$ 2093/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 44
- Tensile Strength, Ultimate: 1240 - 1520 MPa
- Tensile Strength, Yield: 1060 - 1380 MPa
- Elongation at Break: 1.0 - 5.0 %
$ 1988/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 43
- Hardness, Vickers: 353 - 424
- Tensile Strength, Ultimate: 1200 - 1420 MPa
- Tensile Strength, Yield: 1030 - 1280 MPa
$ 1595/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 68 - 90
- Hardness, Vickers: 121 - 185
- Tensile Strength, Ultimate: 510 - 610 MPa
- Tensile Strength, Yield: 410 - 560 MPa
$ 2125/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 340 - 510 MPa
- Tensile Strength, Yield: 240 - 450 MPa
- Elongation at Break: 4.0 - 15 %
- Modulus of Elasticity: 124 GPa
$ 2007/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 20 - 24
- Tensile Strength, Ultimate: 655 - 724 MPa
- Tensile Strength, Yield: 448 - 517 MPa @Strain 0.200 %
- Elongation at Break: 10 - 20 %
$ 1521/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Hardness, Vickers: 353 - 413
- Tensile Strength, Ultimate: 1130 - 1350 MPa
- Tensile Strength, Yield: 960 - 1210 MPa
$ 1529/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 890 - 1070 MPa
- Tensile Strength, Yield: 790 - 1040 MPa
- Elongation at Break: 2.0 - 8.0 %
- Modulus of Elasticity: 131 GPa
$ 1869/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1100 - 1320 MPa
- Tensile Strength, Yield: 990 - 1250 MPa
- Elongation at Break: >= 3.0 %
- Modulus of Elasticity: 131 GPa
$ 1588/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 345 - 480 MPa
- Tensile Strength, Yield: 170 - 345 MPa
- Elongation at Break: 20 - 45 %
- Modulus of Elasticity: 124 GPa
$ 1514/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 760 MPa
- Elongation at Break: >= 10 %
- Modulus of Elasticity: 138 GPa
$ 1936/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 590 - 725 MPa
- Tensile Strength, Yield: 480 - 655 MPa
- Elongation at Break: 4.0 - 20 %
- Modulus of Elasticity: 124 GPa
$ 2216/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: >= 32
- Tensile Strength, Ultimate: >= 931 MPa
- Tensile Strength, Yield: >= 827 MPa @Strain 0.200 %
- Elongation at Break: >= 7 %
$ 2117/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: >= 32
- Tensile Strength, Ultimate: >= 931 MPa
- Tensile Strength, Yield: >= 827 MPa @Strain 0.200 %
- Elongation at Break: >= 4 %
$ 1901/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: >= 30
- Tensile Strength, Ultimate: >= 683 MPa
- Tensile Strength, Yield: >= 652 MPa @Strain 0.200 %
- Elongation at Break: >= 4 %
$ 1481/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: >= 30
- Tensile Strength, Ultimate: >= 862 MPa
- Tensile Strength, Yield: >= 758 MPa @Strain 0.200 %
- Elongation at Break: >= 10 %
$ 1513/MT
- Density: 8.94 g/cc
- Hardness, Brinell: >= 260
- Tensile Strength, Ultimate: >= 758 MPa
- Tensile Strength, Yield: >= 621 MPa @Strain 0.200 %
- Elongation at Break: >= 15 %
$ 1839/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: >= 30
- Tensile Strength, Ultimate: >= 758 MPa
- Tensile Strength, Yield: >= 724 MPa @Strain 0.200 %
- Elongation at Break: >= 4 %
$ 2002/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 88 - 101
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1589/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 38 - 43
- Tensile Strength, Ultimate: 1030 - 1210 MPa
- Tensile Strength, Yield: 827 - 1030 MPa @Strain 0.200 %
- Elongation at Break: 1 - 3 %
$ 2088/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 35 - 41
- Tensile Strength, Ultimate: 1170 - 1450 MPa
- Tensile Strength, Yield: 930 - 1140 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 1848/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 650 - 870 MPa
- Elongation at Break: >= 10 %
- Modulus of Elasticity: 138 GPa
$ 1563/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 25 - 34
- Hardness, Vickers: 255 - 339
- Tensile Strength, Ultimate: >= 820 MPa
- Tensile Strength, Yield: 650 - 800 MPa
$ 1631/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 55 - 65
- Tensile Strength, Ultimate: 379 - 414 MPa
