$ 2233/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore D: 36
- Tensile Strength, Ultimate: 43.0 MPa
- Elongation at Break: 550 %
- 50% Modulus: 0.00510 GPa
$ 1491/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 35.0 MPa
- Elongation at Break: 650 %
- Tensile Modulus: 0.0200 GPa
$ 1567/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Ultimate: 26.2 MPa
- Elongation at Break: 450 %
- Volume Resistivity: 5.00e+9 ohm-cm
- Surface Resistivity per Square: 5.00e+9 ohm
$ 1539/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 92 - 98 @Time 5.00 sec
- Tensile Strength: 33.9 MPa
- Elongation at Break: 370 %
$ 1692/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 15 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C
- Hardness, Shore D: 52
- Tensile Strength, Ultimate: 56.0 MPa
$ 2208/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 37.0 MPa
- Elongation at Break: 625 %
- 50% Modulus: 0.00480 GPa
$ 1525/MT
- Specific Gravity: 1.45 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0015 cm/cm
- Hardness, Shore D: 72
- Tensile Strength, Ultimate: 78.0 MPa
$ 1980/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 39.0 MPa
- Elongation at Break: 540 %
- Tensile Modulus: 0.0240 GPa
$ 1663/MT
- Specific Gravity: 1.41 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0015 cm/cm
- Hardness, Shore D: 74
- Tensile Strength, Ultimate: 77.0 MPa
$ 1997/MT
- Specific Gravity: 1.06 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Ultimate: 29.0 MPa
- Elongation at Break: 720 %
- Tensile Modulus: 0.0110 GPa
$ 2429/MT
- Specific Gravity: 1.64 g/cc
- Filler Content: 50 %
- Linear Mold Shrinkage: 0.0013 cm/cm
- Hardness, Shore D: 75
- Tensile Strength, Ultimate: 93.0 MPa
$ 1737/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 89 - 95 @Time 5.00 sec
- Tensile Strength: 58.99 MPa
- Tensile Strength: 60.85 MPa
$ 1949/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0070 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore A: 94
$ 2536/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.00 - 0.0060 cm/cm
- Melt Flow: 24 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 88
$ 1757/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore D: 55
- Tensile Strength, Ultimate: 53.0 MPa
- Elongation at Break: 500 %
- Tensile Modulus: 0.125 GPa
$ 1578/MT
- Specific Gravity: 1.19 g/cc
- Viscosity: 1800 - 2400 cP
- Hardness, Shore A: 84
- Tensile Strength, Ultimate: 45.0 MPa
- Elongation at Break: 670 %
$ 1624/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 7.0 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 90
$ 1453/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 5.0 - 15 g/10 min @Load 8.70 kg, Temperature 175 °C
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 30.0 MPa
$ 2260/MT
- Specific Gravity: 1.35 g/cc
- Filler Content: 18 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Shore D: 72
- Tensile Strength, Ultimate: 59.0 MPa
$ 1960/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 37.0 MPa
- Elongation at Break: 650 %
- 50% Modulus: 0.00500 GPa
$ 1520/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 630 %
- 50% Modulus: 0.00590 GPa
$ 1527/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore D: 49 @Time 5.00 sec
- Tensile Strength: 65.5 MPa
- Tensile Strength: 65.5 MPa @Temperature 23.0 °C, Time 0.000 sec
$ 1917/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.00 - 0.0060 cm/cm
- Melt Flow: 20 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 83
$ 1460/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 95
- Tensile Strength, Yield: 37.9 MPa
- Elongation at Break: 700 %
- 100% Modulus: 0.0103 GPa
$ 2061/MT
- Specific Gravity: 1.24 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0080 cm/cm
- Linear Mold Shrinkage: 0.0090 cm/cm
- Hardness, Shore D: 62 - 68 @Time 5.00 sec
$ 1579/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 @Time 5.00 sec
- Tensile Strength: 37.9 MPa
- Tensile Strength: 28.42 MPa @Temperature 75.0 °C, Time 4.838e+6 sec
$ 1845/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 39.0 MPa
- Elongation at Break: 680 %
- 50% Modulus: 0.00380 GPa
$ 1587/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 840 %
