$ 1833/MT
- Density: 0.935 g/cc
- Density: 1.09 g/cc
- Water Absorption: 0.10 - 0.20 %
- Viscosity: 400 - 600 cP
- Hardness, Shore D: 80 @Temperature 100 °C, Time 10800 sec
$ 1543/MT
- Density: 1.80 g/cc
- Viscosity: 1500 cP @Temperature 100 °C
- Viscosity: 180000 cP @Temperature 25.0 °C
- Hardness, Shore D: >= 70 @Temperature 120 °C
- Hardness, Shore D: 90 @Temperature 25.0 °C
$ 1861/MT
- Tensile Strength at Break: 34.5 - 75.8 MPa
- Flexural Strength: 34.5 - 89.6 MPa
- Compressive Strength: 55.2 - 110 MPa
$ 2045/MT
- Density: 0.935 g/cc
- Density: 1.09 g/cc
- Water Absorption: 0.10 - 0.20 %
- Viscosity: 450 - 650 cP
- Hardness, Shore D: 80 @Temperature 100 °C, Time 10800 sec
$ 1481/MT
- Viscosity: 30000 cP @Temperature 25.0 °C
- Thermal Conductivity: 0.586 - 0.795 W/m-K
- Maximum Service Temperature, Air: 300 °C
- Pot Life: 1200 min @Temperature 25.0 °C
$ 1655/MT
- Hardness, Shore A: 68
- Tensile Strength at Break: 0.159 MPa
- Elongation at Break: 130 %
- Color: Gray
$ 1670/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 50.0 °C
- Carbon, C: 7.2 %
- Surface Resistivity per Square: <= 400000 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1864/MT
- Viscosity: 600 cP
- Hardness, Rockwell M: 98
- Tensile Strength at Break: 44.1 MPa
- Elongation at Break: 3.3 %
- Flexural Strength: 92.4 MPa
$ 1463/MT
- Viscosity: 2500 cP
- Hardness, Shore D: 82
- Tensile Strength, Ultimate: 53.8 MPa
- Elongation at Break: 6.5 %
- Izod Impact, Notched: 0.454 J/cm
$ 1770/MT
- Density: 0.959 g/cc
- Density: 3.12 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 2060/MT
- Density: 1.16 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 71.7 MPa
- Elongation at Break: 5.9 %
- Tensile Modulus: 2.61 GPa
$ 1657/MT
- Density: 1.44 g/cc
- Viscosity: 120 cP @Temperature 100 °C
- Viscosity: 20000 cP @Temperature 25.0 °C
- Hardness, Shore D: >= 70 @Temperature 120 °C
- Hardness, Shore D: 90 @Temperature 25.0 °C
$ 1469/MT
- Density: 1.80 g/cc
- Viscosity: 1500 cP @Temperature 100 °C
- Viscosity: 180000 cP @Temperature 25.0 °C
- Hardness, Shore D: >= 70 @Temperature 120 °C
- Hardness, Shore D: 90 @Temperature 25.0 °C
$ 1534/MT
- Tensile Strength at Break: 62.1 MPa
- Flexural Strength: 72.4 MPa
- Compressive Strength: 82.7 MPa
$ 2027/MT
- Density: 0.959 g/cc
- Density: 3.12 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 2499/MT
- Water Absorption: 0.10 - 0.50 %
- Linear Mold Shrinkage: 0.0010 cm/cm
- Hardness, Shore D: >= 90
- Tensile Strength at Break: 49.6 MPa
- Elongation at Break: 1.8 %
$ 2384/MT
- Density: 0.959 g/cc
- Density: 1.14 g/cc
- Water Absorption: 0.22 % @Time 605000 sec
- Viscosity: 1900 cP
- Compressive Strength: 77.2 MPa
$ 1617/MT
- Density: 1.09 g/cc
- Density: 1.14 g/cc
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 27 %
- Tensile Modulus: 5.45 GPa
$ 1506/MT
- Water Absorption: 0.20 %
- Viscosity Measurement: 120 @Temperature 25.0 - 27.0 °C
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 51.0 MPa
- Elongation at Break: 3.0 %
$ 1690/MT
- Viscosity Measurement: 12000
- Hardness, Rockwell M: 111
- Tensile Strength, Ultimate: 39.0 MPa
- Elongation at Break: 1.6 %
- Flexural Yield Strength: 96.53 MPa
$ 1462/MT
- Maximum Service Temperature, Air: <= 25.0 °C
- Dielectric Constant: 5.4 @Frequency 60.0 Hz, Temperature 100 °C
- Dissipation Factor: 0.088 @Frequency 60.0 Hz, Temperature 100 °C
- Cure Time: 120 min @Temperature 100 - 120 °C
- Cure Time: 120 - 240 min @Temperature 120 - 160 °C
$ 1644/MT
- Solids Content: 81.5 %
- Maximum Service Temperature, Air: 120 °C
- Surface Resistivity per Square: <= 0.010 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
