Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched price 2187 per MT

Physical Properties
Density
8.20 g/cc

Mechanical Properties
Tensile Strength, Ultimate
949 MPa @Temperature -78.0 °C
Tensile Strength, Ultimate
1311 MPa @Temperature -196 °C
Tensile Strength, Yield
513 MPa @Strain 0.200 %, Temperature -78.0 °C
Elongation at Break
53 % @Temperature -196 °C
Elongation at Break
63 % @Temperature -78.0 °C
Modulus of Elasticity
207 GPa @Temperature -78.0 °C
Modulus of Elasticity
214 GPa @Temperature -196 °C
Poissons Ratio
0.298
Poissons Ratio
0.315 @Temperature 426 °C
Poissons Ratio
0.319 @Temperature -78.0 °C
Poissons Ratio
0.325 @Temperature 650 °C
Poissons Ratio
0.339 @Temperature 816 °C

Thermal Properties
CTE, linear
15.3 µm/m-°C @Temperature 23.0 - 300 °C
CTE, linear
15.6 µm/m-°C @Temperature 23.0 - 400 °C
CTE, linear
16.0 µm/m-°C @Temperature 23.0 - 500 °C
CTE, linear
16.7 µm/m-°C @Temperature 23.0 - 600 °C
CTE, linear
17.2 µm/m-°C @Temperature 23.0 - 700 °C
CTE, linear
17.5 µm/m-°C @Temperature 23.0 - 800 °C
CTE, linear
17.8 µm/m-°C @Temperature 23.0 - 1000 °C
CTE, linear
17.8 µm/m-°C @Temperature 23.0 - 900 °C
CTE, linear
18.4 µm/m-°C @Temperature 23.0 - 1100 °C
Specific Heat Capacity
0.435 J/g-°C @Temperature >=100 °C
Thermal Conductivity
15.9 W/m-K @Temperature 300 °C
Thermal Conductivity
17.3 W/m-K @Temperature 400 °C
Thermal Conductivity
18.6 W/m-K @Temperature 500 °C
Thermal Conductivity
20.0 W/m-K @Temperature 600 °C
Thermal Conductivity
20.0 W/m-K @Temperature 200 °C
Melting Point
1288 - 1354 °C
Solidus
1288 °C
Liquidus
1354 °C

Optical Properties
Emissivity (0-1)
0.88 @Temperature 1090 °C

Component Elements Properties
Carbon, C
0.080 - 0.16 %
Cb + Ta
0.75 - 1.25 %
Chromium, Cr
20 - 22.5 %
Cobalt, Co
18.5 - 21 %
Iron, Fe
33 %
Manganese, Mn
1.0 - 2.0 %
Molybdenum, Mo
2.5 - 3.5 %
Nickel, Ni
19 - 21 %
Nitrogen, N
0.10 - 0.20 %
Silicon, Si
<= 1.0 %
Tungsten, W
2.0 - 3.0 %

Electrical Properties
Electrical Resistivity
0.0000930 ohm-cm @Temperature 22.0 °C

Alternative products

Haynes Multimet® alloy, investment-cast, as-cast accurate 99%

$ 2096/MT

Density: 8.20 g/cc
Hardness, Brinell: 241
Hardness, Knoop: 255
Hardness, Rockwell C: 21
Hardness, Vickers: 247

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction accurate 99%

$ 1518/MT

Density: 8.20 g/cc
Hardness, Brinell: 318
Hardness, Knoop: 343
Hardness, Rockwell C: 34
Hardness, Vickers: 332

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction accurate 99%

$ 1901/MT

Density: 8.20 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 388

Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched accurate 99%

$ 1589/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, SMAW, 9.5 mm plate accurate 99%

$ 1589/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 724 MPa
Elongation at Break: 28 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled accurate 99%

$ 1517/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction accurate 99%

$ 2073/MT

Density: 8.20 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 388

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction accurate 99%

$ 1909/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, SMAW, 3.2 mm sheet accurate 99%

$ 1984/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 800 MPa
Elongation at Break: 27 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled accurate 99%

$ 2005/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 811 MPa
Tensile Strength, Ultimate: 572 MPa @Temperature 649 °C
Tensile Strength, Yield: 493 MPa @Strain 0.200 %
Tensile Strength, Yield: 338 MPa @Strain 0.200 %, Temperature 649 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched

Seller from Istanbul – 2021-07-31:

Seller from Istanbul work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2413 per MT

Seller from Tehran – 2021-05-21:

Seller from Tehran work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2187 per MT