- 50% Modulus: 0.00150 GPa
$ 1825/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 10 - 25 g/10 min @Load 8.70 kg, Temperature 210 °C
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 45.0 MPa
$ 1694/MT
- Specific Gravity: 1.17 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 57 - 63 @Time 5.00 sec
- Tensile Strength: 49.0 MPa
- Tensile Strength, Ultimate: 28.91 MPa @Temperature 70.0 °C, Time 3.629e+6 sec
$ 1813/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 24.8 MPa
- Elongation at Break: 800 %
- Taber Abrasion, mg/1000 Cycles: 3.5
$ 1494/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 31.0 MPa
- Elongation at Break: 655 %
- 50% Modulus: 0.00490 GPa
$ 1469/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 72 - 78 @Time 5.00 sec
- Tensile Strength: 37.9 MPa
- Elongation at Break: 680 %
$ 1554/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0060 cm/cm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore A: 90
$ 1765/MT
- Specific Gravity: 1.11 g/cc
- Viscosity: 72000 cP @Temperature 204 °C
- Brookfield Viscosity: 900 cP
- Brookfield Viscosity: 3700 cP
- Hardness, Shore A: 80
$ 1535/MT
- Specific Gravity: 1.31 g/cc
- Filler Content: 10 %
- Filler Content: 10 %
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.00060 cm/cm
$ 1464/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 88
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 760 %
- 100% Modulus: 0.00520 GPa
$ 1784/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 1.59 mm
- Linear Mold Shrinkage, Transverse: -0.00100 - 0.0040 cm/cm @Thickness 1.59 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 224 °C
- Hardness, Shore A: 81 - 89
$ 1514/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 90
- Hardness, Shore D: 47
- Tensile Strength at Break: 26.0 MPa
- Elongation at Break: 450 %
$ 2100/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 54
- Tensile Strength, Ultimate: 14.0 MPa
- Elongation at Break: 380 %
$ 1800/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0090 cm/cm
- Melt Flow: 15 g/10 min @Load 0.160 kg, Temperature 224 °C
- Hardness, Shore A: 96
$ 1525/MT
- Specific Gravity: 1.31 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore D: 65 - 71 @Time 5.00 sec
- Tensile Strength: 40.0 MPa
- Elongation at Break: 40 %
$ 1560/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 77 - 83 @Time 5.00 sec
- Tensile Strength: 23.4 MPa
- Elongation at Break: 710 %
$ 1519/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 87 - 93 @Time 5.00 sec
- Tensile Strength: 65.5 MPa
- Elongation at Break: 500 %
$ 1917/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0090 cm/cm
- Linear Mold Shrinkage: 0.013 cm/cm
- Hardness, Shore D: 42 - 48 @Time 5.00 sec
$ 2237/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 20 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C
- Hardness, Shore A: 98
- Hardness, Shore D: 56
$ 1938/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Melt Flow: 9.0 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 90
$ 2033/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 45.0 MPa
- Elongation at Break: 610 %
- Tensile Modulus: 0.0290 GPa
$ 1555/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: -0.00300 - 0.0080 cm/cm
- Melt Flow: 11 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 72
$ 2051/MT
- Specific Gravity: 1.44 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.00070 cm/cm
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Shore D: 55 - 61 @Time 5.00 sec
$ 2379/MT
- Specific Gravity: 1.24 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 10 - 35 g/10 min @Load 8.70 kg, Temperature 205 °C
- Hardness, Shore A: 95
- Hardness, Shore D: 50
$ 1473/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0080 cm/cm @Thickness 1.59 mm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0080 cm/cm @Thickness 1.59 mm
- Melt Flow: 23 g/10 min @Load 8.70 kg, Temperature 190 °C
- Hardness, Shore A: 88 - 96
$ 1895/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0014 cm/cm
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 44.8 MPa
$ 2572/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 42.0 MPa
- Elongation at Break: 655 %
- 50% Modulus: 0.00490 GPa
