$ 1624/MT
- Density: 0.925 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- ESCR 10% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 10.5 MPa @Thickness 3.17 mm
$ 1478/MT
- Density: 0.938 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- ESCR 10% Igepal®: 110 hour @Temperature 50.0 °C
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 20.6 MPa @Thickness 3.17 mm
$ 2032/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0150 - 0.0250 g/cc
$ 1521/MT
- Density: 0.922 g/cc
- Apparent Bulk Density: 0.580 g/cc
- Melt Flow: 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength, Ultimate: 12.4 MPa
$ 1918/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 23.0 MPa
$ 1498/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0100 - 0.0150 g/cc
$ 1663/MT
- Density: 0.935 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 220 hour
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.3 MPa
$ 2307/MT
- Density: 0.931 g/cc
- Melt Flow: 72 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength, Yield: 14.0 MPa
- Tensile Strength, Yield: 17.0 MPa
$ 2297/MT
- Tensile Strength at Break: 20.0 MPa
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Break: 1250 %
- Elongation at Yield: 8.0 %
- Flexural Modulus, 1% Secant: 1300 MPa
$ 1731/MT
- Density: 0.938 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.0 MPa
- Film Tensile Strength at Yield, TD: 16.0 MPa
- Film Elongation at Break, MD: 800 %
$ 1841/MT
- Density: >= 0.0192 g/cc
- Mean Unexpanded Bead Size (mm): 0.85
- Targeted Pentane Content (wt%): 3.8
$ 1519/MT
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0216 g/cc
- Bead Size: 0.85 mm
- Pentane: 5.1 wt%
$ 1829/MT
- Density: 0.950 g/cc
- Oxygen Transmission Rate: 1920 cc/m²/day
- Thickness: 38.0 microns
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 67
$ 1476/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0250 g/cc
- Density: 0.0250 - 0.100 g/cc
- Bead Size: 0.300 - 0.700 mm
- Bead Size: 0.400 - 0.700 mm
$ 1967/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1549/MT
- Density: 0.955 g/cc
- ESCR 100% Igepal®: >= 500 hour
- High Load Melt Index: 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 830 %
$ 2340/MT
- Density: 0.957 g/cc
- Environmental Stress Crack Resistance: 100 hour
- Melt Flow: 0.41 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 31.0 MPa
$ 1717/MT
- Density: 0.920 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1589/MT
- Density: >= 0.0120 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Mean Unexpanded Bead Size (mm): 0.85
- Targeted Pentane Content (wt%): 6.5
$ 1590/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 30.0 MPa
- Elongation at Break: 12 %
$ 2579/MT
- Specific Gravity: 1.18 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength: 64.0 MPa
$ 1493/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 26.0 MPa
- Tensile Strength, Yield: 28.0 MPa
$ 1617/MT
- Density: 0.924 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Vicat Softening Point: 94.0 °C
$ 1639/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0192 g/cc
- Density: >= 0.0240 g/cc
- Bead Size: 0.65 mm
- Pentane: 4.3 wt%
$ 1472/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0200 g/cc
- Bead Size: 0.5 mm
- Pentane: 5.4 wt%
$ 2239/MT
- Density: 0.912 g/cc
- Thickness: 51.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 7.38 MPa
- Film Tensile Strength at Yield, TD: 7.38 MPa
$ 2503/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1520/MT
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0192 g/cc
- Bead Size: 0.85 mm
- Pentane: 4.4 wt%
$ 1678/MT
- Bulk Density: 0.720 g/cc
- Density: 0.924 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 9.00 MPa
$ 1955/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0300 g/cc
- Density: 0.0300 - 0.100 g/cc
- Bead Size: 0.600 - 1.00 mm
- Bead Size: 0.700 - 1.00 mm
$ 2542/MT
- Density: 0.938 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.0 MPa
- Film Tensile Strength at Yield, TD: 16.0 MPa
- Film Elongation at Break, MD: 800 %
$ 1514/MT
- Density: >= 0.0128 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0184 g/cc
- Mean Unexpanded Bead Size (mm): 0.85
- Targeted Pentane Content (wt%): 5.5
$ 1779/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0180 - 0.0400 g/cc
$ 1692/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0180 - 0.0400 g/cc
