Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled price 2005 per MT

Physical Properties
Density
8.20 g/cc

Mechanical Properties
Tensile Strength, Ultimate
811 MPa
Tensile Strength, Ultimate
572 MPa @Temperature 649 °C
Tensile Strength, Yield
493 MPa @Strain 0.200 %
Tensile Strength, Yield
338 MPa @Strain 0.200 %, Temperature 649 °C
Elongation at Break
30 %
Elongation at Break
25 % @Temperature 649 °C
Modulus of Elasticity
214 GPa
Modulus of Elasticity
159 GPa @Temperature 649 °C
Poissons Ratio
0.298
Poissons Ratio
0.315 @Temperature 426 °C
Poissons Ratio
0.319 @Temperature -78.0 °C
Poissons Ratio
0.325 @Temperature 650 °C
Poissons Ratio
0.339 @Temperature 816 °C
Shear Modulus
82.4 GPa

Thermal Properties
CTE, linear
15.3 µm/m-°C @Temperature 23.0 - 300 °C
CTE, linear
15.6 µm/m-°C @Temperature 23.0 - 400 °C
CTE, linear
16.0 µm/m-°C @Temperature 23.0 - 500 °C
CTE, linear
16.7 µm/m-°C @Temperature 23.0 - 600 °C
CTE, linear
17.2 µm/m-°C @Temperature 23.0 - 700 °C
CTE, linear
17.5 µm/m-°C @Temperature 23.0 - 800 °C
CTE, linear
17.8 µm/m-°C @Temperature 23.0 - 900 °C
CTE, linear
17.8 µm/m-°C @Temperature 23.0 - 1000 °C
CTE, linear
18.4 µm/m-°C @Temperature 23.0 - 1100 °C
Specific Heat Capacity
0.435 J/g-°C @Temperature >=100 °C
Thermal Conductivity
15.9 W/m-K @Temperature 300 °C
Thermal Conductivity
17.3 W/m-K @Temperature 400 °C
Thermal Conductivity
18.6 W/m-K @Temperature 500 °C
Thermal Conductivity
20.0 W/m-K @Temperature 600 °C
Thermal Conductivity
20.0 W/m-K @Temperature 200 °C
Melting Point
1288 - 1354 °C
Solidus
1288 °C
Liquidus
1354 °C

Optical Properties
Emissivity (0-1)
0.88 @Temperature 1090 °C

Component Elements Properties
Carbon, C
0.080 - 0.16 %
Cb + Ta
0.75 - 1.25 %
Chromium, Cr
20 - 22.5 %
Cobalt, Co
18.5 - 21 %
Iron, Fe
33 %
Manganese, Mn
1.0 - 2.0 %
Molybdenum, Mo
2.5 - 3.5 %
Nickel, Ni
19 - 21 %
Nitrogen, N
0.10 - 0.20 %
Silicon, Si
<= 1.0 %
Tungsten, W
2.0 - 3.0 %

Electrical Properties
Electrical Resistivity
0.0000930 ohm-cm @Temperature 22.0 °C

Alternative products

Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched accurate 49%

$ 2187/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 949 MPa @Temperature -78.0 °C
Tensile Strength, Ultimate: 1311 MPa @Temperature -196 °C
Tensile Strength, Yield: 513 MPa @Strain 0.200 %, Temperature -78.0 °C
Elongation at Break: 53 % @Temperature -196 °C

Haynes Multimet® alloy, GTAW, 3.2 mm sheet accurate 49%

$ 1611/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 746 MPa
Elongation at Break: 22 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, investment-cast, as-cast accurate 49%

$ 2096/MT

Density: 8.20 g/cc
Hardness, Brinell: 241
Hardness, Knoop: 255
Hardness, Rockwell C: 21
Hardness, Vickers: 247

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction accurate 49%

$ 1901/MT

Density: 8.20 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 388

Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours accurate 49%

$ 2449/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 675 MPa
Tensile Strength, Ultimate: 103 MPa @Temperature 1066 °C
Tensile Strength, Ultimate: 150 MPa @Temperature 982 °C
Tensile Strength, Ultimate: 230 MPa @Temperature 899 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction accurate 49%

$ 1593/MT

Density: 8.20 g/cc
Hardness, Brinell: 342
Hardness, Knoop: 371
Hardness, Rockwell C: 37
Hardness, Vickers: 358

Haynes Multimet® alloy, GTAW, 9.5 mm plate accurate 49%

$ 1610/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 730 MPa
Elongation at Break: 19 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled accurate 49%

$ 1517/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction accurate 49%

$ 2073/MT

Density: 8.20 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 388

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale nl. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled

Seller from Hong Kong – 2021-05-16:

Seller from Hong Kong work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2131 per MT

Seller from Seoul – 2021-08-14:

Seller from Seoul work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2005 per MT