$ 1654/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 958 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1444/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1000 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
- Elongation at Break: 41 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1594/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1069 MPa
- Tensile Strength, Yield: 552 MPa @Strain 0.200 %
- Elongation at Break: 47 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1481/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 818 MPa
- Tensile Strength, Yield: 411 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 211 GPa
$ 1993/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 63 @Thickness 12.7 mm
- Hardness, Rockwell A: 66 @Thickness 1.45 mm
- Tensile Strength, Ultimate: 1207 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1253 MPa @Thickness 1.45 mm
$ 2004/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 43 %
- Modulus of Elasticity: 205 GPa
$ 2008/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1813/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 246
- Hardness, Knoop: 267
- Hardness, Rockwell C: 21.9
- Hardness, Vickers: 252
$ 1517/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 1241 MPa
- Tensile Strength, Yield: 1110 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Reduction of Area: 45 %
$ 1477/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Yield: 407 MPa @Strain 0.200 %
$ 1707/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 585 MPa @Strain 0.200 %
- Elongation at Break: 38 %
- Modulus of Elasticity: 218 GPa
$ 2267/MT
- Density: 8.64 g/cc
- Hardness, Brinell: 155 @Thickness 1.70 mm
- Hardness, Brinell: 159 @Thickness 3.20 mm
- Hardness, Knoop: 172 @Thickness 1.70 mm
- Hardness, Knoop: 176 @Thickness 3.20 mm
$ 1509/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 470 MPa @Strain 0.200 %
- Elongation at Break: 30 %
- Modulus of Elasticity: 208 GPa
$ 1630/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 794 MPa
- Tensile Strength, Ultimate: 234 MPa @Temperature 927 °C
- Tensile Strength, Ultimate: 385 MPa @Temperature 815 °C
- Tensile Strength, Ultimate: 480 MPa @Temperature 704 °C
$ 1478/MT
- Density: 8.25 g/cc
- Tensile Strength, Ultimate: 1047 MPa
- Tensile Strength, Ultimate: 179 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 677 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 858 MPa @Temperature 760 °C
$ 1628/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 64 @Thickness 12.7 mm
- Hardness, Rockwell A: 64 @Thickness 1.45 mm
- Tensile Strength, Ultimate: 996 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1231 MPa @Thickness 1.45 mm
$ 1932/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 278
- Hardness, Rockwell C: 24
- Hardness, Vickers: 263
$ 2256/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 164
- Hardness, Knoop: 182
- Hardness, Rockwell B: 95.6
- Hardness, Vickers: 223
$ 1463/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 38.5 %
- Modulus of Elasticity: 211 GPa
$ 1795/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Ultimate: 33.0 MPa @Temperature 1204 °C
- Tensile Strength, Ultimate: 46.0 MPa @Temperature 1149 °C
- Tensile Strength, Ultimate: 68.0 MPa @Temperature 1093 °C
$ 1789/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Yield: 319 MPa @Strain 0.200 %
- Elongation at Break: 26 %
- Reduction of Area: 19 %
$ 1459/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1420 MPa
- Tensile Strength, Yield: 1262 MPa @Strain 0.200 %
$ 2543/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 805 MPa
- Tensile Strength, Ultimate: 570 MPa @Temperature 649 °C
- Elongation at Break: 38.6 %
- Elongation at Break: 26.5 % @Temperature 649 °C
$ 1735/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1510/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1672/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1532/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1629/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 34.3 %
- Modulus of Elasticity: 205 GPa
$ 1589/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 57
- Tensile Strength, Ultimate: 847 MPa
- Tensile Strength, Yield: 416 MPa @Strain 0.200 %
- Reduction of Area: 32 %
$ 1881/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1724 MPa
- Tensile Strength, Yield: 1682 MPa @Strain 0.200 %
$ 2190/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 495 MPa @Strain 0.200 %
- Elongation at Break: 39.1 %
- Modulus of Elasticity: 211 GPa
$ 2401/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 701 MPa
- Tensile Strength, Yield: 295 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Reduction of Area: 23 %
$ 1819/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 342
- Hardness, Knoop: 371
- Hardness, Rockwell C: 37
- Hardness, Vickers: 358
$ 1913/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 835 MPa
- Tensile Strength, Yield: 395 MPa @Strain 0.200 %
- Elongation at Break: 33 %
- Modulus of Elasticity: 205 GPa
$ 1556/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 821 MPa
- Tensile Strength, Yield: 429 MPa @Strain 0.200 %
- Reduction of Area: 26 %
- Modulus of Elasticity: 132 GPa @Temperature 1093 °C
$ 1673/MT
- Density: 8.07 g/cc
- Tensile Strength, Ultimate: 715 MPa
- Tensile Strength, Yield: 325 MPa @Strain 0.200 %
- Elongation at Break: 21 %
- Modulus of Elasticity: 197 GPa
$ 2208/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 252
- Hardness, Knoop: 274
- Hardness, Rockwell C: 23.3
- Hardness, Vickers: 259
$ 1527/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1717/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 752 MPa
- Tensile Strength, Ultimate: 641 MPa @Temperature 400 °C
$ 1503/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 703 MPa
- Tensile Strength, Ultimate: 496 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 565 MPa @Temperature 260 °C
- Tensile Strength, Yield: 469 MPa @Strain 0.200 %
$ 1502/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 55 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 882 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 918 MPa @Thickness 1.45 mm
$ 2075/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1027 MPa
- Tensile Strength, Yield: 531 MPa @Strain 0.200 %
- Elongation at Break: 44 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1506/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 780 MPa
- Tensile Strength, Yield: 430 MPa @Strain 0.200 %
- Elongation at Break: 46.5 %
- Modulus of Elasticity: 205 GPa
$ 1461/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 379
- Hardness, Knoop: 414
- Hardness, Rockwell C: 41
- Hardness, Vickers: 399
$ 1683/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 815 MPa
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %
- Elongation at Break: 37.9 %
- Modulus of Elasticity: 205 GPa
$ 1541/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 805 MPa
- Tensile Strength, Yield: 375 MPa @Strain 0.200 %
- Elongation at Break: 47 %
- Modulus of Elasticity: 205 GPa
$ 1771/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1007 MPa
- Tensile Strength, Yield: 586 MPa @Strain 0.200 %
- Elongation at Break: 29 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1498/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 53 @Thickness 1.45 mm
- Hardness, Rockwell A: 56 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 879 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 904 MPa @Thickness 1.45 mm
$ 1568/MT
- Density: 8.07 g/cc
- Tensile Strength, Ultimate: 725 MPa
- Tensile Strength, Yield: 340 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Modulus of Elasticity: 197 GPa
$ 1898/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 995 MPa
- Tensile Strength, Ultimate: 30.0 MPa @Temperature 1205 °C
- Tensile Strength, Ultimate: 32.0 MPa @Temperature 1150 °C
