$ 1579/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1599/MT
- Bulk Density: 0.650 g/cc
- Density: 1.05 g/cc
- Water Absorption: <= 0.10 %
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength at Break: 30.0 MPa
$ 2159/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0220 - 0.0800 g/cc
- Apparent Bulk Density: 0.0210 g/cc
- Apparent Bulk Density: 0.0250 g/cc
- Particle Size: 400 - 750 µm
$ 1445/MT
- Specific Gravity: 0.920 g/cc
- Brookfield Viscosity: 0.060 cP
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 20
- Tensile Strength at Break: 4.00 MPa
$ 1477/MT
- Specific Gravity: 0.939 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 15.0 MPa
$ 1661/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 25.0 - 80.0 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2181/MT
- Specific Gravity: 0.919 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1494/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 46
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 900 %
$ 1605/MT
- Specific Gravity: 0.917 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1672/MT
- Specific Gravity: 0.916 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 2025/MT
- Specific Gravity: 0.917 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1907/MT
- Specific Gravity: 0.954 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 27.0 MPa
$ 2058/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 25.0 - 80.0 microns
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1531/MT
- Specific Gravity: 0.940 g/cc
- Brookfield Viscosity: 0.030 cP
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 22.0 MPa
$ 1989/MT
- Specific Gravity: 0.940 g/cc
- Brookfield Viscosity: 0.060 cP
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 6.00 MPa
$ 1996/MT
- Specific Gravity: 0.924 g/cc
- Vinyl Acetate Content: 5.0 %
- Thickness: 50.0 - 200 microns
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 95
$ 1546/MT
- Bulk Density: 0.650 g/cc
- Density: 1.04 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1988/MT
- Specific Gravity: 0.921 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength, Yield: 9.00 MPa
$ 2381/MT
- Specific Gravity: 0.933 g/cc
- Thickness: 18.0 - 50.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
$ 2057/MT
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 68
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 600 %
- 300% Modulus: 0.00350 GPa
$ 1503/MT
- Specific Gravity: 0.929 g/cc
- Vinyl Acetate Content: 9.0 %
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 95
- Hardness, Shore D: 40
$ 1715/MT
- Specific Gravity: 0.920 g/cc
- Brookfield Viscosity: 0.090 cP
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 44
- Tensile Strength at Break: 20.0 MPa
$ 1904/MT
- Specific Gravity: 0.953 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 23 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 500 %
$ 1458/MT
- Specific Gravity: 0.925 g/cc
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 47
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength, Yield: 10.0 MPa
$ 2124/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1721/MT
- Specific Gravity: 0.922 g/cc
- Thickness: 50.0 - 250 microns
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1532/MT
- Specific Gravity: 0.923 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 13.0 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1464/MT
- Specific Gravity: 0.941 g/cc
- Vinyl Acetate Content: 19 %
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89
- Hardness, Shore D: 33
$ 1529/MT
- Specific Gravity: 0.924 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength, Yield: 12.0 MPa
- Flexural Modulus: 0.200 GPa
$ 1481/MT
- Specific Gravity: 0.952 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 500 %
$ 1565/MT
- Specific Gravity: 1.05 g/cc
- Bulk Density: 0.650 g/cc
- Water Absorption: <= 0.10 % @Time 86400 sec
- Melt Flow: 2.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength at Break: 25.0 MPa
$ 1549/MT
- Specific Gravity: 0.938 g/cc
- Vinyl Acetate Content: 17 %
- Thickness: 50.0 - 200 microns
- Melt Flow: 0.47 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
$ 1571/MT
- Bulk Density: 0.650 g/cc
- Density: 1.05 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1570/MT
- Specific Gravity: 0.887 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: >= 800 %