$ 2525/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1475/MT
- Density: 0.954 g/cc
- ESCR 100% Igepal®: <= 10 hour
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 22.0 MPa
$ 1762/MT
- Density: 0.962 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 69
- Film Tensile Strength at Yield, MD: 27.0 MPa
$ 1857/MT
- Density: 0.926 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.0 MPa
- Film Tensile Strength at Yield, TD: 14.0 MPa
$ 1803/MT
- Density: 0.921 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 8.20 MPa
- Tensile Strength, Yield: 9.40 MPa
$ 1567/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0350 g/cc
- Density: 0.0350 - 0.100 g/cc
- Bead Size: 0.300 - 0.700 mm
- Bead Size: 0.400 - 0.700 mm
$ 2078/MT
- Density: >= 0.0120 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Bead Size: 1.4 mm
- Pentane: 6.8 wt%
$ 1480/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: 48 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 900 %
$ 2185/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0192 g/cc
- Mean Unexpanded Bead Size (mm): 0.5
- Targeted Pentane Content (wt%): 6.2
$ 1492/MT
- Density: 0.919 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 34.5 MPa
- Film Tensile Strength at Yield, MD: 10.0 MPa
$ 1491/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 820 %
$ 2064/MT
- Density: 0.951 g/cc
- Melt Flow: 32 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 30.5 cm
- Hardness, Shore D: 62
- Tensile Strength, Yield: 23.0 MPa
$ 1558/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1446/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1627/MT
- Density: 0.960 g/cc
- Water Vapor Transmission: 2.79 g/m²/day
- Oxygen Transmission Rate: 1628 cc/m²/day
- Thickness: 38.0 microns
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1499/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1788/MT
- Density: 0.921 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1495/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1971/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0192 g/cc
- Density: >= 0.0224 g/cc
- Mean Unexpanded Bead Size (mm): 0.85
- Targeted Pentane Content (wt%): 4.1
$ 1477/MT
- Specific Gravity: 1.28 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0015 - 0.0035 cm/cm
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength: 90.0 MPa
$ 1557/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0220 - 0.0500 g/cc
$ 2595/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.00 MPa
- Film Tensile Strength at Yield, TD: 8.00 MPa
- Film Elongation at Break, MD: 550 %
$ 1823/MT
- Density: 0.922 g/cc
- Water Vapor Transmission: 17.0 g/m²/day
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 5.10 cm
- Drawdown: 8.10 m/s
$ 1912/MT
- Density: 0.918 g/cc
- Thickness: 38.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 8.96 MPa
$ 1688/MT
- Density: 0.935 g/cc
- Density: 0.946 g/cc
- Water Absorption: 0.010 %
- Environmental Stress Crack Resistance: >= 1000 hour
- Oxidative Induction Time (OIT): 10 min
$ 1716/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Thickness: 12.7 - 76.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
$ 2107/MT
- Density: 0.946 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Oxidative Induction Time (OIT): 10 min
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 1660/MT
- Density: 0.924 g/cc
- Thickness: >= 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.2 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1819/MT
- Density: 0.947 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.34 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 23.0 MPa
$ 1580/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0180 - 0.0400 g/cc
$ 2023/MT
- Density: 0.921 g/cc
- Thickness: 25.0 microns
- Thickness: 25.0 - 150 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
$ 1855/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 43.0 MPa
- Elongation at Break: 8.0 %
$ 1469/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 43.0 MPa
- Elongation at Break: 8.0 %
$ 1562/MT
- Density: 0.918 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1799/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.00900 - 0.0150 g/cc
$ 1535/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0200 g/cc