- Tensile Strength, Ultimate: 58.0 MPa @Temperature 1095 °C
$ 1707/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 38 %
- Modulus of Elasticity: 211 GPa
$ 1537/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Ultimate: 524 MPa @Temperature 760 °C
$ 2348/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 785 MPa
- Tensile Strength, Ultimate: 310 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 610 MPa @Temperature 538 °C
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
$ 1577/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 774 MPa
- Tensile Strength, Yield: 321 MPa @Strain 0.200 %
- Elongation at Break: 66 %
- Reduction of Area: 73 %
$ 1657/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 277
- Hardness, Knoop: 301
- Hardness, Rockwell C: 27.9
- Hardness, Vickers: 287
$ 1711/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Ultimate: 496 MPa @Temperature 760 °C
$ 2198/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 640 MPa @Strain 0.200 %
- Elongation at Break: 26.6 %
- Modulus of Elasticity: 205 GPa
$ 1469/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 640 MPa @Strain 0.200 %
- Elongation at Break: 26.6 %
- Modulus of Elasticity: 205 GPa
$ 1584/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 890 MPa
- Tensile Strength, Yield: 395 MPa @Strain 0.200 %
- Elongation at Break: 34 %
- Modulus of Elasticity: 211 GPa
$ 1780/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 640 MPa @Strain 0.200 %
- Elongation at Break: 26.6 %
- Modulus of Elasticity: 205 GPa
$ 1539/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 640 MPa @Strain 0.200 %
- Elongation at Break: 26.6 %
- Modulus of Elasticity: 205 GPa
$ 1548/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 169
- Hardness, Knoop: 187
- Hardness, Rockwell B: 98.5
- Hardness, Vickers: 245
$ 1931/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 306
- Hardness, Knoop: 373
- Hardness, Rockwell C: 37.1
- Hardness, Vickers: 359
$ 1979/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 262
- Hardness, Knoop: 284
- Hardness, Rockwell C: 25.1
- Hardness, Vickers: 270
$ 1509/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 266
- Hardness, Knoop: 283
- Hardness, Rockwell C: 26
- Hardness, Vickers: 275
$ 1499/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 964 MPa
- Tensile Strength, Yield: 678 MPa @Strain 0.200 %
- Elongation at Break: 25 %
- Reduction of Area: 24 %
$ 1486/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 838 MPa
- Tensile Strength, Yield: 354 MPa @Strain 0.200 %
- Elongation at Break: 38 %
- Reduction of Area: 31 %
$ 1828/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Yield: 400 MPa @Strain 0.200 %
$ 1742/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 1324 MPa
- Tensile Strength, Yield: 1158 MPa @Strain 0.200 %
- Elongation at Break: 8.0 %
- Reduction of Area: 14 %
$ 1792/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 830 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 45.4 %
- Modulus of Elasticity: 205 GPa
$ 1480/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1700/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 411
- Hardness, Knoop: 451
- Hardness, Rockwell C: 44
- Hardness, Vickers: 434
$ 1479/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 500 MPa
- Tensile Strength, Yield: 415 MPa
- Elongation at Break: 14 %
- Reduction of Area: 50 %
$ 2435/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 848 MPa
- Tensile Strength, Yield: 586 MPa @Strain 0.200 %
- Elongation at Break: 18 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 2404/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 279
- Hardness, Rockwell C: 24.3
- Hardness, Vickers: 265
$ 1471/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1014 MPa
- Tensile Strength, Ultimate: 793 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 903 MPa @Temperature 427 °C
- Tensile Strength, Ultimate: 910 MPa @Temperature 316 °C
$ 1790/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 970 MPa
- Tensile Strength, Yield: 665 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 208 GPa
$ 1522/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 945 MPa
- Tensile Strength, Ultimate: 130 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 245 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 415 MPa @Temperature 870 °C
$ 2222/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 1410 MPa
- Tensile Strength, Yield: 1170 MPa @Strain 0.200 %
- Elongation at Break: 8.0 %
- Modulus of Elasticity: 205 GPa
$ 1984/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 785 MPa
- Tensile Strength, Yield: 495 MPa @Strain 0.200 %
- Elongation at Break: 9.1 %
- Modulus of Elasticity: 225 GPa
$ 1747/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 830 MPa
- Tensile Strength, Ultimate: 295 MPa @Temperature 870 °C
- Tensile Strength, Yield: 555 MPa
- Tensile Strength, Yield: 275 MPa @Temperature 870 °C
$ 1710/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 805 MPa
- Tensile Strength, Ultimate: 110 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 210 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 340 MPa @Temperature 870 °C
$ 1836/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 865 MPa
- Tensile Strength, Yield: 375 MPa @Strain 0.200 %
- Elongation at Break: 24.7 %
- Modulus of Elasticity: 205 GPa
$ 2465/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 1305 MPa
- Tensile Strength, Yield: 1075 MPa @Strain 0.200 %
- Elongation at Break: 10.1 %
- Modulus of Elasticity: 205 GPa
$ 1489/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 605 MPa @Strain 0.200 %
- Elongation at Break: 35.2 %
- Modulus of Elasticity: 218 GPa
$ 2342/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 820 MPa
- Tensile Strength, Ultimate: 300 MPa @Temperature 870 °C
- Tensile Strength, Yield: 475 MPa
- Tensile Strength, Yield: 240 MPa @Temperature 870 °C
$ 1526/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 731 MPa
- Tensile Strength, Yield: 372 MPa @Strain 0.200 %
$ 1499/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 863 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 1796/MT
- Density: 8.89 g/cc
- Hardness, Rockwell B: 87
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 601.2 MPa @Thickness 4.80 - 25.4 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 613 MPa @Thickness 1.60 - 4.70 mm, Temperature 538 °C
$ 1451/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 282
- Hardness, Knoop: 323
- Hardness, Rockwell C: 31.1
- Hardness, Vickers: 309
$ 1477/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 683 MPa
- Tensile Strength, Yield: 310 MPa @Strain 0.200 %
- Elongation at Break: 60 %
- Modulus of Elasticity: 202 GPa
$ 1459/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 985 MPa
- Tensile Strength, Yield: 670 MPa @Strain 0.200 %
- Elongation at Break: 13 %
- Modulus of Elasticity: 208 GPa
$ 1706/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 610 MPa @Strain 0.200 %
- Elongation at Break: 30.3 %
- Modulus of Elasticity: 205 GPa
$ 1505/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 324 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 202 GPa
$ 1877/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 50.4 %
- Modulus of Elasticity: 232 GPa
$ 1778/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 775 MPa
- Tensile Strength, Yield: 412 MPa @Strain 0.200 %
- Reduction of Area: 62 %
$ 1579/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1075 MPa
- Tensile Strength, Yield: 475 MPa @Strain 0.200 %
- Elongation at Break: 26.6 %
- Modulus of Elasticity: 232 GPa
$ 2181/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 400
- Hardness, Knoop: 437
- Hardness, Rockwell C: 43
- Hardness, Vickers: 422
$ 1561/MT
- Density: 8.07 g/cc
- Tensile Strength, Ultimate: 725 MPa
- Tensile Strength, Yield: 305 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 197 GPa
