$ 1538/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 185 MPa
$ 1687/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 150 MPa
$ 1653/MT
- Density: 1.18 g/cc
- Moisture Absorption: 2.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 80.0 MPa
$ 1581/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength, Yield: 80.0 MPa
$ 1637/MT
- Density: 1.70 g/cc
- Moisture Absorption: 1.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 235 MPa
$ 1746/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 1444/MT
- Density: 1.47 g/cc
- Filler Content: 20 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2052/MT
- Density: 1.33 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 150 MPa
$ 1866/MT
- Density: 1.36 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 2.1 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage: 0.0020 cm/cm
$ 2036/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1535/MT
- Density: 1.68 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1757/MT
- Density: 1.62 g/cc
- Moisture Absorption: 1.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 125 MPa
$ 2311/MT
- Density: 1.45 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 115 MPa
$ 1461/MT
- Density: 1.31 g/cc
- Moisture Absorption: 1.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 275 MPa
$ 1736/MT
- Density: 1.54 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 90.0 MPa
$ 1737/MT
- Density: 1.16 g/cc
- Moisture Absorption: 2.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 2466/MT
- Density: 1.42 g/cc
- Filler Content: 15 %
- Moisture Absorption at Equilibrium: 0.16 %
- Water Absorption at Saturation: 0.43 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1651/MT
- Density: 1.33 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Modulus: 2.75 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m² @Temperature 23.0 °C
$ 1526/MT
- Density: 1.57 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 150 MPa
$ 1446/MT
- Density: 1.23 g/cc
- Filler Content: 15 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 7.5 %
- Linear Mold Shrinkage: 0.014 cm/cm
$ 1665/MT
- Density: 1.25 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 85.0 MPa
$ 1676/MT
- Density: 1.44 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 24.0 GPa
$ 1873/MT
- Density: 1.26 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 45.0 MPa
$ 1497/MT
- Density: 0.960 g/cc
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 2.50 GPa
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature -30.0 °C
$ 1729/MT
- Density: 0.930 g/cc
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: >= 100 %
- Tensile Modulus: 1.00 GPa
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature -30.0 °C
$ 1488/MT
- Density: 1.82 g/cc
- Filler Content: 45 %
- Moisture Absorption at Equilibrium: 0.10 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1494/MT
- Density: 1.04 g/cc
- Moisture Absorption: 2.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 45.0 MPa
$ 1662/MT
- Density: 1.83 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1707/MT
- Density: 1.56 g/cc
- Moisture Absorption: 1.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 175 MPa
$ 1446/MT
- Density: 1.15 g/cc
- Moisture Absorption: 2.60 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 85.0 MPa
$ 2066/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 85.0 MPa
$ 1650/MT
- Density: 1.18 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1932/MT
- Density: 1.51 g/cc
- Moisture Absorption: 1.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 100 MPa
$ 2525/MT
- Density: 1.23 g/cc
- Moisture Absorption: 2.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1606/MT
- Density: 1.27 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 150 MPa
$ 2495/MT
- Density: 1.58 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 110 MPa
$ 2293/MT
- Density: 1.32 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 170 MPa
$ 1542/MT
- Density: 1.35 g/cc
- Filler Content: 25 %
- Moisture Absorption at Equilibrium: 1.6 %
- Water Absorption at Saturation: 5.5 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1603/MT
- Density: 1.39 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1559/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 185 MPa
$ 1670/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 185 MPa
$ 1503/MT
- Density: 1.30 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1496/MT
- Density: 1.36 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 1.9 %
- Water Absorption at Saturation: 6.0 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2003/MT
