Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) price 1762 per MT

Physical Properties
Density
8.86 g/cc

Mechanical Properties
Tensile Strength, Ultimate
793 MPa
Tensile Strength, Ultimate
453 MPa @Temperature 760 °C
Tensile Strength, Yield
301 MPa @Strain 0.200 %
Elongation at Break
40 %
Elongation at Break
20 % @Temperature 760 °C
Modulus of Elasticity
122 GPa @Temperature 1049 °C
Modulus of Elasticity
136 GPa @Temperature 1000 °C
Modulus of Elasticity
143 GPa @Temperature 954 °C
Modulus of Elasticity
151 GPa @Temperature 904 °C
Modulus of Elasticity
157 GPa @Temperature 854 °C
Modulus of Elasticity
163 GPa @Temperature 800 °C
Modulus of Elasticity
171 GPa @Temperature 700 °C
Modulus of Elasticity
181 GPa @Temperature 577 °C
Modulus of Elasticity
181 GPa @Temperature 632 °C
Modulus of Elasticity
187 GPa @Temperature 500 °C
Modulus of Elasticity
192 GPa @Temperature 410 °C
Modulus of Elasticity
202 GPa @Temperature 221 °C
Modulus of Elasticity
219 GPa @Temperature 14.0 °C

Thermal Properties
CTE, linear
12.3 µm/m-°C @Temperature 21.0 - 316 °C
CTE, linear
12.7 µm/m-°C @Temperature 21.0 - 427 °C
CTE, linear
13.4 µm/m-°C @Temperature 21.0 - 538 °C
CTE, linear
14.0 µm/m-°C @Temperature 21.0 - 649 °C
CTE, linear
14.7 µm/m-°C @Temperature 21.0 - 760 °C
CTE, linear
15.3 µm/m-°C @Temperature 21.0 - 871 °C
CTE, linear
15.8 µm/m-°C @Temperature 21.0 - 982 °C
Specific Heat Capacity
0.419 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.440 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.456 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.469 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.477 J/g-°C @Temperature 480 °C
Specific Heat Capacity
0.485 J/g-°C @Temperature 540 °C
Specific Heat Capacity
0.523 J/g-°C @Temperature 570 °C
Specific Heat Capacity
0.565 J/g-°C @Temperature 590 °C
Specific Heat Capacity
0.578 J/g-°C @Temperature 680 °C
Specific Heat Capacity
0.578 J/g-°C @Temperature 700 °C
Specific Heat Capacity
0.582 J/g-°C @Temperature 660 °C
Specific Heat Capacity
0.586 J/g-°C @Temperature 620 °C
Thermal Conductivity
11.5 W/m-K
Thermal Conductivity
13.1 W/m-K @Temperature 100 °C
Thermal Conductivity
13.1 W/m-K @Temperature 200 °C
Thermal Conductivity
14.4 W/m-K @Temperature 300 °C
Thermal Conductivity
16.5 W/m-K @Temperature 400 °C
Thermal Conductivity
18.0 W/m-K @Temperature 500 °C
Thermal Conductivity
20.3 W/m-K @Temperature 600 °C
Thermal Conductivity
23.6 W/m-K @Temperature 700 °C
Melting Point
1300 - 1400 °C
Solidus
1300 °C
Liquidus
1400 °C

Component Elements Properties
Al + Ti
<= 0.50 %
Carbon, C
<= 0.080 %
Chromium, Cr
7.0 %
Cobalt, Co
<= 0.20 %
Copper, Cu
<= 0.35 %
Iron, Fe
<= 5.0 %
Manganese, Mn
<= 0.80 %
Molybdenum, Mo
16 %
Nickel, Ni
71 %
Silicon, Si
<= 1.0 %
Tungsten, W
<= 0.50 %

Electrical Properties
Electrical Resistivity
0.000120 ohm-cm
Electrical Resistivity
0.000124 ohm-cm @Temperature 815 °C
Electrical Resistivity
0.000126 ohm-cm @Temperature 705 °C

Alternative products

Crucible Compaction Metals P/M 625 Corrosion Resistant Alloy accurate 89%

$ 1926/MT

Environmental Stress Crack Resistance: 336 hour
Environmental Stress Crack Resistance: 720 hour
Environmental Stress Crack Resistance: 4320 hour
Tensile Strength, Ultimate: 850 MPa
Tensile Strength, Ultimate: 1010 MPa

Carlson C 201 Commercially Pure Nickel accurate 69%

$ 1760/MT

Density: 8.89 g/cc
Tensile Strength at Break: >= 379 MPa
Tensile Strength, Yield: >= 82.7 MPa @Strain 0.200 %
Elongation at Break: >= 40 %
Modulus of Elasticity: 193 GPa

Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW accurate 79%

$ 1561/MT

Density: 8.64 g/cc
Tensile Strength, Ultimate: 777 MPa
Tensile Strength, Ultimate: 602 MPa @Temperature 538 °C
Tensile Strength, Ultimate: 654 MPa @Temperature 260 °C
Tensile Strength, Yield: 471 MPa @Strain 0.200 %

Carlson C 200 Commercially Pure Nickel accurate 69%

$ 1560/MT

Density: 8.89 g/cc
Tensile Strength at Break: >= 379 MPa
Tensile Strength, Yield: >= 103 MPa @Strain 0.200 %
Elongation at Break: >= 40 %
Modulus of Elasticity: 193 GPa

Haynes Hastelloy® N, weld metal as welded accurate 99%

$ 2254/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Ultimate: 507 MPa @Temperature 649 °C
Elongation at Break: 39.3 %
Elongation at Break: 18.1 % @Temperature 649 °C

ATI Allegheny Ludlum Stainless Steel 334 (UNS S33400) accurate 69%

$ 1629/MT

Density: 8.03 g/cc
Hardness, Rockwell B: 82
Tensile Strength, Ultimate: 572.4 MPa
Tensile Strength, Ultimate: 103.4 MPa @Temperature 982 °C
Tensile Strength, Ultimate: 469 MPa @Temperature 538 °C

Special Metals NIMONIC® Alloy 81 accurate 89%

$ 1911/MT

Density: 8.06 g/cc
Tensile Strength, Ultimate: 830 MPa @Temperature 650 °C
Tensile Strength, Ultimate: 1050 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 600 MPa @Strain 0.200 %
Tensile Strength, Yield: 520 MPa @Strain 0.200 %, Temperature 650 °C

Crucible Steel 20 Cb Plus Stainless Steel accurate 69%

$ 1991/MT

Density: 8.05 g/cc
Hardness, Brinell: 179
Tensile Strength, Ultimate: 655 MPa
Tensile Strength, Ultimate: 200 MPa @Temperature 871 °C
Tensile Strength, Ultimate: 572 MPa @Temperature 204 °C

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 79%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)

Seller from Madrid – 2021-02-27:

Seller from Madrid work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2587 per MT

Seller from Monterrey – 2021-07-24:

Seller from Monterrey work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1949 per MT

Seller from Chittagong – 2021-05-06:

Seller from Chittagong work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1762 per MT

Seller from Tehran – 2021-03-28:

Seller from Tehran work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2306 per MT