- Cure Time: >= 1440 min @Temperature 22.0 - 30.0 °C
$ 1661/MT
- Solids Content: 100 %
- Hardness, Shore A: 52
- Tensile Strength at Break: 1.69 MPa
- Elongation at Break: 250 %
- Color: Brown, Black, or other Dark Colors
$ 2035/MT
- Water Absorption: 0.22 %
- Viscosity Measurement: 1600
- Hardness, Shore D: 83
- Tensile Strength, Ultimate: 58.61 MPa
- Elongation at Break: 5.5 %
$ 1528/MT
- Density: 1.04 g/cc
- Density: 1.11 g/cc
- Transmission, Visible: 90 %
- Cure Time: 60.0 - 180 min @Temperature 100 °C
- Cure Time: 5760 - 11520 min @Temperature 20.0 °C
$ 1639/MT
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
- Compressive Strength: 62.1 - 89.6 MPa
- Shear Strength: 17.2 - 20.7 MPa
$ 1471/MT
- Solids Content: 50.9 %
- Maximum Service Temperature, Air: 80.0 °C
- Surface Resistivity per Square: <= 0.70 ohm
- Cure Time: >= 720 min @Temperature 22.0 - 30.0 °C
- Color: Gray
$ 1773/MT
- Density: 0.983 g/cc
- Density: 1.49 g/cc
- Water Absorption: 0.25 % @Time 605000 sec
- Viscosity: 9500 cP
- Compressive Strength: 118 MPa
$ 2522/MT
- Density: 0.947 g/cc
- Density: 1.14 g/cc
- Hardness, Shore D: 64
- Hardness, Shore D: 64
- Hardness, Shore D: 70
$ 1593/MT
- Solids Content: 100 %
- Viscosity: <= 8000 cP
- Hardness, Shore D: 75
- Cure Time: 60.0 - 120 min @Temperature 82.222 - 98.889 °C
- Cure Time: 5760 - 8640 min @Temperature 15.556 - 26.667 °C
$ 1451/MT
- Density: 1.17 g/cc
- Density: 3.12 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 2497/MT
- Water Absorption: 4.5 % @Time 2.59e+6 sec
- Water Absorption: 4.9 % @Time 2.59e+6 sec
- Viscosity: 1600 cP
- Hardness, Shore D: 37 @Temperature 75.0 °C
- Hardness, Shore D: 58 @Temperature 75.0 °C
$ 1947/MT
- Water Absorption: 5.8 % @Time 7200 sec
- Viscosity: 2460 cP
- Hardness, Shore A: 70 @Temperature 75.0 °C
- Hardness, Shore D: 60 @Temperature 25.0 °C
- Hardness, Shore D: 80 @Temperature 0.000 °C
$ 2311/MT
- Water Absorption: 0.70 % @Time 7200 sec
- Viscosity: 550 cP
- Hardness, Shore D: 83 @Temperature 75.0 °C
- Hardness, Shore D: 89 @Temperature 0.000 °C
- Hardness, Shore D: 89 @Temperature 25.0 °C
$ 2248/MT
- Density: 1.17 g/cc
- Density: 3.12 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 1713/MT
- Water Absorption: 2.4 % @Time 2.59e+6 sec
- Viscosity: 2650 cP
- Hardness, Shore D: 80 @Temperature 25.0 °C
- Hardness, Shore D: 86 @Temperature 0.000 °C
- Hardness, Shore D: 90 @Temperature -60.0 °C
$ 1517/MT
- Water Absorption: 0.20 %
- Viscosity Measurement: 100 @Temperature 25.0 - 27.0 °C
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 51.0 MPa
- Elongation at Break: 3.0 %
$ 2042/MT
- Density: 1.09 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 2.0 - 3.0 %
- Tensile Modulus: 3.07 GPa
$ 1678/MT
- Specific Gravity: 1.08 g/cc
- Density: 0.972 g/cc
- Solids Content: 41.2 %
- Viscosity: 10.5 - 18 cP
- Pot Life: 720 min
$ 1739/MT
- Viscosity: 200 cP
- Hardness, Shore D: 85
- Tensile Strength at Break: 62.7 MPa
- Elongation at Break: 14 %
- Flexural Strength: 62.7 MPa
$ 2236/MT
- Density: 1.17 g/cc
- Water Absorption: 0.50 - 0.60 %
- Water Absorption: 0.70 - 0.80 %
- Viscosity: 6500 - 8000 cP
- Vapor Pressure: <= 0.0000133 bar @Temperature 20.0 °C
$ 1512/MT
- Maximum Service Temperature, Air: 85.0 °C
- Pot Life: 60 min @Temperature 25.0 °C
- Color: Green
- Hardening Time (min): 120 to 360
- Parts by Weight (pbw): 100
$ 1792/MT
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
- Compressive Strength: 62.1 - 89.6 MPa
- Shear Strength: 17.2 - 20.7 MPa
$ 1942/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Solids Content: 100 %
- Viscosity: 1750 cP
- Pot Life: 25 min
