$ 1486/MT
- Density: 0.930 g/cc
- Moisture Vapor Transmission: 0.910 cc-mm/m²-24hr-atm
- Oxygen Transmission: 158 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Melt Flow: 2.5 g/10 min
- Film Elongation at Break, MD: 580 %
$ 1739/MT
- Density: 0.933 g/cc
- Density: 0.940 g/cc
- Vinyl Acetate Content: 12 %
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 96
$ 1452/MT
- Density: 0.935 g/cc
- Vinyl Acetate Content: 15 %
- Melt Index of Compound: 8.0 g/10 min
- Hardness, Shore A: 91
- Hardness, Shore D: 40
$ 2102/MT
- Density: 0.944 g/cc
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 78
- Hardness, Shore D: 28
- Tensile Strength at Break: 14.0 MPa
$ 1634/MT
- Density: 0.928 g/cc
- Viscosity: 1.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 3.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 112 °C
- Melting Point: 130 °C
$ 1966/MT
- Density: 0.920 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 112 °C
- Melting Point: 127 °C
- Vicat Softening Point: 93.0 °C
$ 1800/MT
- Density: 0.910 g/cc
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 103 °C
- Melting Point: 119 °C
- Vicat Softening Point: 84.0 °C
$ 1497/MT
- Density: 1.19 g/cc
- Oxygen Transmission: 0.470 cc-mm/m²-24hr-atm
- Viscosity: 200000 cP @Shear Rate 100 1/s, Temperature 300 °C
- Flexural Modulus: 2.80 GPa
- Deflection Temperature at 0.46 MPa (66 psi): 126 °C
$ 1569/MT
- Density: 0.926 g/cc
- Melt Flow: 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 67.0 °C
- Melting Point: 87.0 °C
- Vicat Softening Point: 60.0 °C
$ 2308/MT
- Density: 0.950 g/cc
- Melt Flow: 6.0 g/10 min
- Melting Point: 48.0 °C
- Melting Point: 73.0 °C
- Vicat Softening Point: 47.0 °C
- Melt Temperature: 175 - 215 °C
$ 1800/MT
- Density: 0.950 g/cc
- Melt Flow: 22.5 g/10 min
$ 2049/MT
- Density: 1.01 g/cc
- Melt Flow: 7.5 g/10 min
$ 1939/MT
- Density: 0.930 g/cc
- Melt Flow: 60 g/10 min
$ 1702/MT
- Density: 0.930 g/cc
- Melt Flow: 36 g/10 min
$ 1482/MT
- Density: 0.960 g/cc
- Melt Flow: 25 g/10 min
$ 1710/MT
- Density: 0.933 g/cc
- Viscosity: 3.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 115 °C
- Melting Point: 129 °C
$ 1590/MT
- Density: 0.950 g/cc
- Viscosity: 1.20e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 58.0 °C
- Melting Point: 80.0 °C
$ 2444/MT
- Density: 0.940 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 94.0 °C
- Vicat Softening Point: 60.0 °C
- Rear Barrel Temperature: 140 °C
$ 2504/MT
- Density: 0.930 g/cc
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 95
- Hardness, Shore D: 45
- Tensile Strength at Break: 13.0 MPa
$ 2047/MT
- Density: 0.940 g/cc
- Vinyl Acetate Content: 18 %
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 68.0 °C
- Melting Point: 89.0 °C
- Vicat Softening Point: 69.0 °C
$ 1662/MT
- Density: 0.930 g/cc
- Moisture Vapor Transmission: 0.940 cc-mm/m²-24hr-atm
- Oxygen Transmission: 181 cc-mm/m²-24hr-atm
- Viscosity: 2.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 0.35 g/10 min
$ 1985/MT
- Density: 0.980 g/cc
- Viscosity: 900000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 55.0 °C
- Melting Point: 75.0 °C
$ 1638/MT
- Density: 0.930 g/cc
- Melt Flow: 7.0 g/10 min
- Coefficient of Friction: 0.34
- Coefficient of Friction: 0.66
- Melting Point: 79.0 °C
$ 1540/MT
- Density: 0.915 g/cc
- Viscosity: 900000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 4.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 92.0 °C
- Melting Point: 106 °C
$ 1502/MT
- Density: 0.940 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 5.20 MPa
- Elongation at Break: 950 %
$ 1767/MT
- Density: 0.930 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 540 %
- Film Elongation at Break, TD: 560 %
- Secant Modulus, MD: 0.170 GPa
$ 2127/MT
- Density: 0.920 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 14.4 MPa
- Tensile Strength, Yield: 9.60 MPa
$ 1674/MT
- Density: 0.960 g/cc
- Viscosity: 700000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 5.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 52.0 °C
- Melting Point: 74.0 °C
$ 1594/MT
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Seal Strength: 1300 g/25 mm