$ 1635/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 770 MPa
- Tensile Strength, Yield: 295 MPa @Strain 0.200 %
- Elongation at Break: 29 %
- Modulus of Elasticity: 205 GPa
$ 1609/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 809 MPa
- Tensile Strength, Yield: 321 MPa @Strain 0.200 %
- Elongation at Break: 26 %
- Reduction of Area: 23 %
$ 1884/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 900 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 208 GPa
$ 1492/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 810 MPa
- Tensile Strength, Yield: 380 MPa @Strain 0.200 %
- Elongation at Break: 48 %
- Modulus of Elasticity: 205 GPa
$ 2013/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 342
- Hardness, Knoop: 371
- Hardness, Rockwell C: 37
- Hardness, Vickers: 358
$ 2187/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 949 MPa @Temperature -78.0 °C
- Tensile Strength, Ultimate: 1311 MPa @Temperature -196 °C
- Tensile Strength, Yield: 513 MPa @Strain 0.200 %, Temperature -78.0 °C
- Elongation at Break: 53 % @Temperature -196 °C
$ 1749/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1295 MPa
- Tensile Strength, Yield: 1105 MPa @Strain 0.200 %
- Elongation at Break: 9.7 %
- Modulus of Elasticity: 211 GPa
$ 1541/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 52
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 383 MPa @Strain 0.200 %
- Elongation at Break: 60 %
$ 1844/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1130 MPa
- Tensile Strength, Yield: 815 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Modulus of Elasticity: 208 GPa
$ 1953/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 990 MPa
- Tensile Strength, Yield: 555 MPa @Strain 0.200 %
- Elongation at Break: 36.3 %
- Modulus of Elasticity: 211 GPa
$ 1611/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 746 MPa
- Elongation at Break: 22 %
- Poissons Ratio: 0.298
- Poissons Ratio: 0.315 @Temperature 426 °C
$ 2312/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1138 MPa
- Tensile Strength, Yield: 972 MPa @Strain 0.200 %
$ 2334/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1034 MPa
- Tensile Strength, Yield: 593 MPa @Strain 0.200 %
$ 1578/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 524 MPa @Temperature 760 °C
$ 2050/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 738 MPa
- Tensile Strength, Yield: 492 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 211 GPa
$ 1759/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 1055 MPa
- Tensile Strength, Ultimate: 565 MPa @Temperature 760 °C
- Tensile Strength, Yield: 755 MPa
- Tensile Strength, Yield: 400 MPa @Temperature 760 °C
$ 1918/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 352 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 202 GPa
$ 1654/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 975 MPa
- Tensile Strength, Yield: 575 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1729/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1548/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 560 MPa @Strain 0.200 %
- Elongation at Break: 32.3 %
- Modulus of Elasticity: 211 GPa
$ 1619/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 790 MPa
- Tensile Strength, Yield: 365 MPa @Strain 0.200 %
- Elongation at Break: 44.8 %
- Modulus of Elasticity: 205 GPa
$ 2475/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 278
- Hardness, Rockwell C: 24
- Hardness, Vickers: 263
$ 2386/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 411
- Hardness, Knoop: 451
- Hardness, Rockwell C: 44
- Hardness, Vickers: 434
$ 2048/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 935 MPa
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %
- Elongation at Break: 39.2 %
- Modulus of Elasticity: 211 GPa
$ 1519/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 805 MPa
- Tensile Strength, Ultimate: 320 MPa @Temperature 870 °C
- Tensile Strength, Yield: 455 MPa
- Tensile Strength, Yield: 235 MPa @Temperature 870 °C
$ 1596/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 369
- Hardness, Knoop: 403
- Hardness, Rockwell C: 40
- Hardness, Vickers: 388
$ 2063/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 389
- Hardness, Knoop: 426
- Hardness, Rockwell C: 42
- Hardness, Vickers: 410
$ 1846/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 925 MPa
- Tensile Strength, Yield: 435 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1788/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1172 MPa
- Tensile Strength, Yield: 1041 MPa @Strain 0.200 %
$ 2475/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1014 MPa
- Tensile Strength, Yield: 579 MPa @Strain 0.200 %
$ 1543/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 271
- Hardness, Rockwell C: 24
- Hardness, Vickers: 263
$ 1557/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 910 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 33 %
- Modulus of Elasticity: 211 GPa
$ 1661/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 334
- Hardness, Knoop: 362
- Hardness, Rockwell C: 36
- Hardness, Vickers: 349
$ 1789/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 879 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 885 MPa @Thickness 1.45 mm
$ 1751/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Yield: 595 MPa @Strain 0.200 %
- Elongation at Break: 34.6 %
- Modulus of Elasticity: 211 GPa
$ 1564/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 919 MPa @Thickness 1.45 mm
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %, Thickness 12.7 mm
$ 1536/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1472/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 57
- Tensile Strength, Ultimate: 867 MPa
- Tensile Strength, Yield: 385 MPa @Strain 0.200 %
- Elongation at Break: 60 %
$ 1615/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1130 MPa
- Tensile Strength, Yield: 920 MPa @Strain 0.200 %
- Elongation at Break: 16.8 %
- Modulus of Elasticity: 211 GPa
$ 1668/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 2244/MT
- Density: 8.25 g/cc
- Tensile Strength, Ultimate: 1285 MPa
- Tensile Strength, Ultimate: 75.0 MPa @Temperature 1093 °C
- Tensile Strength, Ultimate: 274 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 702 MPa @Temperature 871 °C
$ 1607/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 675 MPa
- Tensile Strength, Ultimate: 195 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 295 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 315 MPa @Temperature 760 °C
$ 1694/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 317
- Hardness, Knoop: 344
- Hardness, Rockwell C: 33.8
- Hardness, Vickers: 330
$ 1615/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 752 MPa @Thickness 25.4 mm
- Tensile Strength, Ultimate: 752 MPa @Thickness 1.60 mm
- Tensile Strength, Ultimate: 758 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 765 MPa @Thickness 3.17 mm
$ 1547/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 24.8 %
- Modulus of Elasticity: 205 GPa
$ 1664/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 960 MPa
- Tensile Strength, Yield: 505 MPa @Strain 0.200 %
- Elongation at Break: 38.1 %
- Modulus of Elasticity: 211 GPa
$ 1606/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 789 MPa
- Tensile Strength, Ultimate: 426 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 482 MPa @Temperature 704 °C
- Tensile Strength, Ultimate: 568 MPa @Temperature 649 °C
$ 1870/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1085 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
- Elongation at Break: 28.7 %
- Modulus of Elasticity: 232 GPa
$ 1605/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Yield: 455 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1761/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 960 MPa