- Film Tensile Strength at Break, MD: 13.0 MPa
- Melting Point: 110 °C
$ 1613/MT
- Specific Gravity: 0.920 g/cc
- Brookfield Viscosity: 0.10 cP
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 12.0 MPa
$ 2470/MT
- Bulk Density: 0.700 g/cc
- Density: 1.13 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1524/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
$ 1520/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
$ 1738/MT
- Specific Gravity: 0.921 g/cc
- Thickness: 25.0 - 80.0 microns
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1532/MT
- Specific Gravity: 0.925 g/cc
- Vinyl Acetate Content: 7.0 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 95
- Hardness, Shore D: 43
$ 1456/MT
- Specific Gravity: 0.918 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46
- Tensile Strength, Yield: 10.0 MPa
- Flexural Modulus: 0.120 GPa
$ 1665/MT
- Specific Gravity: 0.923 g/cc
- Thickness: 30.0 - 100 microns
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1716/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength, Yield: 10.0 MPa
$ 1927/MT
- Specific Gravity: 0.952 g/cc
- Vinyl Acetate Content: 28 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 31
$ 1557/MT
- Specific Gravity: 0.950 g/cc
- Brookfield Viscosity: 0.040 cP
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 26.0 MPa
$ 1867/MT
- Specific Gravity: 0.922 g/cc
- Thickness: 50.0 - 250 microns
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2370/MT
- Specific Gravity: 0.917 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength, Yield: 9.00 MPa
- Flexural Modulus: 0.110 GPa
$ 1722/MT
- Specific Gravity: 0.919 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1742/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 45 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 66
$ 1462/MT
- Specific Gravity: 0.917 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength, Yield: 9.00 MPa
- Flexural Modulus: 0.110 GPa
$ 1511/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
- Tensile Strength at Break: 27.0 MPa
$ 1679/MT
- Bulk Density: 0.650 g/cc
- Density: 1.04 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1555/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1463/MT
- Specific Gravity: 0.941 g/cc
- Vinyl Acetate Content: 19 %
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89
$ 1472/MT
- Specific Gravity: 0.926 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1607/MT
- Specific Gravity: 0.936 g/cc
- Environmental Stress Crack Resistance: >= 350 hour
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 54
- Tensile Strength at Break: 21.0 MPa
$ 1486/MT
- Specific Gravity: 0.956 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 20.0 MPa
$ 1636/MT
- Density: 0.0160 - 0.0300 g/cc
$ 2043/MT
- Specific Gravity: 0.924 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength, Yield: 12.0 MPa
- Flexural Modulus: 0.180 GPa
$ 1855/MT
- Specific Gravity: 0.951 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 20.0 MPa
$ 1518/MT
- Specific Gravity: 0.940 g/cc
- Brookfield Viscosity: 0.75 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 18.0 MPa
$ 1492/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 18.0 - 50.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1679/MT
- Bulk Density: 0.650 g/cc
- Density: 1.04 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2402/MT
- Specific Gravity: 0.919 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1635/MT
- Bulk Density: 0.650 g/cc
- Density: 1.05 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1490/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0120 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0180 g/cc
- Density: 0.0120 - 0.0250 g/cc
- Particle Size: 900 - 1600 µm
$ 1826/MT
- Melt Temperature: 200 - 230 °C
$ 2310/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1571/MT
- Specific Gravity: 0.923 g/cc
- Vinyl Acetate Content: 4.5 %
- Thickness: 30.0 - 150 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 96
$ 1534/MT
- Specific Gravity: 0.940 g/cc
- Brookfield Viscosity: 0.40 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 20.0 MPa
$ 1861/MT
- Specific Gravity: 0.921 g/cc
- Thickness: 40.0 - 150 microns
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 2242/MT
- Bulk Density: 0.650 g/cc
