$ 2139/MT
- Specific Gravity: 1.02 - 1.08 g/cc
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 35.9 MPa
- Flexural Yield Strength: 58.6 MPa
- Flexural Modulus: 2.00 GPa
$ 2441/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 45.5 MPa
- Tensile Modulus: 2.76 GPa
- Flexural Yield Strength: 82.7 MPa
$ 2282/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 9.86 MPa
- Elongation at Break: 410 %
- 100% Modulus: 0.00400 GPa
- Melt Temperature: 143 °C
$ 1822/MT
- Density: 1.07 g/cc
- Hardness, Rockwell R: 80
- Tensile Strength, Ultimate: 27.6 MPa
- Flexural Yield Strength: 45.5 MPa
- Flexural Modulus: 1.70 GPa
$ 2304/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 53.1 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 77.2 MPa
$ 1878/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 40
- Tensile Strength, Yield: 7.10 MPa
- Elongation at Break: 510 %
- 100% Modulus: 0.00283 GPa
- Melt Temperature: 138 °C
$ 1903/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.010 cm/cm
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 70 %
$ 1667/MT
- Specific Gravity: 1.04 g/cc @Temperature 22.8 °C
- Filler Content: 12 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 20 %
$ 1528/MT
- Specific Gravity: 1.05 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 100 %
$ 1972/MT
- Shrinkage: 2.0 - 3.5 %
- Processing Temperature: 82.2 °C
- Processing Temperature: 127 °C
- Processing Temperature: 135 °C
- Processing Temperature: 166 °C
$ 1721/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 19.8 MPa
- Elongation at Break: 290 %
- 100% Modulus: 0.0152 GPa
- Melt Temperature: 188 °C
$ 1534/MT
- Specific Gravity: 1.24 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 cm/cm
- Tensile Strength, Yield: 33.8 MPa
- Elongation at Break: 10 %
$ 2591/MT
- Hardness, Shore A: 83
- Maximum Service Temperature, Air: 23.9 °C
- Wire Style: specialty compounds
$ 2102/MT
- Hardness, Shore A: 89
- Maximum Service Temperature, Air: 23.9 °C
- Wire Style: communication cable riser comp
$ 1989/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 52.4 MPa
- Tensile Modulus: 2.28 GPa
- Flexural Modulus: 2.07 GPa
$ 1690/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1924/MT
- Specific Gravity: 1.06 g/cc
- Hardness, Rockwell R: 113
- Tensile Strength, Yield: 44.8 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 57.2 MPa
$ 1525/MT
- Hardness, Shore A: 83
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: electric power and control cables
$ 2054/MT
- Specific Gravity: 1.30 - 1.38 g/cc
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 40.7 MPa
- Flexural Yield Strength: 66.2 MPa
- Flexural Modulus: 2.28 GPa
$ 1662/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1636/MT
- Specific Gravity: 0.960 g/cc @Temperature 22.8 °C
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: >= 400 %
$ 1749/MT
- Specific Gravity: 1.02 - 1.08 g/cc
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 37.2 MPa
- Flexural Yield Strength: 61.4 MPa
- Flexural Modulus: 1.93 GPa
$ 1549/MT
- Density: 1.05 g/cc
- Hardness, Rockwell R: 96
- Tensile Strength, Ultimate: 34.5 MPa
- Flexural Yield Strength: 55.2 MPa
- Flexural Modulus: 1.90 GPa
$ 1472/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 106
- Tensile Strength at Break: 57.9 MPa
- Tensile Strength, Yield: 58.6 MPa
- Elongation at Break: 300 %
$ 1549/MT
- Specific Gravity: 1.05 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.014 cm/cm
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 100 %
$ 1841/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 52.4 MPa
- Tensile Modulus: 2.28 GPa
- Flexural Yield Strength: 96.5 MPa
$ 1455/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Shore A: 95
- Tensile Strength, Yield: 21.75 MPa
- Elongation at Break: 230 %
- 100% Modulus: 0.0205 GPa
- Melt Temperature: 193 °C
$ 1847/MT
- Specific Gravity: 1.05 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Flexural Yield Strength: 68.9 MPa
- Flexural Modulus: 2.34 GPa
- Izod Impact, Unnotched: 4.00 J/cm
$ 2357/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 92
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 300 %
- 100% Modulus: 0.0145 GPa
- Melt Temperature: 193 °C
$ 1691/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 31.7 MPa
- Tensile Modulus: 1.93 GPa
- Flexural Yield Strength: 51.7 MPa
$ 2036/MT
- Hardness, Shore A: 89