$ 1606/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Ultimate: 53.1 MPa
- Elongation at Break: 300 %
- Flexural Modulus: 1.03 GPa
$ 1476/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 224 °C
- Hardness, Shore D: 58
$ 1616/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 630 %
- 50% Modulus: 0.00590 GPa
$ 1674/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 40 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 34.5 MPa
- Elongation at Break: 600 %
$ 1510/MT
- Specific Gravity: 1.22 g/cc
- Viscosity: 85000 cP @Temperature 204 °C
- Brookfield Viscosity: 600 cP
- Hardness, Shore A: 90
- Hardness, Shore D: 45
$ 1622/MT
- Specific Gravity: 1.17 g/cc
- Loss On Ignition: 30 %
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 27.6 MPa
$ 1865/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 45.0 MPa
- Elongation at Break: 535 %
- Tensile Modulus: 0.327 GPa
$ 1695/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 43 - 49
- Elongation at Break: 400 %
- 100% Modulus: 0.0135 GPa
$ 1765/MT
- Specific Gravity: 1.16 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore D: 47 - 53 @Time 5.00 sec
- Tensile Strength: 60.0 MPa
- Tensile Strength, Ultimate: 46.8 MPa @Temperature 70.0 °C, Time 3.629e+6 sec
$ 1479/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 28.0 MPa
- Elongation at Break: 725 %
- 50% Modulus: 0.00410 GPa
$ 1522/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore D: 50
- Tensile Strength, Ultimate: 48.0 MPa
- Elongation at Break: 530 %
- 50% Modulus: 0.00920 GPa
$ 1931/MT
- Specific Gravity: 1.22 g/cc
- Viscosity: 670 - 1290 cP
- Hardness, Shore A: 93
- Hardness, Shore D: 44
- Tensile Strength, Ultimate: 63.0 MPa
$ 1996/MT
- Specific Gravity: 1.19 g/cc
- Viscosity: 460 - 680 cP
- Hardness, Shore A: 65
- Tensile Strength, Ultimate: 37.0 MPa
- Elongation at Break: 590 %
$ 1662/MT
- Specific Gravity: 1.32 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Shore D: 63 - 69 @Time 5.00 sec
$ 2142/MT
- Specific Gravity: 1.08 g/cc
- Hardness, Shore A: 74
- Tensile Strength, Ultimate: 26.2 MPa
- Elongation at Break: 660 %
- Compression Set: 24 %
$ 2060/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 28.0 MPa
- Elongation at Break: 730 %
- 50% Modulus: 0.00400 GPa
$ 1462/MT
- Specific Gravity: 1.25 g/cc
- Loss On Ignition: 32 %
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 27.6 MPa
$ 1451/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore D: 57
- Tensile Strength, Ultimate: 39.0 MPa
- Elongation at Break: 545 %
- 50% Modulus: 0.0129 GPa
$ 1478/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 40.7 MPa
- Elongation at Break: 600 %
$ 1521/MT
- Specific Gravity: 1.21 g/cc
- Brookfield Viscosity: 50 cP
- Brookfield Viscosity: 440 cP
- Hardness, Shore D: 54
- Tensile Strength: 46.2 MPa
$ 2546/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 29.0 MPa
- Elongation at Break: 730 %
- Tensile Modulus: 0.0100 GPa
$ 1447/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 39
- Tensile Strength, Ultimate: 20.0 MPa
- Elongation at Break: 620 %
$ 1565/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 37.0 MPa
- Elongation at Break: 625 %
- 50% Modulus: 0.00480 GPa
$ 1812/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0010 - 0.0050 cm/cm
- Melt Index of Compound: 52 g/10 min @Load 8.70 kg, Temperature 190 °C
- Hardness, Shore A: 87
$ 2098/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore D: 70
- Tensile Strength, Ultimate: 42.0 MPa
- Elongation at Break: 355 %
- 50% Modulus: 0.0204 GPa
$ 1768/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 36.0 MPa
- Elongation at Break: 530 %
$ 2316/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 33.0 MPa
- Elongation at Break: 630 %
- 50% Modulus: 0.00460 GPa
$ 1507/MT
- Specific Gravity: 1.53 g/cc
- Hardness, Shore A: 90
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: 20.0 MPa
- Elongation at Break: 625 %
$ 1979/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Shore A: 67 - 73 @Time 5.00 sec
- Tensile Strength: 22.1 MPa
- Tensile Stress: 2.60 MPa @Strain 100 %
- Tensile Stress: 4.50 MPa @Strain 300 %
$ 1574/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 700 - 1000 cP