- Tensile Strength, Yield: 172 - 310 MPa @Strain 0.200 %
- Elongation at Break: 15 - 25 %
$ 1572/MT
- Density: 8.14 g/cc
- Hardness, Rockwell B: 80 - 90
- Tensile Strength, Ultimate: 586 - 621 MPa
- Tensile Strength, Yield: 345 - 414 MPa @Strain 0.200 %
- Elongation at Break: 5 - 25 %
$ 2019/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 102
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1661/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 210 MPa
- Elongation at Break: 20 - 60 %
$ 1476/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 760 MPa
- Elongation at Break: >= 10 %
- Modulus of Elasticity: 138 GPa
$ 1703/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: >= 98
- Hardness, Rockwell C: <= 31
- Hardness, Vickers: 225 - 309
- Tensile Strength, Ultimate: >= 680 MPa
$ 1585/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 102
- Tensile Strength, Ultimate: 620 - 870 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 1577/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 60 - 80
- Tensile Strength, Ultimate: 440 - 560 MPa
- Tensile Strength, Yield: 340 - 520 MPa
- Elongation at Break: 10 - 15 %
$ 1491/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 95 - 102
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 680 - 830 MPa
- Elongation at Break: 5.0 - 15 %
$ 1451/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 690 MPa
- Elongation at Break: 10 - 25 %
$ 1735/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 95 - 102
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 650 - 870 MPa
- Elongation at Break: 5.0 - 25 %
$ 1713/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 620 - 750 MPa
- Tensile Strength, Yield: 480 - 560 MPa
- Elongation at Break: 3.0 - 15 %
$ 1816/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 280 MPa
- Elongation at Break: 35 - 60 %
$ 1630/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 33 - 39
- Tensile Strength, Ultimate: 1030 - 1320 MPa
- Tensile Strength, Yield: 890 - 1070 MPa
- Elongation at Break: 3.0 - 10 %
$ 1862/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 88 - 101
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1539/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 34 - 39
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 930 - 1140 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 2194/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 90 - 102
- Tensile Strength, Ultimate: 620 - 870 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 2127/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 35 - 41
- Tensile Strength, Ultimate: 1170 - 1450 MPa
- Tensile Strength, Yield: 990 - 1280 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 2172/MT
- Density: 8.80 g/cc
- Hardness, Rockwell B: 95 - 102
- Hardness, Vickers: 210 - 278
- Tensile Strength, Ultimate: 750 - 900 MPa
- Tensile Strength, Yield: 650 - 870 MPa
$ 1587/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 33 - 42
- Hardness, Vickers: 325 - 413
- Tensile Strength, Ultimate: 1200 - 1320 MPa
- Tensile Strength, Yield: 1030 - 1250 MPa
$ 1603/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 45
- Hardness, Vickers: 373 - 446
- Tensile Strength, Ultimate: 1310 - 1520 MPa
- Tensile Strength, Yield: 1130 - 1420 MPa
$ 1498/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 890 - 1210 MPa
- Elongation at Break: 3.0 - 10 %
$ 1850/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 101
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 2239/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 44
- Tensile Strength, Ultimate: 1240 - 1520 MPa
- Tensile Strength, Yield: 1060 - 1350 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1563/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 750 - 940 MPa
- Tensile Strength, Yield: 620 - 870 MPa
- Elongation at Break: 2.0 - 15 %
- Modulus of Elasticity: 131 GPa
$ 2419/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 620 - 800 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 3.0 - 25 %
- Modulus of Elasticity: 131 GPa
$ 1799/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1200 - 1450 MPa