- Density: 1.05 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 27 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1660/MT
- Density: 1.07 g/cc
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Ultimate: 67.0 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 3.55 GPa
$ 1810/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1782/MT
- Specific Gravity: 0.925 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 13.0 MPa
$ 2107/MT
- Specific Gravity: 0.900 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 5.00 MPa
- Film Tensile Strength at Yield, TD: 5.00 MPa
$ 1484/MT
- Specific Gravity: 0.925 g/cc
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 18.0 MPa
- Tensile Strength, Yield: 12.5 MPa
$ 1492/MT
- Specific Gravity: 0.935 g/cc
- Vinyl Acetate Content: 14 %
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 92
$ 1451/MT
- Specific Gravity: 0.917 g/cc
- Melt Flow: 65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength, Yield: 9.00 MPa
- Flexural Modulus: 0.110 GPa
$ 2376/MT
- Specific Gravity: 0.900 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 5.00 MPa
- Film Tensile Strength at Yield, TD: 5.00 MPa
$ 1580/MT
- Specific Gravity: 0.935 g/cc
- Vinyl Acetate Content: 14 %
- Thickness: 50.0 - 200 microns
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 92
$ 1459/MT
- Specific Gravity: 0.955 g/cc
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength, Yield: 27.0 MPa
$ 2171/MT
- Density: 0.0110 - 0.0200 g/cc
$ 1564/MT
- Specific Gravity: 0.934 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.0 MPa
- Film Tensile Strength at Yield, TD: 18.0 MPa
$ 1597/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 950 %
$ 1484/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0120 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0180 g/cc
- Density: 0.0120 - 0.0250 g/cc
- Particle Size: 900 - 1600 µm
$ 1664/MT
- Specific Gravity: 0.919 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46
- Tensile Strength at Break: 11.0 MPa
- Tensile Strength, Yield: 9.00 MPa
$ 1940/MT
- Specific Gravity: 0.921 g/cc
- Thickness: 18.0 - 50.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1992/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1684/MT
- Specific Gravity: 0.951 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 20.0 MPa
$ 1687/MT
- Bulk Density: 0.650 g/cc
- Density: 1.05 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1617/MT
- Specific Gravity: 0.938 g/cc
- Vinyl Acetate Content: 17 %
- Thickness: 50.0 - 200 microns
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
$ 1719/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 69
- Tensile Strength at Break: 17.0 MPa
$ 1633/MT
- Specific Gravity: 0.938 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 4.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 17.0 MPa
- Film Tensile Strength at Yield, TD: 16.0 MPa
$ 1558/MT
- Specific Gravity: 0.919 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength, Yield: 10.0 MPa
- Flexural Modulus: 0.130 GPa
$ 1521/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 69
- Tensile Strength at Break: 17.0 MPa
$ 2048/MT
- Specific Gravity: 0.935 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.0 MPa
- Film Tensile Strength at Yield, TD: 17.0 MPa
$ 1966/MT
- Specific Gravity: 0.939 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 15.0 MPa
$ 1661/MT
- Specific Gravity: 0.935 g/cc
- Vinyl Acetate Content: 14 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 92
- Hardness, Shore D: 40
$ 1552/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1535/MT
- Bulk Density: 0.650 g/cc
- Density: 1.04 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1949/MT
- Specific Gravity: 0.926 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 13.0 MPa
$ 1509/MT
- Specific Gravity: 0.929 g/cc
- Vinyl Acetate Content: 9.0 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
- Hardness, Shore D: 42
$ 1779/MT
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 24.0 MPa
- Elongation at Break: 550 %
- 300% Modulus: 0.00400 GPa
$ 1681/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0120 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0180 g/cc
- Density: 0.0120 - 0.0250 g/cc
- Particle Size: 900 - 1600 µm
$ 1558/MT
- Specific Gravity: 0.929 g/cc
- Vinyl Acetate Content: 9.0 %