- Maximum Service Temperature, Air: 32.2 °C
- Wire Style: fire protective cables
$ 1848/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 53.1 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 77.2 MPa
$ 1641/MT
- Specific Gravity: 1.04 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: >= 400 %
$ 1615/MT
- Density: 1.24 g/cc
- Water Absorption: 0.020 %
- Viscosity: 190400 cP @Shear Rate 3000 1/s, Temperature 191 °C
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 1.8 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1518/MT
- Specific Gravity: 0.900 g/cc
- Tensile Strength, Yield: 27.6 MPa
- Flexural Modulus: 1.24 GPa
- Izod Impact, Unnotched: 1.60 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 90.0 °C
$ 1908/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 20.4 MPa
- Elongation at Break: 320 %
- 100% Modulus: 0.00752 GPa
- Melt Temperature: 188 °C
$ 1671/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 48.80 MPa
- Tensile Modulus: 2.32 GPa
- Flexural Yield Strength: 85.998 MPa
$ 1866/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 92
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 300 %
- 100% Modulus: 0.0172 GPa
- Melt Temperature: 193 °C
$ 2000/MT
- Specific Gravity: 2.00 g/cc
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 550 %
- Flexural Yield Strength: 44.8 MPa
$ 2214/MT
- Specific Gravity: 0.950 g/cc
- Hardness, Shore D: 68
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 1000 %
- Tensile Modulus: 0.827 GPa
$ 1584/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1952/MT
- Specific Gravity: 1.15 g/cc @Temperature 22.8 °C
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.013 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 10 %
$ 1884/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 53.1 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 77.2 MPa
$ 1561/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 410 %
- 100% Modulus: 0.00627 GPa
- Melt Temperature: 166 °C
$ 2177/MT
- Specific Gravity: 1.21 - 1.28 g/cc
- Hardness, Rockwell R: 98
- Tensile Strength, Yield: 39.3 MPa
- Flexural Yield Strength: 64.8 MPa
- Flexural Modulus: 2.14 GPa
$ 1908/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 73.1 MPa
- Tensile Modulus: 4.044 GPa
- Flexural Yield Strength: 93.1 MPa
$ 1790/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 470 %
- Brittleness Temperature: -50.0 °C
$ 1872/MT
- Specific Gravity: 0.970 g/cc
- Hardness, Rockwell L: 88
- Tensile Strength at Break: 7.770 MPa
- Elongation at Break: 627 %
- Flexural Modulus: 0.1190 GPa
$ 1584/MT
- Hardness, Shore D: 50
- Maximum Service Temperature, Air: 32.2 °C
- Wire Style: appliance wire
$ 1864/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 8.55 MPa
- Elongation at Break: 340 %
- 100% Modulus: 0.00379 GPa
- Melt Temperature: 143 °C
$ 2332/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 7.24 MPa
- Elongation at Break: 350 %
- 100% Modulus: 0.00372 GPa
- Melt Temperature: 143 °C
$ 1778/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 2275/MT
- Hardness, Shore A: 98
- Maximum Service Temperature, Air: 23.9 °C
- Wire Style: communication cable riser comp
$ 1530/MT
- Hardness, Shore A: 90
- Maximum Service Temperature, Air: 51.7 °C
- Wire Style: specialty compounds
$ 2017/MT
- Specific Gravity: 1.08 g/cc @Temperature 22.8 °C
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Tensile Strength, Yield: 33.4 MPa
- Elongation at Break: 15 %
$ 1774/MT
- Specific Gravity: 0.740 g/cc
- Tensile Strength, Yield: 19.4 MPa
- Flexural Modulus: 0.8770 GPa
- Izod Impact, Unnotched: NB
- Deflection Temperature at 0.46 MPa (66 psi): 71.1 °C
$ 1753/MT
- Shrinkage: 1.5 - 2.0 %
- Processing Temperature: 87.8 °C
- Processing Temperature: 143 °C
- Processing Temperature: 154 - 163 °C
- Processing Temperature: 166 °C
$ 2281/MT
- Specific Gravity: 1.23 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Tensile Strength, Yield: 89.6 MPa
- Elongation at Break: 2.0 %
$ 1618/MT
- Specific Gravity: 0.960 g/cc @Temperature 22.8 °C
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 70 %
$ 2166/MT
- Specific Gravity: 1.27 - 1.30 g/cc
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 40.7 MPa
- Flexural Yield Strength: 66.2 MPa
- Flexural Modulus: 2.48 GPa
$ 1504/MT
- Hardness, Shore A: 90
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: fire protective cables
$ 2007/MT