- Density: 1.37 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 1.9 %
- Water Absorption at Saturation: 6.0 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1980/MT
- Density: 1.43 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 170 MPa
$ 2545/MT
- Density: 1.45 g/cc
- Moisture Absorption: 1.60 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 210 MPa
$ 1598/MT
- Density: 1.46 g/cc
- Filler Content: 40 %
- Moisture Absorption at Equilibrium: 1.6 %
- Water Absorption at Saturation: 5.0 %
- Linear Mold Shrinkage: 0.0020 cm/cm
$ 2516/MT
- Density: 1.46 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 200 MPa
$ 2528/MT
- Density: 1.57 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 230 MPa
$ 1594/MT
- Density: 1.55 g/cc
- Filler Content: 50 %
- Moisture Absorption at Equilibrium: 1.3 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage: 0.0020 cm/cm
$ 2082/MT
- Density: 1.58 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 220 MPa
$ 2170/MT
- Density: 1.36 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 6.0 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 1734/MT
- Density: 1.49 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 1995/MT
- Density: 1.23 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 2018/MT
- Density: 1.14 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.7 %
- Water Absorption at Saturation: 8.5 %
- Linear Mold Shrinkage: 0.014 cm/cm
$ 2135/MT
- Density: 1.18 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.2 %
- Water Absorption at Saturation: 7.0 %
- Linear Mold Shrinkage: 0.013 cm/cm
$ 1541/MT
- Density: 1.07 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 1733/MT
- Density: 1.15 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.7 %
- Water Absorption at Saturation: 8.0 %
- Linear Mold Shrinkage: 0.013 cm/cm
$ 1477/MT
- Density: 1.38 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 125 MPa
$ 2021/MT
- Density: 1.40 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 140 MPa
$ 1938/MT
- Density: 1.27 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 90.0 MPa
$ 1688/MT
- Density: 1.67 g/cc
- Moisture Absorption: 1.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 1639/MT
- Density: 1.34 g/cc
- Moisture Absorption: 1.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1693/MT
- Density: 1.44 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.40 %
- Linear Mold Shrinkage: 0.015 cm/cm
$ 1929/MT
- Density: 1.38 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 95.0 MPa
$ 2043/MT
- Density: 1.38 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 60.0 MPa
$ 1660/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 85.0 MPa
$ 2251/MT
- Density: 1.45 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength at Break: 55.0 MPa
$ 1663/MT
- Density: 1.42 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength at Break: 55.0 MPa
$ 1923/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 5.50 GPa
$ 1588/MT
- Density: 1.14 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 3.0 %
- Water Absorption at Saturation: 9.0 %
- Linear Mold Shrinkage: 0.011 cm/cm
$ 2060/MT
- Density: 1.13 g/cc
- Moisture Absorption: 3.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength at Break: 80.0 MPa
$ 1580/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 175 MPa
$ 2283/MT
- Density: 1.54 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1664/MT
- Density: 1.45 g/cc
- Filler Content: 20 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.40 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 2123/MT
- Density: 1.40 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1619/MT
- Density: 1.53 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 6.50 GPa
$ 1832/MT
- Density: 1.34 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.5 %
- Water Absorption at Saturation: 7.5 %
- Linear Mold Shrinkage: 0.010 cm/cm
$ 2196/MT
- Density: 1.21 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 60.0 MPa
$ 1584/MT
- Density: 1.73 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 17.0 GPa
$ 2540/MT
- Density: 1.55 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 0.14 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2082/MT
- Density: 1.33 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 110 MPa
$ 2103/MT
- Density: 1.29 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 1.8 %
- Water Absorption at Saturation: 5.5 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1805/MT
