Materion ToughMet® T3 AT120 (OD price 2216 per MT

Physical Properties
Density
8.94 g/cc

Mechanical Properties
Hardness, Rockwell C
>= 32
Tensile Strength, Ultimate
>= 931 MPa
Tensile Strength, Yield
>= 827 MPa @Strain 0.200 %
Elongation at Break
>= 7 %
Modulus of Elasticity
128 GPa
Poissons Ratio
0.33
Fatigue Strength
414 MPa @# of Cycles 1.00e+6
Shear Modulus
47.9 GPa

Thermal Properties
CTE, linear
16.0 µm/m-°C @Temperature 21.1 - 102 °C
Thermal Conductivity
38.0 W/m-K

Component Elements Properties
Copper, Cu
77 %
Nickel, Ni
15 %
Tin, Sn
8.0 %

Electrical Properties
Electrical Resistivity
0.0000192 ohm-cm
Magnetic Permeability
<= 1.001

Alternative products

Materion ToughMet® T3 AT120 (OD≥4") accurate 74%

$ 2117/MT

Density: 8.94 g/cc
Hardness, Rockwell C: >= 32
Tensile Strength, Ultimate: >= 931 MPa
Tensile Strength, Yield: >= 827 MPa @Strain 0.200 %
Elongation at Break: >= 4 %

Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate accurate 74%

$ 1500/MT

Density: 8.387 g/cc
Hardness, Brinell: 102 @Temperature 871 °C
Hardness, Brinell: 167 @Temperature 760 °C
Hardness, Brinell: 203 @Temperature 649 °C
Hardness, Brinell: 226 @Temperature 538 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction accurate 74%

$ 1518/MT

Density: 8.20 g/cc
Hardness, Brinell: 318
Hardness, Knoop: 343
Hardness, Rockwell C: 34
Hardness, Vickers: 332

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction accurate 74%

$ 1901/MT

Density: 8.20 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 388

Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched accurate 74%

$ 1589/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, GTAW, 6.35 mm plate accurate 74%

$ 1486/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 768 MPa
Elongation at Break: 21 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, SMAW, 3.2 mm sheet accurate 74%

$ 1984/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 800 MPa
Elongation at Break: 27 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled accurate 74%

$ 2005/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 811 MPa
Tensile Strength, Ultimate: 572 MPa @Temperature 649 °C
Tensile Strength, Yield: 493 MPa @Strain 0.200 %
Tensile Strength, Yield: 338 MPa @Strain 0.200 %, Temperature 649 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction accurate 74%

$ 2223/MT

Density: 8.20 g/cc
Hardness, Brinell: 290
Hardness, Knoop: 311
Hardness, Rockwell C: 30
Hardness, Vickers: 301

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, grenadines boat sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Materion ToughMet® T3 AT120 (OD

Seller from Melbourne – 2021-04-24:

Seller from Melbourne work with company: PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2216 per MT