- Hot Tack Strength: 1150 g/25 mm
- Melting Point: 82.0 °C
- Melting Point: 100 °C
$ 1973/MT
- Density: 1.00 g/cc
- Melt Flow: 25 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 5.90 MPa
- Elongation at Break: 950 %
$ 1935/MT
- Density: 0.926 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 240 %
- Film Elongation at Break, TD: 680 %
$ 1944/MT
- Density: 0.930 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 84.0 °C
- Melting Point: 103 °C
- Vicat Softening Point: 86.0 °C
$ 2085/MT
- Density: 0.920 g/cc
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51
- Tensile Strength, Ultimate: 18.6 MPa
- Tensile Strength, Yield: 9.60 MPa
$ 2179/MT
- Density: 0.925 g/cc
- Viscosity: 2.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 109 °C
- Melting Point: 125 °C
$ 2042/MT
- Processing Temperature: >= 221 °C
$ 1471/MT
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hot Tack Strength: 500 g/25 mm
- Melting Point: 87.0 °C
- Melting Point: 109 °C
- Vicat Softening Point: 90.0 °C
$ 1563/MT
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 500 %
- Film Elongation at Break, TD: 450 %
- Secant Modulus, MD: 0.165 GPa
- Secant Modulus, TD: 0.152 GPa
$ 2170/MT
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 83.0 °C
- Melting Point: 104 °C
- Vicat Softening Point: 88.0 °C
- Nozzle Temperature: 300 °C
- Melt Temperature: 260 - 315 °C
$ 1748/MT
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 450 %
- Film Elongation at Break, TD: 450 %
- Secant Modulus, MD: 0.159 GPa
- Secant Modulus, TD: 0.131 GPa
$ 2091/MT
- Density: 0.930 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 95.0 °C
- Vicat Softening Point: 72.0 °C
- Rear Barrel Temperature: 140 °C
$ 1662/MT
- Density: 1.90 g/cc
- Melt Index of Compound: 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 2.76 MPa
- Elongation at Break: 550 %
$ 2125/MT
- Density: 0.935 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 117 °C
- Melting Point: 135 °C
- Vicat Softening Point: 119 °C
$ 1739/MT
- Density: 0.938 g/cc
- Viscosity: 1.20e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 88.0 °C
- Melting Point: 99.0 °C
$ 1494/MT
- Density: 0.946 g/cc
- Viscosity: 900000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 6.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 51.0 °C
- Melting Point: 74.0 °C
$ 2240/MT
- Density: 0.920 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 16.1 MPa
- Tensile Strength, Yield: 9.60 MPa
$ 2208/MT
- Density: 0.980 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 90.0 °C
- Vicat Softening Point: 68.0 °C
- Rear Barrel Temperature: 140 °C
$ 2413/MT
- Density: 0.927 g/cc
- Viscosity: 1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 110 °C
- Melting Point: 125 °C
$ 2003/MT
- Density: 0.980 g/cc
- Melt Flow: 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 59
- Tensile Strength at Break: 3.40 MPa
- Elongation at Break: 1213 %
$ 1730/MT
- Bulk Density: 0.577 g/cc
- Density: 0.940 g/cc
- Melt Flow: 5.0 - 11 g/10 min
- Melting Point: 72.0 °C
$ 1579/MT
- Density: 0.912 g/cc
- Viscosity: 2.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 95.0 °C
- Melting Point: 110 °C
$ 1611/MT
- Density: 0.940 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 78.0 °C
- Melting Point: 97.0 °C
- Vicat Softening Point: 79.0 °C
$ 2070/MT
- Density: 0.980 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 3.40 MPa
- Elongation at Break: 1050 %
$ 1936/MT
- Density: 0.947 g/cc
- Viscosity: 300000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 51.0 °C
- Melting Point: 70.0 °C
$ 1458/MT
- Density: 0.930 g/cc
- Melt Index of Compound: 450 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 42
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 500 %
$ 1529/MT
- Density: 1.02 g/cc
- Melt Flow: 25 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 4.20 MPa
- Elongation at Break: 1200 %
$ 1723/MT
- Melt Flow: 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 35.20 MPa
- Tensile Strength at Break: 42.1 MPa
- Elongation at Break: 350 %
- Elongation at Break: 350 %
$ 1694/MT
- Specific Gravity: 0.950 g/cc