- Density: 1.52 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 0.14 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1812/MT
- Density: 1.31 g/cc
- Filler Content: 25 %
- Moisture Absorption at Equilibrium: 2.2 %
- Water Absorption at Saturation: 7.0 %
- Linear Mold Shrinkage: 0.0020 cm/cm
$ 1632/MT
- Density: 1.31 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 160 MPa
$ 1626/MT
- Density: 1.20 g/cc
- Moisture Absorption: 2.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 2010/MT
- Density: 1.72 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 150 MPa
$ 1992/MT
- Density: 1.56 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1820/MT
- Density: 1.37 g/cc
- Filler Content: 10 %
- Moisture Absorption at Equilibrium: 0.18 %
- Water Absorption at Saturation: 0.45 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1545/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 1910/MT
- Density: 1.56 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 220 MPa
$ 1778/MT
- Density: 1.58 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1498/MT
- Density: 1.85 g/cc
- Tensile Strength at Break: 260 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 28.0 GPa
- Izod Impact, Notched (ISO): 16.0 kJ/m² @Temperature 23.0 °C
$ 1469/MT
- Density: 1.63 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1813/MT
- Density: 1.70 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1583/MT
- Density: 1.32 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 50.0 MPa
$ 2449/MT
- Density: 1.08 g/cc
- Moisture Absorption: 2.60 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 60.0 MPa
$ 1561/MT
- Density: 1.40 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0016 cm/cm
- Tensile Strength at Break: 45.0 MPa
$ 1858/MT
- Density: 1.33 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 115 MPa
$ 1556/MT
- Density: 1.34 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.40 %
- Linear Mold Shrinkage: 0.015 cm/cm
$ 2190/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 10.0 GPa
$ 1539/MT
- Density: 1.71 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 140 MPa
$ 2279/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 24.0 GPa
$ 1840/MT
- Density: 1.31 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 80.0 MPa
$ 1658/MT
- Density: 1.28 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 50.0 MPa
$ 1833/MT
- Density: 1.43 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength at Break: 60.0 MPa
$ 1590/MT
- Density: 1.50 g/cc
- Moisture Absorption: 0.800 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 35.0 MPa
$ 1820/MT
- Density: 1.54 g/cc
- Moisture Absorption: 1.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 200 MPa
$ 1625/MT
- Density: 1.20 g/cc
- Moisture Absorption: 2.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1560/MT
- Density: 1.48 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0010 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1452/MT
- Density: 1.58 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength at Break: 50.0 MPa
$ 2546/MT
- Density: 1.31 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 2381/MT
- Density: 1.59 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 140 MPa
$ 1717/MT
- Density: 1.43 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.00 GPa
$ 1542/MT
- Density: 1.53 g/cc
- Filler Content: 15 %
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage: 0.0050 cm/cm
$ 1508/MT
- Density: 1.43 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.00 GPa
$ 1686/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1965/MT
- Density: 1.36 g/cc
- Filler Content: 20 %
- Moisture Absorption at Equilibrium: 0.13 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 2302/MT
- Density: 1.23 g/cc
- Filler Content: 15 %
- Moisture Absorption at Equilibrium: 2.5 %
- Water Absorption at Saturation: 8.0 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1682/MT
- Density: 1.43 g/cc
- Moisture Absorption: 1.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 185 MPa
$ 1498/MT
- Density: 1.50 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1954/MT
- Density: 1.47 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1589/MT
- Density: 1.11 g/cc
- Moisture Absorption: 2.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 65.0 MPa
$ 2256/MT
- Density: 1.69 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 175 MPa
$ 1759/MT
- Density: 1.50 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Tensile Strength, Yield: 50.0 MPa
$ 1741/MT
- Density: 1.58 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 12.0 GPa
$ 1783/MT