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
$ 1934/MT
- Specific Gravity: 0.924 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength, Yield: 12.0 MPa
- Flexural Modulus: 0.200 GPa
$ 1768/MT
- Specific Gravity: 0.922 g/cc
- Thickness: 50.0 - 250 microns
- Melt Flow: 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1533/MT
- Specific Gravity: 0.941 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 20.0 MPa
$ 2245/MT
- Specific Gravity: 0.920 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 2072/MT
- Specific Gravity: 0.911 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 8.00 MPa
$ 1889/MT
- Specific Gravity: 0.917 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1533/MT
- Specific Gravity: 0.955 g/cc
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength, Yield: 27.0 MPa
$ 2197/MT
- Bulk Density: 0.650 g/cc
- Density: 1.05 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1634/MT
- Specific Gravity: 0.940 g/cc
- Brookfield Viscosity: 0.13 cP
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 72
- Tensile Strength at Break: 20.0 MPa
$ 2163/MT
- Specific Gravity: 0.921 g/cc
- Thickness: 40.0 - 150 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1475/MT
- Specific Gravity: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 750 hour
- Melt Flow: 0.40 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 65
$ 1950/MT
- Specific Gravity: 0.933 g/cc
- Thickness: 18.0 - 50.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
$ 1458/MT
- Specific Gravity: 0.920 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1566/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1649/MT
- Brookfield Viscosity: 0.050 cP
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 28.0 MPa
- Elongation at Break: 550 %
- 300% Modulus: 0.00500 GPa
$ 1478/MT
- Specific Gravity: 0.926 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 13.0 MPa
$ 1735/MT
- Specific Gravity: 0.925 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1608/MT
- Density: 0.0180 - 0.0300 g/cc
$ 2088/MT
- Specific Gravity: 0.919 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 2023/MT
- Specific Gravity: 0.916 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1752/MT
- Specific Gravity: 0.935 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.0 MPa
- Film Tensile Strength at Yield, TD: 18.0 MPa
$ 1624/MT
- Specific Gravity: 0.920 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1459/MT
- Specific Gravity: 0.920 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1629/MT
- Specific Gravity: 0.920 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1973/MT
- Specific Gravity: 0.900 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 5.00 MPa
- Film Tensile Strength at Yield, TD: 5.00 MPa
$ 1593/MT
- Specific Gravity: 0.939 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 15.0 MPa
$ 1508/MT
- Specific Gravity: 0.953 g/cc
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 19.0 MPa
$ 1470/MT
- Specific Gravity: 0.953 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 0.80 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 21 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1713/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 25.0 - 80.0 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1606/MT
- Specific Gravity: 0.923 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 13.0 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1644/MT
- Specific Gravity: 0.940 g/cc
- Brookfield Viscosity: 2.0 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 18.0 MPa
$ 1444/MT
- Density: 0.0180 - 0.0350 g/cc
$ 1469/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 69
- Tensile Strength at Break: 17.0 MPa
$ 1839/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 28
- Tensile Strength at Break: 13.0 MPa
- Tensile Strength, Yield: 5.00 MPa
$ 2096/MT
- Specific Gravity: 0.951 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 20.0 MPa
$ 1792/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 21 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 69
- Tensile Strength at Break: 17.0 MPa
$ 2501/MT
- Specific Gravity: 0.917 g/cc
- Melt Flow: 65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength, Yield: 9.00 MPa
- Flexural Modulus: 0.110 GPa
$ 1699/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 2576/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0200 g/cc