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 58.0 MPa
- Elongation at Break: 500 %
$ 1737/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 4.0 g/10 min @Load 8.70 kg, Temperature 190 °C
- Hardness, Shore A: 84
$ 1767/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.0090 cm/cm
- Melt Flow: 40 g/10 min @Load 5.00 kg, Temperature 224 °C
- Hardness, Shore D: 62
$ 1815/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: -0.00200 - 0.0050 cm/cm
- Melt Flow: 40 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore A: 82
$ 1750/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 90
- Hardness, Shore D: 44
- Tensile Strength, Ultimate: 46.0 MPa
- Elongation at Break: 540 %
$ 1574/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 645 %
- 50% Modulus: 0.00470 GPa
$ 1934/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 20 - 40 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore A: 92
- Tensile Strength, Ultimate: 45.0 MPa
$ 1534/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 48.3 MPa
- Elongation at Break: 550 %
$ 1636/MT
- Specific Gravity: 1.19 g/cc
- Viscosity: 2800 - 4000 cP
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: 49.0 MPa
$ 1725/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 40 - 90 cP
- Hardness, Shore D: 79
- Tensile Strength, Ultimate: 34.0 MPa
- Elongation at Break: 110 %
$ 1587/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 1.60 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0060 cm/cm @Thickness 1.60 mm
- Melt Flow: 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 224 °C
- Hardness, Shore D: 51 - 59
$ 2355/MT
- Specific Gravity: 1.24 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 20 - 35 g/10 min @Load 8.70 kg, Temperature 217 °C
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 42.0 MPa
$ 1508/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 89 - 95 @Time 18000 sec
- Tensile Strength: 58.6 MPa
- Tensile Stress: 6.90 MPa @Strain 100 %
$ 1572/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 30.0 MPa
- Elongation at Break: 700 %
- 50% Modulus: 0.00430 GPa
$ 1620/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0070 cm/cm
- Melt Flow: 28 g/10 min @Load 5.00 kg, Temperature 224 °C
- Hardness, Shore D: 76
$ 1792/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 87 - 93 @Time 5.00 sec
- Tensile Strength: 38.3 MPa
- Elongation at Break: 525 %
$ 1741/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0060 cm/cm
- Melt Flow: 32 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore A: 90
$ 1862/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 47.0 MPa
- Elongation at Break: 550 %
$ 1729/MT
- Specific Gravity: 1.17 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 72 - 78 @Time 5.00 sec
- Tensile Strength: 48.3 MPa
- Elongation at Break: 650 %
$ 2125/MT
- Specific Gravity: 1.19 g/cc
- Loss On Ignition: 28 %
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 87 - 93 @Time 5.00 sec
- Tensile Strength: 13.8 MPa
$ 1725/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0090 cm/cm
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 224 °C
- Hardness, Shore D: 64
$ 1530/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 52.0 MPa
- Elongation at Break: 510 %
$ 2315/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore D: 73
- Tensile Strength, Ultimate: 27.0 MPa
- Elongation at Break: 250 %
- 50% Modulus: 0.0272 GPa
$ 1445/MT
- Specific Gravity: 1.28 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0023 cm/cm
- Hardness, Shore D: 57
- Tensile Strength, Ultimate: 32.0 MPa
$ 1618/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0050 cm/cm
- Melt Flow: 6.0 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 92
$ 1686/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Melt Flow: 30 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore D: 53
$ 1612/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 800 %
- 50% Modulus: 0.00350 GPa
$ 1944/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 800 %
- 50% Modulus: 0.00350 GPa
$ 1719/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 95
- Tensile Strength, Ultimate: 49.0 MPa
- Elongation at Break: 620 %
- 50% Modulus: 0.00810 GPa