- Density: 1.13 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 2.25 GPa
- Izod Impact, Notched (ISO): 20.0 kJ/m² @Temperature -30.0 °C
$ 2070/MT
- Density: 1.40 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 80.0 MPa
$ 1530/MT
- Density: 1.54 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength at Break: 115 MPa
$ 1699/MT
- Density: 1.45 g/cc
- Moisture Absorption: 1.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 60.0 MPa
$ 1445/MT
- Density: 1.22 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 200 MPa
$ 1980/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength, Yield: 80.0 MPa
$ 2109/MT
- Density: 1.47 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength at Break: 90.0 MPa
$ 1628/MT
- Density: 1.19 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.5 %
- Water Absorption at Saturation: 8.0 %
- Linear Mold Shrinkage: 0.011 cm/cm
$ 1480/MT
- Density: 1.42 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Tensile Strength, Yield: 60.0 MPa
$ 1498/MT
- Density: 1.70 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 225 MPa
$ 1480/MT
- Density: 1.11 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.25 GPa
- Izod Impact, Notched (ISO): 14.0 kJ/m² @Temperature 23.0 °C
$ 1536/MT
- Density: 1.11 g/cc
- Tensile Strength at Break: 72.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 5.50 GPa
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature 23.0 °C
$ 1805/MT
- Density: 1.05 g/cc
- Tensile Strength at Break: 25.0 MPa
- Tensile Modulus: 2.00 GPa
- Izod Impact, Notched (ISO): 2.50 kJ/m² @Temperature -30.0 °C
- Izod Impact, Notched (ISO): 3.50 kJ/m² @Temperature 23.0 °C
$ 1880/MT
- Density: 0.990 g/cc
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 3.25 GPa
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature -30.0 °C
$ 1499/MT
- Density: 1.11 g/cc
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 5.50 GPa
- Izod Impact, Notched (ISO): 15.0 kJ/m² @Temperature -30.0 °C
$ 1585/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 11.0 GPa
- Izod Impact, Notched (ISO): 15.0 kJ/m² @Temperature -30.0 °C
$ 1907/MT
- Density: 0.990 g/cc
- Tensile Strength at Break: 25.0 MPa
- Tensile Modulus: 1.25 GPa
- Izod Impact, Notched (ISO): 60.0 kJ/m² @Temperature 23.0 °C
- Melting Point: 160 - 165 °C
$ 1565/MT
- Density: 1.11 g/cc
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 1.50 GPa
- Izod Impact, Notched (ISO): 4.00 kJ/m² @Temperature -30.0 °C
$ 1507/MT
- Density: 1.07 g/cc
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.00 GPa
- Izod Impact, Notched (ISO): 25.0 kJ/m² @Temperature 23.0 °C
$ 1541/MT
- Density: 1.20 g/cc
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 7.00 GPa
- Izod Impact, Notched (ISO): 15.0 kJ/m² @Temperature -30.0 °C
$ 1715/MT
- Density: 1.36 g/cc
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 3.50 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m² @Temperature -30.0 °C
$ 1463/MT
- Density: 1.09 g/cc
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 40 %
- Tensile Modulus: 2.25 GPa
- Izod Impact, Notched (ISO): 3.50 kJ/m² @Temperature -30.0 °C
$ 1809/MT
- Density: 1.03 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.25 GPa
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature -30.0 °C
$ 2177/MT
- Density: 0.900 g/cc
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: >= 200 %
- Tensile Modulus: 0.750 GPa
- Izod Impact, Notched (ISO): 60.0 kJ/m² @Temperature 23.0 °C
$ 1899/MT
- Density: 0.950 g/cc
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 3.00 GPa
- Izod Impact, Notched (ISO): 6.00 kJ/m² @Temperature 23.0 °C
$ 2060/MT
- Density: 1.03 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 5.00 GPa
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature 23.0 °C
$ 1488/MT
- Density: 0.930 g/cc
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: >= 100 %
- Tensile Modulus: 1.25 GPa
- Izod Impact, Notched (ISO): 3.00 kJ/m² @Temperature -30.0 °C
$ 1668/MT
- Density: 1.05 g/cc
- Tensile Strength at Break: 20.0 MPa
- Tensile Modulus: 1.75 GPa
- Izod Impact, Notched (ISO): 4.00 kJ/m² @Temperature -30.0 °C
- Izod Impact, Notched (ISO): 10.0 kJ/m² @Temperature 23.0 °C
$ 1519/MT
- Density: 1.05 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 6.0 %
- Linear Mold Shrinkage: 0.017 cm/cm
$ 1772/MT
- Density: 1.18 g/cc
- Moisture Absorption: 2.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 150 MPa
$ 1796/MT
- Density: 1.36 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength at Break: 50.0 MPa
$ 1571/MT
- Density: 1.50 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 170 MPa