- Density: 0.0200 - 0.100 g/cc
- Bead Size: 1.00 - 1.50 mm
- Bead Size: 0.900 - 1.60 mm
$ 2371/MT
- Density: 0.921 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.2 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1562/MT
- Density: 0.9535 g/cc
- ESCR 10% Igepal®: >= 75 hour @Temperature 50.0 °C
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 27.0 MPa
$ 1840/MT
- Density: 0.926 g/cc
- Environmental Stress Crack Resistance: 1.0 hour
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: 190 %
$ 2569/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0192 g/cc
- Bead Size: 0.85 mm
- Pentane: 5.9 wt%
$ 1700/MT
- Density: 0.935 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- ESCR 10% Igepal®: 220 hour @Temperature 50.0 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 17.3 MPa @Thickness 3.17 mm
$ 1613/MT
- Bulk Density: 0.610 g/cc
- Density: 0.958 g/cc
- ESCR 100% Igepal®: 20 hour
- Melt Flow: 0.95 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 67
$ 1545/MT
- Density: >= 0.0120 g/cc
- Density: >= 0.0136 g/cc
- Density: >= 0.0144 g/cc
- Mean Unexpanded Bead Size (mm): 1.4
- Targeted Pentane Content (wt%): 6.3
$ 2016/MT
- Density: 0.930 g/cc
- Melt Flow: 85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength at Break: 9.20 MPa
- Tensile Strength, Yield: 15.2 MPa
$ 1722/MT
- Density: 1.22 g/cc
- Water Absorption: 0.11 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 98.0 MPa
$ 1498/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
- Film Elongation at Break, MD: 690 %
$ 1666/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0200 g/cc
- Density: >= 0.0240 g/cc
- Mean Unexpanded Bead Size (mm): 0.5
- Targeted Pentane Content (wt%): 4.6
$ 1707/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0150 - 0.0300 g/cc
$ 1902/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: >= 2500 hour
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 58
- Tensile Strength, Yield: 10.0 MPa
$ 2438/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.00900 - 0.0150 g/cc
$ 2199/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0200 g/cc
- Bead Size: 0.85 mm
- Pentane: 5.1 wt%
$ 1867/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 2281/MT
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0192 g/cc
- Mean Unexpanded Bead Size (mm): 0.85
- Targeted Pentane Content (wt%): 4.5
$ 1577/MT
- Density: 0.918 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
- Film Elongation at Break, MD: 500 %
$ 1487/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0200 g/cc
- Bead Size: 0.5 mm
- Pentane: 4.6 wt%
$ 1746/MT
- Density: 0.917 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 550 %
$ 1800/MT
- Bulk Density: 0.609 - 0.641 g/cc
- Bead Size: 0.305 - 0.508 mm
- Flexural Strength: 0.827 MPa @Strain 5.00 %
- Flexural Strength: 3.17 MPa @Strain 5.00 %
- Flexural Modulus: 0.0276 GPa
$ 1708/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1789/MT
- Density: 0.935 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.5 MPa @Thickness 1.91 mm
- Elongation at Yield: 12 % @Thickness 1.91 mm
$ 1835/MT
- Density: 0.939 g/cc
- ESCR 10% Igepal®: >= 50 hour
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
- Tensile Strength, Ultimate: 27.1 MPa
$ 1499/MT
- Density: 0.961 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength, Yield: 29.0 MPa
$ 2346/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.03 MPa
- Film Tensile Strength at Yield, TD: 9.03 MPa
$ 1729/MT
- Density: 1.08 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell L: 108
$ 2054/MT
- Density: 1.08 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell L: 108
$ 1659/MT
- Density: 1.08 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell L: 108
$ 1494/MT
- Density: 1.08 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell L: 108
$ 1461/MT
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0176 g/cc
- Bead Size: 1.4 mm
- Pentane: 6.3 wt%
$ 2008/MT
- Density: 0.938 g/cc
- Thickness: 20.0 microns
- Melt Flow: 4.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
$ 2446/MT
- Density: 0.936 g/cc
- Moisture Vapor Transmission: 0.230 cc-mm/m²-24hr-atm
- Water Vapor Transmission: 5.20 g/m²/day
- Water Vapor Transmission: 9.00 g/m²/day
- Oxygen Transmission: 78.0 cc-mm/m²-24hr-atm
$ 2441/MT
- Density: 0.962 g/cc
- Environmental Stress Crack Resistance: 25 hour
