$ 1511/MT
- Specific Gravity: 1.42 g/cc
- Water Absorption: 0.100 % @Time 86400 sec
- Additive Loading: 20.0 %
- Linear Mold Shrinkage: 0.000500 - 0.00150 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 123 MPa
$ 2195/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.12 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: >= 10 %
$ 1486/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 7.0 - 10 %
- Tensile Modulus: 2.76 GPa
$ 1839/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0025 - 0.0045 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 4.0 - 6.0 %
- Tensile Modulus: 3.79 GPa
$ 1461/MT
- Specific Gravity: 1.13 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 1.0 - 1.5 %
$ 1758/MT
- Specific Gravity: 1.18 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 121 MPa
- Elongation at Break: 1.0 - 1.5 %
$ 2137/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 1.0 - 2.0 %
- Tensile Modulus: 6.21 GPa
$ 1672/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: >= 10 %
$ 1814/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.72 GPa
$ 1820/MT
- Specific Gravity: 1.40 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 31.0 MPa
- Elongation at Break: 3.0 - 6.0 %
$ 1561/MT
- Specific Gravity: 1.13 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 1.0 - 1.5 %
$ 1534/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 3.45 GPa
$ 1526/MT
- Specific Gravity: 1.15 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 81.4 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 2168/MT
- Specific Gravity: 1.45 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 11.0 GPa
$ 1741/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength at Break: 65.5 MPa
- Elongation at Break: 2.0 - 4.0 %
- Tensile Modulus: 3.45 GPa
- Flexural Strength: 114 MPa
$ 2145/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage: 0.00500 - 0.00700 cm/cm @Thickness 3.20 mm
- Melt Flow: 13.0 - 17.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 38.6 MPa
- Elongation at Break: >= 10.0 %
$ 2206/MT
- Specific Gravity: 1.10 g/cc
- Filler Content: 10 %
- Water Absorption: 0.24 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
$ 1643/MT
- Specific Gravity: 1.10 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: 8.0 - 12 %
$ 1636/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength at Break: 51.7 MPa
$ 1664/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 6.0 - 9.0 %
- Tensile Modulus: 3.10 GPa
$ 1866/MT
- Specific Gravity: 1.34 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 159 MPa
- Elongation at Break: 0.50 - 1.5 %
$ 2003/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1772/MT
- Specific Gravity: 1.08 g/cc
- Filler Content: 5 %
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: 10 - 15 %
$ 2028/MT
- Specific Gravity: 1.34 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 159 MPa
- Elongation at Break: 0.50 - 1.5 %
$ 2062/MT
- Specific Gravity: 1.45 g/cc
- Filler Content: 30 %
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
$ 1647/MT
- Specific Gravity: 1.19 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1674/MT
- Specific Gravity: 1.40 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 68.3 MPa
- Elongation at Break: 2.0 - 2.5 %
$ 1858/MT
- Specific Gravity: 1.29 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 12.1 GPa
$ 2032/MT
- Specific Gravity: 1.18 g/cc
- Filler Content: 5 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 72.4 MPa
- Elongation at Break: 4.0 - 6.0 %
$ 1445/MT
- Specific Gravity: 1.50 g/cc
- Filler Content: 20 %
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
$ 1645/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: >= 10 %
$ 1623/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 3.17 mm
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 55.8 MPa
- Elongation at Break: >= 10 %
$ 1507/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0045 - 0.0075 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 65.5 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.76 GPa
$ 1582/MT
- Specific Gravity: 1.32 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0015 - 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1698/MT
- Specific Gravity: 1.32 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0015 - 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1633/MT
- Specific Gravity: 1.32 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0015 - 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1991/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 2012/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 96.5 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1672/MT
- Specific Gravity: 1.08 g/cc
- Filler Content: 10 %
- Water Absorption: 0.18 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
$ 1659/MT
- Specific Gravity: 1.16 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: >= 10 %
$ 2095/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 35.9 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.72 GPa
$ 1523/MT
- Specific Gravity: 1.40 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 103 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 2105/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.00250 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 82.7 MPa
- Elongation at Break: 1.50 - 2.50 %
- Tensile Modulus: 5.86 GPa
$ 2452/MT
- Specific Gravity: 1.19 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 1.5 - 2.5 %
$ 1822/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 82.7 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1572/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 31.0 MPa
- Elongation at Break: 8.0 - 10 %
