperature: -30.0 °C
- Melt Temperature: 185 °C
$ 1738/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 7.93 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00414 GPa
- Melt Temperature: 171 °C
$ 2336/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 90 - 96
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 190.4 %
- Elongation at Yield: 280 %
$ 1999/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00758 GPa
- Melt Temperature: 177 °C
$ 1906/MT
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00689 GPa
- Brittleness Temperature: -40.0 °C
- Oxygen Index: 25 %
$ 2206/MT
- Specific Gravity: 1.32 - 1.38 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.48 GPa
$ 2012/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Rockwell R: 106
- Hardness, Shore D: 80
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.58 GPa
$ 2383/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 69 - 75
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 425 %
- 100% Modulus: 0.00483 GPa
- Melt Temperature: 182 °C
$ 1536/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 9.51 MPa
- Elongation at Yield: 255 %
- 100% Modulus: 0.00503 GPa
- Melt Temperature: 168 °C
$ 1653/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Hardness, Shore A: 57 - 63
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 500 %
- 100% Modulus: 0.00241 GPa
- Melt Temperature: 168 °C
$ 1611/MT
- Specific Gravity: 1.42 - 1.46 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 370 %
- 100% Modulus: 0.00621 GPa
- Brittleness Temperature: -38.0 °C
$ 1504/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 71 - 77
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 330 %
- Melt Temperature: 149 °C
$ 2051/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 285.8 %
- Elongation at Yield: 375 %
$ 1976/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 52 - 58
- Tensile Strength, Yield: 7.24 MPa
- Elongation at Yield: 360 %
- 100% Modulus: 0.00276 GPa
- Melt Temperature: 166 °C
$ 1558/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 326.3 %
- Elongation at Yield: 332.3 %
$ 2150/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 91 - 97
- Hardness, Shore D: 45 - 51
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 270.4 %
$ 2462/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 28.3 MPa
- Tensile Modulus: 1.65 GPa
- Flexural Strength: 46.9 MPa
$ 1490/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 88
- Hardness, Shore D: 81
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.72 GPa
$ 1682/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 68 - 74
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 400 %
- Melt Temperature: 177 °C
$ 1520/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Rockwell R: 90
- Hardness, Shore D: 78
- Tensile Strength, Yield: 39.41 MPa
- Tensile Modulus: 2.832 GPa
$ 1569/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 370 %
- 100% Modulus: 0.00896 GPa
$ 1798/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00896 GPa
$ 1451/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 78
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.81 GPa
$ 1637/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.00689 GPa
$ 2048/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 83 - 89
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.01086 GPa
$ 1807/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 267.5 %
- Elongation at Yield: 320 %
$ 1707/MT
- Specific Gravity: 1.45 - 1.49 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00621 GPa
$ 1755/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 79 - 85
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 272.8 %
- Elongation at Yield: 315 %
$ 1468/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Yield: 288.1 %
- Elongation at Yield: 330 %
$ 1541/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 55.8 MPa
- Tensile Modulus: 2.55 GPa
$ 1637/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 225 %
- Elongation at Yield: 228 %
$ 1753/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 73 - 79
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 261.8 %
- Elongation at Yield: 279 %
$ 2049/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 60 - 66
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00345 GPa
$ 1994/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 47.6 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 89.6 MPa
- Izod Impact, Notched: 0.267 J/cm @Thickness 3.17 mm
$ 1729/MT
- Specific Gravity: 1.65 - 1.69 g/cc
- Hardness, Shore D: 50 - 56
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 245.6 %
- Elongation at Yield: 275 %
$ 1810/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 41 - 47
- Tensile Strength, Yield: 21.4 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0141 GPa
$ 1648/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 66 - 72
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Yield: 300 %
- Brittleness Temperature: -30.0 °C
- Melt Temperature: 171 °C
$ 1668/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Yield: 290.5 %
- Elongation at Yield: 294 %
$ 2551/MT
- Specific Gravity: 1.50 - 1.54 g/cc
- Hardness, Shore A: 91 - 97
- Hardness, Shore D: 43 - 49
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 250 %
$ 2028/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Yield: 335 %
- 100% Modulus: 0.00689 GPa
$ 1544/MT
- Specific Gravity: 1.26 - 1.30 g/cc
- Hardness, Shore A: 68 - 74
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00500 GPa
$ 2463/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 48.3 MPa
- Tensile Modulus: 2.62 GPa
- Flexural Strength: 82.7 MPa
$ 1762/MT
- Specific Gravity: 1.31 g/cc
- Tensile Strength, Yield: 44.02 MPa
- Tensile Modulus: 2.99 GPa
- Flexural Strength: 73.43 MPa
- Izod Impact, Notched: 6.83 J/cm @Thickness 6.35 mm, Temperature 0.000 °C
$ 2132/MT
- Specific Gravity: 1.29 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 36.5 MPa
- Tensile Modulus: 2.41 GPa
$ 1910/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore D: 54 - 60
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.0190 GPa
$ 1517/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 280 %
- Elongation at Yield: 327.6 %
$ 1706/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 325 %
- 100% Modulus: 0.00931 GPa
- Melt Temperature: 177 °C
$ 2333/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.0110 GPa
- Melt Temperature: 182 °C
$ 1551/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 54 - 60
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00310 GPa
- Melt Temperature: 154 °C