$ 1478/MT
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 55.0 MPa
- Compressive Yield Strength: 62.0 MPa
- Maximum Service Temperature, Air: 75.0 °C
$ 1496/MT
- Viscosity Measurement: 400
- Hardness, Rockwell M: 96
- Tensile Strength, Ultimate: 73.84 MPa
- Elongation at Break: 7.5 %
- Flexural Yield Strength: 81.56 MPa
$ 1675/MT
- Solids Content: 88.4 %
- Maximum Service Temperature, Air: 110 °C
- Surface Resistivity per Square: <= 0.70 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
- Cure Time: >= 1440 min @Temperature 22.0 - 30.0 °C
$ 1692/MT
- Density: 1.80 g/cc
- Viscosity: 1500 cP @Temperature 100 °C
- Viscosity: 180000 cP @Temperature 25.0 °C
- Hardness, Shore D: >= 70 @Temperature 120 °C
- Hardness, Shore D: 90 @Temperature 25.0 °C
$ 1461/MT
- Water Absorption: 0.20 %
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 51.0 MPa
- Elongation at Break: 3.0 %
- Flexural Yield Strength: 83.0 MPa
- Compressive Yield Strength: 115 MPa
$ 2391/MT
- Viscosity: 1500 cP
- Hardness, Rockwell M: 95
- Tensile Strength at Break: 61.4 MPa
- Elongation at Break: 7.6 %
- Flexural Strength: 100 MPa
$ 1589/MT
- Viscosity Measurement: 2300
- Hardness, Rockwell M: 75
- Tensile Strength, Ultimate: 54.33 MPa
- Elongation at Break: 14.4 %
- Flexural Yield Strength: 78.81 MPa
$ 1606/MT
- Hardness, Shore D: 62
- Tensile Strength at Break: 3.31 MPa
- Elongation at Break: 60 %
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -59.4 °C
$ 1539/MT
- Density: 1.19 g/cc
- Water Absorption: 0.40 - 0.50 %
- Water Absorption: 0.50 - 0.60 %
- Viscosity: 200 - 300 cP @Temperature 60.0 °C
- Viscosity: 1000 - 2000 cP @Temperature 40.0 °C
$ 2207/MT
- Water Absorption: 0.40 % @Time 28800 sec
- Viscosity: 2000 cP
- Hardness, Shore D: 85
- Tensile Strength, Ultimate: 68.3 MPa
- Flexural Strength: 105 MPa
$ 1650/MT
- Density: 1.07 g/cc
- Solids Content: 48 %
- Brookfield Viscosity: 200 cP
- Brookfield Viscosity: 300 cP
- Brookfield Viscosity: 500 cP
$ 1884/MT
- Viscosity: 17000 cP
- Hardness, Rockwell M: 121
- Tensile Strength at Break: 26.2 MPa
- Elongation at Break: 0.70 %
- Flexural Strength: 100 MPa
$ 2407/MT
- Viscosity Measurement: 1500
- Hardness, Rockwell M: 87
- Tensile Strength, Ultimate: 47.78 MPa
- Elongation at Break: 14.4 %
- Flexural Yield Strength: 73.02 MPa
$ 1725/MT
- Solids Content: 100 %
- Hardness, Shore A: 30 - 35
- Tensile Strength at Break: 1.38 - 1.72 MPa
- Elongation at Break: 300 - 350 %
- Color: Brown, Black, or other Dark Colors
$ 1650/MT
- Water Absorption: 0.10 - 0.50 %
- Linear Mold Shrinkage: 0.0010 cm/cm
- Hardness, Shore D: >= 90
- Tensile Strength at Break: 57.9 MPa
- Elongation at Break: 1.0 %
$ 1472/MT
- Viscosity: 3200 cP
- Hardness, Shore D: 85
- Tensile Strength, Ultimate: 58.6 MPa
- Elongation at Break: 6.1 %
- Izod Impact, Notched: 0.299 J/cm
$ 1835/MT
- Viscosity: 800 cP
- Hardness, Shore D: 84
- Tensile Strength at Break: 54.5 MPa
- Elongation at Break: 16 %
- Flexural Strength: 71.0 MPa
$ 1470/MT
- Solids Content: 100 %
- Hardness, Shore A: 35 - 40
- Tensile Strength at Break: 1.03 - 1.38 MPa
- Elongation at Break: 250 - 300 %
- Color: Most Colors
$ 1804/MT
- Viscosity: 4000 cP
- Hardness, Shore D: 87
- Tensile Strength, Ultimate: 60.7 MPa
- Elongation at Break: 5.8 %
- Izod Impact, Notched: 0.267 J/cm
$ 1895/MT
- Density: 1.04 g/cc
- Solids Content: 60 %
- Volatile Organic Compounds (VOC) Content: 415.8 g/l
- Viscosity: 20 cP
- Pot Life: 180 - 300 min
- Koenig Pendulum Hardness: 140 sec
$ 1517/MT
- Density: 1.57 g/cc
- Solids Content: 80 %
- Hardness, Shore A: 36
- Tensile Strength at Break: 0.0483 MPa
- Elongation at Break: 970 %
