$ 2021/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.03 GPa
$ 1892/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 28.3 MPa
- Elongation at Break: >= 100 %
$ 1669/MT
- Specific Gravity: 1.16 g/cc
- Filler Content: 35 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1464/MT
- Specific Gravity: 1.01 g/cc
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 6.0 - 7.0 %
- Tensile Modulus: 2.41 GPa
- Flexural Strength: 68.9 MPa
$ 2034/MT
- Specific Gravity: 1.22 g/cc
- Filler Content: 40 %
- Water Absorption: 0.020 %
- Linear Mold Shrinkage: 0.0015 - 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
$ 1477/MT
- Specific Gravity: 0.980 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: >= 10 %
$ 1537/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: >= 10 %
$ 2002/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.9 MPa
$ 2569/MT
- Specific Gravity: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 33.1 MPa
$ 2534/MT
- Specific Gravity: 1.11 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.011 - 0.016 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: >= 10 %
$ 1717/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Melt Flow: 0.50 - 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: >= 10 %
$ 1918/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: 6.0 - 8.0 %
- Tensile Modulus: 2.07 GPa
$ 1507/MT
- Specific Gravity: 1.08 g/cc
- Filler Content: 25 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2286/MT
- Specific Gravity: 1.12 g/cc
- Water Absorption: 0.030 % @Temperature 23.0 °C, Time 86400 sec
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 72.4 MPa
$ 2065/MT
- Specific Gravity: 2.00 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.014 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 - 5.0 g/10 min
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1857/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 18 - 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 13.8 MPa
$ 1579/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 5 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 24.8 MPa
- Elongation at Break: >= 10 %
$ 1860/MT
- Specific Gravity: 1.06 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 28.3 MPa
- Elongation at Break: 6.0 - 9.0 %
$ 1463/MT
- Specific Gravity: 1.03 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 25.5 MPa
- Elongation at Break: <= 10 %
$ 1580/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 32.4 MPa
- Elongation at Break: >= 10 %
$ 1916/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.015 - 0.025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.38 GPa
$ 1448/MT
- Specific Gravity: 1.02 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.018 - 0.025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
$ 1824/MT
- Specific Gravity: 1.42 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 28.3 MPa
- Elongation at Break: 2.0 %
$ 2016/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 51.7 MPa
$ 2065/MT
- Specific Gravity: 0.950 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: 8.0 %
$ 1527/MT
- Specific Gravity: 1.05 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0050 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 36.5 MPa
- Elongation at Break: 5.0 - 8.0 %
$ 1866/MT
- Specific Gravity: 0.770 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 9.31 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.76 GPa
$ 1936/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 5.0 - 8.0 %
- Tensile Modulus: 2.21 GPa
$ 2505/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: >= 300 %
$ 2108/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 62.1 MPa
$ 2491/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2110/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 40 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1513/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 79.3 MPa
$ 1723/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 79.3 MPa
$ 2114/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.00100 - 0.00200 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: >= 10.0 %
- Tensile Modulus: 0.483 GPa
$ 1818/MT
- Specific Gravity: 1.23 g/cc
- Filler Content: 40 %
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.8 MPa
$ 1810/MT
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.010 % @Temperature 23.0 °C, Time 86400 sec
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1503/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0045 - 0.0055 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
$ 2072/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 30 %
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 53.8 MPa
$ 2497/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 30.3 MPa
- Elongation at Break: >= 10 %
$ 1910/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: >= 10 %
$ 2286/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0070 - 0.011 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: >= 10 %
$ 1880/MT
- Specific Gravity: 0.770 g/cc
- Water Absorption: 0.040 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 2130/MT
- Specific Gravity: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.014 - 0.018 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: >= 10 %
$ 2215/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm @Thickness 3.17 mm
- Melt Flow: 0.50 - 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 22.8 MPa
$ 1965/MT
- Specific Gravity: 1.07 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 56.9 MPa
- Elongation at Break: 4.5 - 5.5 %
$ 2388/MT
- Specific Gravity: 1.33 g/cc
- Filler Content: 50 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 63.4 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1662/MT
- Specific Gravity: 0.970 g/cc
- Filler Content: 10 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2218/MT
- Specific Gravity: 1.48 g/cc
- Additive Loading: 60 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1739/MT
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1814/MT
- Specific Gravity: 1.35 g/cc
- Additive Loading: 20.0 %