$ 1740/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 20 - 40 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Hardness, Shore D: 37
$ 2159/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Hardness, Shore D: 30
- Tensile Strength, Ultimate: 35.0 MPa
- Elongation at Break: 760 %
$ 1506/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: -0.00100 - 0.0060 cm/cm
- Melt Flow: 28 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 83
$ 1848/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0060 cm/cm
- Linear Mold Shrinkage: 0.0090 cm/cm
- Hardness, Shore A: 87 - 93 @Time 5.00 sec
$ 1455/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 48.3 MPa
- Tensile Strength: 33.81 MPa @Temperature 75.0 °C, Time 4.838e+6 sec
$ 2213/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 31.0 MPa
- Elongation at Break: 700 %
- 50% Modulus: 0.00400 GPa
$ 1483/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 130000 cP @Temperature 204 °C
- Brookfield Viscosity: 800 - 1300 cP
- Hardness, Shore A: 40
- Tensile Strength: 37.9 MPa
$ 1634/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 800 %
- 50% Modulus: 0.00350 GPa
$ 2235/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 36.0 MPa
- Elongation at Break: 435 %
- 50% Modulus: 0.0175 GPa
$ 2163/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: -0.00200 - 0.0060 cm/cm
- Melt Flow: 13 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 86
$ 2321/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 30.0 MPa
- Elongation at Break: 540 %
$ 1771/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 37.0 MPa
- Elongation at Break: 640 %
- 50% Modulus: 0.00550 GPa
$ 2049/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 5.0 - 20 g/10 min @Load 8.70 kg, Temperature 210 °C
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 48.0 MPa
$ 2305/MT
- Specific Gravity: 1.21 g/cc
- Viscosity: 600 - 1200 cP
- Hardness, Shore A: 93
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 68.0 MPa
$ 1567/MT
- Specific Gravity: 1.22 g/cc
- Water Vapor Transmission: 500 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 3000 g/m²/day @Temperature 38.0 °C
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0080 cm/cm
$ 1521/MT
- Specific Gravity: 1.21 g/cc
- Brookfield Viscosity: 60 - 70 cP
- Brookfield Viscosity: 70 - 80 cP
- Brookfield Viscosity: 180 - 200 cP
- Hardness, Shore D: 78
$ 1618/MT
- Specific Gravity: 1.17 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore D: 57 - 63 @Time 5.00 sec
- Tensile Strength: 53.8 MPa
- Tensile Strength, Ultimate: 46.268 MPa @Temperature 70.0 °C, Time 3.629e+6 sec
$ 1674/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: 670 %
- 100% Modulus: 0.00510 GPa
$ 1565/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 74
- Tensile Strength, Ultimate: 43.4 MPa
- Elongation at Break: 660 %
- Compression Set: 21 %
$ 1953/MT
- Specific Gravity: 1.21 g/cc
- Viscosity: 2400 cP
- Viscosity: 28000 cP @Temperature 204 °C
- Brookfield Viscosity: 475 cP
- Hardness, Shore A: 85
$ 1906/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 83
- Hardness, Shore D: 30
- Tensile Strength, Ultimate: 32.0 MPa
- Elongation at Break: 790 %
$ 1632/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm
- Melt Flow: 7.0 g/10 min @Load 8.70 kg, Temperature 224 °C
- Hardness, Shore A: 85
$ 1533/MT
- Specific Gravity: 1.16 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 15 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C
- Hardness, Shore A: 98
- Hardness, Shore D: 55
$ 2111/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 40.0 MPa
- Elongation at Break: 650 %
- 50% Modulus: 0.00490 GPa
$ 1456/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 42.0 MPa
- Elongation at Break: 655 %
- 50% Modulus: 0.00490 GPa
$ 2022/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: 51.0 MPa
- Elongation at Break: 530 %
$ 1931/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 800 %
- 50% Modulus: 0.00350 GPa
$ 1934/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 89
- Hardness, Shore D: 37
- Tensile Strength, Ultimate: 44.0 MPa
- Elongation at Break: 625 %
$ 1829/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 550 %