- Melt Flow: 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 29.0 MPa
$ 1696/MT
- Density: 0.962 g/cc
- Environmental Stress Crack Resistance: 25 hour
- Melt Flow: 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 29.0 MPa
$ 1833/MT
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength, Yield: 22.3 MPa
- Elongation at Break: 650 %
- Elongation at Yield: 9.0 %
- Flexural Modulus, 1% Secant: 960 MPa
$ 1631/MT
- Density: 0.938 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- ESCR 10% Igepal®: 110 hour @Temperature 50.0 °C
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 20.6 MPa @Thickness 3.17 mm
$ 1651/MT
- Density: 0.947 g/cc
- Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Break: 1000 %
$ 1931/MT
- Density: 0.954 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 6.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
- Tensile Strength, Yield: 28.0 MPa
$ 2000/MT
- Density: 1.21 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 81.0 MPa
$ 1509/MT
- Density: 0.934 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.0 MPa
- Film Tensile Strength at Yield, TD: 17.0 MPa
$ 1608/MT
- Density: 0.918 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
- Film Elongation at Break, MD: 500 %
$ 2519/MT
- Density: 0.919 g/cc
- Environmental Stress Crack Resistance: 100 hour
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength, Yield: 8.90 MPa
$ 1893/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1601/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1634/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1870/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0170 - 0.0300 g/cc
$ 1480/MT
- Density: 0.959 g/cc
- ESCR 100% Igepal®: 45 hour
- High Load Melt Index: 11 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 30.0 MPa
$ 1930/MT
- Density: 0.941 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.2 MPa
- Elongation at Yield: 12 %
$ 2164/MT
- Density: 0.926 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.0 MPa
- Film Tensile Strength at Yield, TD: 14.0 MPa
$ 1589/MT
- Density: 0.921 g/cc
- Thickness: 75.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2220/MT
- Density: 0.924 g/cc
- Environmental Stress Crack Resistance: 150 hour
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: 300 %
$ 1733/MT
- Density: 0.966 g/cc
- Moisture Vapor Transmission: 0.00418 cc-mm/m²-24hr-atm @Temperature 38.0 °C
- Oxygen Transmission: 1.767 cc-mm/m²-24hr-atm
- Thickness: 38.0 microns
- Thickness: 25.0 - 75.0 microns
$ 1454/MT
- Density: 0.921 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 8.20 MPa
- Tensile Strength, Yield: 9.40 MPa
$ 1499/MT
- Density: 0.946 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.0 MPa
$ 1493/MT
- Density: 0.960 g/cc
- Water Vapor Transmission: 4.20 g/m²/day
- Oxygen Transmission Rate: 1705 cc/m²/day
- Thickness: 38.0 microns
- Melt Flow: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1930/MT
- Density: 0.918 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.20 MPa
- Film Tensile Strength at Yield, TD: 9.50 MPa
$ 1934/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 830 %
$ 1468/MT
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0200 g/cc
- Bead Size: 0.5 mm
- Pentane: 5.4 wt%
$ 1646/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0100 - 0.0200 g/cc
$ 1774/MT
- Density: 0.918 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1464/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0200 - 0.0350 g/cc
$ 1701/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1775/MT
- Density: >= 0.0224 g/cc
- Mean Unexpanded Bead Size (mm): 0.5
- Targeted Pentane Content (wt%): 3.6
$ 1667/MT
- Density: 0.919 g/cc
- Thickness: >= 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1476/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 820 %
$ 1718/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 830 %
$ 1460/MT
- Density: 0.947 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 830 %
$ 1649/MT
- Density: 1.15 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 67.0 MPa
$ 1522/MT
- Density: 0.949 g/cc
- Water Absorption: 0.010 %
- Environmental Stress Crack Resistance: >= 1000 hour
- Oxidative Induction Time (OIT): 10 min
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2099/MT
- Density: 0.921 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 2068/MT