- Tensile Strength, Ultimate: 34.0 MPa @Temperature 1205 °C
- Tensile Strength, Ultimate: 46.0 MPa @Temperature 1150 °C
- Tensile Strength, Ultimate: 62.0 MPa @Temperature 1095 °C
$ 1710/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 258
- Hardness, Knoop: 281
- Hardness, Rockwell C: 24.5
- Hardness, Vickers: 266
$ 1540/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 696 MPa
- Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 503 MPa @Temperature 538 °C
- Tensile Strength, Yield: 365 MPa @Strain 0.200 %
$ 1496/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 222
- Hardness, Knoop: 260
- Hardness, Rockwell A: 60
- Hardness, Rockwell B: 97
$ 1927/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 228
- Hardness, Knoop: 241
- Hardness, Rockwell C: 18
- Hardness, Vickers: 232
$ 2453/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 52
- Tensile Strength, Ultimate: 874 MPa
- Tensile Strength, Yield: 390 MPa @Strain 0.200 %
- Elongation at Break: 55 %
$ 1561/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 777 MPa
- Tensile Strength, Ultimate: 602 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 654 MPa @Temperature 260 °C
- Tensile Strength, Yield: 471 MPa @Strain 0.200 %
$ 2321/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 389
- Hardness, Knoop: 426
- Hardness, Rockwell C: 42
- Hardness, Vickers: 410
$ 1577/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1260 MPa
- Tensile Strength, Ultimate: 285 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 740 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 945 MPa @Temperature 650 °C
$ 2400/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 825 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 58 %
- Modulus of Elasticity: 208 GPa
$ 1473/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1858/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 379 MPa @Strain 0.200 %
$ 1912/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 274
- Hardness, Knoop: 298
- Hardness, Rockwell C: 27.4
- Hardness, Vickers: 284
$ 1467/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 167
- Hardness, Knoop: 185
- Hardness, Rockwell B: 97.2
- Hardness, Vickers: 235
$ 2192/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 579 MPa @Strain 0.200 %
$ 1796/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Yield: 324 MPa @Strain 0.200 %
- Elongation at Break: 65 %
- Reduction of Area: 67 %
$ 1493/MT
- Density: 8.25 g/cc
- Tensile Strength, Ultimate: 664 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 924 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 1047 MPa @Temperature 649 °C
- Tensile Strength, Yield: 506 MPa @Strain 0.200 %, Temperature 871 °C
$ 1623/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 995 MPa
- Tensile Strength, Yield: 715 MPa @Strain 0.200 %
- Elongation at Break: 31.8 %
- Modulus of Elasticity: 211 GPa
$ 1913/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 510 MPa @Strain 0.200 %
$ 1484/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 985 MPa
- Tensile Strength, Yield: 660 MPa @Strain 0.200 %
- Elongation at Break: 17 %
- Modulus of Elasticity: 208 GPa
$ 1739/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 910 MPa
- Tensile Strength, Yield: 614 MPa @Strain 0.200 %
- Elongation at Break: 17 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1509/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 975 MPa
- Tensile Strength, Yield: 570 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1767/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 740 MPa
- Tensile Strength, Ultimate: 200 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 225 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 380 MPa @Temperature 760 °C
$ 1643/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 985 MPa
- Tensile Strength, Ultimate: 83.0 MPa @Temperature 1205 °C
- Tensile Strength, Ultimate: 96.0 MPa @Temperature 1150 °C
- Tensile Strength, Ultimate: 145 MPa @Temperature 1095 °C
$ 1553/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 795 MPa
- Tensile Strength, Yield: 365 MPa @Strain 0.200 %
- Elongation at Break: 50.7 %
- Modulus of Elasticity: 205 GPa
$ 2049/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 696 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 379 MPa @Strain 0.200 %
$ 1656/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 44 %
- Modulus of Elasticity: 208 GPa
$ 1760/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 41 %
- Modulus of Elasticity: 211 GPa
$ 2367/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1160 MPa
- Tensile Strength, Ultimate: 885 MPa @Temperature 650 °C
- Tensile Strength, Yield: 940 MPa @Strain 0.200 %
- Tensile Strength, Yield: 715 MPa @Strain 0.200 %, Temperature 650 °C
$ 1938/MT
- Density: 9.22 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Ultimate: 675 MPa @Temperature 540 °C
- Tensile Strength, Ultimate: 705 MPa @Temperature 425 °C
- Tensile Strength, Ultimate: 715 MPa @Temperature 650 °C
$ 2080/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 565 MPa @Strain 0.200 %
- Elongation at Break: 35 %
- Modulus of Elasticity: 218 GPa
$ 2254/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 507 MPa @Temperature 649 °C
- Elongation at Break: 39.3 %
- Elongation at Break: 18.1 % @Temperature 649 °C
$ 1512/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 258
- Hardness, Knoop: 280
- Hardness, Rockwell C: 24.4
- Hardness, Vickers: 265
$ 1516/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 524 MPa @Strain 0.200 %
$ 1658/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Modulus of Elasticity: 232 GPa
$ 1755/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 435 MPa @Strain 0.200 %
- Elongation at Break: 32 %
- Modulus of Elasticity: 208 GPa
$ 2522/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 900 MPa
- Tensile Strength, Yield: 655 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 225 GPa
$ 1651/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 290 MPa @Temperature 870 °C
- Tensile Strength, Yield: 425 MPa
- Tensile Strength, Yield: 215 MPa @Temperature 870 °C
$ 1766/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1070 MPa
- Tensile Strength, Ultimate: 270 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 425 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 600 MPa @Temperature 760 °C
$ 1577/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 261
- Hardness, Knoop: 283
- Hardness, Rockwell C: 24.9
- Hardness, Vickers: 268
$ 1684/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 975 MPa
- Tensile Strength, Yield: 560 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1814/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 385 MPa @Strain 0.200 %
- Elongation at Break: 43.7 %
- Modulus of Elasticity: 211 GPa
$ 1662/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 710 MPa
- Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 393 MPa @Strain 0.200 %
$ 1934/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 710 MPa
- Tensile Strength, Ultimate: 524 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 552 MPa @Temperature 427 °C
- Tensile Strength, Ultimate: 572 MPa @Temperature 316 °C
$ 1713/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 35 %
- Modulus of Elasticity: 205 GPa
$ 1854/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 830 MPa
- Tensile Strength, Yield: 410 MPa @Strain 0.200 %
- Elongation at Break: 36 %
- Modulus of Elasticity: 205 GPa
$ 1896/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 876 MPa
- Tensile Strength, Yield: 614 MPa @Strain 0.200 %
- Elongation at Break: 11 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1768/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 565 MPa @Temperature 649 °C
- Tensile Strength, Yield: 323 MPa @Strain 0.200 %
- Elongation at Break: 46 %
$ 2241/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 208 GPa