- Tensile Strength, Yield: 1130 - 1380 MPa
- Elongation at Break: >= 2.0 %
- Modulus of Elasticity: 131 GPa
$ 1594/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 690 MPa
- Elongation at Break: 10 - 25 %
$ 1659/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 990 - 1210 MPa
- Elongation at Break: 4.0 - 10 %
$ 1667/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 39 - 45
- Tensile Strength, Ultimate: 1270 - 1560 MPa
- Tensile Strength, Yield: 1100 - 1320 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 2576/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 750 - 940 MPa
- Tensile Strength, Yield: 620 - 870 MPa
- Elongation at Break: 2.0 - 15 %
- Modulus of Elasticity: 131 GPa
$ 2186/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1200 - 1450 MPa
- Tensile Strength, Yield: 1130 - 1380 MPa
- Elongation at Break: >= 2.0 %
- Modulus of Elasticity: 131 GPa
$ 1686/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 28 - 38
- Hardness, Vickers: 285 - 369
- Tensile Strength, Ultimate: >= 960 MPa
- Tensile Strength, Yield: 790 - 940 MPa
$ 2053/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 990 - 1210 MPa
- Elongation at Break: 4.0 - 10 %
$ 2253/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 990 - 1210 MPa
- Elongation at Break: 4.0 - 10 %
$ 1546/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1310 - 1590 MPa
- Tensile Strength, Yield: 1200 - 1520 MPa
- Elongation at Break: >= 2.0 %
- Modulus of Elasticity: 131 GPa
$ 1491/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 95 - 102
- Hardness, Vickers: 216 - 287
- Tensile Strength, Ultimate: 750 - 940 MPa
- Tensile Strength, Yield: 650 - 830 MPa
$ 1630/MT
- Density: 8.14 g/cc
- Hardness, Rockwell C: 43 - 47
- Tensile Strength, Ultimate: 1240 - 1340 MPa
- Tensile Strength, Yield: 1140 - 1240 MPa @Strain 0.200 %
- Elongation at Break: 0.5 - 3 %
$ 1466/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 38 - 43
- Tensile Strength, Ultimate: 1030 - 1210 MPa
- Tensile Strength, Yield: 827 - 1030 MPa @Strain 0.200 %
- Elongation at Break: 1 - 3 %
$ 1581/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 23 - 30
- Hardness, Vickers: 250 - 301
- Tensile Strength, Ultimate: 820 - 940 MPa
- Tensile Strength, Yield: 650 - 870 MPa
$ 1788/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1340 - 1590 MPa
- Tensile Strength, Yield: 1240 - 1520 MPa
- Elongation at Break: >= 1.0 %
- Modulus of Elasticity: 131 GPa
$ 2320/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 250 MPa
- Elongation at Break: 20 - 60 %
$ 1490/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 92 - 103
- Tensile Strength, Ultimate: 620 - 900 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 2158/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 50
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 60.0 - 210 MPa
- Elongation at Break: 20 - 35 %
$ 2592/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 45
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 170 - 320 MPa
- Elongation at Break: 20 - 35 %
$ 1758/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 39 - 45
- Tensile Strength, Ultimate: 1270 - 1560 MPa
- Tensile Strength, Yield: 1100 - 1320 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1571/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 39 - 45
- Tensile Strength, Ultimate: 1270 - 1560 MPa
- Tensile Strength, Yield: 1100 - 1320 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1816/MT
- Tensile Strength, Ultimate: 655 MPa
- Tensile Strength, Yield: 345 MPa
- Elongation at Break: 8.0 %
- Aluminum, Al: 9.7 - 10.9 %
- Copper, Cu: >= 78 %
$ 1775/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 960 - 1140 MPa
- Tensile Strength, Yield: 890 - 1110 MPa
- Elongation at Break: 1.0 - 6.0 %
- Modulus of Elasticity: 131 GPa
$ 1464/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 103
- Tensile Strength, Ultimate: 620 - 900 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 1494/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 33 - 42
- Hardness, Vickers: 325 - 413
- Tensile Strength, Ultimate: 1200 - 1320 MPa
- Tensile Strength, Yield: 1030 - 1250 MPa