- 50% Modulus: 0.00920 GPa
$ 1599/MT
- Specific Gravity: 1.16 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 52 - 58 @Time 5.00 sec
- Tensile Strength: 57.9 MPa
- Tensile Strength, Ultimate: 49.21 MPa @Temperature 70.0 °C, Time 3.629e+6 sec
$ 2129/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 31.7 MPa
- Elongation at Break: 450 %
$ 2036/MT
- Specific Gravity: 1.21 g/cc
- Water Vapor Transmission: 650 g/m²/day
- Water Vapor Transmission: 6500 g/m²/day
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 77 - 83 @Time 5.00 sec
$ 1606/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 15 - 40 g/10 min @Load 8.70 kg, Temperature 215 °C
- Hardness, Shore A: 92
- Tensile Strength, Ultimate: 43.0 MPa
$ 1837/MT
- Specific Gravity: 1.29 g/cc
- Loss On Ignition: 32 %
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 87 - 93 @Time 5.00 sec
- Tensile Strength: 27.9 MPa
$ 1550/MT
- Specific Gravity: 1.19 g/cc
- Brookfield Viscosity: 200 cP
- Brookfield Viscosity: 1500 cP
- Hardness, Shore A: 80
- Tensile Strength: 50.3 MPa
$ 1540/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0090 cm/cm
- Melt Flow: 13 g/10 min @Load 8.70 kg, Temperature 190 °C
- Hardness, Shore A: 94
$ 1764/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 47.0 MPa
- Elongation at Break: 530 %
$ 1654/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 1.60 mm
- Linear Mold Shrinkage, Transverse: -0.00200 - 0.0050 cm/cm @Thickness 1.60 mm
- Melt Flow: 39 g/10 min @Load 8.70 kg, Temperature 190 °C
- Hardness, Shore A: 80 - 88
$ 1513/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 60 - 100 cP
- Hardness, Shore D: 63
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 220 %
$ 1830/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Ultimate: 25.0 MPa
- Elongation at Break: 700 %
- 50% Modulus: 0.00270 GPa
$ 2204/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.050
- Hardness, Shore A: 92
- Tensile Strength, Ultimate: 45.0 MPa
- Elongation at Break: 580 %
$ 1490/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 37.2 MPa
- Tensile Strength, Ultimate: 37.2 MPa
$ 1566/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Ultimate: 41.0 MPa
- Elongation at Break: 345 %
- 50% Modulus: 0.0254 GPa
$ 1527/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage: 0.010 cm/cm
- Hardness, Shore D: 47 - 53 @Time 5.00 sec
$ 2119/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 100 - 200 cP
- Hardness, Shore A: 95
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 54.0 MPa
$ 1500/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 30.0 MPa
- Elongation at Break: 650 %
- 50% Modulus: 0.00410 GPa
$ 1602/MT
- Specific Gravity: 1.45 g/cc
- Filler Content: 30 %
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.00040 cm/cm
- Linear Mold Shrinkage: 0.0010 cm/cm
$ 1828/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 30.0 MPa
- Elongation at Break: 650 %
- 50% Modulus: 0.00500 GPa
$ 2282/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 30 - 70 cP
- Hardness, Shore A: 95
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 54.0 MPa
$ 1446/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 640 %
- 50% Modulus: 0.00550 GPa
$ 1636/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 89 - 95 @Time 5.00 sec
- Tensile Strength: 62.1 MPa
- Tensile Strength: 62.1 MPa @Temperature 23.0 °C, Time 0.000 sec
$ 1698/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 48
- Tensile Strength, Ultimate: 33.0 MPa
- Elongation at Break: 485 %
$ 1475/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Ultimate: 30.0 MPa
- Elongation at Break: 500 %
- 50% Modulus: 0.00800 GPa
$ 1726/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 48
- Tensile Strength, Ultimate: 52.0 MPa
- Elongation at Break: 560 %
$ 1752/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 48
- Tensile Strength, Ultimate: 52.0 MPa
- Elongation at Break: 560 %
$ 2107/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 48
- Tensile Strength, Ultimate: 52.0 MPa
- Elongation at Break: 560 %
$ 1646/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 48
- Tensile Strength, Ultimate: 52.0 MPa
- Elongation at Break: 560 %
$ 1936/MT
- Specific Gravity: 1.18 g/cc