$ 1906/MT
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
- Compressive Strength: 62.1 - 89.6 MPa
- Shear Strength: 17.2 - 20.7 MPa
$ 2071/MT
- Density: 1.516 g/cc
- Solids Content: 80 %
- Hardness, Shore A: 40
- Tensile Strength at Break: 0.110 MPa
- Elongation at Break: 1000 %
$ 1666/MT
- Viscosity: 1100 cP
- Hardness, Shore D: 81
- Tensile Strength at Break: 56.5 MPa
- Elongation at Break: 15 %
- Flexural Strength: 77.9 MPa
$ 1563/MT
- Viscosity: 700 cP
- Hardness, Shore D: 81
- Tensile Strength at Break: 51.7 MPa
- Elongation at Break: 17 %
- Flexural Strength: 69.6 MPa
$ 1509/MT
- Solids Content: 98 %
- Maximum Service Temperature, Air: 90.0 °C
- Surface Resistivity per Square: <= 0.60 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
- Cure Time: >= 1440 min @Temperature 22.0 - 30.0 °C
$ 1502/MT
- Density: 0.962 g/cc
- Solids Content: 47.4 %
- Viscosity Measurement: 25
- Film Elongation at Break, MD: >= 60 %
- Impact Test: 18.1 J
$ 1950/MT
- Viscosity: 4000 - 6000 cP
- Viscosity: 70 cP @Temperature 70.0 °C
- Hardness, Rockwell M: 109
- Tensile Strength, Ultimate: 68.95 MPa
- Elongation at Break: 3.0 %
$ 1473/MT
- Density: 1.23 g/cc
- Water Absorption: 0.25 - 0.35 %
- Water Absorption: 0.30 - 0.45 %
- Viscosity: 200 - 600 cP @Temperature 120 °C
- Vapor Pressure: <= 0.0000133 bar @Temperature 20.0 °C
$ 1727/MT
- Density: 1.08 g/cc
- Volatiles: 0.00 %
- Hardness, Shore D: 80
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 2.8 %
$ 1513/MT
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 55.0 MPa
- Compressive Yield Strength: 62.0 MPa
- Maximum Service Temperature, Air: 100 - 110 °C
$ 1736/MT
- Viscosity: 1300 cP
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 13.1 MPa
- Elongation at Break: 55 %
- Izod Impact, Notched: 1.13 J/cm
$ 1961/MT
- Solids Content: 100 %
- Hardness, Shore D: <= 65
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 40 %
- Pot Life: 30 min
$ 1719/MT
- Density: 1.20 g/cc
- Viscosity: 20000 - 40000 cP @Temperature 21.0 °C
- Vapor Pressure: 0.00133 bar @Temperature 180 °C
- Vapor Pressure: <= 0.00533 bar @Temperature 60.0 °C
- Tensile Strength, Ultimate: 55.16 MPa
$ 1722/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Volatiles: 7.9 %
- Vapor Pressure: <= 0.0400 bar
- Adhesive Bond Strength: 2.28 MPa
$ 1841/MT
- Hardness, Shore A: 28
- Tensile Strength at Break: 0.393 MPa
- Elongation at Break: 600 %
- Dry Time: 12 - 16 hour
- Pot Life: 60 - 90 min
$ 1865/MT
- Solids Content: 100 %
- Volatile Organic Compounds (VOC) Content: 0.00 g/l
- Hardness, Shore D: 53 - 55
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 4.0 %
$ 1544/MT
- Density: 1.16 g/cc
- Water Absorption: 0.30 - 0.40 % @Time 864000 sec
- Viscosity: 46 cP @Temperature 65.0 °C
- Hardness, Rockwell M: 85
- Tensile Strength, Ultimate: 67.6 MPa
$ 1489/MT
- Hardness, Shore A: 55
- Hardness, Shore A: 36 @Time 10.0 sec
- Hardness, Shore D: 18
- Hardness, Shore D: 50
- Hardness, Shore D: 78
$ 1970/MT
- Water Absorption: 0.80 % @Time 86400 sec
- Hardness, Shore D: 13 @Time 601 sec
- Hardness, Shore D: 33 @Time 1800 sec
- Hardness, Shore D: 60 @Time 3600 sec
- Hardness, Shore D: 74 @Time 86400 sec
$ 1472/MT
- Density: 0.935 g/cc
- Density: 1.09 g/cc
- Water Absorption: 0.20 - 0.40 %
- Viscosity: 400 - 600 cP
- Hardness, Shore D: 65 @Temperature 100 °C, Time 10800 sec
$ 1979/MT
- Viscosity Measurement: 100 @Temperature 70.0 °C
- Hardness, Rockwell M: 101
- Tensile Strength, Ultimate: 78.46 MPa
- Elongation at Break: 8.5 %
- Flexural Yield Strength: 112.7 MPa
$ 1451/MT
- Density: 1.22 g/cc
- Water Absorption: 0.20 - 0.25 %
- Water Absorption: 0.40 - 0.50 %