$ 1495/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 92 - 98
- Hardness, Shore D: 45 - 51
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Yield: 289 %
$ 1671/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore D: 46 - 52
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.0162 GPa
- Melt Temperature: 191 °C
$ 1976/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 238.7 %
- Elongation at Yield: 310 %
$ 1499/MT
- Specific Gravity: 1.16 - 1.20 g/cc
- Hardness, Shore A: 58 - 64
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00414 GPa
$ 1700/MT
- Specific Gravity: 1.41 - 1.45 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Yield: 342 %
- Elongation at Yield: 342 %
$ 1479/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Yield: 370 %
- Brittleness Temperature: -40.0 °C
- Melt Temperature: 182 °C
$ 2261/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore D: 87 - 93
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Yield: 340 %
- 100% Modulus: 0.0110 GPa
- Melt Temperature: 188 °C
$ 1722/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Shore D: 75
- Tensile Strength, Yield: 37.9 MPa
- Tensile Modulus: 2.28 GPa
$ 2040/MT
- Specific Gravity: 1.50 g/cc
- Tensile Strength, Yield: 54.5 MPa
- Tensile Modulus: 2.94 GPa
- Izod Impact, Notched: 1.55 J/cm @Thickness 6.35 mm
- Deflection Temperature at 1.8 MPa (264 psi): 113 °C
$ 1682/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.62 GPa
$ 1708/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Hardness, Shore A: 61 - 67
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00431 GPa
$ 2322/MT
- Specific Gravity: 1.31 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.52 GPa
- Flexural Strength: 75.8 MPa
- Izod Impact, Notched: 5.34 J/cm @Thickness 6.35 mm
$ 1921/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore D: 39 - 45
- Tensile Strength, Yield: 21.4 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.0165 GPa
$ 2327/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Rockwell R: 90
- Hardness, Shore D: 78
- Tensile Strength, Yield: 39.3 MPa
- Tensile Modulus: 2.83 GPa
$ 1602/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore D: 56 - 62
- Tensile Strength, Yield: 24.5 MPa
- Elongation at Yield: 260 %
- 100% Modulus: 0.0217 GPa
$ 1574/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 50.3 MPa
- Tensile Modulus: 2.83 GPa
$ 2371/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Hardness, Shore A: 54 - 60
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00310 GPa
- Melt Temperature: 171 °C
$ 1838/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 273 %
- Elongation at Yield: 325 %
$ 1661/MT
- Specific Gravity: 1.42 - 1.46 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 233.8 %
- Elongation at Yield: 242 %
$ 1802/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00500 GPa
$ 1578/MT
- Specific Gravity: 1.61 - 1.65 g/cc
- Hardness, Shore D: 48 - 54
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 217.5 %
- Elongation at Yield: 250 %
$ 1617/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 75 - 81
- Tensile Strength, Yield: 16.38 MPa
- Elongation at Yield: 261.8 %
- Elongation at Yield: 350 %
$ 2507/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 91 - 97
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.0162 GPa
$ 1669/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00689 GPa
$ 1628/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 232.1 %
- Elongation at Yield: 236.5 %
$ 2431/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 279.5 %
- Elongation at Yield: 279.8 %
$ 1471/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 90 - 96
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0138 GPa
$ 2006/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 65 - 71
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00483 GPa
- Melt Temperature: 160 °C
$ 1921/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00965 GPa
$ 2170/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00689 GPa
$ 1546/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 21.89 MPa
- Elongation at Yield: 297.5 %
- Elongation at Yield: 350 %
$ 2178/MT
- Specific Gravity: 1.59 - 1.63 g/cc
- Hardness, Shore D: 41 - 47
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 216 %
- Elongation at Yield: 270 %
$ 1506/MT
- Specific Gravity: 1.58 - 1.62 g/cc
- Hardness, Shore D: 51 - 57
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 200 %
- 100% Modulus: 0.0162 GPa
$ 1913/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 83 - 89
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 265.7 %
- Elongation at Yield: 310 %
$ 1802/MT
- Specific Gravity: 1.50 - 1.54 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Yield: 340 %
- 100% Modulus: 0.00552 GPa
- Melt Temperature: 171 °C
$ 1958/MT
- Specific Gravity: 1.48 - 1.52 g/cc
- Hardness, Shore D: 60 - 66
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 270.6 %
- Elongation at Yield: 291 %
$ 1460/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 76 - 82
- Hardness, Shore A: 83 - 89
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 302.4 %
$ 1778/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.0103 GPa
- Melt Temperature: 188 °C
$ 1467/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00362 GPa
$ 1525/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 68 - 74
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Yield: 280.7 %
- Elongation at Yield: 350 %
$ 1862/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Yield: 292.6 %
- Elongation at Yield: 350 %
$ 1693/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.0138 GPa
- Melt Temperature: 191 °C
$ 1858/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 79 - 85
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 280.7 %
- Elongation at Yield: 350 %
$ 1635/MT
- Specific Gravity: 1.44 g/cc
- Maximum Service Temperature, Air: 204 °C
$ 1472/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 45 - 51
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 248.3 %
- Elongation at Yield: 266.3 %
$ 2009/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore D: 47 - 53
- Tensile Strength, Yield: 22.58 MPa
- Elongation at Yield: 290 %
- 100% Modulus: 0.0176 GPa
$ 1696/MT
- Specific Gravity: 1.51 g/cc
- Tensile Strength, Yield: 51.7 MPa
- Elongation at Yield: 4.0 %
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 94.5 MPa
$ 2000/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Yield: 450 %
- 100% Modulus: 0.00534 GPa
- Melt Temperature: 171 °C
$ 1933/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.00862 GPa
$ 2210/MT