$ 1477/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 205 - 345 MPa
- Tensile Strength, Yield: 280 - 720 MPa @Strain 0.200 %
- Elongation at Break: 35 - 55 %
- Modulus of Elasticity: 124 GPa
$ 1523/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 96
- Hardness, Vickers: 176 - 216
- Tensile Strength, Ultimate: 580 - 690 MPa
- Tensile Strength, Yield: 510 - 660 MPa
$ 1551/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 37 - 44
- Tensile Strength, Ultimate: 1200 - 1490 MPa
- Tensile Strength, Yield: 990 - 1320 MPa
- Elongation at Break: 4.0 - 9.0 %
$ 2006/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 91 - 102
- Tensile Strength, Ultimate: 620 - 870 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1960/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 380 - 510 MPa
- Tensile Strength, Yield: 310 - 480 MPa
- Elongation at Break: 5.0 - 20 %
- Modulus of Elasticity: 124 GPa
$ 2387/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 96 - 102
- Hardness, Vickers: 216 - 287
- Tensile Strength, Ultimate: 680 - 830 MPa
- Tensile Strength, Yield: 620 - 800 MPa
$ 1563/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 280 MPa
- Elongation at Break: 35 - 60 %
$ 1545/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 95 - 102
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 650 - 870 MPa
- Elongation at Break: 5.0 - 25 %
$ 2550/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 95 - 102
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 680 - 830 MPa
- Elongation at Break: 5.0 - 15 %
$ 1598/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 170 - 340 MPa
- Tensile Strength, Yield: 35.0 - 170 MPa
- Elongation at Break: 40 - 60 %
- Modulus of Elasticity: 124 GPa
$ 1779/MT
- Tensile Strength, Ultimate: 724 MPa
- Tensile Strength, Yield: 431 MPa
- Elongation at Break: 9.0 %
- Aluminum, Al: 9.7 - 10.9 %
- Copper, Cu: >= 78 %
$ 1493/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 74 - 82
- Tensile Strength, Ultimate: 483 - 517 MPa
- Tensile Strength, Yield: 241 - 276 MPa @Strain 0.200 %
- Elongation at Break: 20 - 25 %
$ 1980/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 91 - 103
- Tensile Strength, Ultimate: 620 - 900 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1544/MT
- Tensile Strength, Ultimate: 655 MPa
- Tensile Strength, Yield: 386 MPa
- Elongation at Break: 9.0 %
- Aluminum, Al: 9.7 - 10.9 %
- Copper, Cu: >= 78 %
$ 1625/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 400 - 540 MPa
- Tensile Strength, Yield: 130 - 210 MPa
- Elongation at Break: 30 - 60 %
- Modulus of Elasticity: 131 GPa
$ 1643/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 690 MPa
- Elongation at Break: 8.0 - 20 %
$ 1556/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 50
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 60.0 - 210 MPa
- Elongation at Break: 20 - 35 %
$ 1639/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 60 - 80
- Tensile Strength, Ultimate: 440 - 560 MPa
- Tensile Strength, Yield: 340 - 520 MPa
- Elongation at Break: 10 - 15 %
$ 1448/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1310 - 1590 MPa
- Tensile Strength, Yield: 1200 - 1520 MPa
- Elongation at Break: >= 2.0 %
- Modulus of Elasticity: 131 GPa
$ 1804/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 37 - 44
- Tensile Strength, Ultimate: 1200 - 1490 MPa
- Tensile Strength, Yield: 990 - 1320 MPa
- Elongation at Break: 4.0 - 9.0 %
$ 2150/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 34 - 39
- Tensile Strength, Ultimate: 1000 - 1070 MPa
- Tensile Strength, Yield: 931 - 1000 MPa @Strain 0.200 %
- Elongation at Break: 2 - 4 %
$ 2302/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 92 - 103
- Tensile Strength, Ultimate: 620 - 900 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1484/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 38 - 43
- Tensile Strength, Ultimate: 1030 - 1210 MPa
- Tensile Strength, Yield: 827 - 1030 MPa @Strain 0.200 %
- Elongation at Break: 1 - 3 %
$ 1932/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 102