$ 1882/MT
- Density: 1.50 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 170 MPa
$ 1650/MT
- Density: 1.55 g/cc
- Filler Content: 50 %
- Moisture Absorption at Equilibrium: 1.5 %
- Water Absorption at Saturation: 4.5 %
- Linear Mold Shrinkage: 0.0010 cm/cm
$ 1552/MT
- Density: 1.06 g/cc
- Moisture Absorption: 2.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 50.0 MPa
$ 1615/MT
- Density: 1.27 g/cc
- Moisture Absorption: 2.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 145 MPa
$ 2387/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 7.5 %
- Tensile Modulus: 3.50 GPa
- Izod Impact, Notched (ISO): 7.00 kJ/m² @Temperature -30.0 °C
$ 1790/MT
- Density: 1.04 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 50.0 MPa
$ 1853/MT
- Density: 1.11 g/cc
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 2.25 GPa
- Izod Impact, Notched (ISO): 40.0 kJ/m² @Temperature -30.0 °C
$ 2272/MT
- Density: 1.46 g/cc
- Filler Content: 40 %
- Moisture Absorption at Equilibrium: 1.8 %
- Water Absorption at Saturation: 5.5 %
- Linear Mold Shrinkage: 0.0020 cm/cm
$ 1984/MT
- Density: 1.30 g/cc
- Filler Content: 25 %
- Moisture Absorption at Equilibrium: 1.9 %
- Water Absorption at Saturation: 6.0 %
- Linear Mold Shrinkage: 0.010 cm/cm
$ 1531/MT
- Density: 1.33 g/cc
- Filler Content: 20 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 7.0 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1628/MT
- Density: 1.29 g/cc
- Filler Content: 20 %
- Moisture Absorption at Equilibrium: 2.1 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 1849/MT
- Density: 1.52 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength at Break: 50.0 MPa
$ 1594/MT
- Density: 1.61 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 125 MPa
$ 2286/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1535/MT
- Density: 1.13 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 3.0 %
- Water Absorption at Saturation: 10 %
- Linear Mold Shrinkage: 0.012 cm/cm
$ 1565/MT
- Density: 1.63 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 250 MPa
$ 2160/MT
- Density: 1.44 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 115 MPa
$ 1520/MT
- Density: 1.52 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength at Break: 60.0 MPa
$ 1785/MT
- Density: 1.53 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 135 MPa
$ 1638/MT
- Density: 1.24 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 75.0 MPa
$ 2141/MT
- Density: 1.31 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 115 MPa
$ 1611/MT
- Density: 1.20 g/cc
- Moisture Absorption: 2.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 90.0 MPa
$ 1514/MT
- Density: 1.10 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 65.0 MPa
$ 1732/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
- Tensile Strength at Break: 135 MPa
$ 1530/MT
- Density: 1.22 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 40.0 MPa
$ 1723/MT
- Density: 1.25 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2339/MT
- Density: 1.21 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 2051/MT
- Density: 1.31 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 1589/MT
- Density: 1.31 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Linear Mold Shrinkage: 0.016 cm/cm
$ 1973/MT
- Density: 1.73 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 19.0 GPa
$ 1750/MT
- Density: 1.53 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 6.50 GPa
$ 1539/MT
- Density: 1.23 g/cc
- Filler Content: 15 %
- Moisture Absorption at Equilibrium: 2.3 %
- Water Absorption at Saturation: 7.0 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 1901/MT
- Density: 1.68 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 0.10 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1461/MT
- Density: 1.70 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 0.10 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 1608/MT
- Density: 1.75 g/cc
- Moisture Absorption: 1.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 275 MPa
$ 1703/MT
- Density: 1.68 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 16.0 GPa
$ 1734/MT
- Density: 1.45 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 70.0 MPa
$ 1872/MT
- Density: 1.23 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 65.0 MPa
$ 1639/MT
- Density: 1.41 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 200 MPa
$ 1786/MT
- Density: 1.20 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength at Break: 115 MPa
$ 1640/MT
- Density: 1.51 g/cc
- Moisture Absorption: 1.60 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 200 MPa