- Specific Gravity: 1.42 - 1.46 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 17.75 MPa
- Elongation at Yield: 233 %
- Elongation at Yield: 280 %
$ 1973/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 42.1 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 75.8 MPa
- Izod Impact, Notched: 6.41 J/cm @Thickness 6.35 mm
$ 1765/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Rockwell R: 108
- Hardness, Shore D: 79
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.76 GPa
$ 1547/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 340 %
- 100% Modulus: 0.0110 GPa
$ 1683/MT
- Specific Gravity: 1.43 - 1.47 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 13.4 MPa
- Elongation at Yield: 269.6 %
- Elongation at Yield: 330 %
$ 2074/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 8.62 MPa
- Elongation at Yield: 240 %
- 100% Modulus: 0.00593 GPa
- Melt Temperature: 166 °C
$ 2044/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 281.1 %
- Elongation at Yield: 350 %
$ 1780/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 233.4 %
- Elongation at Yield: 300 %
$ 1980/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 76 - 82
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 292.7 %
- Elongation at Yield: 360 %
$ 1509/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 79
- Tensile Strength, Yield: 45.5 MPa
- Tensile Modulus: 3.03 GPa
$ 2177/MT
- Specific Gravity: 1.13 - 1.17 g/cc
- Hardness, Shore A: 51 - 57
- Hardness, Shore A: 57 - 63
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Yield: 500 %
$ 1834/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 97
- Tensile Strength at Break: 36.42 MPa
- Tensile Strength, Yield: 41.4 MPa
$ 1471/MT
- Specific Gravity: 1.17 - 1.21 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00517 GPa
$ 1553/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 280 %
- Elongation at Yield: 320.3 %
$ 1794/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Rockwell R: 93
- Hardness, Shore D: 80
- Tensile Strength, Yield: 46.7 MPa
- Tensile Modulus: 3.22 GPa
$ 1891/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 82 - 88
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 262.4 %
$ 1472/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 76 - 82
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 292.7 %
- Elongation at Yield: 360 %
$ 2055/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore D: 43 - 49
- Hardness, Shore D: 55 - 61
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Yield: 280 %
$ 2525/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0117 GPa
- Melt Temperature: 182 °C
$ 1447/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 286.4 %
- Elongation at Yield: 292.8 %
$ 2120/MT
- Tensile Strength, Yield: 52.08 MPa
- Tensile Modulus: 2.59 GPa
- Izod Impact, Notched: 0.280 J/cm
- Deflection Temperature at 1.8 MPa (264 psi): 110 °C
- Actual Burn Time, seconds: <5
$ 2255/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Yield: 360 %
- 100% Modulus: 0.00500 GPa
$ 1447/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 18.10 MPa
- Elongation at Yield: 275.6 %
- Elongation at Yield: 325 %
$ 1449/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 73 - 79
- Tensile Strength, Yield: 15.00 MPa
- Elongation at Yield: 253.6 %
- Elongation at Yield: 340 %
$ 1644/MT
- Specific Gravity: 1.47 - 1.51 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 216 %
- Elongation at Yield: 270 %
$ 1667/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 80
- Tensile Strength, Yield: 46.2 MPa
- Tensile Modulus: 2.41 GPa
$ 1972/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 258.7 %
- Elongation at Yield: 330 %
$ 1987/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore A: 74 - 80
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Yield: 160 %
- 100% Modulus: 0.00717 GPa
$ 1488/MT
- Specific Gravity: 1.54 - 1.58 g/cc
- Hardness, Shore D: 37 - 43
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 264 %
- Elongation at Yield: 275 %
$ 2102/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 82
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 3.10 GPa
$ 2169/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 75 - 81
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 380 %
$ 1534/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 272.7 %
- Elongation at Yield: 340 %
$ 1471/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 77 - 83
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 252.8 %
$ 1821/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 271.4 %
- Elongation at Yield: 335 %
$ 1870/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 276.3 %
- Elongation at Yield: 300 %
$ 1536/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 92 - 98
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0152 GPa
$ 1760/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Yield: 266.6 %
- Elongation at Yield: 320 %
$ 1552/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore D: 52 - 58
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 253.8 %
- Elongation at Yield: 300 %
$ 2090/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 250.6 %
- Elongation at Yield: 320 %
$ 2068/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 40.0 MPa
- Tensile Modulus: 2.41 GPa
$ 2480/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 21.20 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0152 GPa
- Melt Temperature: 191 °C
$ 1883/MT
- Specific Gravity: 1.61 - 1.65 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 270 %
- 100% Modulus: 0.0103 GPa
$ 2101/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 330.1 %
- Elongation at Yield: 346.2 %
$ 1473/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 13.27 MPa
- Elongation at Yield: 288.8 %
- Elongation at Yield: 375 %
$ 1555/MT
- Specific Gravity: 1.43 - 1.47 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 277.2 %
- Elongation at Yield: 330 %
$ 1807/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 75.8 MPa
$ 1899/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 82
- Tensile Strength, Yield: 49.0 MPa
- Tensile Modulus: 3.10 GPa
$ 1572/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 57 - 63
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 490 %
- 100% Modulus: 0.00310 GPa
- Melt Temperature: 171 °C
$ 1551/MT
- Specific Gravity: 1.31 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.52 GPa
- Flexural Strength: 75.8 MPa
- Izod Impact, Notched: 5.34 J/cm @Thickness 6.35 mm
$ 1808/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 253.8 %
- Elongation at Yield: 300 %
$ 1747/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 91 - 97