- Viscosity: 20 - 30 cP @Temperature 120 °C
- Viscosity: 80 - 150 cP @Temperature 70.0 °C
$ 1588/MT
- Solids Content: 50 %
- Viscosity: 300 cP
- Pot Life: 480 - 720 min @Temperature 70.0 - 80.0 °C
- Pencil Hardness: 3
$ 1615/MT
- Density: 1.44 g/cc
- Viscosity: 120 cP @Temperature 100 °C
- Viscosity: 20000 cP @Temperature 25.0 °C
- Hardness, Shore D: >= 70 @Temperature 120 °C
- Hardness, Shore D: 90 @Temperature 25.0 °C
$ 2422/MT
- Maximum Service Temperature, Air: 95.0 °C
- Volume Resistivity: 4.00e+13 ohm-cm
- Dielectric Constant: 3.4 @Frequency 60.0 Hz, Temperature 23.0 °C
- Dielectric Constant: 4.2 @Frequency 60.0 Hz, Temperature 100 °C
- Dielectric Constant: 4.5 @Frequency 60.0 Hz, Temperature 150 °C
$ 2306/MT
- Solids Content: 100 %
- Hardness, Shore A: 70
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 25 - 30 %
- Cure Time: 1440 - 4320 min
$ 1520/MT
- Density: 0.959 g/cc
- Density: 1.80 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 1560/MT
- Density: 1.75 g/cc
- Water Absorption: 0.25 - 0.30 %
- Water Absorption: 0.30 - 0.35 %
- Viscosity: 5000 - 50000 cP @Temperature 120 °C
- Vapor Pressure: <= 0.0000133 bar @Temperature 20.0 °C
$ 1683/MT
- Solids Content: 100 %
- Hardness, Shore A: 40 - 45
- Tensile Strength at Break: 1.69 MPa
- Elongation at Break: 300 - 400 %
- Cure Time: 1440 min
$ 1504/MT
- Viscosity: 12000 cP
- Hardness, Rockwell M: 115
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: 1.1 %
- Flexural Strength: 82.7 MPa
$ 1546/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 50.0 °C
- Carbon, C: 6.1 %
- Surface Resistivity per Square: <= 300000 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1708/MT
- Solids Content: 100 %
- Hardness, Shore D: 65
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -59.4 °C
$ 1911/MT
- Maximum Service Temperature, Air: 130 °C
- Pot Life: 40 min @Temperature 25.0 °C
- Color: Green
- Hardening Time (min): 60 to 360
- Parts by Weight (pbw): 100
$ 1781/MT
- Water Absorption: 0.49 % @Time 605000 sec
- Viscosity: 2500 cP
- Tensile Strength at Break: 59.3 MPa
- Elongation at Break: 6.0 %
- Compressive Strength: 77.9 MPa
$ 1683/MT
- Solids Content: 100 %
- Hardness, Shore A: 61
- Tensile Strength at Break: 3.48 MPa
- Elongation at Break: 620 %
- Color: Black
$ 1712/MT
- Density: 1.08 g/cc
- Volatiles: 0.00 %
- Viscosity: 180 cP
- Tensile Strength at Break: 57.2 MPa
- Elongation at Break: 4.8 %
$ 1569/MT
- Density: 1.18 g/cc
- Water Absorption: 0.30 - 0.50 %
- Water Absorption: 0.70 - 1.0 %
- Viscosity: 1600 - 2000 cP
- Vapor Pressure: <= 0.0000133 bar @Temperature 20.0 °C
$ 1500/MT
- Viscosity Measurement: 100
- Hardness, Rockwell M: 87
- Tensile Strength, Ultimate: 65.29 MPa
- Elongation at Break: 8.1 %
- Flexural Yield Strength: 93.91 MPa
$ 2271/MT
- Solids Content: 25 %
- Volatile Organic Compounds (VOC) Content: 240 g/l
- Viscosity: 7.35 cP
- Adhesive Bond Strength: 6.50 MPa
- Maximum Service Temperature, Air: 100 °C
$ 2025/MT
- Viscosity: 1.0 cP
- Viscosity: 11000 - 14000 cP
- Viscosity: 2250 cP @Temperature 25.0 °C
- Hardness, Rockwell M: 106
- Tensile Strength, Ultimate: 78.6 MPa
$ 1668/MT
- Solids Content: 100 %
- Volatile Organic Compounds (VOC) Content: 0.00 g/l
- Hardness, Shore D: 42
- Tensile Strength at Break: 10.1 MPa
- Elongation at Break: 84 %
$ 1545/MT
- Density: 1.44 g/cc
- Viscosity: 120 cP @Temperature 100 °C
- Viscosity: 20000 cP @Temperature 25.0 °C
- Hardness, Shore D: >= 70 @Temperature 120 °C
- Hardness, Shore D: 90 @Temperature 25.0 °C
$ 1504/MT
- Density: 1.10 g/cc
- Water Absorption: 0.20 - 0.35 %
- Water Absorption: 0.30 - 0.45 %
- Viscosity: 3500 - 6500 cP