- Specific Gravity: 1.18 - 1.25 g/cc
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 35.9 MPa
- Flexural Yield Strength: 55.2 MPa
- Flexural Modulus: 2.00 GPa
$ 1832/MT
- Shrinkage: 2.0 - 3.5 %
- Processing Temperature: 82.2 °C
- Processing Temperature: 127 °C
- Processing Temperature: 135 °C
- Processing Temperature: 166 °C
$ 1548/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 1.6 %
- Tensile Strength, Yield: 83.4 MPa
- Shear Strength: 25.5 MPa
$ 1907/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 60
$ 1729/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 62
$ 1600/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 64.5 MPa
- Tensile Modulus: 2.41 GPa
- Flexural Yield Strength: 93.1 MPa
$ 1559/MT
- Water Absorption: 0.20 %
- Tensile Strength, Yield: 64.8 MPa
- Tensile Modulus: 2.76 GPa
- Compressive Modulus: 2.76 GPa
- Maximum Service Temperature, Air: 76.7 °C
$ 2331/MT
- Hardness, Shore A: 70
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: festoon cable insulation
$ 1492/MT
- Specific Gravity: 0.900 g/cc
- Tensile Strength, Yield: 27.6 MPa
- Flexural Yield Strength: 64.8 MPa
- Flexural Modulus: 1.24 GPa
- CTE, linear: 108 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 90.0 °C
$ 1510/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 58
$ 1885/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore D: 69
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 375 %
- Flexural Modulus: 1.38 GPa
$ 1586/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 390 %
- 100% Modulus: 0.00931 GPa
- Melt Temperature: 177 °C
$ 2358/MT
- Specific Gravity: 0.960 g/cc @Temperature 22.8 °C
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: >= 400 %
$ 1997/MT
- Shrinkage: 2.0 - 3.0 %
- Processing Temperature: 82.2 °C
- Processing Temperature: 127 °C
- Processing Temperature: 135 °C
- Processing Temperature: 166 °C
$ 1870/MT
- Hardness, Shore A: 85
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: portable cords and parallel wire
$ 1506/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Rockwell L: 85
- Tensile Strength, Yield: 40.0 MPa
- Tensile Modulus: 2.48 GPa
- Flexural Yield Strength: 51.7 MPa
$ 2076/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 47.2 MPa
- Tensile Modulus: 2.34 GPa
- Flexural Yield Strength: 71.0 MPa
$ 1460/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 64.5 MPa
- Tensile Modulus: 2.41 GPa
- Flexural Yield Strength: 93.1 MPa
$ 1530/MT
- Specific Gravity: 1.49 - 1.55 g/cc
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 37.9 MPa
- Flexural Yield Strength: 62.1 MPa
- Flexural Modulus: 2.34 GPa
$ 2105/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Rockwell R: 87
- Tensile Strength, Yield: 31.0 MPa
- Flexural Yield Strength: 49.0 MPa
- Flexural Modulus: 1.93 GPa
$ 1595/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 360 %
- 100% Modulus: 0.0145 GPa
- Melt Temperature: 188 °C
$ 1805/MT
- Specific Gravity: 1.09 g/cc
- Tensile Strength, Yield: 62.1 MPa
- Elongation at Break: 83 %
- Flexural Yield Strength: 95.8 MPa
- Flexural Modulus: 2.28 GPa
$ 2484/MT
- Specific Gravity: 1.02 - 1.08 g/cc
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 32.4 MPa
- Flexural Yield Strength: 48.3 MPa
- Flexural Modulus: 1.59 GPa
$ 1450/MT
- Specific Gravity: 1.02 - 1.08 g/cc
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 32.4 MPa
- Flexural Yield Strength: 48.3 MPa
- Flexural Modulus: 1.59 GPa
$ 1782/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 55.2 MPa
- Tensile Modulus: 2.00 GPa
- Flexural Yield Strength: 85.15 MPa
$ 2041/MT
- Specific Gravity: 1.04 g/cc
- Hardness, Rockwell L: 68
- Tensile Strength, Yield: 24.1 MPa
- Tensile Modulus: 1.86 GPa
- Flexural Yield Strength: 48.3 MPa
$ 1704/MT
- Specific Gravity: 1.02 - 1.08 g/cc
- Hardness, Rockwell R: 98
- Tensile Strength, Yield: 34.5 MPa
- Flexural Yield Strength: 53.8 MPa
- Flexural Modulus: 1.93 GPa
$ 1985/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 34.5 MPa
- Tensile Modulus: 1.79 GPa
- Flexural Yield Strength: 71.0 MPa
$ 2028/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.010 cm/cm
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Break: 70 %
$ 2150/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 16.3 MPa
- Elongation at Break: 345 %
- 100% Modulus: 0.00896 GPa
- Melt Temperature: 177 °C