- Hardness, Shore D: 42 - 48
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 291.5 %
$ 1655/MT
- Specific Gravity: 1.43 - 1.47 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 276.2 %
- Elongation at Yield: 330 %
$ 1496/MT
- Specific Gravity: 1.42 - 1.46 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 310 %
- 100% Modulus: 0.00517 GPa
- Melt Temperature: 171 °C
$ 1464/MT
- Specific Gravity: 1.16 - 1.20 g/cc
- Hardness, Shore A: 58 - 64
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Yield: 450 %
- 100% Modulus: 0.00362 GPa
$ 1886/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 18.3 MPa
- Elongation at Yield: 290 %
- 100% Modulus: 0.0131 GPa
$ 1536/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 264.3 %
- Elongation at Yield: 283.5 %
$ 1556/MT
- Specific Gravity: 1.19 - 1.23 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 267.1 %
- Elongation at Yield: 350 %
$ 2173/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 400 %
- Brittleness Temperature: -40.0 °C
- Melt Temperature: 166 °C
$ 1560/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 272 %
- Elongation at Yield: 320 %
$ 1754/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 78
- Tensile Strength, Yield: 44.1 MPa
- Tensile Modulus: 2.72 GPa
$ 1824/MT
- Specific Gravity: 1.53 - 1.57 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 17.48 MPa
- Elongation at Yield: 207.5 %
- Elongation at Yield: 250 %
$ 1533/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore D: 58 - 64
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Yield: 280 %
- 100% Modulus: 0.0193 GPa
$ 2171/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 267.5 %
- Elongation at Yield: 320 %
$ 1541/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore A: 59 - 65
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 299.6 %
- Elongation at Yield: 350 %
$ 1801/MT
- Specific Gravity: 1.45 - 1.49 g/cc
- Hardness, Shore D: 59 - 65
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Yield: 251.4 %
- Elongation at Yield: 290 %
$ 1714/MT
- Specific Gravity: 1.45 - 1.49 g/cc
- Hardness, Shore D: 59 - 65
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Yield: 251.4 %
- Elongation at Yield: 290 %
$ 2470/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 76 - 82
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Yield: 284.2 %
- Elongation at Yield: 350 %
$ 1601/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.41 GPa
$ 1881/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Hardness, Shore A: 79 - 85
- Tensile Strength, Yield: 18.3 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00827 GPa
$ 1816/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Melt Flow: 84.3 g/10 min @Load 14.91 kg, Temperature 175 °C
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 410 %
$ 2450/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Melt Flow: 84.3 g/10 min @Load 14.91 kg, Temperature 175 °C
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 410 %
$ 1605/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Melt Flow: 84.3 g/10 min @Load 14.91 kg, Temperature 175 °C
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 410 %
$ 1793/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 59 - 65
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00310 GPa
- Melt Temperature: 163 °C
$ 1723/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 219 %
- Elongation at Yield: 300 %
$ 1548/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 296 %
- Elongation at Yield: 400 %
$ 1501/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 79 - 85
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.008791 GPa
$ 2031/MT
- Specific Gravity: 1.48 - 1.52 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 235.5 %
- Elongation at Yield: 300 %
$ 1866/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 9.31 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00483 GPa
- Melt Temperature: 149 °C
$ 1804/MT
- Specific Gravity: 1.32 g/cc
- Tensile Strength, Yield: 46.9 MPa
- Tensile Modulus: 2.65 GPa
- Flexural Strength: 75.8 MPa
- Izod Impact, Notched: 1.33 J/cm @Thickness 6.35 mm, Temperature 23.0 °C
$ 1452/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 79
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.62 GPa
$ 1881/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 61 - 67
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00379 GPa
- Melt Temperature: 166 °C
$ 2280/MT
- Specific Gravity: 1.48 g/cc
- Hardness, Rockwell R: 109
- Hardness, Shore D: 83
- Tensile Strength, Yield: 40.8 MPa
- Tensile Modulus: 2.65 GPa
$ 2043/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 80 - 86
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Yield: 291.1 %
$ 1542/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 16.38 MPa
- Elongation at Yield: 263.8 %
- Elongation at Yield: 340 %
$ 1462/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 303.8 %
- Elongation at Yield: 370 %
$ 1506/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 82 - 88
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 292.5 %
$ 1895/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 47.6 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Strength: 89.6 MPa
- Izod Impact, Notched: 0.267 J/cm @Thickness 3.17 mm
$ 1684/MT
- Specific Gravity: 1.51 - 1.55 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 9.549 MPa
- Elongation at Yield: 305 %
- 100% Modulus: 0.00555 GPa
- Melt Temperature: 182 °C
$ 2217/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 37.2 MPa
- Tensile Modulus: 2.21 GPa
- Izod Impact, Notched: 0.801 J/cm @Thickness 3.17 mm, Temperature -40.0 °C
$ 2183/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 81 - 87
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Yield: 266.5 %
$ 2092/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 21.89 MPa
- Elongation at Yield: 310 %
- 100% Modulus: 0.0155 GPa
- Melt Temperature: 191 °C
$ 1559/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.0100 GPa
$ 2306/MT
- Specific Gravity: 1.32 - 1.38 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.48 GPa
$ 1563/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore D: 54 - 60
- Tensile Strength, Yield: 22.86 MPa
- Elongation at Yield: 244.4 %
- Elongation at Yield: 280 %
$ 2115/MT
- Specific Gravity: 1.353 g/cc
- Hardness, Rockwell R: 98.8
- Hardness, Shore D: 73.2
- Tensile Strength, Yield: 39.6 MPa
- Tensile Modulus: 1.97 GPa
$ 2201/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 312.6 %
- Elongation at Yield: 350 %
$ 1556/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 302.1 %