- Density: 0.924 g/cc
- Environmental Stress Crack Resistance: 150 hour
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: 300 %
$ 1499/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0170 - 0.0300 g/cc
$ 2020/MT
- Density: 0.958 g/cc
- Water Vapor Transmission: 2.64 g/m²/day
- Oxygen Transmission Rate: 1488 cc/m²/day
- Thickness: 38.0 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1937/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0200 - 0.0350 g/cc
$ 1474/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0230 - 0.0600 g/cc
$ 2020/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0190 - 0.0400 g/cc
$ 1519/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0200 g/cc
- Density: 0.0200 - 0.100 g/cc
- Bead Size: 0.600 - 1.00 mm
- Bead Size: 0.700 - 1.00 mm
$ 1475/MT
- Density: 0.921 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1685/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 32.0 MPa
- Elongation at Break: 27 %
$ 2038/MT
- Density: 0.917 g/cc
- Water Vapor Transmission: 18.0 g/m²/day
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 5.50 cm
- Drawdown: >= 9.10 m/s
$ 2180/MT
- Density: >= 0.0128 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0184 g/cc
- Bead Size: 0.85 mm
- Pentane: 5.3 wt%
$ 1756/MT
- Specific Gravity: 1.16 g/cc
- Filler Content: 12 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength: 56.0 MPa
$ 1809/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 2.2 %
$ 1719/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1644/MT
- Density: 0.945 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 60
- Tensile Strength, Yield: 22.5 MPa
$ 2017/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 49.7 MPa
- Elongation at Break: 1.8 %
$ 2576/MT
- Density: 0.936 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 60
- Tensile Strength at Break: 30.0 MPa
$ 1890/MT
- Density: 0.916 g/cc
- Thickness: 25.0 microns
- Thickness: 12.7 - 127 microns
- Melt Flow: 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.50 MPa
$ 1627/MT
- Specific Gravity: 1.16 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength: 55.0 MPa
$ 2070/MT
- Density: 0.926 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 11.2 MPa
$ 2020/MT
- Density: 0.939 g/cc
- Environmental Stress Crack Resistance: 40 - 50 hour
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 1551/MT
- Density: 0.935 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.5 MPa @Thickness 1.91 mm
- Elongation at Yield: 12 % @Thickness 1.91 mm
$ 1567/MT
- Density: 0.0168 g/cc
- Density: 0.0210 g/cc
- Density: 0.0216 g/cc
- Particle Size: 800 - 1700 µm
- Tensile Strength, Ultimate: 0.331 MPa
$ 1771/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0250 g/cc
- Density: 0.0250 - 0.100 g/cc
- Bead Size: 0.300 - 0.700 mm
- Bead Size: 0.200 - 0.800 mm
$ 1664/MT
- Density: 0.944 g/cc
- ESCR 10% Igepal®: 200 hour
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.4 MPa
- Tensile Strength, Yield: 23.5 MPa
$ 1575/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0250 g/cc
- Density: 0.0250 - 0.100 g/cc
- Bead Size: 0.300 - 0.700 mm
- Bead Size: 0.400 - 0.700 mm
$ 2090/MT
- Density: >= 0.0120 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0144 g/cc
- Bead Size: 0.85 mm
- Pentane: 6.2 wt%
$ 2199/MT
- Density: 0.919 g/cc
- Thickness: 20.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 2428/MT
- Density: 0.924 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 54
- Tensile Strength at Break: 11.0 MPa
- Tensile Strength, Yield: 12.0 MPa
$ 1495/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1855/MT
- Specific Gravity: 1.16 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength: 64.0 MPa
$ 1713/MT
- Density: >= 0.0192 g/cc
- Mean Unexpanded Bead Size (mm): 1.4
- Targeted Pentane Content (wt%): 4.1
$ 1532/MT
- Density: 0.941 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.2 MPa
- Elongation at Yield: 12 %
$ 1691/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0300 g/cc
- Density: 0.0300 - 0.100 g/cc
- Bead Size: 1.00 - 1.50 mm
- Bead Size: 0.900 - 1.60 mm
$ 1914/MT
- Density: 0.919 g/cc
- Thickness: >= 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1644/MT
- Density: 0.962 g/cc
- Moisture Vapor Transmission: 0.0300 cc-mm/m²-24hr-atm
- Water Vapor Transmission: 0.800 g/m²/day