$ 1708/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 1.6 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1814/MT
- Specific Gravity: 1.14 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Yield: 41.4 MPa
- Elongation at Break: 2.5 %
$ 1647/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 53.1 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 77.2 MPa
$ 2042/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 53.1 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 77.2 MPa
$ 2310/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1480/MT
- Specific Gravity: 1.03 g/cc
- Hardness, Rockwell L: 63
- Tensile Strength, Yield: 22.8 MPa
- Tensile Modulus: 1.65 GPa
- Flexural Yield Strength: 40.0 MPa
$ 2070/MT
- Specific Gravity: 1.06 g/cc
- Hardness, Shore D: 66
- Tensile Strength, Yield: 30.3 MPa
- Flexural Yield Strength: 37.9 MPa
- Flexural Modulus: 1.24 GPa
$ 1900/MT
- Density: 1.07 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 98
$ 1444/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 51
$ 1791/MT
- Specific Gravity: 1.04 g/cc
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.14 GPa
- Flexural Yield Strength: 68.9 MPa
$ 2163/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 498 %
- 100% Modulus: 0.00296 GPa
- Melt Temperature: 149 °C
$ 2060/MT
- Specific Gravity: 1.19 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.013 cm/cm
- Tensile Strength, Yield: 32.4 MPa
- Elongation at Break: 30 %
$ 1569/MT
- Specific Gravity: 1.27 - 1.30 g/cc
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 42.1 MPa
- Flexural Yield Strength: 64.8 MPa
- Flexural Modulus: 2.41 GPa
$ 2557/MT
- Specific Gravity: 1.15 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 150 %
$ 2393/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 55
$ 2579/MT
- Specific Gravity: 1.33 - 1.38 g/cc
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 39.3 MPa
- Flexural Yield Strength: 62.1 MPa
- Flexural Modulus: 2.21 GPa
$ 1572/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 64.5 MPa
- Tensile Modulus: 2.41 GPa
- Flexural Yield Strength: 93.1 MPa
$ 1577/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.011 cm/cm
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 70 %
$ 2169/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 37.9 MPa
- Tensile Modulus: 1.52 GPa
- Flexural Yield Strength: 71.0 MPa
$ 1798/MT
- Specific Gravity: 1.05 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 2.0 %
$ 1491/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.14 GPa
- Flexural Yield Strength: 67.6 MPa
$ 2051/MT
- Hardness, Shore A: 72
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: specialty compounds
$ 1947/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Rockwell R: 60
- Tensile Strength, Yield: 20.0 MPa
- Flexural Yield Strength: 31.0 MPa
- Flexural Modulus: 1.03 GPa
$ 1611/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 96
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 270 %
- 100% Modulus: 0.0221 GPa
- Melt Temperature: 193 °C
$ 1664/MT
- Specific Gravity: 1.07 g/cc
- Tensile Strength at Break: 30.3 MPa
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: 400 %
- Flexural Modulus: 1.10 GPa
$ 1821/MT
- Specific Gravity: 1.04 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Tensile Strength, Yield: 33.1 MPa
- Elongation at Break: 30 %
$ 1961/MT
- Specific Gravity: 1.04 g/cc
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 34.5 MPa
- Tensile Modulus: 1.93 GPa
- Flexural Yield Strength: 51.7 MPa
$ 1701/MT
- Specific Gravity: 1.15 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: >= 400 %
$ 1462/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Shore D: 65
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 200 %
- Flexural Modulus: 1.52 GPa
$ 1540/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Tensile Strength, Yield: 59.3 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 2.76 GPa
$ 1787/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Rockwell M: 96
- Tensile Strength, Yield: >= 72.4 MPa
$ 1867/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 470 %
- 100% Modulus: 0.00407 GPa
- Melt Temperature: 154 °C
$ 1794/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1994/MT
- Specific Gravity: 1.12 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 4.0 %
$ 1518/MT
- Specific Gravity: 1.14 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0035 cm/cm