- Elongation at Yield: 350 %
$ 1819/MT
- Specific Gravity: 1.43 - 1.47 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 277.2 %
- Elongation at Yield: 330 %
$ 2064/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 43 - 49
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 261.3 %
- Elongation at Yield: 325 %
$ 1792/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 252 %
- Elongation at Yield: 300 %
$ 1923/MT
- Specific Gravity: 1.32 g/cc
- Tensile Strength, Yield: 46.2 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 82.7 MPa
- Izod Impact, Notched: 1.33 J/cm @Thickness 3.17 mm
$ 1505/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 90 - 96
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 174.6 %
- Elongation at Yield: 300 %
$ 1606/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 71 - 77
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 200 %
- 100% Modulus: 0.00552 GPa
$ 1581/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 325 %
- Flammability, UL94: V-2 @Thickness >=0.750 mm
$ 1582/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 32.4 MPa
- Tensile Modulus: 1.93 GPa
- Flexural Strength: 50.3 MPa
$ 1719/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 275.9 %
- Elongation at Yield: 330 %
$ 1650/MT
- Specific Gravity: 1.42 - 1.46 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 220 %
- Elongation at Yield: 275 %
$ 2224/MT
- Specific Gravity: 1.50 g/cc
- Hardness, Rockwell R: 111
- Hardness, Shore D: 82
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Yield: 4.2 %
$ 1740/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 49.6 MPa
- Tensile Modulus: 2.90 GPa
- Flexural Strength: 89.6 MPa
- Izod Impact, Notched: 0.160 J/cm @Thickness 6.35 mm
$ 1571/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 90 - 96
- Tensile Strength, Yield: 21.2 MPa
- Elongation at Yield: 355 %
- 100% Modulus: 0.0145 GPa
- Melt Temperature: 188 °C
$ 1835/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 49.6 MPa
- Tensile Modulus: 2.90 GPa
- Flexural Strength: 89.6 MPa
- Izod Impact, Notched: 0.160 J/cm @Thickness 6.35 mm
$ 1546/MT
- Specific Gravity: 1.17 - 1.21 g/cc
- Hardness, Shore A: 68 - 74
- Tensile Strength, Yield: 12.93 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00534 GPa
$ 2372/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 251.1 %
- Elongation at Yield: 300 %
$ 1492/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 3.50 GPa
- Flexural Strength: 80.7 MPa
$ 2091/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore D: 57 - 63
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Yield: 276.3 %
- Elongation at Yield: 300 %
$ 1623/MT
- Specific Gravity: 1.61 - 1.65 g/cc
- Hardness, Shore D: 52 - 58
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 212.5 %
- Elongation at Yield: 250 %
$ 2232/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 80
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.86 GPa
$ 1459/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 3.28 GPa
- Izod Impact, Notched: 1.17 J/cm @Thickness 6.35 mm
$ 2237/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore D: 39 - 45
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0145 GPa
$ 1669/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Rockwell R: 104
- Hardness, Shore D: 80
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 4.83 GPa
$ 1673/MT
- Specific Gravity: 1.34 g/cc
- Tensile Strength, Yield: 50.3 MPa
- Tensile Modulus: 2.86 GPa
- Flexural Strength: 89.6 MPa
- Izod Impact, Notched: 0.160 J/cm @Thickness 6.35 mm
$ 1808/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 9.31 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00448 GPa
- Melt Temperature: 171 °C
$ 2180/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 222.7 %
- Elongation at Yield: 290 %
$ 1599/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.00621 GPa
$ 1493/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Hardness, Shore A: 56 - 62
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Yield: 390 %
$ 1600/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 81 - 87
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 237.6 %
$ 1739/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 325 %
- 100% Modulus: 0.0103 GPa
- Melt Temperature: 182 °C
$ 2306/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00758 GPa
- Brittleness Temperature: -35.0 °C
- Melt Temperature: 182 °C
$ 2552/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Hardness, Shore A: 61 - 67
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00414 GPa
$ 1964/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore D: 57 - 63
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Yield: 276.3 %
- Elongation at Yield: 325 %
$ 1493/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 280.8 %
- Elongation at Yield: 325 %
$ 1540/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00896 GPa
$ 1775/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 90 - 96
- Hardness, Shore D: 42 - 48
- Tensile Strength, Yield: 19.82 MPa
- Elongation at Yield: 271.9 %
$ 1485/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.01017 GPa
- Melt Temperature: 171 °C
$ 1950/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.41 GPa
$ 1656/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 81
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.97 GPa
$ 1557/MT
- Specific Gravity: 1.30 g/cc
- Tensile Strength, Yield: 40.7 MPa
- Tensile Modulus: 2.39 GPa
- Flexural Strength: 65.5 MPa
- Flexural Modulus: 2.17 GPa
$ 1548/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Rockwell R: 87.5
- Hardness, Shore D: 81
- Tensile Strength, Yield: 43.2 MPa
- Tensile Modulus: 2.70 GPa
$ 1660/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 87 - 93
- Hardness, Shore D: 38 - 43
- Hardness, Shore D: 47 - 53
- Tensile Strength, Yield: 19.3 MPa
$ 2374/MT
- Specific Gravity: 1.48 - 1.52 g/cc
- Hardness, Shore A: 92 - 98
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 310 %
- 100% Modulus: 0.0138 GPa
$ 1694/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 13.4 MPa
- Elongation at Yield: 355 %
- 100% Modulus: 0.00552 GPa
- Melt Temperature: 182 °C
$ 1809/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 83 - 89
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 273 %
- Elongation at Yield: 285.3 %
$ 1507/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 300 %
- Melt Temperature: 177 °C
$ 1862/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 261.1 %
- Elongation at Yield: 340 %
$ 1915/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 52 - 58