$ 1661/MT
- Specific Gravity: 1.51 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 66.9 MPa
- Elongation at Break: 1.0 - 3.0 %
$ 1707/MT
- Specific Gravity: 1.19 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 103 MPa
- Elongation at Break: 1.5 - 2.5 %
$ 1452/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 42.7 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.28 GPa
$ 2590/MT
- Specific Gravity: 1.30 g/cc
- Filler Content: 15 %
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 51.7 MPa
$ 1876/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.00400 - 0.00800 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 51.7 MPa
- Elongation at Break: >= 10.0 %
- Tensile Modulus: 2.76 GPa
$ 2584/MT
- Specific Gravity: 1.40 g/cc
- Additive Loading: 15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 63.4 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 2384/MT
- Specific Gravity: 1.32 g/cc
- Filler Content: 10 %
- Water Absorption: 0.20 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
$ 1475/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 40.7 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.41 GPa
$ 1495/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 10.0 %
- Linear Mold Shrinkage: 0.00200 - 0.00600 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 79.3 MPa
- Elongation at Break: 3.00 - 5.00 %
$ 1884/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 49.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.41 GPa
$ 2422/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.07 GPa
$ 1510/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 42.7 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.41 GPa
$ 1899/MT
- Specific Gravity: 1.33 g/cc
- Filler Content: 15 %
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
$ 1453/MT
- Specific Gravity: 1.10 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 96.5 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1519/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 61.4 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.76 GPa
$ 1830/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 3.17 mm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: >= 40 %
$ 1981/MT
- Specific Gravity: 1.38 g/cc
- Filler Content: 30 %
- Water Absorption: 0.16 %
- Linear Mold Shrinkage: 0.00050 - 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
$ 1452/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 65.5 MPa
- Elongation at Break: 2.0 - 5.0 %
- Tensile Modulus: 4.14 GPa
$ 1566/MT
- Specific Gravity: 1.05 g/cc
- Filler Content: 2 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 42.7 MPa
- Elongation at Break: >= 10 %
$ 2072/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength at Break: 55.2 MPa
$ 1562/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.00600 - 0.00800 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: >= 10.0 %
- Tensile Modulus: 1.93 GPa
$ 2487/MT
- Specific Gravity: 1.36 g/cc
- Filler Content: 20 %
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0015 - 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
$ 1781/MT
- Specific Gravity: 1.41 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 152 MPa
- Elongation at Break: 0.50 - 1.5 %
$ 2131/MT
- Specific Gravity: 1.37 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 1.5 - 3.0 %
$ 1478/MT
- Specific Gravity: 1.36 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.00050 - 0.0015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 82.7 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1537/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.07 GPa
$ 1531/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Melt Flow: 35 - 50 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Rockwell R: 122
$ 1619/MT
- Specific Gravity: 1.13 g/cc
- Filler Content: 20 %
- Water Absorption: 0.17 %
- Linear Mold Shrinkage: 0.00050 - 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
$ 1741/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 42.7 MPa
$ 1596/MT
- Specific Gravity: 1.13 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 6.0 - 8.0 %
$ 1616/MT
- Specific Gravity: 1.32 g/cc
- Filler Content: 10 %
- Water Absorption: 0.20 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 96
$ 2301/MT
- Specific Gravity: 1.51 g/cc
- Additive Loading: 15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1607/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 1.0 - 2.0 %
- Tensile Modulus: 7.58 GPa
$ 1513/MT
- Specific Gravity: 1.40 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: 3.0 - 6.0 %
$ 1742/MT
- Specific Gravity: 1.33 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 131 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 2274/MT
- Specific Gravity: 1.07 g/cc
- Additive Loading: 5.0 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 53.8 MPa
- Elongation at Break: 2.5 - 4.0 %
$ 2115/MT
- Specific Gravity: 1.22 g/cc
- Additive Loading: 15 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 1.5 - 2.5 %
$ 1622/MT
- Specific Gravity: 1.22 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 2.0 %
$ 2171/MT
- Specific Gravity: 1.10 g/cc
- Filler Content: 6 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: 4.0 - 8.0 %
$ 2260/MT
- Specific Gravity: 1.34 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: 3.0 - 5.0 %
$ 1486/MT
- Specific Gravity: 1.25 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 1.5 - 2.5 %
$ 1659/MT
- Specific Gravity: 1.30 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 77.9 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 2382/MT
- Specific Gravity: 1.51 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 2137/MT