- Tensile Strength, Yield: 79.3 MPa
- Elongation at Break: 2.0 %
$ 1953/MT
- Specific Gravity: 1.18 - 1.26 g/cc
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 34.5 MPa
- Flexural Yield Strength: 53.8 MPa
- Flexural Modulus: 1.93 GPa
$ 1497/MT
- Specific Gravity: 1.03 g/cc
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 37.2 MPa
- Tensile Modulus: 2.14 GPa
- Flexural Yield Strength: 66.2 MPa
$ 1607/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 60
$ 1866/MT
- Hardness, Shore A: 92
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: appliance wire
$ 1797/MT
- Specific Gravity: 1.01 - 1.06 g/cc
- Hardness, Rockwell R: 91
- Tensile Strength, Yield: 31.7 MPa
- Flexural Yield Strength: 51.7 MPa
- Flexural Modulus: 1.86 GPa
$ 1604/MT
- Specific Gravity: 1.04 g/cc
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 24.1 MPa
- Tensile Modulus: 1.86 GPa
- Flexural Yield Strength: 48.3 MPa
$ 1509/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 37.5 MPa
- Flexural Yield Strength: 62.7 MPa
- Flexural Modulus: 1.99 GPa
$ 2298/MT
- Specific Gravity: 0.960 g/cc @Temperature 22.8 °C
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Break: 125 %
$ 1663/MT
- Density: 1.47 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 3.9 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 99
$ 1544/MT
- Specific Gravity: 1.04 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 115 %
$ 1771/MT
- Specific Gravity: 1.30 - 1.38 g/cc
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 40.0 MPa
- Flexural Yield Strength: 63.4 MPa
- Flexural Modulus: 2.21 GPa
$ 1487/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -35.0 °C
$ 1623/MT
- Specific Gravity: 1.18 - 1.25 g/cc
- Hardness, Rockwell R: 87
- Tensile Strength, Yield: 31.7 MPa
- Flexural Yield Strength: 45.5 MPa
- Flexural Modulus: 1.52 GPa
$ 1718/MT
- Specific Gravity: 1.07 g/cc
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 20.7 MPa
- Flexural Modulus: 1.38 GPa
- Izod Impact, Unnotched: 2.67 J/cm
$ 1881/MT
- Specific Gravity: 1.01 g/cc @Temperature 22.8 °C
- Filler Content: 12 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 33.1 MPa
- Elongation at Break: 20 %
$ 2471/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 41.4 MPa
- Tensile Modulus: 2.14 GPa
- Flexural Yield Strength: 67.6 MPa
$ 1499/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 91
- Tensile Strength, Yield: 26.6 MPa
- Elongation at Break: 310 %
- 100% Modulus: 0.0141 GPa
- Melt Temperature: 193 °C
$ 1707/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage: 0.012 cm/cm
- Tensile Strength, Yield: 31.0 MPa
$ 2446/MT
- Specific Gravity: 0.950 g/cc
- Hardness, Shore D: 68
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: >= 600 %
- Tensile Modulus: 0.827 GPa
$ 1581/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Rockwell L: 55
- Tensile Strength, Yield: 24.1 MPa
- Tensile Modulus: 1.86 GPa
- Flexural Yield Strength: 48.3 MPa
$ 1686/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 10 %
$ 1546/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 10 %
$ 2361/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 10 %
$ 1637/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 10 %
$ 1835/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 10 %
$ 1647/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 2.6 %
- Tensile Strength, Yield: 83.4 MPa
- Shear Strength: 25.5 MPa
$ 1551/MT
- Specific Gravity: 1.05 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.014 cm/cm
- Tensile Strength, Yield: 35.2 MPa
- Elongation at Break: 30 %
$ 1706/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Hardness, Rockwell M: 100
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 4.5 %
$ 1833/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 31.0 MPa
- Tensile Modulus: 2.00 GPa
- Flexural Yield Strength: 55.2 MPa
$ 1715/MT
- Specific Gravity: 1.35 - 1.40 g/cc
- Hardness, Rockwell R: 103
- Tensile Strength, Yield: 40.7 MPa
- Flexural Yield Strength: 66.9 MPa
- Flexural Modulus: 2.28 GPa
$ 1596/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 8.48 MPa
- Elongation at Break: 390 %
- 100% Modulus: 0.00310 GPa
- Melt Temperature: 143 °C
$ 1694/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore D: 66
- Tensile Strength, Yield: 31.0 MPa
- Tensile Modulus: 0.655 GPa
- Flexural Modulus: 1.55 GPa
$ 1926/MT
- Specific Gravity: 0.950 g/cc