- Tensile Strength, Yield: 8.62 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00293 GPa
- Melt Temperature: 168 °C
$ 1563/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 18.3 MPa
- Elongation at Yield: 219.6 %
- Elongation at Yield: 300 %
$ 1687/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 18.3 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.0110 GPa
$ 1623/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Rockwell R: 90
- Hardness, Shore D: 78
- Tensile Strength, Yield: 39.41 MPa
- Tensile Modulus: 2.832 GPa
$ 1653/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Rockwell R: 90
- Hardness, Shore D: 78
- Tensile Strength, Yield: 39.41 MPa
- Tensile Modulus: 2.832 GPa
$ 1806/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 325 %
- Melt Temperature: 177 °C
$ 1870/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 91 - 97
- Hardness, Shore D: 41 - 47
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 275 %
$ 1755/MT
- Specific Gravity: 1.48 - 1.52 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 290 %
- 100% Modulus: 0.00896 GPa
- Melt Temperature: 182 °C
$ 1617/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.59 GPa
- Flexural Strength: 76.5 MPa
- Izod Impact, Notched: 1.60 J/cm @Thickness 6.35 mm
$ 1607/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 43.4 MPa
- Tensile Modulus: 2.62 GPa
$ 1629/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 234.9 %
- Elongation at Yield: 300 %
$ 1486/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 80
- Tensile Strength, Yield: 45.5 MPa
- Tensile Modulus: 2.76 GPa
$ 1619/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0145 GPa
$ 1816/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 55.2 MPa
- Tensile Modulus: 3.41 GPa
$ 1960/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 80
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.83 GPa
$ 1459/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore D: 50 - 56
- Hardness, Shore D: 61 - 67
- Tensile Strength, Yield: 25.9 MPa
- Elongation at Yield: 250 %
$ 2255/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 83
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.62 GPa
$ 1557/MT
- Specific Gravity: 1.47 - 1.51 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 325 %
- 100% Modulus: 0.0100 GPa
- Melt Temperature: 185 °C
$ 1691/MT
- Specific Gravity: 1.38 - 1.42 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0131 GPa
$ 2114/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 46.2 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 82.7 MPa
$ 1469/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Yield: 330 %
- 100% Modulus: 0.0124 GPa
$ 1509/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.62 GPa
$ 2511/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 91 - 97
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 246.3 %
- Elongation at Yield: 300 %
$ 1474/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore D: 47 - 53
- Hardness, Shore D: 56 - 62
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Yield: 291.2 %
$ 1865/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Rockwell R: 106
- Hardness, Shore D: 75
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.45 GPa
$ 2390/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 76 - 82
- Hardness, Shore A: 83 - 89
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 280 %
$ 2052/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 269.1 %
- Elongation at Yield: 325 %
$ 1656/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 46.9 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Strength: 82.0 MPa
$ 2092/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 230.1 %
- Elongation at Yield: 300 %
$ 1903/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Melt Flow: 46 g/10 min @Load 14.91 kg, Temperature 175 °C
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 405 %
$ 1710/MT
- Specific Gravity: 1.45 - 1.49 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 14.4 MPa
- Elongation at Yield: 277.2 %
- Elongation at Yield: 315 %
$ 1463/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 78
- Tensile Strength, Yield: 41.5 MPa
- Tensile Modulus: 2.91 GPa
$ 1927/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 77 - 83
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Yield: 252.8 %
$ 2439/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 61 - 67
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 360 %
- 100% Modulus: 0.00414 GPa
$ 1839/MT
- Specific Gravity: 1.55 - 1.65 g/cc
- Hardness, Rockwell R: 104
- Hardness, Shore D: 80
- Tensile Strength, Yield: 46.2 MPa
- Tensile Modulus: 4.14 GPa
$ 1479/MT
- Specific Gravity: 1.39 - 1.43 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 285.7 %
- Elongation at Yield: 325 %
$ 1599/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 64 - 70
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00414 GPa
$ 1723/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0148 GPa
- Melt Temperature: 185 °C
$ 1871/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 279.8 %
- Elongation at Yield: 325 %
$ 2201/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 267.8 %
- Elongation at Yield: 315 %
$ 2058/MT
- Specific Gravity: 1.18 - 1.22 g/cc
- Melt Flow: 125 g/10 min @Load 14.91 kg, Temperature 175 °C
- Hardness, Shore A: 59 - 65
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Yield: 425 %
$ 1690/MT
- Specific Gravity: 1.32 g/cc
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.55 GPa
- Flexural Strength: 81.4 MPa
- Izod Impact, Notched: 1.33 J/cm @Thickness 6.35 mm
$ 1666/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00431 GPa
$ 1521/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Rockwell R: 116
- Hardness, Shore D: 81
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.97 GPa
$ 1792/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 236.3 %
- Elongation at Yield: 315 %
$ 1546/MT
- Specific Gravity: 1.57 - 1.61 g/cc
- Hardness, Shore D: 53 - 59
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 192.8 %
- Elongation at Yield: 200 %
$ 2282/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore D: 53 - 59
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Yield: 264 %
- Elongation at Yield: 300 %
$ 1705/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00552 GPa
- Melt Temperature: 171 °C
$ 1568/MT
- Specific Gravity: 1.34 - 1.38 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 325 %
- 100% Modulus: 0.00827 GPa
$ 2179/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 42 - 48
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 293 %
- Elongation at Yield: 303.6 %