- Viscosity: 30 - 60 cP @Temperature 60.0 °C
$ 2108/MT
- Density: 1.33 g/cc
- Solids Content: 81 %
- Hardness, Shore A: 23
- Tensile Strength at Break: 0.0276 MPa
- Elongation at Break: 1000 %
$ 1479/MT
- Water Absorption: 3.1 % @Time 7200 sec
- Water Absorption: 5.0 % @Time 2.59e+6 sec
- Water Absorption: 5.0 % @Time 2.59e+6 sec
- Water Absorption: 5.2 % @Time 2.59e+6 sec
- Viscosity: 1120 cP
$ 2372/MT
- Viscosity Measurement: 700
- Hardness, Rockwell M: 70
- Tensile Strength, Ultimate: 47.09 MPa
- Elongation at Break: 9.1 %
- Flexural Yield Strength: 64.8 MPa
$ 1474/MT
- Water Absorption: 6.2 % @Time 7200 sec
- Water Absorption: 11.9 % @Time 2.59e+6 sec
- Water Absorption: 12.2 % @Time 2.59e+6 sec
- Viscosity: 2570 cP
- Hardness, Shore A: 11 @Temperature 75.0 °C
$ 1990/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 60.0 °C
- Carbon, C: 69 %
- Surface Resistivity per Square: <= 0.010 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1988/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 50.0 °C
- Carbon, C: 7.2 %
- Surface Resistivity per Square: <= 200000 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1508/MT
- Density: 1.14 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 42.1 MPa
- Elongation at Break: 11 %
- Tensile Modulus: 1.54 GPa
$ 1625/MT
- Solids Content: 100 %
- Hardness, Shore D: >= 80
- Tensile Strength at Break: 35.2 MPa
- Flexural Strength: 57.2 MPa
- Flexural Modulus: 1.45 GPa
$ 1934/MT
- Tensile Strength at Break: 49.9 MPa
- Elongation at Break: 1.34 %
- Tensile Modulus: 6.76 GPa
- Maximum Service Temperature, Air: 126 °C
- Volume Resistivity: 3.00e+13 ohm-cm
$ 1925/MT
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 55.0 MPa
- Compressive Yield Strength: 62.0 MPa
- Maximum Service Temperature, Air: 100 - 110 °C
$ 1823/MT
- Volatile Organic Compounds (VOC) Content: 0.00 g/l
- Elongation at Break: 7.6 %
- Compressive Strength: 124 MPa
- Adhesive Bond Strength: 13.01 MPa
- Coefficient of Friction: 1.43
$ 1492/MT
- Specific Gravity: 1.06 g/cc
- Volatile Organic Compounds (VOC) Content: 335.5 g/l
- Viscosity: 100 - 400 cP
- Tensile Strength at Break: 40.7 MPa
- Elongation at Break: 190 %
$ 1908/MT
- Viscosity Measurement: 60 @Temperature 70.0 °C
- Hardness, Rockwell M: 96
- Tensile Strength, Ultimate: 79.22 MPa
- Elongation at Break: 18.2 %
- Flexural Yield Strength: 131 MPa
$ 1625/MT
- Viscosity: 8000 cP @Temperature 25.0 °C
- Thermal Conductivity: 0.167 - 0.201 W/m-K
- Maximum Service Temperature, Air: 295 °C
- Pot Life: 840 min @Temperature 25.0 °C
$ 2592/MT
- Density: 1.19 g/cc
- Water Absorption: 0.30 - 0.40 %
- Water Absorption: 0.60 - 1.0 %
- Viscosity: 4500 - 6000 cP
- Vapor Pressure: <= 0.0000133 bar @Temperature 20.0 °C
$ 1513/MT
- Water Absorption: 1.1 % @Time 28800 sec
- Viscosity: 400 cP
- Hardness, Shore D: 85
- Tensile Strength, Ultimate: 67.78 MPa
- Flexural Strength: 103.05 MPa
$ 1463/MT
- Solids Content: 79 %
- Maximum Service Temperature, Air: 70.0 °C
- Carbon, C: 15 %
- Surface Resistivity per Square: <= 200000 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1448/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 50.0 °C
- Carbon, C: 6.8 %
- Surface Resistivity per Square: <= 300000 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1488/MT
- Water Absorption: 0.10 - 0.50 %
- Linear Mold Shrinkage: 0.0010 cm/cm
- Hardness, Shore D: >= 85
- Tensile Strength at Break: 35.9 MPa
- Elongation at Break: 3.6 %
$ 1513/MT
- Viscosity: 11000 - 14000 cP
- Viscosity: 110 cP @Temperature 70.0 °C
- Hardness, Rockwell M: 106
- Tensile Strength, Ultimate: 65.84 MPa
- Elongation at Break: 4.4 %