- Tensile Strength, Ultimate: 620 - 870 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 1815/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 101
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1515/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 250 MPa
- Elongation at Break: 20 - 60 %
$ 1772/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 50
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 130 - 280 MPa
- Elongation at Break: 20 - 35 %
$ 1590/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 103
- Tensile Strength, Ultimate: 620 - 900 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 1626/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 440 - 560 MPa
- Tensile Strength, Yield: 370 - 520 MPa
- Elongation at Break: 2.0 - 20 %
- Modulus of Elasticity: 138 GPa
$ 1490/MT
- Density: 8.30 g/cc
- Hardness, Rockwell B: 80 - 85
- Tensile Strength, Ultimate: 517 - 586 MPa
- Tensile Strength, Yield: 276 - 345 MPa @Strain 0.200 %
- Elongation at Break: 15 - 30 %
$ 1447/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 35 - 41
- Tensile Strength, Ultimate: 1170 - 1450 MPa
- Tensile Strength, Yield: 990 - 1280 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 2250/MT
- Density: 8.14 g/cc
- Hardness, Rockwell B: 80 - 90
- Tensile Strength, Ultimate: 586 - 621 MPa
- Tensile Strength, Yield: 345 - 414 MPa @Strain 0.200 %
- Elongation at Break: 5 - 25 %
$ 1877/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 32 - 39
- Tensile Strength, Ultimate: 1030 - 1250 MPa
- Tensile Strength, Yield: 860 - 1070 MPa
- Elongation at Break: 3.0 - 10 %
$ 1886/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 50
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 130 - 280 MPa
- Elongation at Break: 20 - 35 %
$ 1617/MT
- Density: 8.91 g/cc
- Hardness, Rockwell C: 28 - 32
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 689 MPa @Strain 0.200 %
- Elongation at Break: 4 %
$ 1808/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 50
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 60.0 - 210 MPa
- Elongation at Break: 20 - 35 %
$ 1636/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 102
- Tensile Strength, Ultimate: 620 - 870 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 1594/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 28 - 35
- Hardness, Vickers: 285 - 343
- Tensile Strength, Ultimate: 930 - 1040 MPa
- Tensile Strength, Yield: 750 - 940 MPa
$ 1642/MT
- Density: 8.22 g/cc
- Hardness, Rockwell C: 40 - 45
- Tensile Strength, Ultimate: 1140 - 1250 MPa
- Tensile Strength, Yield: 1060 - 1170 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1655/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 20 - 24
- Tensile Strength, Ultimate: 689 - 724 MPa
- Tensile Strength, Yield: 483 - 517 MPa @Strain 0.200 %
- Elongation at Break: 10 - 20 %
$ 1926/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 650 - 870 MPa
- Elongation at Break: >= 10 %
- Modulus of Elasticity: 138 GPa
$ 1624/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 32 - 39
- Tensile Strength, Ultimate: 1030 - 1320 MPa
- Tensile Strength, Yield: 860 - 1070 MPa
- Elongation at Break: 3.0 - 10 %
$ 1669/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1270 - 1490 MPa
- Tensile Strength, Yield: 1170 - 1450 MPa
- Elongation at Break: >= 2.0 %
- Modulus of Elasticity: 131 GPa
$ 2441/MT
- Hardness, Rockwell B: 96
- Tensile Strength, Ultimate: 793 MPa
- Elongation at Break: 18 %
- Compressive Yield Strength: 621 MPa
- Charpy Impact: 67.8 J
$ 1917/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 60 - 80
- Tensile Strength, Ultimate: 440 - 560 MPa
- Tensile Strength, Yield: 340 - 520 MPa
- Elongation at Break: 10 - 15 %
$ 1762/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 20 - 26
- Hardness, Vickers: 230 - 271
- Tensile Strength, Ultimate: 750 - 830 MPa
- Tensile Strength, Yield: 550 - 760 MPa
$ 2510/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 31 - 37
- Hardness, Vickers: 309 - 363
- Tensile Strength, Ultimate: 1030 - 1110 MPa
- Tensile Strength, Yield: 860 - 970 MPa
$ 1454/MT
- Density: 8.94 g/cc
- Hardness, Rockwell B: 62 - 75