- Linear Mold Shrinkage: 0.00700 - 0.0100 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 21.4 MPa
$ 1746/MT
- Specific Gravity: 1.04 g/cc
- Additive Loading: 15 %
- Linear Mold Shrinkage: 0.015 - 0.025 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: >= 10 %
$ 2089/MT
- Specific Gravity: 1.03 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0010 - 0.0025 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 24.8 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 1560/MT
- Specific Gravity: 0.990 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: >= 10 %
$ 1739/MT
- Specific Gravity: 0.990 g/cc
- Additive Loading: 15 %
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: >= 10 %
$ 1943/MT
- Specific Gravity: 1.45 g/cc
- Filler Content: 20 %
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1486/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 30.3 MPa
$ 1748/MT
- Specific Gravity: 1.08 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.0090 - 0.013 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 29.6 MPa
- Elongation at Break: >= 10 %
$ 1766/MT
- Specific Gravity: 1.24 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: >= 10 %
$ 2141/MT
- Specific Gravity: 2.50 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 0.50 - 1.0 %
- Tensile Modulus: 6.55 GPa
$ 2029/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 121 MPa
- Elongation at Break: 1.5 - 2.5 %
$ 1572/MT
- Specific Gravity: 1.25 g/cc
- Filler Content: 40 %
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0070 - 0.011 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 30.3 MPa
$ 2448/MT
- Specific Gravity: 1.26 g/cc
- Filler Content: 30 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 95
$ 1495/MT
- Specific Gravity: 1.03 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 60.0 MPa
$ 1916/MT
- Specific Gravity: 1.12 g/cc
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 64.1 MPa
$ 2366/MT
- Specific Gravity: 1.12 g/cc
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1810/MT
- Specific Gravity: 1.33 g/cc
- Additive Loading: 50 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 1.5 - 2.5 %
$ 1749/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 4.0 - 7.0 %
- Tensile Modulus: 1.72 GPa
$ 2168/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.030 % @Time 86400 sec
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 22.8 MPa
$ 2098/MT
- Specific Gravity: 0.970 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 38.6 MPa
$ 1484/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 2.0 - 5.0 %
- Tensile Modulus: 6.55 GPa
$ 1637/MT
- Specific Gravity: 1.10 g/cc
- Additive Loading: 10 %
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 3.0 - 4.0 %
- Tensile Modulus: 4.48 GPa
$ 2088/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 8.0 - 10 %
$ 2007/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 19.3 MPa
$ 1609/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: 4.0 - 6.0 %
$ 1718/MT
- Specific Gravity: 1.09 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.0090 - 0.013 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: >= 10 %
$ 1983/MT
- Specific Gravity: 2.50 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 0.50 - 1.0 %
- Tensile Modulus: 6.55 GPa
$ 1562/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 40 %
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 24.8 MPa
$ 1456/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 5.52 GPa
$ 2090/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 0.689 GPa
$ 2289/MT
- Specific Gravity: 1.10 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.1 MPa
- Elongation at Break: 4.0 - 6.0 %
$ 2059/MT
- Specific Gravity: 1.54 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 46.9 MPa
- Elongation at Break: 4.0 - 8.0 %
- Tensile Modulus: 5.52 GPa
$ 1605/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 46.9 MPa
$ 1518/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 6.0 - 10 %
- Tensile Modulus: 1.52 GPa
$ 1773/MT
- Specific Gravity: 1.04 g/cc
- Additive Loading: 20.0 %
- Linear Mold Shrinkage: 0.00200 - 0.00600 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 60.3 MPa
- Elongation at Break: 3.50 - 6.00 %
$ 2023/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1715/MT
- Specific Gravity: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 44.1 MPa
$ 1957/MT
- Specific Gravity: 1.46 g/cc
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 68.9 MPa
$ 2231/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 29.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.38 GPa
$ 2096/MT
- Specific Gravity: 1.03 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 63.4 MPa
- Elongation at Break: 4.0 - 5.0 %
$ 1573/MT
- Specific Gravity: 1.25 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0070 - 0.011 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 30.3 MPa
- Elongation at Break: >= 10 %
$ 1444/MT
- Specific Gravity: 1.02 g/cc
- Linear Mold Shrinkage: 0.014 - 0.018 cm/cm @Thickness 3.17 mm
- Melt Flow: 37 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 3.0 %
$ 2225/MT
- Specific Gravity: 1.08 g/cc
- Filler Content: 25 %
- Water Absorption: 0.020 %
- Linear Mold Shrinkage: 0.0090 - 0.013 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 29.6 MPa
$ 1570/MT
- Specific Gravity: 0.990 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
$ 2114/MT
- Specific Gravity: 0.900 g/cc
- Additive Loading: 2.0 %
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: >= 10 %
$ 2005/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 3.0 - 4.0 %
- Tensile Modulus: 6.21 GPa
$ 1818/MT
- Specific Gravity: 0.980 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.012 - 0.016 cm/cm @Thickness 3.17 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 33.1 MPa
$ 1622/MT
- Specific Gravity: 0.990 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 15 - 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
$ 1481/MT
- Specific Gravity: 1.25 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 31.0 MPa
$ 1993/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 0.965 GPa
$ 1605/MT