$ 2363/MT
- Density: 1.04 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.3 %
- Water Absorption at Saturation: 8.0 %
- Linear Mold Shrinkage: 0.015 cm/cm
$ 2421/MT
- Density: 1.23 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 65.0 MPa
$ 1807/MT
- Density: 1.65 g/cc
- Filler Content: 45 %
- Moisture Absorption at Equilibrium: 0.10 %
- Water Absorption at Saturation: 0.27 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2171/MT
- Density: 1.23 g/cc
- Moisture Absorption: 2.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 125 MPa
$ 2298/MT
- Density: 1.47 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1624/MT
- Density: 1.35 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.2 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage: 0.012 cm/cm
$ 1464/MT
- Density: 1.54 g/cc
- Filler Content: 15 %
- Moisture Absorption at Equilibrium: 0.13 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 cm/cm
$ 1453/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 105 MPa
$ 1800/MT
- Density: 1.13 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 2.25 GPa
- Izod Impact, Notched (ISO): 30.0 kJ/m² @Temperature -30.0 °C
$ 1600/MT
- Density: 1.52 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Tensile Strength at Break: 230 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 20.0 GPa
$ 1894/MT
- Density: 1.27 g/cc
- Moisture Absorption: 1.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 225 MPa
$ 2482/MT
- Density: 1.50 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 0.13 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 1858/MT
- Density: 1.04 g/cc
- Moisture Absorption: 2.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 40.0 MPa
$ 1546/MT
- Density: 1.69 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1572/MT
- Density: 1.32 g/cc
- Filler Content: 25 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 6.2 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2142/MT
- Density: 1.48 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1520/MT
- Density: 1.09 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.2 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage: 0.015 cm/cm
$ 2174/MT
- Density: 1.33 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1651/MT
- Density: 1.15 g/cc
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 2.25 GPa
- Izod Impact, Notched (ISO): 30.0 kJ/m² @Temperature -30.0 °C
$ 2423/MT
- Density: 1.53 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 100 MPa
$ 1809/MT
- Density: 1.49 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 10.0 GPa
$ 2280/MT
- Density: 1.15 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 80.0 MPa
$ 1563/MT
- Density: 1.35 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 2.1 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2436/MT
- Density: 1.09 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 60.0 MPa
$ 1545/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 175 MPa
$ 1881/MT
- Density: 1.20 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 2570/MT
- Density: 1.30 g/cc
- Filler Content: 30 %
- Moisture Absorption at Equilibrium: 1.5 %
- Water Absorption at Saturation: 5.0 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 1912/MT
- Density: 1.31 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 1540/MT
- Density: 1.19 g/cc
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 5.00 GPa
- Izod Impact, Notched (ISO): 5.50 kJ/m² @Temperature 23.0 °C
$ 1584/MT
- Density: 1.47 g/cc
- Filler Content: 20 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.40 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 2525/MT
- Density: 1.09 g/cc
- Moisture Absorption: 2.30 % @Temperature 23.0 °C
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: >= 200 %
- Tensile Modulus: 0.250 GPa
$ 2217/MT
- Density: 1.58 g/cc
- Moisture Absorption: 0.200 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 150 MPa
$ 1509/MT
- Density: 1.09 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.2 %
- Water Absorption at Saturation: 8.0 %
- Linear Mold Shrinkage: 0.014 cm/cm
$ 1984/MT
- Density: 1.61 g/cc
- Moisture Absorption: 0.100 % @Temperature 23.0 °C
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 14.0 GPa
$ 2598/MT
- Density: 1.08 g/cc
- Filler Content: 0.00 %
- Moisture Absorption at Equilibrium: 2.5 %
- Water Absorption at Saturation: 8.5 %
- Linear Mold Shrinkage: 0.013 cm/cm
Delivery Thermoplastic Eurotec
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
trinidad shipyard. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.