$ 1730/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 120 °C
- Surface Resistivity per Square: <= 0.010 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
- Cure Time: >= 1440 min @Temperature 22.0 - 30.0 °C
$ 2261/MT
- Viscosity: 150 cP @Temperature 80.0 °C
- Tensile Strength at Break: 49.0 MPa
- Flexural Strength: 101 MPa
- Compressive Strength: 256 MPa
- Thermal Conductivity: 0.167 - 0.201 W/m-K
$ 2077/MT
- Water Absorption: 4.5 % @Time 2.59e+6 sec
- Water Absorption: 4.5 % @Time 2.59e+6 sec
- Water Absorption: 4.9 % @Time 7200 sec
- Water Absorption: 5.3 % @Time 2.59e+6 sec
- Viscosity: 1270 cP
$ 1636/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 60.0 °C
- Carbon, C: 4.4 %
- Surface Resistivity per Square: <= 6.00e+6 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1955/MT
- Density: 1.23 g/cc
- Water Absorption: 0.25 - 0.30 %
- Water Absorption: 0.25 - 0.30 %
- Viscosity: 50 - 150 cP @Temperature 60.0 °C
- Viscosity: 200 - 400 cP @Temperature 40.0 °C
$ 2096/MT
- Maximum Service Temperature, Air: 85.0 °C
- Pot Life: 120 min @Temperature 25.0 °C
- Color: Green
- Hardening Time (min): 180 to 480
- Parts by Weight (pbw): 100
$ 1524/MT
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 1.2 %
- Tensile Modulus: 10.0 GPa
- Maximum Service Temperature, Air: 150 °C
- Volume Resistivity: 8.00e+13 ohm-cm
$ 1549/MT
- Viscosity: 1.0 cP
- Viscosity: 4000 - 6000 cP
- Viscosity: 900 cP @Temperature 25.0 °C
- Hardness, Rockwell M: 107
- Tensile Strength, Ultimate: 66.32 MPa
$ 1755/MT
- Hardness, Shore D: 80
- Tensile Strength, Ultimate: 55.0 MPa
- Compressive Yield Strength: 62.0 MPa
- Maximum Service Temperature, Air: 75.0 °C
$ 1877/MT
- Water Absorption: 2.3 % @Time 7200 sec
- Viscosity: 1650 cP
- Hardness, Shore D: 76 @Temperature 75.0 °C
- Hardness, Shore D: 85 @Temperature 25.0 °C
- Hardness, Shore D: 87 @Temperature 0.000 °C
$ 2064/MT
- Density: 1.18 g/cc
- Water Absorption: 0.30 - 0.40 %
- Water Absorption: 0.40 - 0.50 %
- Viscosity: 1000 - 2000 cP @Temperature 40.0 °C
- Viscosity: 10000 - 15000 cP @Temperature 21.0 °C
$ 1923/MT
- Density: 1.14 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 77.9 MPa
- Elongation at Break: 4.9 %
- Tensile Modulus: 2.84 GPa
$ 2125/MT
- Density: 0.959 g/cc
- Density: 3.12 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 2007/MT
- Viscosity: 4000 - 6000 cP
- Viscosity: 14000 - 20000 cP
- Viscosity: 6500 cP @Temperature 25.0 °C
- Hardness, Rockwell M: 82
- Tensile Strength, Ultimate: 46.95 MPa
$ 1936/MT
- Density: 0.971 g/cc
- Density: 1.09 g/cc
- Water Absorption: 0.10 - 0.20 %
- Viscosity: 300 - 500 cP
- Hardness, Shore D: 85 @Temperature 100 °C, Time 10800 sec
$ 1491/MT
- Solids Content: 100 %
- Hardness, Shore A: 48 - 50
- Tensile Strength at Break: 1.86 MPa
- Elongation at Break: 800 %
- Color: Brown, Black, or other Dark Colors
$ 1556/MT
- Cure Time: 30.0 - 60.0 min @Temperature 80.0 - 120 °C
- Cure Time: 2880 - 10080 min @Temperature 20.0 °C
- Pot Life: 30 - 40 min @Temperature 25.0 °C
- Hardening Time (min): 30-180
$ 1681/MT
- Water Absorption: 4.5 % @Time 2.59e+6 sec
- Water Absorption: 4.6 % @Time 2.59e+6 sec
- Water Absorption: 4.6 % @Time 7200 sec
- Water Absorption: 4.7 % @Time 2.59e+6 sec
- Viscosity: 1050 cP
$ 2165/MT
- Solids Content: 77 %
- Maximum Service Temperature, Air: 70.0 °C
- Carbon, C: 20 %
- Surface Resistivity per Square: <= 1e+05
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1516/MT
- Viscosity: 500 cP
- Hardness, Shore D: 89
- Tensile Strength at Break: 63.4 MPa
- Elongation at Break: 14 %
- Flexural Strength: 97.9 MPa
$ 1513/MT
- Volatile Organic Compounds (VOC) Content: 257.6 g/l