- Melt Index of Compound: 4.0 g/10 min
- Hardness, Shore D: 65
- Tensile Strength at Break: 22.1 MPa
- Tensile Strength, Yield: 15.9 MPa
$ 1550/MT
- Specific Gravity: 1.043 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.139 GPa
$ 1553/MT
- Specific Gravity: 0.970 g/cc
- Melt Index of Compound: 4.0 g/10 min
- Hardness, Shore D: 62
- Tensile Strength at Break: 19.3 MPa
- Tensile Strength, Yield: 13.8 MPa
$ 1482/MT
- Density: 0.957 g/cc
- Vinyl Acetate Content: 32 %
- Melt Flow: 43 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 73
- Hardness, Shore D: 24
$ 1509/MT
- Density: 0.975 g/cc
- Vinyl Acetate Content: 32 %
- Melt Flow: 43 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Melting Point: 63.0 °C
$ 2414/MT
- Density: 0.951 g/cc
- Vinyl Acetate Content: 28 %
- Melt Flow: 400 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 62
- Ring & Ball Softening Point: 82.0 °C
- Cloud Point in Paraffin Wax, °C: 66
$ 1521/MT
- Density: 0.951 g/cc
- Vinyl Acetate Content: 28 %
- Melt Flow: 150 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 69
- Ring & Ball Softening Point: 88.0 °C
- Cloud Point in Paraffin Wax, °C: 66
$ 1824/MT
- Density: 0.951 g/cc
- Vinyl Acetate Content: 28 %
- Melt Flow: 43 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 73
- Ring & Ball Softening Point: 110 °C
- Cloud Point in Paraffin Wax, °C: 66
$ 1504/MT
- Density: 0.951 g/cc
- Vinyl Acetate Content: 28 %
- Melt Index of Compound: 6.0 g/10 min
- Hardness, Shore A: 85
- Hardness, Shore D: 33
$ 1501/MT
- Density: 0.951 g/cc
- Vinyl Acetate Content: 28 %
- Melt Index of Compound: 3.0 g/10 min
- Hardness, Shore A: 86
- Hardness, Shore D: 35
$ 1956/MT
- Density: 0.940 g/cc
- Moisture Vapor Transmission: 0.590 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Oxygen Transmission: 177 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Melt Flow: 1.2 g/10 min
- Film Elongation at Break, MD: 450 %
$ 1585/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 12 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 76.0 °C
- Melting Point: 95.0 °C
- Vicat Softening Point: 71.0 °C
$ 2516/MT
- Density: 0.930 g/cc
- Moisture Vapor Transmission: 0.910 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Oxygen Transmission: 201 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Viscosity: 2.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 0.35 g/10 min
$ 1738/MT
- Density: 0.940 g/cc
- Moisture Vapor Transmission: 1.30 cc-mm/m²-24hr-atm
- Oxygen Transmission: 197 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Melt Flow: 2.5 g/10 min
- Film Elongation at Break, MD: 575 %
$ 1445/MT
- Density: 0.940 g/cc
- Moisture Vapor Transmission: 1.65 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Oxygen Transmission: 229 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Viscosity: 2.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 0.70 g/10 min
$ 1865/MT
- Density: 0.940 g/cc
- Moisture Vapor Transmission: 1.42 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Oxygen Transmission: 264 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Melt Flow: 0.70 g/10 min
- Film Elongation at Break, MD: 530 %
$ 2508/MT
- Density: 0.940 g/cc
- Moisture Vapor Transmission: 1.50 cc-mm/m²-24hr-atm
- Oxygen Transmission: 185 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Viscosity: 1.20e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.5 g/10 min
$ 2145/MT
- Density: 0.940 g/cc
- Moisture Vapor Transmission: 1.46 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Oxygen Transmission: 211 cc-mm/m²-24hr-atm @Thickness 0.0254 mm
- Viscosity: 1.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.5 g/10 min
$ 2279/MT
- Density: 0.940 g/cc
- Melt Flow: 30 g/10 min
- Coefficient of Friction: 0.17
- Coefficient of Friction: 0.43
- Melting Point: 65.0 °C
$ 1582/MT
- Density: 0.950 g/cc
- Melt Flow: 25 g/10 min
- Melting Point: 45.0 °C
- Melting Point: 70.0 °C
- Vicat Softening Point: 43.0 °C
$ 1719/MT
- Density: 0.950 g/cc
- Melt Flow: 3.0 g/10 min
- Melting Point: 51.0 °C
- Melting Point: 73.0 °C
- Vicat Softening Point: 49.0 °C
$ 1683/MT
- Density: 0.950 g/cc