$ 1568/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 905 MPa
- Tensile Strength, Ultimate: 330 MPa @Temperature 870 °C
- Tensile Strength, Yield: 430 MPa
- Tensile Strength, Yield: 270 MPa @Temperature 870 °C
$ 1734/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Ultimate: 469 MPa @Temperature 760 °C
$ 2299/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 585 MPa @Strain 0.200 %
- Elongation at Break: 34.2 %
- Modulus of Elasticity: 218 GPa
$ 1728/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 139
- Hardness, Knoop: 186
- Hardness, Rockwell B: 98
- Hardness, Vickers: 241
$ 1772/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 276
- Hardness, Knoop: 312
- Hardness, Rockwell C: 29.6
- Hardness, Vickers: 298
$ 1552/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1600/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 1100 MPa
- Tensile Strength, Ultimate: 580 MPa @Temperature 760 °C
- Tensile Strength, Yield: 795 MPa
- Tensile Strength, Yield: 445 MPa @Temperature 760 °C
$ 1945/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1451/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 66
- Tensile Strength, Ultimate: 1004 MPa
- Tensile Strength, Yield: 742 MPa @Strain 0.200 %
- Elongation at Break: 19 %
$ 2372/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 827 MPa
- Tensile Strength, Ultimate: 624 MPa @Temperature 593 °C
- Tensile Strength, Yield: 328 MPa @Strain 0.200 %
- Elongation at Break: 49 %
$ 1516/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1715/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1480 MPa
- Tensile Strength, Yield: 1275 MPa @Strain 0.200 %
- Elongation at Break: 6.0 %
- Modulus of Elasticity: 211 GPa
$ 2028/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 796 MPa
- Tensile Strength, Yield: 340 MPa @Strain 0.200 %
- Elongation at Break: 46.8 %
- Modulus of Elasticity: 122 GPa @Temperature 1049 °C
$ 1496/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 45 %
- Modulus of Elasticity: 208 GPa
$ 2096/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 241
- Hardness, Knoop: 255
- Hardness, Rockwell C: 21
- Hardness, Vickers: 247
$ 2139/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 395 MPa @Strain 0.200 %
- Elongation at Break: 25.8 %
- Modulus of Elasticity: 205 GPa
$ 1585/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54
- Tensile Strength, Ultimate: 852 MPa
- Tensile Strength, Yield: 354 MPa @Strain 0.200 %
- Elongation at Break: 53 %
$ 2234/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 33 %
- Modulus of Elasticity: 211 GPa
$ 1503/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 620 MPa
- Tensile Strength, Yield: 330 MPa
- Elongation at Break: 62 %
- Reduction of Area: 69 %
$ 1506/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 767 MPa
- Tensile Strength, Ultimate: 30.0 MPa @Temperature 1204 °C
- Tensile Strength, Ultimate: 41.0 MPa @Temperature 1149.0 °C
- Tensile Strength, Ultimate: 74.0 MPa @Temperature 1093 °C
$ 1831/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 980 MPa
- Tensile Strength, Yield: 525 MPa @Strain 0.200 %
- Elongation at Break: 35.7 %
- Modulus of Elasticity: 211 GPa
$ 1759/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 905 MPa
- Tensile Strength, Yield: 535 MPa @Strain 0.200 %
- Elongation at Break: 33.4 %
- Modulus of Elasticity: 205 GPa
$ 1831/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1453/MT
- Density: 9.22 g/cc
- Tensile Strength, Ultimate: 890 MPa
- Tensile Strength, Yield: 385 MPa @Strain 0.200 %
- Elongation at Break: 60.4 %
- Modulus of Elasticity: 216 GPa
$ 1453/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 317 MPa @Strain 0.200 %
- Elongation at Break: 64 %
- Reduction of Area: 77 %
$ 2239/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 980 MPa
- Tensile Strength, Yield: 555 MPa @Strain 0.200 %
- Elongation at Break: 35.6 %
- Modulus of Elasticity: 211 GPa
$ 1500/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 334
- Hardness, Knoop: 362
- Hardness, Rockwell C: 36
- Hardness, Vickers: 349
$ 1540/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Yield: 545 MPa @Strain 0.200 %
- Elongation at Break: 34 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1649/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 425 MPa @Strain 0.200 %
- Elongation at Break: 46.6 %
- Modulus of Elasticity: 211 GPa
$ 1901/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 870 MPa
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %
- Elongation at Break: 37 %
- Modulus of Elasticity: 211 GPa
$ 1518/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 318
- Hardness, Knoop: 343
- Hardness, Rockwell C: 34
- Hardness, Vickers: 332
$ 1452/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 34.8 %
- Modulus of Elasticity: 205 GPa
$ 1997/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 159
- Hardness, Knoop: 176
- Hardness, Rockwell B: 92
- Hardness, Vickers: 201
$ 1746/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 51 %
- Modulus of Elasticity: 211 GPa
$ 2022/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 931 MPa
- Tensile Strength, Yield: 669 MPa @Strain 0.200 %
- Elongation at Break: 9.0 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1901/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 369
- Hardness, Knoop: 403
- Hardness, Rockwell C: 40
- Hardness, Vickers: 388
$ 1839/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 980 MPa
- Tensile Strength, Yield: 525 MPa @Strain 0.200 %
- Elongation at Break: 35.5 %
- Modulus of Elasticity: 211 GPa
$ 2053/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 250
- Hardness, Knoop: 272
- Hardness, Rockwell C: 22.9
- Hardness, Vickers: 257
$ 2369/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 422
- Hardness, Knoop: 464
- Hardness, Rockwell C: 45
- Hardness, Vickers: 446
$ 1925/MT
- Density: 8.25 g/cc
- Hardness, Brinell: 360 @Temperature 760 °C
- Hardness, Knoop: 392 @Temperature 760 °C
- Hardness, Rockwell B: 86 @Temperature 760 °C
- Hardness, Rockwell C: 39 @Temperature 760 °C
$ 2028/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1250 MPa
- Tensile Strength, Ultimate: 295 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 510 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 745 MPa @Temperature 760 °C
$ 1531/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Ultimate: 400 MPa @Temperature 870 °C
- Tensile Strength, Yield: 505 MPa
- Tensile Strength, Yield: 350 MPa @Temperature 870 °C
$ 1510/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 43 %
- Modulus of Elasticity: 211 GPa
$ 1452/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 820 MPa
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %
- Elongation at Break: 17 %
- Modulus of Elasticity: 205 GPa
$ 1492/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 796 MPa
- Tensile Strength, Ultimate: 525 MPa @Temperature 704 °C
- Tensile Strength, Yield: 316 MPa @Strain 0.200 %
- Elongation at Break: 46 %
$ 1918/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 863 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 920 MPa @Thickness 1.45 mm
$ 1728/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 360 MPa @Strain 0.200 %
- Elongation at Break: 55 %
- Modulus of Elasticity: 208 GPa
$ 1575/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 375
- Hardness, Knoop: 410
- Hardness, Rockwell C: 40.6
- Hardness, Vickers: 394
$ 2083/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1140 MPa
- Tensile Strength, Yield: 845 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Modulus of Elasticity: 208 GPa
$ 1465/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 917 MPa
- Tensile Strength, Yield: 655 MPa @Strain 0.200 %
- Elongation at Break: 10 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 2567/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 261
- Hardness, Knoop: 277