- Tensile Strength, Ultimate: 345 - 517 MPa
- Tensile Strength, Yield: 138 - 276 MPa @Strain 0.200 %
- Elongation at Break: >= 30 %
$ 1817/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 88 - 101
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1563/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: >= 95
- Hardness, Rockwell C: <= 23
- Hardness, Vickers: 210 - 251
- Tensile Strength, Ultimate: 680 - 760 MPa
$ 1536/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 280 - 450 MPa
- Tensile Strength, Yield: 170 - 380 MPa
- Elongation at Break: 5.0 - 25 %
- Modulus of Elasticity: 124 GPa
$ 1713/MT
- Density: 8.14 g/cc
- Hardness, Rockwell C: 20 - 25
- Tensile Strength, Ultimate: 655 - 724 MPa
- Tensile Strength, Yield: 414 - 483 MPa @Strain 0.200 %
- Elongation at Break: 10 - 15 %
$ 1450/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 78
- Hardness, Vickers: 90 - 144
- Tensile Strength, Ultimate: 410 - 540 MPa
- Tensile Strength, Yield: 200 - 380 MPa
$ 1689/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 280 - 450 MPa
- Tensile Strength, Yield: 170 - 380 MPa
- Elongation at Break: 5.0 - 25 %
- Modulus of Elasticity: 124 GPa
$ 1959/MT
- Density: 8.80 g/cc
- Hardness, Rockwell B: 98 - 103
- Tensile Strength, Ultimate: 790 - 930 MPa
- Tensile Strength, Yield: 655 - 790 MPa
- Elongation at Break: >= 11 %
$ 2229/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 590 - 725 MPa
- Tensile Strength, Yield: 510 - 690 MPa
- Elongation at Break: 4.0 - 15 %
- Modulus of Elasticity: 124 GPa
$ 1731/MT
- Density: 8.91 g/cc
- Hardness, Rockwell C: >= 27
- Tensile Strength, Ultimate: >= 724 MPa
- Tensile Strength, Yield: >= 621 MPa
- Elongation at Break: >= 3 %
$ 1552/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 78 - 88
- Tensile Strength, Ultimate: 480 - 590 MPa
- Tensile Strength, Yield: 370 - 560 MPa
- Elongation at Break: 2.0 - 8.0 %
$ 2141/MT
- Density: 8.30 g/cc
- Hardness, Rockwell B: 80 - 85
- Tensile Strength, Ultimate: 517 - 586 MPa
- Tensile Strength, Yield: 276 - 345 MPa @Strain 0.200 %
- Elongation at Break: 15 - 30 %
$ 1602/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 20 - 24
- Tensile Strength, Ultimate: 689 - 724 MPa
- Tensile Strength, Yield: 483 - 517 MPa @Strain 0.200 %
- Elongation at Break: 10 - 20 %
$ 1460/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 78 - 88
- Tensile Strength, Ultimate: 480 - 590 MPa
- Tensile Strength, Yield: 370 - 560 MPa
- Elongation at Break: 2.0 - 8.0 %
$ 1743/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 890 - 1210 MPa
- Elongation at Break: 3.0 - 10 %
$ 2427/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: >= 30
- Tensile Strength, Ultimate: >= 862 MPa
- Tensile Strength, Yield: >= 758 MPa @Strain 0.200 %
- Elongation at Break: >= 6 %
$ 1628/MT
- Density: 8.94 g/cc
- Hardness, Rockwell C: 24
- Hardness, Vickers: 260
- Tensile Strength, Ultimate: >= 896 MPa
- Tensile Strength, Yield: >= 827 MPa
$ 1552/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 60.0 - 210 MPa
- Elongation at Break: 20 - 60 %
- Modulus of Elasticity: 138 GPa
$ 2075/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 103
- Tensile Strength, Ultimate: 620 - 900 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 30 %
$ 1972/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 44
- Hardness, Vickers: 373 - 435
- Tensile Strength, Ultimate: 1270 - 1490 MPa
- Tensile Strength, Yield: 1100 - 1320 MPa
$ 1785/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 250 MPa
- Elongation at Break: 20 - 60 %
$ 2304/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 32 - 38
- Hardness, Vickers: 317 - 378
- Tensile Strength, Ultimate: 1060 - 1210 MPa
- Tensile Strength, Yield: 930 - 1180 MPa
$ 2546/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 621 - 689 MPa
- Tensile Strength, Yield: 483 - 552 MPa @Strain 0.200 %
- Elongation at Break: 5 - 10 %
$ 1473/MT
- Density: 8.94 g/cc
- Hardness, Brinell: >= 260
- Tensile Strength, Ultimate: >= 758 MPa
- Tensile Strength, Yield: >= 621 MPa @Strain 0.200 %
- Elongation at Break: >= 12 %
$ 1621/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 951 - 1090 MPa