- Vinyl Acetate Content: 28 %
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 48.0 °C
- Melting Point: 72.0 °C
- Vicat Softening Point: 49.0 °C
$ 2221/MT
- Density: 0.968 g/cc
- Vinyl Acetate Content: 40 %
- Melt Index of Compound: 2.1 - 3.9 g/10 min
- Hardness, Shore A: 52
- Tensile Strength at Break: 9.80 MPa
$ 2389/MT
- Density: 0.965 g/cc
- Viscosity Measurement: 0.70 @Temperature 30.0 °C
- Vinyl Acetate Content: 40 %
- Melt Index of Compound: 52 g/10 min
- Hardness, Shore A: 40
$ 2398/MT
- Density: 0.934 g/cc
- Vinyl Acetate Content: 18 %
- Melt Flow: 500 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Ring & Ball Softening Point: 88.0 °C
- Cloud Point in Paraffin Wax, °C: 66
$ 1976/MT
- Density: 0.937 g/cc
- Vinyl Acetate Content: 18 %
- Melt Flow: 150 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 84
- Ring & Ball Softening Point: 99.0 °C
- Cloud Point in Paraffin Wax, °C: 66
$ 1947/MT
- Density: 0.941 g/cc
- Vinyl Acetate Content: 18 %
- Melt Index of Compound: 8.0 g/10 min
- Hardness, Shore A: 88
- Hardness, Shore D: 38
$ 2294/MT
- Density: 0.941 g/cc
- Vinyl Acetate Content: 18 %
- Melt Index of Compound: 2.5 g/10 min
- Hardness, Shore A: 90
- Hardness, Shore D: 39
$ 1520/MT
- Density: 0.933 g/cc
- Vinyl Acetate Content: 12 %
- Melt Index of Compound: 2.5 g/10 min
- Hardness, Shore A: 95
- Hardness, Shore D: 44
$ 1717/MT
- Density: 0.933 g/cc
- Vinyl Acetate Content: 12 %
- Melt Index of Compound: 0.30 g/10 min
- Hardness, Shore A: 96
- Hardness, Shore D: 45
$ 2495/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 9.3 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 97
- Hardness, Shore D: 46
$ 1745/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 9.5 %
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 98
- Hardness, Shore D: 47
$ 1590/MT
- Density: 0.948 g/cc
- Vinyl Acetate Content: 25 %
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 83
- Hardness, Shore D: 28
$ 1507/MT
- Density: 0.948 g/cc
- Vinyl Acetate Content: 25 %
- Melt Index of Compound: 2.0 g/10 min
- Hardness, Shore A: 87
- Hardness, Shore D: 36
$ 1590/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 7.0 %
- Melt Index of Compound: 7.0 g/10 min
- Hardness, Shore A: 95
- Hardness, Shore D: 46
$ 1488/MT
- Density: 0.950 g/cc
- Viscosity: 700000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 10.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 48.0 °C
- Melting Point: 74.0 °C
$ 2350/MT
- Density: 0.930 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 83.0 °C
- Melting Point: 96.0 °C
- Vicat Softening Point: 84.0 °C
$ 1857/MT
- Density: 0.940 g/cc
- Melt Index of Compound: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 520 %
$ 2061/MT
- Density: 0.890 g/cc
- Viscosity: 1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 101 °C
- Melting Point: 156 °C
$ 1703/MT
- Density: 0.910 g/cc
- Melt Flow: 5.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 96.0 °C
- Melting Point: 105 °C
- Vicat Softening Point: 80.0 °C
$ 1550/MT
- Density: 0.924 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89
- Hardness, Shore D: 31
- Tensile Strength at Break: 10.0 MPa
$ 2422/MT
- Density: 0.930 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 97
- Hardness, Shore D: 46
- Tensile Strength at Break: 13.0 MPa
$ 1481/MT
- Density: 0.940 g/cc
- Melt Flow: 55 g/10 min
$ 1704/MT
- Density: 0.940 g/cc
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 74.0 °C
- Melting Point: 95.0 °C
- Vicat Softening Point: 72.0 °C
$ 2564/MT
- Density: 0.950 g/cc
- Viscosity: 1.40e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Seal Strength: 1200 g/25 mm
- Seal Strength: 1400 g/25 mm
$ 1569/MT
- Density: 0.960 g/cc
- Viscosity: 1.00e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Seal Strength: 2500 - 3000 g/25 mm
- Seal Strength: 4500 g/25 mm
$ 1448/MT
- Density: 0.950 g/cc
- Melt Flow: 32 g/10 min
- Coefficient of Friction: 0.48
- Coefficient of Friction: 0.95
- Melting Point: 55.0 °C
$ 1556/MT
- Density: 0.930 g/cc
- Viscosity: 1.10e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 596 %