- Hardness, Shore D: 68
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 1000 %
- Tensile Modulus: 0.827 GPa
$ 1704/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.010 cm/cm
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Break: 200 %
$ 1446/MT
- Specific Gravity: 0.850 g/cc
- Hardness, Rockwell R: 98
- Flexural Modulus: 2.07 GPa
- CTE, linear: 90.0 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 1.8 MPa (264 psi): 92.2 °C
$ 1457/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 106
- Tensile Strength at Break: 57.9 MPa
- Tensile Strength, Yield: 58.6 MPa
- Elongation at Break: 300 %
$ 1949/MT
- Hardness, Shore A: 90
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: machine tool wire
$ 1824/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 32.4 MPa
- Tensile Modulus: 1.93 GPa
- Flexural Yield Strength: 51.7 MPa
$ 2313/MT
- Specific Gravity: 1.04 g/cc
- Hardness, Rockwell R: 81
- Tensile Strength, Yield: 31.0 MPa
- Tensile Modulus: 1.93 GPa
- Flexural Yield Strength: 62.1 MPa
$ 1802/MT
- Specific Gravity: 1.03 - 1.08 g/cc
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 27.6 MPa
- Flexural Yield Strength: 44.8 MPa
- Flexural Modulus: 1.79 GPa
$ 1449/MT
- Specific Gravity: 1.15 g/cc @Temperature 22.8 °C
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.017 cm/cm
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 40 %
$ 1568/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Hardness, Barcol: 50
- Hardness, Rockwell M: 98
$ 1505/MT
- Specific Gravity: 1.04 g/cc @Temperature 22.8 °C
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Tensile Strength, Yield: 21.4 MPa
- Elongation at Break: >= 400 %
$ 2219/MT
- Specific Gravity: 1.19 - 1.24 g/cc
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 55.2 MPa
- Flexural Yield Strength: 82.7 MPa
- Flexural Modulus: 2.28 GPa
$ 1734/MT
- Specific Gravity: 1.19 - 1.24 g/cc
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 55.2 MPa
- Flexural Yield Strength: 82.7 MPa
- Flexural Modulus: 2.28 GPa
$ 1616/MT
- Specific Gravity: 0.960 g/cc @Temperature 22.8 °C
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Tensile Strength, Yield: 55.2 MPa
- Elongation at Break: 8.0 %
$ 2332/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -25.0 °C
$ 1641/MT
- Specific Gravity: 1.35 - 1.45 g/cc
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 40.7 MPa
- Flexural Yield Strength: 65.5 MPa
- Flexural Modulus: 2.21 GPa
$ 1544/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 37.9 MPa
- Tensile Modulus: 2.07 GPa
- Flexural Yield Strength: 57.2 MPa
$ 1844/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 64.5 MPa
- Tensile Modulus: 2.41 GPa
- Flexural Yield Strength: 93.1 MPa
$ 2042/MT
- Specific Gravity: 1.02 - 1.08 g/cc
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 33.1 MPa
- Flexural Yield Strength: 55.2 MPa
- Flexural Modulus: 1.86 GPa
$ 1829/MT
- Density: 1.36 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 3.9 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 97
$ 2079/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 61.4 MPa
- Flexural Yield Strength: 97.9 MPa
- Flexural Modulus: 2.34 GPa
$ 1450/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 61.4 MPa
- Flexural Yield Strength: 97.9 MPa
- Flexural Modulus: 2.34 GPa
$ 1654/MT
- Hardness, Shore A: 65
- Maximum Service Temperature, Air: 40.6 °C
- Wire Style: festoon cable jacket
$ 1524/MT
- Specific Gravity: 1.25 g/cc @Temperature 22.8 °C
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.011 cm/cm
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: >= 200 %
$ 1901/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 52.4 MPa
- Tensile Modulus: 2.28 GPa
- Flexural Yield Strength: 96.5 MPa
$ 2244/MT
- Specific Gravity: 1.03 - 1.05 g/cc
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 190 %
- Flexural Yield Strength: 57.2 MPa
$ 2111/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 37.9 MPa
- Tensile Modulus: 1.52 GPa
- Flexural Yield Strength: 71.0 MPa
$ 1751/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.21 GPa
- Flexural Yield Strength: 75.8 MPa
$ 1744/MT
- Specific Gravity: 1.15 g/cc @Temperature 22.8 °C
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Break: 15 %
Delivery Thermoplastic Spartech
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
vessels for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.