$ 1624/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore D: 61 - 67
- Tensile Strength, Yield: 25.2 MPa
- Elongation at Yield: 240 %
- 100% Modulus: 0.0234 GPa
- Melt Temperature: 188 °C
$ 2470/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00965 GPa
- Melt Temperature: 177 °C
$ 1972/MT
- Specific Gravity: 1.41 - 1.45 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Yield: 291.5 %
- Elongation at Yield: 325 %
$ 1911/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 60 - 66
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00328 GPa
$ 1770/MT
- Specific Gravity: 1.47 - 1.51 g/cc
- Hardness, Shore A: 83 - 89
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.00848 GPa
- Melt Temperature: 182 °C
$ 1596/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 40.0 MPa
- Tensile Modulus: 2.41 GPa
$ 1635/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 18.3 MPa
- Elongation at Yield: 273.4 %
- Elongation at Yield: 340 %
$ 2177/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Melt Flow: 47.71 g/10 min @Load 23.9 kg, Temperature 175 °C
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 375 %
$ 1530/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Yield: 267.1 %
- Elongation at Yield: 350 %
$ 1597/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 91 - 97
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 325 %
- Melt Temperature: 182 °C
$ 1583/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.007343 GPa
$ 2160/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0121 GPa
$ 1451/MT
- Specific Gravity: 1.46 - 1.50 g/cc
- Hardness, Shore A: 92 - 98
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 240.6 %
- Elongation at Yield: 300 %
$ 1559/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Melt Flow: 12.64 g/10 min @Load 23.9 kg, Temperature 175 °C
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 325 %
$ 1737/MT
- Specific Gravity: 1.40 - 1.44 g/cc
- Hardness, Shore A: 86 - 92
- Hardness, Shore A: 89 - 95
- Tensile Strength, Yield: 16.72 MPa
- Elongation at Yield: 280.5 %
$ 2575/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Rockwell R: 112
- Hardness, Shore D: 79
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.62 GPa
$ 1947/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.008446 GPa
$ 1514/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Yield: 320 %
- 100% Modulus: 0.0131 GPa
- Melt Temperature: 191 °C
$ 1945/MT
- Specific Gravity: 1.35 - 1.39 g/cc
- Hardness, Shore A: 75 - 81
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 345 %
- 100% Modulus: 0.00672 GPa
$ 1778/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.0110 GPa
$ 2209/MT
- Specific Gravity: 1.34 - 1.40 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 49.6 MPa
- Tensile Modulus: 2.76 GPa
$ 2173/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 78
- Tensile Strength, Yield: 36.7 MPa
- Tensile Modulus: 2.00 GPa
$ 2150/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 75 - 81
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 292.4 %
$ 2122/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 37.9 MPa
- Tensile Modulus: 2.28 GPa
- Izod Impact, Notched: 0.801 J/cm @Thickness 3.17 mm, Temperature -40.0 °C
$ 1988/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Yield: 360 %
- 100% Modulus: 0.00500 GPa
$ 1522/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 54 - 60
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0207 GPa
- Melt Temperature: 185 °C
$ 2157/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Rockwell R: 110
- Hardness, Shore D: 80
- Tensile Strength, Yield: 46.2 MPa
- Tensile Modulus: 2.41 GPa
$ 1526/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 276.9 %
- Elongation at Yield: 390 %
$ 1881/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 76 - 82
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 400 %
- Brittleness Temperature: -40.0 °C
$ 1982/MT
- Specific Gravity: 1.26 - 1.30 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 330 %
- 100% Modulus: 0.00414 GPa
- Melt Temperature: 171 °C
$ 1659/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Yield: 357.4 %
- Elongation at Yield: 378 %
$ 1520/MT
- Specific Gravity: 0.500 - 0.600 g/cc
- Hardness, Shore D: 57.8
- Tensile Strength, Yield: 13.2 MPa
- Tensile Modulus: 1.81 GPa
- Flexural Strength: 24.5 MPa
$ 1887/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 91 - 97
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Yield: 250 %
- Brittleness Temperature: -22.0 °C
- Melt Temperature: 182 °C
$ 1781/MT
- Specific Gravity: 1.19 - 1.23 g/cc
- Hardness, Shore A: 51 - 57
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Yield: 400 %
- 100% Modulus: 0.00241 GPa
- Melt Temperature: 163 °C
$ 1606/MT
- Specific Gravity: 1.46 - 1.50 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00827 GPa
- Melt Temperature: 182 °C
$ 1593/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 75 - 81
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 300 %
$ 1709/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 75 - 81
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 300 %
$ 2177/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 300 %
- Elongation at Yield: 307.5 %
$ 1701/MT
- Specific Gravity: 1.23 - 1.27 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 340 %
- Flammability, UL94: V-1 @Thickness 0.580 mm
$ 1584/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 74 - 80
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 320 %
- Elongation at Yield: 400 %
$ 1538/MT
- Specific Gravity: 1.46 - 1.50 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00503 GPa
- Melt Temperature: 166 °C
$ 1513/MT
- Specific Gravity: 1.53 - 1.57 g/cc
- Hardness, Shore D: 52 - 58
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 200 %
- 100% Modulus: 0.0125 GPa
$ 2091/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Yield: 385 %
- 100% Modulus: 0.00517 GPa
$ 1813/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 301.75 %
- Elongation at Yield: 355 %
$ 1573/MT
- Specific Gravity: 1.24 - 1.28 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.0124 GPa
- Melt Temperature: 182 °C
$ 1505/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 44 - 50
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 252.3 %
- Elongation at Yield: 300 %
$ 1667/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 71 - 77
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 350 %
- 100% Modulus: 0.00496 GPa
- Melt Temperature: 171 °C
$ 1566/MT
- Specific Gravity: 1.31 - 1.35 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.00689 GPa
- Melt Temperature: 174 °C