- Adhesive Bond Strength: 2.05 MPa
- Coefficient of Friction: 1.3
- Flash Point: 100 °C
- Abrasive Resistance (g): 0.101
- Hardening Time (min): 120
$ 1821/MT
- Density: 1.17 g/cc
- Density: 2.76 g/cc
- Hardness, Shore D: 83 - 87
- Tensile Strength at Break: 3.45 - 41.4 MPa
- Flexural Strength: 3.45 - 48.3 MPa
$ 2001/MT
- Water Absorption: 4.5 % @Time 7200 sec
- Viscosity: 2300 cP
- Hardness, Shore D: 46 @Temperature 75.0 °C
- Hardness, Shore D: 79 @Temperature 25.0 °C
- Hardness, Shore D: 86 @Temperature 0.000 °C
$ 1798/MT
- Maximum Service Temperature, Air: 160 °C
- Pot Life: 360 - 480 min @Temperature 25.0 °C
- Color: Green
- Hardening Time (min): 36 to 60
- Parts by Weight (pbw): 100
$ 1803/MT
- Density: 0.935 g/cc
- Density: 1.09 g/cc
- Water Absorption: 0.10 - 0.30 %
- Viscosity: 500 - 700 cP
- Hardness, Shore D: 75 @Temperature 100 °C, Time 10800 sec
$ 1634/MT
- Density: 0.947 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 140 %
- Maximum Service Temperature, Air: <= 25.0 °C
$ 2403/MT
- Water Absorption: 0.70 % @Time 86400 sec
- Hardness, Shore D: 14 @Time 601 sec
- Hardness, Shore D: 39 @Time 1800 sec
- Hardness, Shore D: 70 @Time 3600 sec
- Hardness, Shore D: 78 @Time 86400 sec
$ 1766/MT
- Density: 0.947 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 140 %
- Maximum Service Temperature, Air: <= 25.0 °C
$ 1682/MT
- Density: 0.935 g/cc
- Density: 1.09 g/cc
- Water Absorption: 0.20 - 0.40 %
- Viscosity: 350 - 500 cP
- Hardness, Shore D: 60 @Temperature 100 °C, Time 10800 sec
$ 1529/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 90.0 °C
- Carbon, C: 64 %
- Surface Resistivity per Square: <= 0.50 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 1632/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 90.0 °C
- Carbon, C: 64 %
- Surface Resistivity per Square: <= 0.50 ohm
- Cure Time: 30.0 - 180 min @Temperature 50.0 - 100 °C
$ 2418/MT
- Viscosity: 200 cP
- Hardness, Rockwell M: 88
- Tensile Strength at Break: 57.9 MPa
- Elongation at Break: 5.1 %
- Flexural Strength: 83.4 MPa
$ 1741/MT
- Water Absorption: 4.4 % @Time 2.59e+6 sec
- Water Absorption: 4.4 % @Time 2.59e+6 sec
- Water Absorption: 4.9 % @Time 7200 sec
- Water Absorption: 5.4 % @Time 2.59e+6 sec
- Viscosity: 1390 cP
$ 2176/MT
- Water Absorption: 7.4 % @Time 2.59e+6 sec
- Water Absorption: 7.5 % @Time 2.59e+6 sec
- Viscosity: 2440 cP
- Hardness, Shore A: 63 @Temperature 75.0 °C
- Hardness, Shore A: 64 @Temperature 25.0 °C
$ 2449/MT
- Water Absorption: 2.5 % @Time 7200 sec
- Viscosity: 2000 cP
- Hardness, Shore D: 75 @Temperature 75.0 °C
- Hardness, Shore D: 83 @Temperature 25.0 °C
- Hardness, Shore D: 87 @Temperature 0.000 °C
$ 1750/MT
- Density: 1.22 g/cc
- Water Absorption: 0.15 - 0.20 %
- Water Absorption: 0.20 - 0.30 %
- Viscosity: 1000 - 2500 cP
- Vapor Pressure: <= 0.0000267 bar @Temperature 50.0 °C
$ 2533/MT
- Viscosity: 30000 cP @Temperature 25.0 °C
- Thermal Conductivity: 0.586 - 0.795 W/m-K
- Maximum Service Temperature, Air: 300 °C
- Pot Life: 1200 min @Temperature 25.0 °C
$ 1798/MT
- Viscosity: 17000 cP @Temperature 25.0 °C
- Thermal Conductivity: 0.167 - 0.201 W/m-K
- Maximum Service Temperature, Air: 259 °C
$ 1696/MT
- Solids Content: 100 %
- Viscosity: <= 1200 cP
- Hardness, Shore D: 35
- Hardness, Shore D: 65
- Hardness, Shore D: 75
$ 1912/MT
- Viscosity: 1800 cP
- Hardness, Shore D: 78
- Tensile Strength, Ultimate: 37.9 MPa
- Elongation at Break: 15.1 %
- Izod Impact, Notched: 0.598 J/cm
Delivery Thermoset Abatron
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
crude oil tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.