- Density: 0.0200 - 0.0350 g/cc
- Particle Size: 600 - 1000 µm
$ 1489/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0160 - 0.0300 g/cc
- Apparent Bulk Density: 0.0150 g/cc
- Apparent Bulk Density: 0.0160 g/cc
- Particle Size: 700 - 1000 µm
$ 2311/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1675/MT
- Specific Gravity: 0.935 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 16.0 MPa
$ 1595/MT
- Specific Gravity: 0.911 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 7.00 MPa
- Film Tensile Strength at Yield, TD: 7.00 MPa
$ 1769/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 2044/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0200 - 0.0800 g/cc
- Apparent Bulk Density: 0.0190 g/cc
- Apparent Bulk Density: 0.0230 g/cc
- Particle Size: 600 - 1100 µm
$ 1806/MT
- Specific Gravity: 0.924 g/cc
- Vinyl Acetate Content: 5.0 %
- Thickness: 50.0 - 200 microns
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 95
$ 2557/MT
- Specific Gravity: 0.929 g/cc
- Vinyl Acetate Content: 9.0 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
- Hardness, Shore D: 42
$ 1590/MT
- Specific Gravity: 0.918 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 45
- Tensile Strength, Yield: 10.0 MPa
- Flexural Modulus: 0.120 GPa
$ 2492/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0100 g/cc
- Density: >= 0.0130 g/cc
- Density: >= 0.0150 g/cc
- Density: 0.0110 - 0.0200 g/cc
- Particle Size: 900 - 1600 µm
$ 1539/MT
- Specific Gravity: 0.941 g/cc
- Vinyl Acetate Content: 19 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89
- Hardness, Shore D: 36
$ 1510/MT
- Specific Gravity: 0.950 g/cc
- Brookfield Viscosity: 2.2 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 29.0 MPa
$ 1584/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1943/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0180 g/cc
- Density: 0.0170 - 0.0350 g/cc
- Particle Size: 600 - 1000 µm
$ 1575/MT
- Bulk Density: 0.589 - 0.630 g/cc
- Density: 0.0120 - 0.0200 g/cc
- Apparent Bulk Density: 0.0120 g/cc
- Apparent Bulk Density: 0.0120 g/cc
- Apparent Bulk Density: 0.0170 g/cc
- Particle Size: 400 - 750 µm
$ 1937/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0110 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0160 g/cc
- Density: 0.0120 - 0.0300 g/cc
- Particle Size: 900 - 1400 µm
$ 1564/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 30.0 - 150 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1961/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 2292/MT
- Brookfield Viscosity: 0.16 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: 600 %
- 300% Modulus: 0.00500 GPa
$ 1663/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0170 g/cc
- Density: 0.0160 - 0.0300 g/cc
- Particle Size: 600 - 1000 µm
$ 1972/MT
- Specific Gravity: 0.921 g/cc
- Thickness: 40.0 - 150 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1834/MT
- Specific Gravity: 0.936 g/cc
- Environmental Stress Crack Resistance: >= 250 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 54
- Tensile Strength at Break: 17.0 MPa
$ 1876/MT
- Specific Gravity: 0.956 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 20.0 MPa
$ 1598/MT
- Specific Gravity: 0.911 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 7.00 MPa
- Film Tensile Strength at Yield, TD: 7.00 MPa
$ 2051/MT
- Specific Gravity: 0.939 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.80 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 20 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 500 %
$ 2124/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 8.00 MPa
$ 1857/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0100 - 0.0150 g/cc
- Apparent Bulk Density: 0.00900 g/cc
- Apparent Bulk Density: 0.0130 g/cc
- Apparent Bulk Density: 0.0150 g/cc
- Particle Size: 1400 - 2200 µm
$ 1841/MT
- Specific Gravity: 0.925 g/cc
- Vinyl Acetate Content: 6.0 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 95
- Hardness, Shore D: 43
$ 2588/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 47
- Tensile Strength, Yield: 11.0 MPa
- Flexural Modulus: 0.130 GPa
$ 1486/MT
- Density: 0.0160 - 0.0300 g/cc
$ 1743/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0120 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0180 g/cc
- Density: 0.0120 - 0.0250 g/cc