- Hardness, Rockwell C: 25
- Hardness, Vickers: 269
$ 2515/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 570 MPa @Strain 0.200 %
- Elongation at Break: 31.7 %
- Modulus of Elasticity: 205 GPa
$ 1838/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 717 MPa
- Tensile Strength, Ultimate: 510 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 572 MPa @Temperature 260 °C
- Tensile Strength, Yield: 462 MPa @Strain 0.200 %
$ 1629/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 1073 MPa
- Tensile Strength, Yield: 439 MPa @Strain 0.200 %
- Reduction of Area: 25 %
- Modulus of Elasticity: 132 GPa @Temperature 1093 °C
$ 1595/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1420 MPa
- Tensile Strength, Yield: 1331 MPa @Strain 0.200 %
$ 2207/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1900/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 972 MPa
- Tensile Strength, Yield: 758 MPa @Strain 0.200 %
$ 1534/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 159
- Hardness, Knoop: 176
- Hardness, Rockwell B: 92
- Hardness, Vickers: 201
$ 1572/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1637/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 279
- Hardness, Rockwell C: 24.3
- Hardness, Vickers: 265
$ 1524/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 128
- Hardness, Knoop: 172
- Hardness, Rockwell B: 90
- Hardness, Vickers: 191
$ 1501/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 843 MPa
- Tensile Strength, Yield: 353 MPa @Strain 0.200 %
- Elongation at Break: 34 %
- Reduction of Area: 28 %
$ 1582/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 1090 MPa
- Tensile Strength, Yield: 715 MPa @Strain 0.200 %
- Elongation at Break: 26.1 %
- Modulus of Elasticity: 218 GPa
$ 1581/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 990 MPa
- Tensile Strength, Yield: 635 MPa @Strain 0.200 %
- Elongation at Break: 32.9 %
- Modulus of Elasticity: 211 GPa
$ 1603/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 190
- Hardness, Knoop: 211
- Hardness, Vickers: 199
- Tensile Strength, Ultimate: 767 MPa
$ 1697/MT
- Density: 8.07 g/cc
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 35 %
- Modulus of Elasticity: 197 GPa
$ 2554/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1145 MPa
- Tensile Strength, Ultimate: 275 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 485 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 715 MPa @Temperature 760 °C
$ 1619/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1045 MPa
- Tensile Strength, Yield: 550 MPa @Strain 0.200 %
- Elongation at Break: 29.1 %
- Modulus of Elasticity: 232 GPa
$ 1483/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 483 MPa @Thickness 9.50 mm, Temperature 760 °C
- Tensile Strength, Ultimate: 584 MPa @Thickness 9.50 mm, Temperature 649 °C
- Tensile Strength, Ultimate: 635 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 643 MPa @Thickness 9.50 mm, Temperature 538 °C
$ 1476/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1050 MPa
- Tensile Strength, Ultimate: 88.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 170 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 350 MPa @Temperature 870 °C
$ 1959/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 208 GPa
$ 2001/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 348 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 2183/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 812 MPa
- Tensile Strength, Yield: 341 MPa @Strain 0.200 %
- Elongation at Break: 40 %
- Reduction of Area: 33 %
$ 1704/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 1080 MPa
- Tensile Strength, Yield: 680 MPa @Strain 0.200 %
- Elongation at Break: 27.1 %
- Modulus of Elasticity: 218 GPa
$ 1537/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 2336/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 266
- Hardness, Knoop: 283
- Hardness, Rockwell C: 26
- Hardness, Vickers: 275
$ 2120/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 1335 MPa
- Tensile Strength, Ultimate: 83.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 220 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 545 MPa @Temperature 870 °C
$ 1851/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 365 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 208 GPa
$ 1835/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 241
- Hardness, Knoop: 255
- Hardness, Rockwell C: 21
- Hardness, Vickers: 247
$ 2206/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 292 MPa
- Tensile Strength, Yield: 150 MPa @Strain 0.200 %
- Elongation at Break: 29.5 %
- Modulus of Elasticity: 205 GPa
$ 2074/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 168
- Hardness, Knoop: 186
- Hardness, Rockwell B: 98.1
- Hardness, Vickers: 241
$ 1770/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 434
- Hardness, Knoop: 478
- Hardness, Rockwell C: 46
- Hardness, Vickers: 459
$ 1475/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 935 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 35.1 %
- Modulus of Elasticity: 218 GPa
$ 2061/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 1190 MPa
- Tensile Strength, Yield: 995 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 205 GPa
$ 1706/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Ultimate: 535 MPa @Temperature 760 °C
- Tensile Strength, Yield: 745 MPa
- Tensile Strength, Yield: 390 MPa @Temperature 760 °C
$ 1720/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1015 MPa
- Tensile Strength, Ultimate: 195 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 370 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 620 MPa @Temperature 760 °C
$ 2057/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1390 MPa
- Tensile Strength, Yield: 1190 MPa @Strain 0.200 %
- Elongation at Break: 7.5 %
- Modulus of Elasticity: 211 GPa
$ 2022/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
$ 1550/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 248
- Hardness, Knoop: 270
- Hardness, Rockwell C: 22.5
- Hardness, Vickers: 255
$ 1464/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 43 %
- Modulus of Elasticity: 211 GPa
$ 1636/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 500 MPa
- Tensile Strength, Yield: 240 MPa @Strain 0.200 %
- Elongation at Break: 25.3 %
- Modulus of Elasticity: 205 GPa
$ 1453/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 26 %
- Modulus of Elasticity: 208 GPa
$ 1968/MT
- Density: 9.22 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Ultimate: 730 MPa @Temperature 540 °C
- Tensile Strength, Ultimate: 735 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 745 MPa @Temperature 425 °C
$ 1757/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 52 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 110 MPa @Thickness 1.10 - 1.60 mm, Temperature 1093 °C
- Tensile Strength, Ultimate: 117 MPa @Thickness 9.50 - 25.4 mm, Temperature 1093 °C
$ 1657/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 331
- Hardness, Knoop: 443
- Hardness, Rockwell C: 43.5
- Hardness, Vickers: 428
$ 1887/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 42.4 %
- Modulus of Elasticity: 205 GPa
$ 1472/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 745 MPa
- Tensile Strength, Yield: 305 MPa @Strain 0.200 %
- Elongation at Break: 29.5 %
- Modulus of Elasticity: 205 GPa
$ 1877/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 276
- Hardness, Knoop: 311
- Hardness, Rockwell C: 29.5
- Hardness, Vickers: 297
$ 1454/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 780 MPa
- Tensile Strength, Ultimate: 290 MPa @Temperature 870 °C
- Tensile Strength, Yield: 395 MPa
- Tensile Strength, Yield: 230 MPa @Temperature 870 °C
$ 2266/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Ultimate: 97.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 175 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 310 MPa @Temperature 870 °C