- Loss On Ignition: 28 %
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 77 - 83 @Time 5.00 sec
- Tensile Strength: 29.7 MPa
$ 1633/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 83
- Tensile Strength: 11.5 MPa
- Tensile Strength: 4.52 MPa @Strain 50.0 %
- Tensile Strength: 5.21 MPa @Strain 100 %
$ 1729/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 51.7 MPa
- Elongation at Break: 615 %
$ 1486/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 10 - 25 g/10 min @Load 8.70 kg, Temperature 170 °C
- Hardness, Shore A: 63
- Tensile Strength, Ultimate: 28.0 MPa
$ 1611/MT
- Specific Gravity: 1.20 g/cc
- Brookfield Viscosity: 5500 cP
- Hardness, Shore A: 85
- Tensile Strength: 42.1 MPa
- Elongation at Break: 490 %
$ 1561/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 42.0 MPa
- Elongation at Break: 650 %
- 50% Modulus: 0.00510 GPa
$ 1556/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Hardness, Shore D: 57 - 63 @Time 5.00 sec
$ 1818/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 84 - 90 @Time 5.00 sec
- Tensile Strength: 51.7 MPa
- Tensile Strength: 38.78 MPa @Temperature 75.0 °C, Time 4.838e+6 sec
$ 2293/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage: 0.014 cm/cm
- Hardness, Shore A: 82 - 88 @Time 5.00 sec
- Tensile Strength: 48.3 MPa
$ 1726/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 43
- Tensile Strength, Ultimate: 8.00 MPa
- Elongation at Break: 430 %
$ 1928/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: -0.00200 - 0.0050 cm/cm
- Melt Flow: 20 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore A: 77
$ 1679/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 10 - 35 g/10 min @Load 8.70 kg, Temperature 195 °C
- Hardness, Shore A: 85
- Hardness, Shore D: 37
$ 1504/MT
- Specific Gravity: 1.19 g/cc
- Viscosity: 180 - 460 cP
- Hardness, Shore A: 65
- Tensile Strength, Ultimate: 37.0 MPa
- Elongation at Break: 590 %
$ 1506/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Melt Flow: 49 g/10 min @Load 1.20 kg, Temperature 224 °C
- Hardness, Shore D: 65
$ 1589/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 46.0 MPa
- Elongation at Break: 600 %
- 50% Modulus: 0.00460 GPa
$ 1856/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: 8.70 MPa
- Elongation at Break: 480 %
$ 1780/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 36.0 MPa
- Elongation at Break: 635 %
- 50% Modulus: 0.00570 GPa
$ 1536/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 44.0 MPa
- Elongation at Break: 410 %
- Tensile Modulus: 0.210 GPa
$ 1654/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 43.0 MPa
- Elongation at Break: 470 %
- 50% Modulus: 0.0161 GPa
$ 1778/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.020
- Hardness, Shore A: 82 - 88
- Tensile Strength: 45.5 MPa
- Elongation at Break: 650 %
$ 1463/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 24.0 MPa
- Elongation at Break: 883 %
- Tensile Modulus: 0.00300 GPa
$ 1511/MT
- Specific Gravity: 1.66 g/cc
- Filler Content: 50 %
- Maximum Moisture Content: 0.020
- Hardness, Shore D: 77 - 83 @Time 5.00 sec
- Tensile Strength: 96.0 MPa
$ 2095/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 810 %
- Tensile Modulus: 0.0120 GPa
$ 2366/MT
- Specific Gravity: 1.26 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 10 - 35 g/10 min @Load 8.70 kg, Temperature 215 °C
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 49.0 MPa
$ 1572/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 36.0 MPa
- Elongation at Break: 750 %
- 50% Modulus: 0.00380 GPa
$ 2355/MT
- Specific Gravity: 1.20 g/cc
- Viscosity: 300 - 700 cP
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 50.0 MPa
- Elongation at Break: 450 %
$ 1607/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore D: 55
- Tensile Strength, Ultimate: 33.0 MPa
- Elongation at Break: 520 %
- 50% Modulus: 0.0113 GPa
$ 1486/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.050
- Melt Flow: 10 - 25 g/10 min @Load 8.70 kg, Temperature 205 °C
- Hardness, Shore A: 95
- Hardness, Shore D: 50
Delivery TPE Lubrizol (former Noveon)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
ship cargo for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.