- Water Vapor Transmission: 3.41 g/m²/day
- Oxygen Transmission: 41.0 cc-mm/m²-24hr-atm
$ 1592/MT
- Specific Gravity: 1.18 g/cc
- Filler Content: 16 %
- Linear Mold Shrinkage: 0.0025 - 0.0045 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 74.0 MPa
$ 1466/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 36.0 MPa
- Elongation at Break: 16 %
$ 1557/MT
- Density: 0.920 g/cc
- Thickness: 20.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.89 MPa
- Film Tensile Strength at Yield, TD: 8.41 MPa
$ 1628/MT
- Density: 0.922 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.2 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 2159/MT
- Density: 0.936 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.2 MPa
- Film Tensile Strength at Yield, TD: 15.1 MPa
$ 1463/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0150 - 0.0200 g/cc
$ 1523/MT
- Density: 0.942 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Ultimate: 24.0 MPa
$ 1622/MT
- Density: >= 0.0128 g/cc
- Density: >= 0.0144 g/cc
- Density: >= 0.0184 g/cc
- Bead Size: 0.85 mm
- Pentane: 6.1 wt%
$ 1724/MT
- Density: 0.925 g/cc
- Thickness: 20.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.2 MPa
- Film Tensile Strength at Yield, TD: 9.80 MPa
$ 1521/MT
- Bulk Density: 0.608 - 0.640 g/cc
- Density: >= 0.0481 g/cc
- Density: >= 0.0481 g/cc
- Flexural Yield Strength: 0.483 MPa
- Flexural Yield Strength: 3.17 MPa
$ 1750/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0170 - 0.0300 g/cc
$ 1729/MT
- Density: 0.920 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1460/MT
- Bulk Density: 0.620 g/cc
- Density: >= 0.0200 g/cc
- Density: 0.0200 - 0.100 g/cc
- Bead Size: 1.00 - 1.50 mm
- Bead Size: 0.900 - 1.60 mm
$ 2296/MT
- Density: 1.19 g/cc
- Water Absorption: 0.12 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 82.0 MPa
$ 1455/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 44.7 MPa
- Elongation at Break: 1.3 %
$ 2144/MT
- Density: 0.918 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
- Film Elongation at Break, MD: 600 %
$ 1525/MT
- Density: 0.960 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 4.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 29.0 MPa
$ 2277/MT
- Density: 0.958 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Break: 1600 %
$ 1449/MT
- Bulk Density: 0.580 g/cc
- Density: 0.951 g/cc
- Melt Flow: 51 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 36.0 cm
- Hardness, Shore D: 62
$ 2561/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 23.0 MPa
$ 1717/MT
- Density: 0.917 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 550 %
$ 2237/MT
- Density: 0.925 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 52 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 36.0 cm
- Hardness, Shore D: 52
$ 1564/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.00900 - 0.0180 g/cc
$ 1537/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1913/MT
- Density: 0.0272 g/cc
- Density: 0.0288 g/cc
- Density: 0.0320 g/cc
- Volatiles: 8.5 %
- Particle Size: 800 - 1700 µm
$ 1631/MT
- Density: 0.917 g/cc
- Thickness: 20.0 microns
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 7.52 MPa
- Film Tensile Strength at Yield, TD: 7.03 MPa
$ 1728/MT
- Density: 0.918 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1799/MT
- Density: 1.20 g/cc
- Water Absorption: 0.19 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 77.0 MPa
$ 1958/MT
- Bulk Density: 0.580 - 0.640 g/cc
- Bulk Density: 0.610 g/cc
- Density: 0.0220 - 0.0350 g/cc
$ 2506/MT
- Density: 0.942 g/cc
- Water Vapor Transmission: 5.40 g/m²/day
- Oxygen Transmission: 65.0 cc-mm/m²-24hr-atm
- Oxygen Transmission Rate: 2400 cc/m²/day
- Thickness: 38.0 microns
$ 1633/MT
- Density: 0.932 g/cc
- Melt Flow: 150 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 50.8 cm
- Hardness, Shore D: 60
- Tensile Strength at Break: 10.0 MPa
$ 1756/MT
- Density: 0.921 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.80 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1895/MT
- Density: 0.961 g/cc
- Environmental Stress Crack Resistance: <= 10 hour
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 29.0 MPa
Delivery Thermoplastic NOVA Chemicals
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale russia. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.