- Film Elongation at Break, TD: 628 %
$ 1831/MT
- Density: 0.943 g/cc
- Viscosity: 800000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 69.0 °C
- Melting Point: 87.0 °C
$ 1792/MT
- Density: 0.924 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Hardness, Shore D: 32
- Tensile Strength at Break: 13.0 MPa
$ 2446/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 9.3 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 97
- Hardness, Shore D: 46
$ 1939/MT
- Density: 0.940 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 490 %
- Film Elongation at Break, TD: 440 %
- Secant Modulus, MD: 0.124 GPa
$ 1607/MT
- Density: 0.960 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 3.40 MPa
- Elongation at Break: 1050 %
$ 1969/MT
- Density: 1.04 g/cc
- Melt Flow: 6.5 g/10 min
$ 1456/MT
- Density: 0.940 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 83.0 °C
- Melting Point: 98.0 °C
- Vicat Softening Point: 77.0 °C
$ 2192/MT
- Density: 0.930 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hot Tack Strength: 800 g/25 mm
- Melting Point: 84.0 °C
- Melting Point: 109 °C
$ 1605/MT
- Density: 1.03 g/cc
- Melt Flow: 7.0 - 23 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 10.90 MPa
- Elongation at Break: 736 %
- Melting Point: 70.0 °C
- Glass Transition Temp, Tg: -36.0 °C
$ 1506/MT
- Density: 0.927 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 98
- Hardness, Shore D: 47
- Tensile Strength at Break: 14.0 MPa
$ 2022/MT
- Density: 0.930 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 88
- Hardness, Shore D: 31
- Tensile Strength at Break: 12.0 MPa
$ 2340/MT
- Density: 0.931 g/cc
- Viscosity: 600000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 66.0 °C
- Melting Point: 91.0 °C
$ 1673/MT
- Density: 0.915 g/cc
- Viscosity: 1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 90.0 °C
- Melting Point: 106 °C
$ 2154/MT
- Density: 0.960 g/cc
- Melt Flow: 70 - 130 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 2.20 MPa
- Elongation at Break: 580 %
- Melting Point: 63.0 °C
$ 2402/MT
- Density: 0.920 g/cc
- Viscosity: 1.60e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 111 °C
- Melting Point: 126 °C
$ 1821/MT
- Density: 0.942 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 87
- Hardness, Shore D: 28
- Tensile Strength at Break: 11.0 MPa
$ 1527/MT
- Density: 0.930 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 87.0 °C
- Melting Point: 99.0 °C
- Vicat Softening Point: 81.0 °C
$ 1793/MT
- Density: 0.940 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89
- Hardness, Shore D: 35
- Tensile Strength at Break: 13.0 MPa
$ 1740/MT
- Density: 0.920 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 105 °C
- Vicat Softening Point: 90.0 °C
- Rear Barrel Temperature: 100 °C
$ 2105/MT
- Density: 0.930 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Seal Strength: 1500 g/25 mm
- Hot Tack Strength: 1000 g/25 mm
- Melting Point: 84.0 °C
$ 1582/MT
- Density: 1.85 g/cc
- Melt Index of Compound: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 1.03 MPa
- Elongation at Break: 350 %
$ 1490/MT
- Density: 1.00 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 6.20 MPa
- Elongation at Break: 1126 %
$ 2214/MT
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Seal Strength: 2300 g/25 mm
- Hot Tack Strength: 1800 g/25 mm
- Melting Point: 84.0 °C
- Melting Point: 102 °C
$ 1724/MT
- Density: 0.928 g/cc
- Viscosity: 200000 cP @Shear Rate 50.0 1/s, Temperature 190 °C
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 62.0 °C
- Melting Point: 87.0 °C
$ 2246/MT
- Density: 1.19 g/cc
- Tensile Strength, Ultimate: 70.0 MPa
- Film Elongation at Break, MD: 20 %
- Flexural Modulus: 2.80 GPa
- Glass Transition Temp, Tg: 125 °C
- Haze: <= 1.0 %
$ 1527/MT
- Density: 0.951 g/cc
- Vinyl Acetate Content: 28 %
- Melt Index of Compound: 25 g/10 min
- Hardness, Shore A: 80
- Hardness, Shore D: 28
$ 1484/MT
- Density: 0.940 g/cc
- Melt Index of Compound: 95 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 560 %
Delivery Thermoplastic DuPont Packaging and Industrial Polymers
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.