$ 1562/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1581/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Ultimate: 55.0 MPa @Temperature 1204 °C
- Tensile Strength, Ultimate: 79.0 MPa @Temperature 1149 °C
- Tensile Strength, Ultimate: 120 MPa @Temperature 1093 °C
$ 1589/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 159
- Hardness, Knoop: 176
- Hardness, Rockwell B: 92
- Hardness, Vickers: 201
$ 1550/MT
- Density: 8.07 g/cc
- Tensile Strength, Ultimate: 735 MPa
- Tensile Strength, Yield: 375 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 197 GPa
$ 1486/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 768 MPa
- Elongation at Break: 21 %
- Poissons Ratio: 0.298
- Poissons Ratio: 0.315 @Temperature 426 °C
$ 1951/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 1395 MPa
- Tensile Strength, Ultimate: 77.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 145 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 420 MPa @Temperature 870 °C
$ 1941/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 29 %
- Modulus of Elasticity: 208 GPa
$ 1892/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1069 MPa
- Tensile Strength, Yield: 558 MPa @Strain 0.200 %
- Elongation at Break: 47 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1571/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 48.7 %
- Modulus of Elasticity: 225 GPa
$ 1620/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Ultimate: 160 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 235 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 415 MPa @Temperature 870 °C
$ 1591/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 915 MPa
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %
- Elongation at Break: 37 %
- Modulus of Elasticity: 211 GPa
$ 2181/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 490 MPa
- Tensile Strength, Yield: 355 MPa
- Elongation at Break: 17 %
- Reduction of Area: 51 %
$ 1768/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 496 MPa @Strain 0.200 %
$ 1736/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1315 MPa
- Tensile Strength, Ultimate: 290 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 800 MPa @Temperature 760 °C
$ 2449/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 675 MPa
- Tensile Strength, Ultimate: 103 MPa @Temperature 1066 °C
- Tensile Strength, Ultimate: 150 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 230 MPa @Temperature 899 °C
$ 1689/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1496/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 812 MPa
- Tensile Strength, Ultimate: 674 MPa @Temperature 538 °C
- Tensile Strength, Yield: 311 MPa @Strain 0.200 %
- Elongation at Break: 50 %
$ 1830/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 359 MPa @Temperature 816 °C
- Tensile Strength, Ultimate: 438 MPa @Temperature 704 °C
- Tensile Strength, Ultimate: 493 MPa @Temperature 649 °C
$ 1469/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 369
- Hardness, Knoop: 403
- Hardness, Rockwell C: 40
- Hardness, Vickers: 388
$ 1852/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Yield: 427 MPa @Strain 0.200 %
$ 1488/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 317 MPa @Strain 0.200 %
- Elongation at Break: 60 %
- Modulus of Elasticity: 202 GPa
$ 2142/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 815 MPa
- Tensile Strength, Ultimate: 100 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 195 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 330 MPa @Temperature 870 °C
$ 2156/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 839 MPa
- Tensile Strength, Yield: 436 MPa @Strain 0.200 %
- Reduction of Area: 33 %
- Modulus of Elasticity: 132 GPa @Temperature 1093 °C
$ 2158/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 58
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Yield: 458 MPa @Strain 0.200 %
- Elongation at Break: 19 %
$ 2463/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 870 MPa
- Tensile Strength, Yield: 535 MPa @Strain 0.200 %
- Elongation at Break: 3.5 %
- Modulus of Elasticity: 225 GPa
$ 1593/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 342
- Hardness, Knoop: 371
- Hardness, Rockwell C: 37
- Hardness, Vickers: 358
$ 1762/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Ultimate: 453 MPa @Temperature 760 °C
- Tensile Strength, Yield: 301 MPa @Strain 0.200 %
- Elongation at Break: 40 %
$ 1538/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 348 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 2011/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 610 MPa
- Tensile Strength, Yield: 260 MPa @Strain 0.200 %
- Elongation at Break: 23.4 %
- Modulus of Elasticity: 205 GPa
$ 1782/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Yield: 320 MPa @Strain 0.200 %
- Elongation at Break: 20.4 %
- Modulus of Elasticity: 205 GPa
$ 1760/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 268
- Hardness, Knoop: 299
- Hardness, Rockwell C: 27.6
- Hardness, Vickers: 285
$ 1562/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 635 MPa @Strain 0.200 %
- Elongation at Break: 24.8 %
- Modulus of Elasticity: 225 GPa
$ 2135/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Ultimate: 579 MPa @Temperature 538 °C
$ 1526/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 867 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 58 %
$ 1771/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 960 MPa
- Tensile Strength, Yield: 555 MPa @Strain 0.200 %
- Elongation at Break: 36.5 %
- Modulus of Elasticity: 211 GPa
$ 1677/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 870 MPa
- Tensile Strength, Ultimate: 310 MPa @Temperature 870 °C
- Tensile Strength, Yield: 555 MPa
- Tensile Strength, Yield: 285 MPa @Temperature 870 °C
$ 2344/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Yield: 407 MPa @Strain 0.200 %
$ 1888/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 490 MPa @Thickness 12.7 mm, Temperature 760 °C
- Tensile Strength, Ultimate: 545 MPa @Thickness 3.17 mm, Temperature 538 °C
$ 1899/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1140 MPa
- Tensile Strength, Yield: 815 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 208 GPa
$ 1563/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Yield: 410 MPa @Strain 0.200 %
- Elongation at Break: 29.4 %
- Modulus of Elasticity: 205 GPa
$ 1955/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 915 MPa
- Tensile Strength, Yield: 495 MPa @Strain 0.200 %
- Elongation at Break: 39.9 %
- Modulus of Elasticity: 218 GPa
$ 1767/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Ultimate: 214 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 352 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 524 MPa @Temperature 760 °C
$ 1848/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1531 MPa
- Tensile Strength, Yield: 1393 MPa @Strain 0.200 %
$ 2205/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 952 MPa
- Tensile Strength, Ultimate: 827 MPa @Temperature 427 °C
- Tensile Strength, Ultimate: 896 MPa @Temperature 316 °C
- Tensile Strength, Ultimate: 924 MPa @Temperature 204 °C
$ 1610/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 730 MPa
- Elongation at Break: 19 %
- Poissons Ratio: 0.298
- Poissons Ratio: 0.315 @Temperature 426 °C
$ 2343/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %
- Elongation at Break: 55 %
- Modulus of Elasticity: 208 GPa
$ 1885/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 676 MPa @Thickness 19.0 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 786 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 800 MPa @Thickness 19.0 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 834 MPa @Thickness 12.7 mm, Temperature 20.0 °C
$ 1599/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 896 MPa