- Tensile Strength, Yield: 931 - 1050 MPa
- Elongation at Break: >= 1 %
- Modulus of Elasticity: 138 GPa
$ 2327/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 250 MPa
- Elongation at Break: 20 - 60 %
$ 1712/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 20 - 24
- Tensile Strength, Ultimate: 689 - 724 MPa
- Tensile Strength, Yield: 483 - 517 MPa @Strain 0.200 %
- Elongation at Break: 10 - 20 %
$ 2141/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 680 - 830 MPa
- Tensile Strength, Yield: 550 - 690 MPa
- Elongation at Break: 10 - 25 %
$ 1840/MT
- Antimony, Sb: <= 0.00070 %
- Arsenic, As: <= 0.00070 %
- Copper, Cu: 99.93 - 99.96 %
- Iron, Fe: <= 0.0020 %
- Lead, Pb: <= 0.00070 %
$ 2400/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 95 - 102
- Tensile Strength, Ultimate: 750 - 970 MPa
- Tensile Strength, Yield: 650 - 870 MPa
- Elongation at Break: 5.0 - 25 %
$ 1749/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 41
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 890 - 1210 MPa
- Elongation at Break: 3.0 - 10 %
$ 1491/MT
- Hardness, Brinell: 187 - 241
- Tensile Strength, Ultimate: 689 MPa
- Tensile Strength, Yield: 345 MPa
- Elongation at Break: 10 %
- Aluminum, Al: 9.0 - 11 %
$ 1943/MT
- Density: 8.30 g/cc
- Hardness, Rockwell B: 80 - 85
- Tensile Strength, Ultimate: 517 - 586 MPa
- Tensile Strength, Yield: 276 - 345 MPa @Strain 0.200 %
- Elongation at Break: 15 - 30 %
$ 1548/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 90 - 102
- Tensile Strength, Ultimate: 620 - 870 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 2541/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 34 - 39
- Tensile Strength, Ultimate: 1000 - 1070 MPa
- Tensile Strength, Yield: 931 - 1000 MPa @Strain 0.200 %
- Elongation at Break: 2 - 4 %
$ 1730/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1200 - 1450 MPa
- Tensile Strength, Yield: 890 - 1250 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 1903/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 890 - 1210 MPa
- Elongation at Break: 3.0 - 10 %
$ 1522/MT
- Density: 8.88 g/cc
- Tensile Strength, Ultimate: 480 - 680 MPa
- Tensile Strength, Yield: 380 - 590 MPa
- Elongation at Break: 4.0 - 30 %
- Modulus of Elasticity: 124 GPa
$ 1796/MT
- Density: 6.95 g/cc
- Hardness, Rockwell C: 39
- Elongation at Break: <= 0.5 %
- Compressive Strength: 1520 MPa
- Thermal Conductivity: 38.0 W/m-K
$ 1908/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 890 - 1070 MPa
- Tensile Strength, Yield: 790 - 1040 MPa
- Elongation at Break: 2.0 - 8.0 %
- Modulus of Elasticity: 131 GPa
$ 1823/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 44
- Tensile Strength, Ultimate: 1240 - 1520 MPa
- Tensile Strength, Yield: 1060 - 1350 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1574/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 960 - 1140 MPa
- Tensile Strength, Yield: 890 - 1110 MPa
- Elongation at Break: 1.0 - 6.0 %
- Modulus of Elasticity: 131 GPa
$ 1577/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 20 - 24
- Tensile Strength, Ultimate: 655 - 724 MPa
- Tensile Strength, Yield: 448 - 517 MPa @Strain 0.200 %
- Elongation at Break: 10 - 20 %
$ 1574/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 32 - 40
- Hardness, Vickers: 317 - 393
- Tensile Strength, Ultimate: >= 1060 MPa
- Tensile Strength, Yield: 930 - 1070 MPa
$ 1521/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 690 MPa
- Elongation at Break: 8.0 - 20 %
$ 1456/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 75 - 90
- Tensile Strength, Ultimate: 414 - 517 MPa
- Tensile Strength, Yield: 276 - 379 MPa @Strain 0.200 %
- Elongation at Break: 10 - 20 %
$ 2539/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 45 - 78
- Hardness, Vickers: 90 - 144
- Tensile Strength, Ultimate: 410 - 530 MPa
- Tensile Strength, Yield: 190 - 250 MPa
$ 1444/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 34 - 38
- Tensile Strength, Ultimate: 1100 - 1320 MPa
- Tensile Strength, Yield: 860 - 1070 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 2141/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 101