- Specific Gravity: 1.24 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0050 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 51.0 MPa
- Elongation at Break: 8.0 - 10 %
$ 1627/MT
- Specific Gravity: 1.24 g/cc
- Filler Content: 40 %
- Water Absorption: 0.14 %
- Linear Mold Shrinkage: 0.00010 - 0.00050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
$ 1859/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 36.5 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 3.10 GPa
$ 2226/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 8.0 - 12 %
$ 1743/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 8.0 - 12 %
$ 1676/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 33.1 MPa
- Elongation at Break: >= 10 %
$ 1893/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 57.2 MPa
- Elongation at Break: 3.0 - 4.0 %
$ 1510/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.0 - 3.0 %
- Tensile Modulus: 6.89 GPa
$ 2080/MT
- Specific Gravity: 1.20 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1492/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: >= 10 %
$ 2060/MT
- Specific Gravity: 1.38 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 114 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1875/MT
- Specific Gravity: 1.29 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 103 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1557/MT
- Specific Gravity: 1.48 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 72.4 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 6.89 GPa
$ 1808/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0060 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 53.1 MPa
- Elongation at Break: >= 10 %
$ 1449/MT
- Specific Gravity: 1.20 g/cc
- Filler Content: 5 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 6.0 - 8.0 %
$ 1533/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 35.2 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.65 GPa
$ 1737/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.0 - 3.0 %
- Tensile Modulus: 9.31 GPa
$ 1505/MT
- Specific Gravity: 1.32 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 4.0 - 7.0 %
$ 1735/MT
- Specific Gravity: 1.20 g/cc
- Additive Loading: 20.0 %
- Linear Mold Shrinkage: 0.00200 - 0.00400 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 1.00 - 3.00 %
$ 2593/MT
- Specific Gravity: 1.38 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.00010 - 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 121 MPa
- Elongation at Break: <= 1.0 %
$ 1849/MT
- Specific Gravity: 1.30 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1461/MT
- Specific Gravity: 1.15 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 3.0 - 7.0 %
$ 1555/MT
- Specific Gravity: 1.30 g/cc
- Filler Content: 20 %
- Water Absorption: 0.17 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
$ 2375/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 53.4 MPa
- Elongation at Break: >= 10 %
$ 2161/MT
- Specific Gravity: 1.19 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: 2.0 %
$ 1680/MT
- Specific Gravity: 1.37 g/cc
- Additive Loading: 15.0 %
- Linear Mold Shrinkage: 0.000500 - 0.00250 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 113 MPa
- Elongation at Break: 1.00 - 2.00 %
$ 1871/MT
- Specific Gravity: 1.38 g/cc
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 129 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 2567/MT
- Specific Gravity: 1.24 g/cc
- Filler Content: 10 %
- Water Absorption: 0.18 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 103 MPa
$ 1494/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: >= 10 %
$ 1739/MT
- Specific Gravity: 1.11 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 65.5 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1614/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 1.0 - 2.0 %
- Tensile Modulus: 6.21 GPa
$ 1993/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 0.100 % @Time 86400 sec
- Additive Loading: 10.0 %
- Linear Mold Shrinkage: 0.00300 - 0.00500 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 118
$ 2073/MT
- Specific Gravity: 1.18 g/cc
- Filler Content: 5 %
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: >= 10 %
$ 1542/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.76 GPa
$ 1486/MT
- Specific Gravity: 1.11 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0050 - 0.0090 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: >= 10 %
$ 1548/MT
- Specific Gravity: 1.36 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1565/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.00050 - 0.0015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 86.2 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1497/MT
- Specific Gravity: 1.25 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 1.0 %
$ 1750/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.00050 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 0.50 - 1.5 %
$ 2234/MT
- Specific Gravity: 1.07 g/cc
- Filler Content: 5 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 53.8 MPa
- Elongation at Break: 2.5 - 4.0 %
$ 1547/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0015 - 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1549/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.011 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.41 GPa
$ 1546/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.41 GPa
$ 1886/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 39.3 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 2.07 GPa
Delivery ABS Polymer RTP Company
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
retired cruise ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.