- Specific Gravity: 4.00 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 4.83 GPa
$ 1948/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 58.6 MPa
$ 1985/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 40 %
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 24.8 MPa
$ 1671/MT
- Specific Gravity: 0.970 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 48.3 MPa
$ 2283/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 18 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 30.3 MPa
$ 1631/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 29.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.45 GPa
$ 1649/MT
- Specific Gravity: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: >= 10 %
$ 1532/MT
- Specific Gravity: 0.960 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.010 - 0.018 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 32.8 MPa
- Elongation at Break: >= 10 %
$ 1709/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.013 - 0.018 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 25.5 MPa
- Elongation at Break: >= 10 %
$ 1923/MT
- Specific Gravity: 0.990 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.018 - 0.024 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 86
- Tensile Strength at Break: 27.6 MPa
$ 2022/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 29.6 MPa
$ 1522/MT
- Specific Gravity: 5.00 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 1.0 - 2.0 %
- Tensile Modulus: 2.76 GPa
$ 1469/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 - 0.016 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: >= 10 %
$ 2583/MT
- Specific Gravity: 0.960 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.012 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: 5.0 - 8.0 %
$ 1853/MT
- Specific Gravity: 0.920 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 20.7 MPa
$ 1873/MT
- Specific Gravity: 1.49 g/cc
- Water Absorption: 0.030 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0045 - 0.0065 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 210 °C
- Hardness, Rockwell R: 104
$ 1659/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: >= 10 %
$ 1455/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1689/MT
- Specific Gravity: 3.00 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 5.0 - 10 %
- Tensile Modulus: 1.38 GPa
$ 2201/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 26.2 MPa
$ 1981/MT
- Specific Gravity: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.014 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: >= 10 %
$ 1539/MT
- Specific Gravity: 1.54 g/cc
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1838/MT
- Specific Gravity: 1.43 g/cc
- Filler Content: 20 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 104
$ 1558/MT
- Specific Gravity: 1.04 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 58.6 MPa
$ 2172/MT
- Specific Gravity: 0.970 g/cc
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 44.99 MPa
$ 2244/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 81.98 MPa
$ 1997/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.17 GPa
$ 1654/MT
- Specific Gravity: 1.26 g/cc
- Filler Content: 30 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 75.8 MPa
$ 1907/MT
- Specific Gravity: 1.36 g/cc
- Additive Loading: 20.0 %
- Linear Mold Shrinkage: 0.00700 - 0.0100 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.1 MPa
$ 1815/MT
- Specific Gravity: 1.00 g/cc
- Filler Content: 15 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1528/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 29.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.03 GPa
$ 2064/MT
- Specific Gravity: 1.04 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 44.1 MPa
$ 1929/MT
- Specific Gravity: 1.04 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 44.1 MPa
$ 1525/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Melt Flow: 0.30 - 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.2 MPa
$ 1586/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 89.6 MPa
$ 1619/MT
- Specific Gravity: 1.02 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: 7.0 - 8.0 %
- Tensile Modulus: 2.41 GPa
$ 2066/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0140 - 0.0200 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: >= 10.0 %
- Tensile Modulus: 0.896 GPa
$ 1710/MT
- Specific Gravity: 1.02 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: 4.0 - 6.0 %
$ 1973/MT
- Specific Gravity: 1.02 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 5.0 - 7.0 %
- Tensile Modulus: 2.76 GPa
$ 1523/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.012 - 0.016 cm/cm @Thickness 3.17 mm
- Melt Flow: 20 - 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.1 MPa
$ 1858/MT
- Specific Gravity: 1.21 g/cc
- Additive Loading: 40 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 89.6 MPa
$ 1741/MT
- Specific Gravity: 0.930 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.52 GPa
$ 1656/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Melt Flow: 0.50 - 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: >= 10 %
$ 2238/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.015 - 0.025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.52 GPa
$ 2378/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 5.0 - 10 %
$ 2339/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage: 0.0150 - 0.0200 cm/cm @Thickness 3.20 mm
- Melt Flow: 35.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: >= 100 %
$ 1774/MT
- Specific Gravity: 1.10 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 32.4 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1478/MT
- Specific Gravity: 0.910 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 29.3 MPa
- Elongation at Break: >= 10 %
$ 1625/MT
- Specific Gravity: 1.33 g/cc
- Additive Loading: 50 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 94.975 MPa
- Elongation at Break: 3.5 %
$ 1611/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.72 GPa
$ 1685/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
$ 2260/MT
- Specific Gravity: 1.37 g/cc