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1700/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 92 - 100
- Tensile Strength, Ultimate: 680 - 900 MPa
- Tensile Strength, Yield: 550 - 690 MPa
- Elongation at Break: 10 - 25 %
$ 1762/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 44
- Tensile Strength, Ultimate: 1240 - 1520 MPa
- Tensile Strength, Yield: 1060 - 1350 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1600/MT
- Hardness, Brinell: 201 - 248
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 469 MPa
- Elongation at Break: 10 %
- Aluminum, Al: 9.0 - 11 %
$ 1646/MT
- Density: 8.80 g/cc
- Hardness, Rockwell B: 89 - 98
- Hardness, Vickers: 180 - 230
- Tensile Strength, Ultimate: 655 - 790 MPa
- Tensile Strength, Yield: 550 - 690 MPa
$ 1709/MT
- Hardness, Brinell: 201 - 248
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 414 MPa
- Elongation at Break: 10 %
- Aluminum, Al: 9.0 - 11 %
$ 1470/MT
- Density: 8.80 g/cc
- Hardness, Rockwell B: 99 - 106
- Tensile Strength, Ultimate: 825 - 965 MPa
- Tensile Strength, Yield: 720 - 860 MPa
- Elongation at Break: >= 10 %
$ 1652/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 38 - 45
- Tensile Strength, Ultimate: 1270 - 1560 MPa
- Tensile Strength, Yield: 1100 - 1320 MPa
- Elongation at Break: 1.0 - 5.0 %
$ 1992/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1340 - 1590 MPa
- Tensile Strength, Yield: 1240 - 1520 MPa
- Elongation at Break: >= 1.0 %
- Modulus of Elasticity: 131 GPa
$ 1645/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 45 - 85
- Tensile Strength, Ultimate: 410 - 590 MPa
- Tensile Strength, Yield: 130 - 210 MPa
- Elongation at Break: 20 - 60 %
$ 2556/MT
- Density: 8.83 g/cc
- Hardness, Rockwell B: 20 - 45
- Tensile Strength, Ultimate: 240 - 380 MPa
- Tensile Strength, Yield: 170 - 320 MPa
- Elongation at Break: 20 - 35 %
$ 1797/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 36 - 42
- Tensile Strength, Ultimate: 1130 - 1320 MPa
- Tensile Strength, Yield: 890 - 1210 MPa
- Elongation at Break: 3.0 - 10 %
$ 2360/MT
- Density: 8.22 g/cc
- Hardness, Rockwell C: 40 - 45
- Tensile Strength, Ultimate: 1140 - 1250 MPa
- Tensile Strength, Yield: 1060 - 1170 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 2050/MT
- Density: 8.36 g/cc
- Hardness, Rockwell B: 88 - 102
- Tensile Strength, Ultimate: 580 - 830 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 8.0 - 20 %
$ 1540/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 32 - 39
- Tensile Strength, Ultimate: 1030 - 1320 MPa
- Tensile Strength, Yield: 860 - 1070 MPa
- Elongation at Break: 4.0 - 10 %
$ 1779/MT
- Density: 8.36 g/cc
- Hardness, Rockwell C: 37 - 44
- Tensile Strength, Ultimate: 1200 - 1490 MPa
- Tensile Strength, Yield: 990 - 1320 MPa
- Elongation at Break: 4.0 - 9.0 %
$ 1734/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 400 - 540 MPa
- Tensile Strength, Yield: 130 - 210 MPa
- Elongation at Break: 30 - 60 %
- Modulus of Elasticity: 131 GPa
$ 1495/MT
- Density: 8.41 g/cc
- Hardness, Rockwell B: 74 - 82
- Tensile Strength, Ultimate: 483 - 517 MPa
- Tensile Strength, Yield: 241 - 276 MPa @Strain 0.200 %
- Elongation at Break: 20 - 25 %
$ 2300/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1270 - 1490 MPa
- Tensile Strength, Yield: 1170 - 1450 MPa
- Elongation at Break: >= 2.0 %
- Modulus of Elasticity: 131 GPa
$ 1552/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 620 - 800 MPa
- Tensile Strength, Yield: 510 - 730 MPa
- Elongation at Break: 3.0 - 25 %
- Modulus of Elasticity: 131 GPa
$ 1936/MT
- Density: 8.41 g/cc
- Hardness, Rockwell C: 34 - 39
- Tensile Strength, Ultimate: 1130 - 1380 MPa
- Tensile Strength, Yield: 930 - 1210 MPa
- Elongation at Break: 4.0 - 9.0 %
$ 1808/MT
- Hardness, Brinell: 187 - 241
- Tensile Strength, Ultimate: 724 MPa
- Tensile Strength, Yield: 379 MPa
- Elongation at Break: 10 %
- Aluminum, Al: 9.0 - 11 %
Delivery Copper Alloy Materion Corporation (former Brush Wellman)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
oil tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.