- Tensile Strength, Ultimate: 752 MPa @Temperature 538 °C
- Tensile Strength, Yield: 600 MPa @Strain 0.200 %
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %, Temperature 538 °C
$ 1716/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1766/MT
- Density: 8.25 g/cc
- Hardness, Brinell: 318 @Temperature 760 °C
- Hardness, Knoop: 343 @Temperature 760 °C
- Hardness, Rockwell B: 97 @Temperature 760 °C
- Hardness, Rockwell C: 34 @Temperature 760 °C
$ 2358/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Yield: 297 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Reduction of Area: 20 %
$ 1458/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 660 MPa
- Tensile Strength, Yield: 260 MPa @Strain 0.200 %
- Elongation at Break: 48 %
- Modulus of Elasticity: 205 GPa
$ 1539/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 970 MPa
- Tensile Strength, Yield: 565 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1626/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56 @Thickness 12.7 mm
- Hardness, Rockwell A: 56 @Thickness 1.45 mm
- Tensile Strength, Ultimate: 877 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 914 MPa @Thickness 1.45 mm
$ 2090/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1902/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 167
- Hardness, Knoop: 185
- Hardness, Rockwell B: 97.1
- Hardness, Vickers: 234
$ 1675/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 896 MPa
- Tensile Strength, Yield: 641 MPa @Strain 0.200 %
$ 2479/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Ultimate: 265 MPa @Temperature 870 °C
- Tensile Strength, Yield: 525 MPa
- Tensile Strength, Yield: 250 MPa @Temperature 870 °C
$ 1517/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 281
- Hardness, Rockwell C: 24.5
- Hardness, Vickers: 266
$ 1770/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 924 MPa
- Tensile Strength, Ultimate: 690 MPa @Temperature 538 °C
- Tensile Strength, Yield: 641 MPa @Strain 0.200 %
- Tensile Strength, Yield: 421 MPa @Strain 0.200 %, Temperature 538 °C
$ 2187/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 320 MPa @Strain 0.200 %
- Elongation at Break: 36 %
- Reduction of Area: 28 %
$ 1675/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 57
- Tensile Strength, Ultimate: 705 MPa
- Tensile Strength, Yield: 425 MPa @Strain 0.200 %
- Elongation at Break: 21 %
$ 1589/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 724 MPa
- Elongation at Break: 28 %
- Poissons Ratio: 0.298
- Poissons Ratio: 0.315 @Temperature 426 °C
$ 1517/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 159
- Hardness, Knoop: 176
- Hardness, Rockwell B: 92
- Hardness, Vickers: 201
$ 2073/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 369
- Hardness, Knoop: 403
- Hardness, Rockwell C: 40
- Hardness, Vickers: 388
$ 1909/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 159
- Hardness, Knoop: 176
- Hardness, Rockwell B: 92
- Hardness, Vickers: 201
$ 1984/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Elongation at Break: 27 %
- Poissons Ratio: 0.298
- Poissons Ratio: 0.315 @Temperature 426 °C
$ 2005/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 811 MPa
- Tensile Strength, Ultimate: 572 MPa @Temperature 649 °C
- Tensile Strength, Yield: 493 MPa @Strain 0.200 %
- Tensile Strength, Yield: 338 MPa @Strain 0.200 %, Temperature 649 °C
$ 2223/MT
- Density: 8.20 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1482/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 920 MPa
- Tensile Strength, Yield: 550 MPa @Strain 0.200 %
- Elongation at Break: 30.6 %
- Modulus of Elasticity: 205 GPa
$ 1637/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 322
- Hardness, Knoop: 416
- Hardness, Rockwell C: 41.2
- Hardness, Vickers: 401
$ 1607/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 1085 MPa
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %
- Elongation at Break: 27.6 %
- Modulus of Elasticity: 218 GPa
$ 1890/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 36 %
- Modulus of Elasticity: 211 GPa
$ 1727/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Yield: 386 MPa @Strain 0.200 %
$ 1996/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 400 MPa @Strain 0.200 %
- Elongation at Break: 52 %
- Modulus of Elasticity: 208 GPa
$ 1860/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 845 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 36.9 %
- Modulus of Elasticity: 205 GPa
$ 1672/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Yield: 645 MPa @Strain 0.200 %
- Elongation at Break: 34.8 %
- Modulus of Elasticity: 205 GPa
$ 2378/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1015 MPa
- Tensile Strength, Yield: 445 MPa @Strain 0.200 %
- Elongation at Break: 22.2 %
- Modulus of Elasticity: 232 GPa
$ 1504/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 360 MPa @Strain 0.200 %
- Elongation at Break: 55 %
- Modulus of Elasticity: 208 GPa
$ 1608/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 883 MPa
- Tensile Strength, Yield: 399 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 1786/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 779 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 779 MPa @Thickness 19.0 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 834 MPa @Thickness 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 834 MPa @Thickness 19.0 mm, Temperature 260 °C
$ 1539/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Yield: 510 MPa @Strain 0.200 %
- Elongation at Break: 10.8 %
- Modulus of Elasticity: 232 GPa
$ 1515/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 261
- Hardness, Knoop: 277
- Hardness, Rockwell C: 25
- Hardness, Vickers: 269
$ 1454/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 310 MPa @Strain 0.200 %
- Elongation at Break: 65 %
- Reduction of Area: 68 %
$ 1519/MT
- Density: 8.25 g/cc
- Hardness, Brinell: 369 @Temperature 760 °C
- Hardness, Knoop: 403 @Temperature 760 °C
- Hardness, Rockwell B: 97 @Temperature 760 °C
- Hardness, Rockwell C: 40 @Temperature 760 °C
$ 1981/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 65 @Thickness 1.45 mm
- Hardness, Rockwell A: 65 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1247 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1276 MPa @Thickness 1.45 mm
$ 1717/MT
- Density: 8.47 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1557/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 503 MPa @Strain 0.200 %
$ 1555/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 780 MPa
- Tensile Strength, Yield: 360 MPa @Strain 0.200 %
- Elongation at Break: 32.8 %
- Modulus of Elasticity: 205 GPa
$ 1764/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 634 MPa @Thickness 23.4 mm, Temperature 400 °C
- Tensile Strength, Ultimate: 634 MPa @Thickness 46.1 mm, Temperature 400 °C
$ 1583/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 784 MPa
- Tensile Strength, Yield: 429 MPa @Strain 0.200 %
- Elongation at Break: 48 %
- Modulus of Elasticity: 211 GPa
$ 2257/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 348
- Hardness, Knoop: 378
- Hardness, Rockwell C: 37.6
- Hardness, Vickers: 364
$ 1712/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 269
- Hardness, Knoop: 300
- Hardness, Rockwell C: 27.8
- Hardness, Vickers: 286
$ 1453/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 55 @Thickness 1.45 mm
- Hardness, Rockwell A: 55 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 867 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 898 MPa @Thickness 1.45 mm
$ 1630/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1324 MPa
- Tensile Strength, Yield: 1200 MPa @Strain 0.200 %
$ 1559/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Yield: 470 MPa
- Elongation at Break: 23 %
- Reduction of Area: 31 %
Delivery Superalloy Haynes International, Inc.
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.