- Particle Size: 900 - 1600 µm
$ 1502/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength, Yield: 10.0 MPa
$ 1472/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0100 - 0.0250 g/cc
- Apparent Bulk Density: 0.00900 g/cc
- Apparent Bulk Density: 0.0130 g/cc
- Apparent Bulk Density: 0.0150 g/cc
- Particle Size: 900 - 1600 µm
$ 1852/MT
- Bulk Density: 0.650 g/cc
- Density: 1.04 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2300/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 47
- Tensile Strength, Yield: 11.0 MPa
- Flexural Modulus: 0.130 GPa
$ 1461/MT
- Specific Gravity: 0.930 g/cc
- Brookfield Viscosity: 0.77 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore A: 68
- Tensile Strength at Break: 4.00 MPa
- Elongation at Break: 440 %
$ 1730/MT
- Specific Gravity: 0.918 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46
- Tensile Strength, Yield: 10.0 MPa
- Flexural Modulus: 0.120 GPa
$ 1783/MT
- Specific Gravity: 0.921 g/cc
- Thickness: 40.0 - 150 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1468/MT
- Specific Gravity: 0.911 g/cc
- Thickness: 8.00 - 50.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 7.00 MPa
- Film Tensile Strength at Yield, TD: 7.00 MPa
$ 1801/MT
- Specific Gravity: 0.938 g/cc
- Vinyl Acetate Content: 17 %
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89
- Hardness, Shore D: 36
$ 1945/MT
- Specific Gravity: 0.915 g/cc
- Melt Flow: 200 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 42
- Tensile Strength, Yield: 8.00 MPa
- Flexural Modulus: 0.100 GPa
$ 1521/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1737/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 1767/MT
- Specific Gravity: 0.934 g/cc
- Thickness: 15.0 - 50.0 microns
- Melt Flow: 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.0 MPa
- Film Tensile Strength at Yield, TD: 18.0 MPa
$ 1492/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0170 - 0.0300 g/cc
- Apparent Bulk Density: 0.0160 g/cc
- Apparent Bulk Density: 0.0180 g/cc
- Particle Size: 400 - 750 µm
$ 1908/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 40.0 - 150 microns
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2009/MT
- Specific Gravity: 0.895 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 26
- Tensile Strength at Break: 9.00 MPa
- Tensile Strength, Yield: 4.00 MPa
$ 1825/MT
- Specific Gravity: 0.939 g/cc
- Thickness: 10.0 - 50.0 microns
- Melt Flow: 0.60 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 15 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 550 %
$ 1533/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: 0.0170 - 0.0800 g/cc
- Apparent Bulk Density: 0.0160 g/cc
- Apparent Bulk Density: 0.0180 g/cc
- Apparent Bulk Density: 0.0220 g/cc
- Particle Size: 100 - 200 µm
$ 2079/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength at Break: 45.0 MPa
$ 2287/MT
- Density: 1.07 g/cc
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Ultimate: 66.0 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 3.50 GPa
$ 1835/MT
- Specific Gravity: 0.953 g/cc
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 19.0 MPa
$ 1904/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0120 g/cc
- Density: >= 0.0160 g/cc
- Density: >= 0.0180 g/cc
- Density: 0.0120 - 0.0250 g/cc
- Particle Size: 900 - 1600 µm
$ 1567/MT
- Specific Gravity: 0.928 g/cc
- Thickness: 40.0 - 150 microns
- Melt Flow: 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1844/MT
- Bulk Density: 0.590 - 0.630 g/cc
- Density: >= 0.0100 g/cc
- Density: >= 0.0150 g/cc
- Density: 0.0110 - 0.0200 g/cc
- Density: >= 0.0160 g/cc
- Particle Size: 900 - 1600 µm
$ 1903/MT
- Specific Gravity: 0.921 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46
- Tensile Strength at Break: 11.0 MPa
- Tensile Strength, Yield: 9.00 MPa
$ 1497/MT
- Bulk Density: 0.650 g/cc
- Density: 1.04 g/cc
- Water Absorption: <= 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1505/MT
- Specific Gravity: 0.924 g/cc
- Thickness: 25.0 - 80.0 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1481/MT
- Specific Gravity: 0.922 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength, Yield: 9.00 MPa
Delivery Thermoplastic Polimeri Europa (Former EniChem)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
cruise ships sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.