$ 1484/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore D: 58 - 64
- Tensile Strength, Yield: 22.3 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0200 GPa
$ 2051/MT
- Specific Gravity: 1.44 - 1.48 g/cc
- Hardness, Shore D: 62 - 68
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Yield: 240 %
- Flammability, UL94: HB @Thickness >=3.00 mm
$ 1600/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Rockwell R: 88
- Hardness, Shore D: 80
- Tensile Strength, Yield: 43.0 MPa
- Tensile Modulus: 2.76 GPa
$ 1483/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Rockwell R: 93
- Hardness, Shore D: 80
- Tensile Strength, Yield: 40.7 MPa
- Tensile Modulus: 3.34 GPa
$ 1595/MT
- Specific Gravity: 1.50 g/cc
- Hardness, Shore D: 76
- Tensile Strength, Yield: 40.7 MPa
- Tensile Modulus: 3.09 GPa
- Flexural Strength: 77.9 MPa
$ 1680/MT
- Specific Gravity: 1.27 - 1.31 g/cc
- Hardness, Shore A: 63 - 69
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 336 %
- Elongation at Yield: 375 %
$ 1524/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 268.6 %
- Elongation at Yield: 340 %
$ 1571/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore D: 39 - 45
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0148 GPa
- Melt Temperature: 185 °C
$ 2205/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 57 - 63
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Yield: 264.9 %
- Elongation at Yield: 300 %
$ 1699/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 88 - 94
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Yield: 254.3 %
- Elongation at Yield: 340 %
$ 1789/MT
- Specific Gravity: 1.73 - 1.77 g/cc
- Hardness, Shore D: 39 - 45
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 220 %
- 100% Modulus: 0.00896 GPa
$ 1712/MT
- Specific Gravity: 1.21 - 1.25 g/cc
- Melt Flow: 26.4 g/10 min @Load 14.91 kg, Temperature 175 °C
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 395 %
$ 1534/MT
- Specific Gravity: 1.28 - 1.32 g/cc
- Hardness, Shore A: 78 - 84
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 299.9 %
- Elongation at Yield: 340 %
$ 1570/MT
- Specific Gravity: 1.44 - 1.48 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 275 %
- 100% Modulus: 0.0152 GPa
- Melt Temperature: 193 °C
$ 1455/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Yield: 300.2 %
- Elongation at Yield: 340 %
$ 1556/MT
- Specific Gravity: 1.58 - 1.62 g/cc
- Hardness, Shore D: 47 - 53
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 160 %
- Elongation at Yield: 200 %
$ 1471/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 81 - 87
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Yield: 325 %
- 100% Modulus: 0.01017 GPa
$ 1488/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 81
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.72 GPa
- Flexural Strength: 89.6 MPa
$ 1545/MT
- Specific Gravity: 1.25 - 1.29 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 20.3 MPa
- Elongation at Yield: 330 %
- 100% Modulus: 0.0124 GPa
$ 1765/MT
- Specific Gravity: 1.36 - 1.40 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 255 %
- Elongation at Yield: 300 %
$ 2303/MT
- Specific Gravity: 1.20 - 1.24 g/cc
- Hardness, Shore A: 51 - 57
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Yield: 425 %
- 100% Modulus: 0.00276 GPa
- Melt Temperature: 166 °C
$ 2374/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore D: 49 - 55
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 285 %
- 100% Modulus: 0.0179 GPa
$ 2131/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Rockwell R: 105
- Hardness, Shore D: 78
- Tensile Strength, Yield: 36.7 MPa
- Tensile Modulus: 2.00 GPa
$ 1520/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Yield: 264.3 %
- Elongation at Yield: 330 %
$ 1526/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 27.6 MPa
- Tensile Modulus: 1.57 GPa
- Flexural Strength: 40.0 MPa
$ 1644/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 57 - 63
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Yield: 460 %
- 100% Modulus: 0.00331 GPa
- Melt Temperature: 166 °C
$ 1579/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 16.9 MPa
- Elongation at Yield: 235.8 %
- Elongation at Yield: 279.4 %
$ 1585/MT
- Specific Gravity: 1.22 - 1.26 g/cc
- Hardness, Shore A: 77 - 83
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Yield: 375 %
- 100% Modulus: 0.00862 GPa
$ 2505/MT
- Specific Gravity: 1.52 - 1.56 g/cc
- Hardness, Shore A: 86 - 92
- Tensile Strength, Yield: 17.75 MPa
- Elongation at Yield: 184.2 %
- Elongation at Yield: 200 %
$ 1810/MT
- Specific Gravity: 1.29 - 1.33 g/cc
- Hardness, Shore A: 70 - 76
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 326.3 %
- Elongation at Yield: 332.3 %
$ 1784/MT
- Specific Gravity: 1.32 g/cc
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.55 GPa
- Flexural Strength: 81.4 MPa
- Izod Impact, Notched: 1.33 J/cm @Thickness 6.35 mm
$ 1635/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 85 - 91
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 264 %
- Elongation at Yield: 300 %
$ 2273/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore D: 78.5
- Tensile Strength, Yield: 39.2 MPa
- Tensile Modulus: 2.54 GPa
- Flexural Strength: 63.4 MPa
$ 1644/MT
- Specific Gravity: 1.37 - 1.41 g/cc
- Hardness, Shore A: 84 - 90
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Yield: 272 %
- Elongation at Yield: 320 %
$ 1531/MT
- Specific Gravity: 1.30 - 1.34 g/cc
- Hardness, Shore A: 67 - 73
- Tensile Strength, Yield: 9.31 MPa
- Elongation at Yield: 365 %
- 100% Modulus: 0.00503 GPa
$ 1786/MT
- Specific Gravity: 1.33 - 1.37 g/cc
- Hardness, Shore A: 82 - 88
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Yield: 231.8 %
- Elongation at Yield: 315 %
$ 1459/MT
- Specific Gravity: 1.32 - 1.36 g/cc
- Hardness, Shore D: 47 - 53
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 300 %
- 100% Modulus: 0.0165 GPa
- Melt Temperature: 191 °C
$ 1460/MT
- Specific Gravity: 1.66 - 1.70 g/cc
- Hardness, Shore D: 50 - 56
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Yield: 255.8 %
- Elongation at Yield: 275 %
$ 1605/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 48.3 MPa
- Tensile Modulus: 2.76 GPa
$ 1499/MT
- Specific Gravity: 1.48 - 1.52 g/cc
- Hardness, Shore A: 87 - 93
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Yield: 265 %
- 100% Modulus: 0.00965 GPa
$ 1672/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Rockwell R: 88
- Hardness, Shore D: 80
- Tensile Strength, Yield: 43.0 MPa
- Tensile Modulus: 2.76 GPa
Delivery Thermoplastic Axiall
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.