- Additive Loading: 20 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 20.7 MPa
$ 1619/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.2 MPa
$ 1533/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 2.5 - 4.0 %
$ 2284/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.72 GPa
$ 1848/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage: 0.0140 - 0.0180 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: >= 10.0 %
$ 1672/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: >= 10 %
$ 2487/MT
- Specific Gravity: 1.42 g/cc
- Filler Content: 15 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2171/MT
- Specific Gravity: 1.25 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0070 - 0.011 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 30.3 MPa
- Elongation at Break: >= 10 %
$ 1558/MT
- Specific Gravity: 1.02 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.020 - 0.025 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
$ 1611/MT
- Specific Gravity: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.013 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 31.7 MPa
- Elongation at Break: >= 10 %
$ 1465/MT
- Specific Gravity: 1.21 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: >= 10 %
$ 2301/MT
- Specific Gravity: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.010 - 0.014 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: >= 10 %
$ 2459/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 41.4 MPa
$ 1718/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 41.4 MPa
$ 2152/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 41.4 MPa
$ 1889/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 41.4 MPa
$ 1485/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.72 GPa
$ 1611/MT
- Specific Gravity: 1.14 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 33.1 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 2232/MT
- Specific Gravity: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: >= 10 %
$ 1477/MT
- Specific Gravity: 0.990 g/cc
- Filler Content: 10 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0090 - 0.014 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 20.7 MPa
$ 1665/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 55.2 MPa
$ 1505/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Melt Flow: 14 - 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 15.9 MPa
$ 1505/MT
- Specific Gravity: 2.00 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 6.55 GPa
$ 1532/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.030 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 50.3 MPa
- Elongation at Break: 3.5 - 4.5 %
$ 1471/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 0.010 % @Temperature 23.0 °C, Time 86400 sec
- Additive Loading: 10 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 85
$ 2120/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 1.0 - 2.0 %
- Tensile Modulus: 11.4 GPa
$ 1515/MT
- Specific Gravity: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 32.4 MPa
- Elongation at Break: >= 10 %
$ 1490/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 0.030 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm
- Melt Flow: 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
$ 1707/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: >= 100 %
$ 1534/MT
- Specific Gravity: 1.12 g/cc
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 75.8 MPa
$ 2126/MT
- Specific Gravity: 0.930 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 26.2 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.03 GPa
$ 1618/MT
- Specific Gravity: 1.47 g/cc
- Additive Loading: 25.0 %
- Linear Mold Shrinkage: 0.00100 - 0.00250 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 3.00 - 4.00 %
$ 1512/MT
- Specific Gravity: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 46.9 MPa
- Elongation at Break: 3.0 - 4.0 %
$ 1454/MT
- Specific Gravity: 1.15 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1638/MT
- Specific Gravity: 1.38 g/cc
- Filler Content: 10 %
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.0045 - 0.0055 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
$ 1859/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: 1.2 %
- Tensile Modulus: 6.21 GPa
$ 1521/MT
- Specific Gravity: 1.14 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 1805/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.0120 - 0.0170 cm/cm @Thickness 3.20 mm
- Melt Flow: <= 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.8 MPa
- Elongation at Break: >= 10.0 %
$ 1623/MT
- Specific Gravity: 1.12 g/cc
- Additive Loading: 30 %
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 74.980 MPa
$ 2450/MT
- Specific Gravity: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.014 - 0.018 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: >= 10 %
$ 2305/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 1.03 GPa
$ 1621/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 33.8 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 2.14 GPa
$ 2517/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.0090 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 0.50 - 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 6.0 - 10 %
$ 2298/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 19.3 MPa
$ 1505/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 3.0 - 4.0 %
- Tensile Modulus: 3.79 GPa
- Flexural Strength: 89.6 MPa
$ 2484/MT
- Specific Gravity: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 37.9 MPa
- Elongation at Break: 7.0 - 9.0 %
$ 1448/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: >= 100 %
$ 1940/MT
- Specific Gravity: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 - 0.016 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 25.5 MPa
- Elongation at Break: >= 10 %
$ 2385/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.012 - 0.017 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 15.2 MPa
$ 1529/MT
- Specific Gravity: 0.990 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 31.0 MPa
- Elongation at Break: >= 10 %
Delivery Polypropylene (PP) RTP Company
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.